• 대한기계학회논문집A
• /
• 제21권9호
• /
• pp.1507-1519
• /
• 1997

This paper aims to clarify the effects of grinding conditions on bending strength in surface grinding of various ferrites with the resin bond diamond wheel. The main conclusions obtained were as follows. At a constant material removal rate, the strength improves with increased wheel depth of cut and decreased workpiece speed. It is desirable to grind at higher peripheral wheel speed and under the critical workpiece speed presented in this paper. Grinding the ferrite of higher brittleness, the wheel depth of cut limited to hold 50% of their inherent strength becomes lower. The effect of various grinding conditions on bending strength becomes more larger in the order of Sr, Mn-Zn and Cu-Ni-Zn. When using the diamond grain of the lower toughness, the bending strength becomes higher, and the wheel wear occurs faster. Considering both bending strength and wheel wear rate, the best concentration of wheel is 100. The ground surfaces exhibit that the fracture process during grinding becomes more brittle in the order of Sr, Mn-Zn and Cu-Ni-Zn.

• 한국전자파학회논문지
• /
• 제17권4호
• /
• pp.330-334
• /
• 2006

본 논문에서 Sendust, Mn-Zn, Ni-Zn, Ba, Sr Ferrite를 사용하여 페인트형 흡수체를 제작하였다. 지지재로서는 enamel, epoxy, urethane 페인트들을 사용하여 각각 흡수능을 측정하였다. 그리고 $Al(OH)_3$으로 코팅한 흡수체의 대역폭은 코팅을 하지 않은 것보다 더 넓어지는 것을 알 수 있다. 또 2 mm 두께의 적층형 흡수체는 X-band에서 대략 20 dB의 흡수능을 보여준다.

• 자원리싸이클링
• /
• 제12권6호
• /
• pp.26-31
• /
• 2003

소성온도를 $1150∼1320 ^{\circ}C$ 영역에서 변화시킨 결과 1MHz-25mT조건에서 전력손실의 절대값이 감소하였으며, 전력손실의 온도의 존성이 소성온도에 따라 다르게 관찰되었다 $1150 ^{\circ}C$에서 소성한 경우 전력손실의 최소가 나타나는 온도가 자기이방성 상수가 "0"이 되는 특정 온도에서 나타나지 않고 측정 온도가 증가함에 따라 증가되는 경향을 보였다. 이러한 원인은 1MHz 대역에서는 grain size에 따라 residual loss가 발생기구가 상이하기 때문으로 판단된다. $1150^{\circ}C$ 소성시 서로 다른 평형산소분압을 이용하여 분위기를 조정한 결과 산소분압이 증가됨에 따라 grain size 와 밀도가 미소하게 증가되는 경향을 보였다. 비저항과 투자율은 115$0^{\circ}C$ 소성시 평형산소분압에 따라 특정한 경향성을 나타내지 않았는데 이는 $Fe^{2+}$ 농도 변화이외에 미세구조의 변화를 동반하였기 때문으로 판단된다. 평형산소분압이 상대적으로 높게 유지된 시편의 경우 $100^{\circ}C$에서 상대적으로 낮은 전력손실값을 나타내었다.서 상대적으로 낮은 전력손실값을 나타내었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.247-250
• /
• 1999

In this study, three kinds of Mn-Zn ferrite/Ni-Zn ferrite/$Ni_2Y$ ferroxplana prepared by the coprecipitation method was compounded with silicon rubber, and thereafter made ring-type specimens with various compositional ratio. The material constant of ferrite/rubber composite absorbers was obtaibed by the 2-port method. The material constants of the ferrite/rubber composite absorber with various compositional ratio of three kinds of ferrite were used to design the matching frequency and thickness with the impedance matching map. We were able to predict the matching condition from the design method.

• 한국정보통신학회:학술대회논문집
• /
• 한국해양정보통신학회 2000년도 춘계종합학술대회
• /
• pp.109-114
• /
• 2000

본 연구에서는 전파흡수체용 ferrite-Rubber Composite에서 Ferrite의 열처리 온도와 Composite의 전파흡수특성과의 상관관계에 관하여 알아보았다. 이때 Ferrite는 스피넬 구조의 형성과 결정입의 비교적 큰 성장을 위하여 1100, 1200, 1300 $^{\circ}C$에서 각각 2시간 열처리 처리하였다. 열처리 온도를 달리하여 제조한 Ferrite-Rubber Composite는 A가 Mn인 경우에는 열처리 온도가 높을수록 반사감쇠량이 작아지는 경향을 보였다. 그러나 A가 Cu와 Mg인 경우 열처리 은도가 높을수록 페라이트의 반사감쇠량이 커지는 경향을 보였다. 이로부터 전파흡수체용 Ferrite는 화학조성에 따라서 적정 열처리 온도가 존재함을 알 수 있었다.

• Journal of Magnetics
• /
• 제19권3호
• /
• pp.210-214
• /
• 2014

The effects of manganese substitution on the crystallographic and magnetic properties of Li-Zn-Cu ferrite, $Li_{0.5}Zn_{0.2}Cu_{0.4}Mn_xFe_{2.1-x}O_4$ ($0.0{\leq}x{\leq}0.8$), were investigated. Ferrites were synthesized via a conventional ceramic method. We confirmed the formation of crystallized particles using X-ray diffraction, field emission scanning electron microscopy and $M{\ddot{o}}ssbauer$ spectroscopy. All of the samples showed a single phase with a spinel structure, and the lattice constants linearly decreased as the substituted manganese content increased, and the particle size of the samples also somewhat decreased as the doped manganese content increased. All the $M{\ddot{o}}ssbauer$ spectra can be fitted with two Zeeman sextets, which are the typical spinel ferrite spectra of $Fe^{3+}$ with A- and B-sites, and one doublet. The cation distribution was determined from the variation of the $M{\ddot{o}}ssbauer$ parameters and of the absorption area ratio. The magnetic behavior of the samples showed that an increase in manganese content led to a decrease in the saturation magnetization, whereas the coercivity was nearly constant throughout. The maximum saturation magnetization was 73.35 emu/g at x = 0.0 in $Li_{0.5}Zn_{0.2}Cu_{0.4}Mn_xFe_{2.1-x}O_4$.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1975년도 제6차 하계학술발표회 및 산학협동세미나 초록
• /
• pp.85-91
• /
• 1975

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 1993년도 제4회 학술발표회 논문개요집
• /
• pp.81-81
• /
• 1993

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2008년도 Asian Magnetics Conference
• /
• pp.235.1-235.1
• /
• 2008

• 한국세라믹학회지
• /
• 제34권6호
• /
• pp.561-568
• /
• 1997

The effects of sintering temperature and oxygen partial pressure on the electromagnetic properties of Mn-Zn ferrites were investigated. The grain increased with increasing temperature. The power loss at 100 kHz was decreased, while the power loss at 500 kHz was increased as the grain size increased with sintering temperature. Sintering with low oxygen partial pressure at 115$0^{\circ}C$ resulted in high density and initial permeability, and decreased the power loss at 100 kHz and 500 kHz. The oxygen partial pressure lower than 10-2 atm. during heating, significantly suppressed the hysteresis loss. However, the oxygen activity did not affect the grain size of sintered cores.