• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.6
• /
• pp.332-336
• /
• 2016

In this study, in order to develop the composition ceramics for ultrasonic sensor with high $d_{33}*g_{33}$, $Pb_{1-3x/2}Bix(Mg_{1/2}W_{1/2})_{0.03}(Ni_{1/3}Nb_{2/3})_{0.09}(Zr_{0.5}Ti_{0.5})_{0.88}O_3$(PMW-PNN-PZT) system ceramics were prepared using CuO as sintering aids. And then, their microstructure, piezoelectric and dielectric characteristics were systemetically investigated with bismuth substitution. The PMW-PNN-PZT ceramic specimens could be sintered at sintering temperature of $940^{\circ}C$ by adding sintering aids. At x=0.015 specimen, the density, electromechanical coupling factor($k_p$), dielectric constant, piezoelectric constant($d_{33}$) and piezoelectric figure of merit($d_{33}*g_{33}$) indicated the optimal properties of $7.90g/cm^3$, 0.67, 2,511, 628 pC/N, and $17.7pm^2/N$, respectively, for duplex ultrasonic sensor application.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.9
• /
• pp.577-580
• /
• 2015

In this paper, in order to develop the composition ceramics with the outstanding piezoelectric properties, $Pb(Mg_{1/2}W_{1/2})_{0.03}(Ni_{1/3}Nb_{2/3})_{0.09}(Zr_{0.5}Ti_{0.5})_{0.88}O_3$ ceramics substituted with $BiFeO_3$ were prepared by the conventional solid-state reaction method. The addition of small amount of $Li_2CO_3$ and $CaCO_3$ as sintering aids decreased the sintering temperature of the ceramics. The effects of $BiFeO_3$ substitution on their piezoelectric and dielectric properties were investigated. when 0.015 mol $BiFeO_3$ was substituted, the optimal physical properties of $d_{33}=590pC/N$, $E_c=8.78kV/mm$ were obtained.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.9
• /
• pp.2565-2570
• /
• 2010

The orthorhombic $MgB_2C_2$ structure contains well-separated parallel graphite-like $B_2C_2^{2-}$ layers which extend infinitely in two dimensions. Three possible ways to distribute B and C atoms in the hexagonal sublattice sites are adopted. Band structures for the hypothetical distribution patterns are examined to assess the electronic stability of these phases and to account for the observed arrangement by means of extended Huckel tight-binding calculations. The preferred choice is the layer with B and C alternating strictly so that B is nearest neighbor to C and vice versa. A rationale for this is given. Due to the alternation of B and C within the honeycomb layers, $MgB_2C_2$ is a band insulator, which through partial substitution of Mg with Li, is predicted to turn metallic with holes in the $\sigma$ bands at the Fermi level.

• Biomolecules & Therapeutics
• /
• v.1 no.1
• /
• pp.20-25
• /
• 1993

DA-125, a new anthracycline derivative, shows significant anticancer activities. We conducted a study to examine the local irritating effect of DA-125 using mice and rabbits. In the skin test in mice, intradermal injection of 0.4 mg of DA-125, compared to a dosage of 0.2 mg of adriamycin, had weak irritating potentials to induce skin ulceration and erythematous induration. A dosage of 0.6 mg of DA-125 produced similar degree of lesions in perivascular irritation model to that of 0.2 mg of adriamycin, but the healing time was shorter in the case of mice treated with DA-125. In ocular irritation study in rabbit, the highest M.O.I.(mean ocular irritation index) of 0.5% DA-125 solution was 0.67, therefore DA-125 could be considered as a practically non-irritating anticancer agent. These results suggest that substitution of DA-125 for Adriamycin would reduces the possibility of outbreaks of local irritation and the severity of the lesions.

• Progress in Superconductivity
• /
• v.12 no.1
• /
• pp.36-40
• /
• 2010

We have studied the anisotropy of the London penetration depth of carbon doped $MgB_2$ single crystals, which was obtained from reversible magnetization measurements with the magnetic field both parallel and perpendicular to the c-axis. Similar to the pure $MgB_2$, the anisotropy of the upper critical field ${\gamma}_H$ decrease with temperature while the anisotropy of the London penetration depth ${\gamma}_{\lambda}$ slowly increases with temperature. However, the temperature dependence of ${\gamma}_H$ is drastically reduced and the value of ${\gamma}_{\lambda}$ becomes nearly ~1 as C is introduced. These results indicate that C substitution increases impurity scattering mainly in the $\sigma$ bands. The temperature dependence of the anisotropies agree well with the theoretical predictions with impurity scattering.

• Progress in Superconductivity
• /
• v.10 no.1
• /
• pp.40-44
• /
• 2008

A combined process of a mechanical ball milling and liquid glycerin ($C_{3}H_{8}O_3$) treatment of boron (B) powder has been conducted to enhance the superconducting properties of $MgB_2$. The individual aims of the mechanical milling and the glycerin treatment were to reduce the grain size of the $MgB_2$ and to achieve homogeneous carbon (C) incorporation into the $MgB_2$, respectively. Four kinds of B powders of as-received, glycerin treated, 2 h milled, and 2 h milled + glycerin treated were prepared. $MgB_2$ bulks were fabricated by in situ process using the prepared B powders. The mechanical ball milling was effective for a grain refinement, and a lattice disorder was easily achieved by glycerin addition. It was found that the critical current density ($J_c$) values were enhanced in the samples with milled B or glycerin treated B only. In the $MgB_2$ bulk prepared with both milled and glycerin treated B, the $J_c$ was further increased due to a higher grain boundary density and a greater C substitution.

• Proceedings of the KIEE Conference
• /
• 1991.11a
• /
• pp.293-295
• /
• 1991

In this study, we investigated the possibilty that $Pb(Mg_{1/3}Nb_{2/3})O_3-PbTiO_3-PbZrO_3$ ceramics with strontium substitutions could be used for piezoelectric sounders. Piezoelectric buzzer is one of them. By partially substituting Sr for Ph, dielectric constants had values greater than 2000, the value proper piezoelectric buzzer, piezoelectric constant($d_{31}$) had a maximum value, 298 $[10^{-12}C/N]$, at the Sr 5 mol % substitution. Sound level of piezoelectric buzzer had the highest value of 91 dB at the Sr 5 mol % substitution.

• Journal of Information Display
• /
• v.13 no.3
• /
• pp.97-100
• /
• 2012

We have conducted two kinds of the so-called charge-compensated aliovalent element substitutions to control the photoluminescence properties of $NaAlSiO_4:Eu^{2+}$ with a special focus on the enhancement of the excitation intensity at 400 nm. The aliovalent element substitutions include cation-cation and cation-anion co-substitutions according to the general formulas $Na_{1-x}M_xAl_{1+x}Si_{1-x}O_4:Eu^{2+}$ and $Na_{1-x}M_xAlSiO_{4-x}N_x:Eu^{2+}$ (M = $Mg^{2+}$, $Ca^{2+}$, and $Sr^{2+}$), respectively. The increase in the relative excitation intensity at 400 nm has been achieved in both types of the co-substitutions. Thus, the present research has demonstrated the effectiveness of the charge-compensated element substitution.

• Journal of the Korean Ceramic Society
• /
• v.27 no.8
• /
• pp.979-990
• /
• 1990

The possible use of bioglass as implant materials is due to its biocompatibility to human body. Even if many animal studies for the bioglasses have been performed, their structures and physical properties are not fully understood. In the present work, several investigations such as Raman spectroscopic analysis, density, thermal expansion coefficient, softening temperature, and refractive index measurement were carried out to find the structures and physical properties of bioglasses, where MgO is substituted for CaO in bioglass composition (46.1%SiO2, 24.4%Na2O, 26.9%CaO, 2.6%P2O5 ; mole%). Hydroxyapatite formation on the glass surface reacted in Tris-buffer solution was also examined. When CaO was replaced by MgO, nonbridging oxygen in glass structuer was diminished but the degree of disorder increased. Thermal expansion and softening properties showed the mixed oxide effect. Hydroxyapatite were formed on the surface of 0~11mole% of MgO containing bioglasses, and the thickness of SiO2-rich layer as well as hydroxyapatite layer were unchanged with MgO content. However, the hydroxyapatite was not formed on the surface of the bioglasses containing over 11 mole percent MgO, even if the glasses were reacted for long period.

• Journal of the Mineralogical Society of Korea
• /
• v.32 no.3
• /
• pp.223-234
• /
• 2019

The geology of the Samdeok Mo deposit consists of Paleozoic Hwajeonri formation, Kowoonri formation, Suchangri formation, Iwonri formation, Hwanggangri formation, Cretaceous, leucocratic porphyritic granite and granitic porphyry. This deposit consists of three quartz veins that filled NS oriented fractured zones in Suchangri formation. Quartz veins vary from 0.05 m to 0.3 m in thickness and extend to about 400 m in strike length. Quartz veins occur as massive, breccia, and cavity textures. Wallrock alteration has silicification, sericitization, argillitization and chloritization. The mineralogy of the quartz veins consists of quartz, fluorite, white mica, biotite, apatite, monazite, rutile, ilmenite, molybdenite, chalcopyrite, Fe-Mg-Mn oxide and Fe oxide. White mica from Samdeok Mo deposit occurs as fine or coarse grains in quartz vein and hostrock and has four mineral assemblages (I type: quartz, molybdenite, Fe oxide and Fe-Mg-Mn oxide, II type: quartz, Fe oxide and Fe-Mg-Mn oxide, III type: quartz and biotite, and IV type: quartz). The structural formular of white mica from quartz vein is $(K_{0.89-0.60}Na_{0.05-0.00}Ca_{0.01-0.00}Sr_{0.02-0.00})_{0.94-0.62}(Al_{1.54-1.12}Mg_{0.36-0.18}Fe_{0.26-0.09}Mn_{0.04-0.00}Ti_{0.02-0.00}Cr_{0.02-0.00}Zn_{0.01-0.00})_{1.91-1.72}(Si_{3.40-3.11}Al_{0.92-0.60})_{4.00}O_{10}(OH_{1.68-1.42}F_{0.58-0.32})_{2.00}$, but white mica of I type has higher FeO content, and lower $SiO_2$ and MgO contents than white micas of other types. Also, compositional variations in white mica from the Samdeok Mo deposit are caused by phengitic or Tschermark substitution ($(Al^{3+})^{VI}+(Al^{3+})^{IV}{\leftrightarrow}(Fe^{2+}{\text{ or }}Mg^{2+})^{VI}+(Si^{4+})^{IV}$) and direct $(Fe^{3+})^{VI}{\leftrightarrow}(Al^{3+})^{VI}$ substitution.