• Polymer(Korea)
• /
• v.33 no.2
• /
• pp.169-174
• /
• 2009

Silicone hydrogels incorporated with poly(ethylene glycol)(PEG) were prepared and characterized to evaluate the effects of PEG on contact lenses. The silicone hydrogels were copolymerized with methacryloxypropyl tris(trimethylsiloxy) silane (TRIS), methyl methacrylate (MMA), N,N-dimethyl acrylamide (DMA) and PEG-containing monomers such as poly(ethylene glycol) methyl ether methacrylate (PEG- MEM). The silicone hydrogels were characterized using Fourier transform infrared spectroscopy (FT-IR), electron spectroscopy of chemical analysis (ESCA), and scanning electron microscopy (SEM). Water absorbance, water contact angle and light transmittance of the silicone hydrogels were evaluated. The experiments of protein adsorption were also carried out to evaluate the protein adsorption in tears. The peak intensity of C-O bond was increased by the incorporation of PEG-containing monomers and thus PEG incorporation into silicone hydrogels could be confirmed. Phase separation was not shown by the SEM observation of the cross-section of silicone hydrogels. Water absorbancy was increased, while water contact angle and light transmittance were decreased with increasing incorporation of the PEG-containing monomers. The absorption of proteins in tears, albumin, lysozyme and $\gamma$-globulin, on the surface of silicone hydrogels was decreased with increasing incorporation of the PEG-containing monomers.

• Korean Journal of Materials Research
• /
• v.14 no.11
• /
• pp.821-827
• /
• 2004

Titanium oxide thin films were prepared on Si(100) substrates by R.F. magnetron reactive sputtering at $30\sim200watt$ R.F power range, and annealed at $600^{\circ}C\sim800^{\circ}C$ for 1 hour. The properties of $TiO_2$ thin films were analyzed using x-ray, ${\alpha}-step$, ellipsometer, scanning electron microscopy, and FT-IR spectrometer. Upon in-situ depositions, the initial phase of $TiO_2$ thin film showed non-crystalline phase at R.F. power $30\sim100$ watt. The crosssection of $TiO_2$ thin films were sbserved to be the columnar structure. With the increasing R.F power and annealing temperature, the grain size, crystallinity, refractive index, and void size of titanium oxides showed a tended to increase. The FT-IR transmittance spectra of titanium oxide thin films have the obsorption band of Ti-O bond, Si-O bond, Si-O-Ti bond and O-H bond. With the increase of R.F. power and annealing temperature, these films have the stronger bond structures. It is considered that such a phenomena is due to phase transition and good crystallinity

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.419-420
• /
• 2008

In this work, we report several experimental data capable of evaluating the phase transition characteristics of (InTe)x(GeTe)y (x = 0.1, 0.3, y =1) pseudo-binary thin films. (InTe)x(GeTe)y phase change thin films have been prepared by thermal evaporator. The crystallization characteristics of amorphous (InTe)x(GeTe)y thin films were investigated by using nano-pulse scanner with 658 nm laser diode (power : 1~17 mW, pulse duration : 10~460 ns) and XRD measurement. It was found that the crystalline speed of In-Ge-Te thin films are faster than $Ge_2Sb_2Te_5$[1] and also the crystalline temperature is higher. Changes in the optical transmittance of as-deposited and annealed films were measured using a UV-VIS-IR spectrophotometer and four-point probe was used to measure the sheeresistance of InGeTe films annealed at different temperature.

• Solar Energy
• /
• v.14 no.2
• /
• pp.29-37
• /
• 1994

Radiative charaacteristics of glass windows and porous absorbing media which can be used for a solar air heater are determined through the measurements of spectral transmittances. Those in the visible range are measured by the UV-IR spectrometer. Refractive index of glass are obtained by the comparison of the measured transmittances and the correlations derived from the electromagnetic theory and are compared to the theoretical ones calculated from the classical dispersion theory. Absorption and back-scattering coefficients of 15-mesh stainless wire screens are calcuated by the comparison of the measured transmittances and the correlations derived from the two flux model.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.6
• /
• pp.1561-1567
• /
• 2021

In this study, we have studied synthesis of zirconia-alumina composite coating materials via a low-temperature sol-gel process. The zirconia-alumina composites were prepared by coating zirconia precursor, alumina precursor, and organosilane mixture on a polyethylene terephthalate substrate through three steps: sol-gel process, low-temperature photocuring process, and heat treatment process. The structural properties and element analysis of the composites were confirmed by FT-IR and XPS. The coated composite showed a transmittance of 96% or more in the visible light region with a wavelength of 420 nm or more and pencil hardness of 9H or more. In case of the composite of the molar ratio of zirconia and alumina of 1:4, the highest nanoindentation hardness was measured with 1.212 GPa.

• Journal of Korean Ophthalmic Optics Society
• /
• v.17 no.2
• /
• pp.135-141
• /
• 2012

Purpose: Polymerization of HEMA(2-hydroxyethyl methacrylate) which can be used in the soft contact lens has been performed by using electron beam(EB) irradiation, and examined the best condition for the polymerization. Comparing the physical properties of the contact lenses to the one fabricated by thermal polymerization method, we check the use possibility of the EB irradiation to the fabrication of the soft contact lens. Methods: We investigated the degree of polymerization of the HEMA according to the composition of the monomer, the additive ratio and the dose of electron beam (0~120 kGy). The degree of polymerization was measured depending on the EB dose to research the best synthetic condition under the EB irradiation. The physical properties of the contact lens such as water content(%), oxygen transmissibility(Dk/t) and optical transmittance were analysed by using the FT-IR results with comparing the two different polymerization method (thermal and electron beam polymerization) with same additive ratio. Results: When the dose of electron beam was above 100 kGy, the degree of polymerization of HEMA was above 99% with regardless using cross-linker and initiator. The water content of the lens fabricated by EB method showed 10% higher than the one by the thermal method which was 40%. The lens fabricated by EB method also showed higher oxygen transmissibility(Dk/t) as same with the water content, and showed twice higher value in the lens fabricated by pure HEMA. According to the FT-IR results, hydrophilic property of the lens fabricated by EB method was increased due to increasing the intermolecular hydrogen bonding. It showed above 90% optical transmittance in the visible range of wavelength on the contact lenses fabricated by the both of two different polymerization method. Conclusions: The polymerization of HEMA without cross-linker and initiator was successful above 100 kGy of EB irradiation. Moreover the lens fabricated from the polymer synthesized by pure HEMA with 100 kGy of EB showed the highest water content and oxygen transmissibility. Therefore EB irradiation is another possible method to synthesize the polymer which can be used for the soft contact lens.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2008.04a
• /
• pp.77-79
• /
• 2008

Polynitro fullerenes were synthesized by reaction C-60 in benzen solution with a mixture of NaNO$_2$ and HNO$_3$. Hydrolysis of polynitro fullerenes in aqueous NaOH gave the corresponding polyhydroxylated fullerenes. Sulfonation reaction was carried out in pyridine solution of ClSO$_3$H. Infrared spectra of the resultant fullerene derivatives showed the characteristic IR bands, corresponding to absorptions of O-H, N-O, and SO$_3$Na functions. Electric resistivity and thermal transmittance of wool fiber absorbed with the water-soluble C-60 were investigated. Thermal transmittances of wool fiber were increased with increasing water-soluble C-60 concentrations, but electric conductivity were decreased with raising water-soluble C-60 uptake values.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.4
• /
• pp.321-324
• /
• 2013

In this study, The RF magnetron sputter and evaporator was on glass substrates 30 mm ${\times}$ 30 mm OMO multilayer thin film structure is applied to the low-e. Structural and optical properties, a thin film was produced, the variable was placed into a variable deposition time of the oxide layer. According to the XRD measurement results there is no peak that satisfies the Bragg's law ($2dsin{\theta}=n{\lambda}$) which confirmed that it is an amorphous structure. RMS value of the results of the AFM measurement, has a roughness of less than 2 nm. transmittance measurements results, visible light region an average 80%, IR region 40% showed.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.9
• /
• pp.969-975
• /
• 2009

In this paper, bonded wafer analysis system is proposed using laser beam transmission; while the transmission model is derived by simulation. Since the failure of bonded wafer stems in void existence, transmittance deviations caused by the thickness of the void are analyzed and variations of the intensity through the void or defect easily have been recognized then the testing power has been increased. In addition, large screen display on laser study has been done which resulted in acquiring a feasible technique for analysis of the whole bonding surface. In this regard, three approaches are demonstrated in which Halogen lamp, IR lamp and laser have been tested and subsequently by results comparison the optimized technique using laser has been derived.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1991.10a
• /
• pp.63-67
• /
• 1991

Amorphous silicon films were deposited on glass, [100] single crystal silicon wafer with thermally grown silicon dioxide, and [100] silicon wafer substrates by Plasma Enhanced Chemical Vapor Deposition(with argon diluted silane source gas). Growth rate, UV optical band edge, and the hydrogen quantity in the amorphous silicon films have been investigated as a function of the preparation conditions by measuring film thickness, UV-absorbency, and FT-IR transmittance. The growth rate of the ${\alpha}$-Si:H films increases with increasing substrate temperture, flow rate and R.F. power density. The UV optical band edge shifts to blue with the increases in the deposition pressure. Increasing substrate temperature shifts the UV optical band edge of the films to red. Hydrogen quantity in the ${\alpha}$-Si:H films increases with an increases in the R.F. powr and decreases with an increase in the substrate temperature.