• Journal of the Korea Concrete Institute
• /
• v.21 no.4
• /
• pp.501-511
• /
• 2009

This study was conducted to develop self-healing ability of concrete so that inspection could be available even in the event of minute cracks without complex works at any time for more economic concrete structure maintenance and longevity. A completely different method has been carried out in comparison with many of similar researches on self-healing concrete. This is a basic study on the development of self-healing concrete using microbial biomineralization. Compounds were generated except for cells by precipitation reaction of CaC$O_3$ during the microbial metabolism and we examined the use as a binder that hardens the surface of sand using biomineralization that Sporosarcina pasteurii precipitates CaC$O_3$. In result, the formation of new mineral and hardening of sand surface could be verified partly, and it was available for cracks to be repaired by calcite with organic (microorganism) and inorganic (CaC$O_3$) complex structure through the basic experiment a little bit. Therefore the use of biomineralization by this sort of microbial metabolism for concrete structure helps to develop absolute repair-concrete like this concrete with microorganism. The effect of microbial application will be one of the most important research tasks having influence on not only repair for concrete structure but also development of new materials able to reduce environmental problems.

• Applied Chemistry for Engineering
• /
• v.20 no.6
• /
• pp.638-645
• /
• 2009

High alumina refractory used in a coal gasifier was analyzed and the degradation mechanism by molten slag was investigated. The depth of refractory severely damaged by slag varied between 12~40 mm, including the adhered slag layer. The sample also showed the cracks formed in parallel to the slag/refractory interface. The degree of degradation varied with the micro-structures in the refractory. Fused alumina grains showed the uneven boundary and pore formation just along the edges, while the tablet alumina showed the slag penetrated between sintered alumina around which the formation of Al-Fe phase was observed. Calcium aluminate cements were not observed at the high temperature zone near the slag/refractory interface, probably due to dissolution into molten slag. Around large grains of alumina, rod shape alumina, which appeared to be recrystallized during cooling, were observed, and large pores were also formed around those grains. Therefore, in high alumina refractories, hot molten slag dissolves the bonding phase and rod-shape alumina phase is recrystallized upon cooling. During this process, cracks are developed due to structural change, and the degradation occurs by physical causes such as structural spalling.

• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.3
• /
• pp.69-75
• /
• 2016

This study investigated the effect of heat treatment conditions not only on the Cr surface crack propagation behaviors but also on the Ni/Cr interfacial reaction characteristics in electroless Ni/electroplated Cr double coating layers on Cu substrate. Clear band layer of Ni-Cr solid solutions were developed at Ni/Cr interface after heat treatment at $750^{\circ}C$ for 6 h. Channeling cracks formed in Cr layer after 1 step heat treatment, that is, heat treatment after Ni/Cr plating, while little channeling cracks formed after 2 step heat treatment, that is, same heat treatments after Ni and Cr plating, respectively, due to residual stress relaxation due to crystallization of Ni layer before Cr plating.

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.213-213
• /
• 2000

This study was performed to investigate types and formation mechanism of cracks in two Al alloy welds, A5083 and A7NO1 spot-welded by pulse Nd: YAG laser, using SEM, EPMA and Micro-XRD. In the weld zone, three types of crack were observed: center line crack($C_{C}$), diagonal crack($C_{D}$), and U shape crack($C_{U}$). Also, HAZ crack($C_{H}$), was observed in the HAZ region, furthermore, mixing crack($C_{M}$), consisting of diagonal crack and HAZ crack was observed.White film was formed at the hot crack region in the fractured surface after it was immersed to 10%NaOH water. In the case of A5083 alloy, white films in C crack and $C_D crack region were composed of low melting phases, Fe₂Si$Al_8$ and eutectic phases, Mg₂Al₃ and Mg₂Si. Such films observed near HAZ crack were also consist of eutectic Mg₂Al₃. In the case of A7N01 alloy, eutectic phases of CuAl₂, $Mg_{32}$ (Al,Zn) ₃, MgZn₂, Al₂CuMg and Mg₂Si were observed in the whitely etched films near $C_{C}$ crack and $C_{D}$ crack regions. The formation of liquid films was due to the segregation of Mg, Si, Fe in the case of A5083 alloy and Zn, Mg, Cu, Si in the case of A7N01 aooly, respectively.The $C_{D}$ and $C_{C}$ cracks were regarded as a result of the occurrence of tensile strain during the welding process. The formation of $C_{M}$ crack is likely to be due to the presence of liquid film at the grain boundary near the fusion line in the base metal as well as in the weld fusion zone during solidification. The $C_{U}$ crack is considered a result of the collapsed keyhole through incomplete closure during rapid solidification. (Received October 7, 1999)

• Journal of the Korean Geosynthetics Society
• /
• v.17 no.4
• /
• pp.169-177
• /
• 2018

Glass fiber reinforced polyester (GFRP) composites are widely used as structural materials in harsh environment such as underground pipes, tanks and boat hulls, which requires long-term water resistance. Especially, these materials might be damaged due to delamination between gelcoat and composites through an osmotic process when they are immersed in water. In this study, GFRP laminates were prepared by surface treatment of UPE (unsaturated polyester) gelcoat by vacuum infusion process to improve the durability of composite materials used in underground pipes. The composite surface coated with gelcoat was examined for surface defects, cracking, and hardness change characteristics in water-immersion environments (different temperatures of $60^{\circ}C$, $75^{\circ}C$, and $85^{\circ}C$). The penetration depth of cracks was investigated by micro CT imaging according to water immersion temperature. It was confirmed that cracks developed into the composites material at $75^{\circ}C$ and $85^{\circ}C$ causing loss of durability of the materials. The point at which the initial crack initiated was defined as the failure time and the life expectancy at $23^{\circ}C$ was measured using the Arrhenius equation. The results from this study is expected to be applied to reliability evaluation of various industrial fields where gelcoat is applied such as civil engineering, construction, and marine industry.

• Journal of the Korean Geosynthetics Society
• /
• v.23 no.2
• /
• pp.1-7
• /
• 2024

Various innovative technologies and methods are being applied to ensure the stability of steep rock slopes. However, there are design limitations concerning site ground conditions, leading to discrepancies between the designed and actual ground conditions during construction. In the case of the retaining wall in Yeosu, where the study area is located, although the construction of a 5-stage retaining wall is planned, at the current completion of the second stage, cracks on the upper part of the wall, settlement in the front of the wall, and seepage have been observed. After the completion of stages one and two, issues regarding cracks and settlement on the upper part of the wall and seepage in the front of the wall were discovered. Thus, there was a need to reevaluate the results of the existing stability assessment. It was confirmed that the issue was due to groundwater leakage, attributed to the lack of clear assessment of the colluvial soil layer during the initial design stage. Therefore, to conservatively reflect groundwater level conditions, a groundwater level contour was positioned at the top of the wall to conduct a slope stability assessment. The assessment results indicated that the safety factor during the rainy season exceeded the required value of 1.3, with a calculated safety factor of 1.31. However, during seismic events, the safety factor was determined to be 1.12, falling short of the required safety factor of 1.3. Therefore, it is suggested that the existing retaining walls constructed during stages one and two undergo reinforcement using methods such as micro-piles with grouting, and additional work should be carried out to ensure a clear assessment of the colluvial soil layer.

• Restorative Dentistry and Endodontics
• /
• v.33 no.6
• /
• pp.507-517
• /
• 2008

There are considerable in vitro and in vivo evidences for remineralization and demineralization occurring simultaneously in incipient enamel caries. In order to "heal" the incipient dental caries, many experiments have been carried out to determine the optimal conditions for remineralization. It was shown that remineralization is affected by different pH, lactic acid concentrations, chemical composition of the enamel, fluoride concentrations, etc. Eighty specimens from sound permanent teeth without demineralization or cracks, 0.15 mm in thickness, were immersed in lactic acid buffered demineralization solutions for 3 days. Dental caries with a surface zone and subsurface lesion were artificially produced. Groups of 10 specimens were immersed for 10 or 12 days in lactic acid buffered remineralization solutions consisting of pH 4.3 or pH 6.0, and 100, 50, 25, or 10 mM lactic acid. After demineralization and remineralization, images were taken by polarizing microscopy (${\times}100$) and micro-computed tomography. The results were obtained by observing images of the specimens and the density of the caries lesions was determined. 1.As the lactic acid concentration of the remineralization solutions with pH 4.3 was higher, the surface zone of the carious enamel increased and an isotropic zone of the subsurface lesion was found. However, the total decalcification depth increased at the same time. 2.In the remineralization solutions with pH 6.0, only the surface zone increased slightly but there was no significant change in the total decalcification depth and subsurface zone. In the lactic acid buffer solutions with the lower pH and higher lactic acid concentration, there were dynamic changes at the deep area of the dental carious lesion.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.6
• /
• pp.178-184
• /
• 2017

This study was aimed to investigate the tensile behaviors of PE(Polyethylene) fiber-reinforced highly ductile cementitious composites with different combinations of micro silica sand and normal sand(river sand) with maximum particle size of 4.75 mm. Flow test result indicated the increase of flowability with higher replacement ratio of river sand. There was no noticeable difference in the mean compressive strength with different replacement ratio of river sand, but the variation in the compressive strength increased as higher amount of river sand was adopted for the replacement. The difference in the uniaxial tensile strength was negligible, but the tensile strain capacity was significantly influenced by the replacement ratio of river sand. It is thought that increased density of multiple cracks induced improved tensile strain capacity when higher percentage of river sand was adopted for fine aggregate. The deviation in the strain capacity increased as the replacement ratio of river sand was higher, as in the compressive strength. This study presented the feasibility of using normal sand instead of micro silica sand for highly ductile cementitious composites with equivalent or better uniaxial tensile performance, even though it might increase the deviation in the performance.

• Restorative Dentistry and Endodontics
• /
• v.26 no.5
• /
• pp.372-378
• /
• 2001

The aim of this in vitro study was to analyze the composition of human tooth enamel in terms of three components, Ca, P, and F after demineralization and remineralization in acid buffer solution. A total of 8 human premolars without any defects and cracks were selected and buccal and lingual sides of the teeth were cleaned with an ultrasonic device and pumice without fluoride 5$\times$5mm windows were opened, and other areas were completely covered with 3-coats of nail varnish to prevent from being in contact with demineralized and remineralized solutions. After demineralization process, each tooth was sectioned into two slices, highly polished one of them with$\gamma$-alumina, and then analyzed the composition of the demineralized tooth with EPMA(electron probe micro-analyzer). The other slices were put into the remineralized solution for 10 days, polished, and analyzed in the same manner. These data were statistically analyzed with one sample t-test(p<0.05). The results were as follows. 1. Normal tooth enamel consists of 49.76% Ca, 39.80% P, and 0.28% F. 2. After demineralization, percentage of Ca and P ratio were decreased by about 5.57 and 5.07% respectively. Percentage of F ratio was also decreased by about 0.01%, which was not statistically significant. 3. After remineralization, percentage of Ca, P increased about by 4.47 and 4.35% respectively Percentage of F decreased by about 0.01%, which was not statistically significant. In conclusion, remineralized solution used in our study has the potential to induce the uptake the Ca and P into the pore sites of the demineralized enamel. But, in the oral cavity. there were rapid temperature change, organic matrix that inhibits the movement of the ions, and limitation of continuous contact with this remineralized solution. Therefore, further in vivo study is necessary.

• Journal of the Korean Geotechnical Society
• /
• v.23 no.12
• /
• pp.25-32
• /
• 2007

This study is to evaluate the effect of chemical attack on durability and deterioration of lining concrete in tunnel. Surface examination, nondestructive inspection, uniaxial compressive strength test, carbonation test, chloride diffusion test, micro-structural analysis were performed to analyze the deterioration of lining concrete in tunnel constructed 70 years ago. From surface examination results, the tunnel had been repaired and reinforced in several times. It has many cracks, water-leakage, efflorescence and exploitation. Compressive strengths obtained from nondestructive inspection and uniaxial compressive strength test have measured $17.5{\sim}34.7MPa$, and $12.8{\sim}40.3MPa$, respectively. Carbonation depth specimen cored from concrete lining has ranged from 3mm to 27mm. From chloride diffusion test, most specimens have low permeability. And the XRD analysis was able to detect ettringite and thaumasite, which were confirmed by SEM and EDS results to be the causes for the deterioration of lining concrete.