• The Korean Journal of Ceramics
• /
• v.6 no.3
• /
• pp.245-249
• /
• 2000

Consolidation of amorphous powders is emerging as a route for synthesis of high strength composite materials. Diffusion processes necessary for consolidation are expected to be more rapid in amorphous state(SRO) than in the crystalline state(LRO). A new synthesis technique of exploiting polymeric ceramic precursors(polysilazane and polyborosilazane) is derived for Si$_3$N$_4$/SiC and boron-modified nanocomposites for extremely high temperature applications up to 200$0^{\circ}C$. The characterization methods include thermal analysis of DTA, and XRD, NMR, TEM, after pyrolysis, as a function of time and temperature.

• Journal of the Mineralogical Society of Korea
• /
• v.11 no.2
• /
• pp.69-84
• /
• 1998

The Daehyun sericite deposit in socheon-myun, Bongwha-gun, Kyungsangbuk-do, Korea, has been formed by the hydrothermal alteration of the Hongjesa granite of Precambrian age, leaving the muscovite granite between ore body and the Hongjesa granite as the wall rock alteration zone. The process of sericitization of granitic rock as well as chemistry and structures of sericites were studied using polarizing microscope, X-ray diffractometer (XRD), electron probe microanalyzer (EPMA) and high resolution transmission electron microscope (HRTEM). There are two genetic types of sericites having different chemistry and structure. The early sericite is of 2M1 polytype and has octahedral composition close to muscovite. It has been formed from the primary muscovite, tourmaline and quartz under a relatively high temperature. The late sericite is of 1M, 2M1 and 3T polytypes and has phengitic composition. It has been formed form feldspar, biotite, muscovite and tourmaline under a relatively low temperature. Chemical analyses show t, the early sericite has less Mg+FeT content and lower Si/AlIV ratio in tetrahedral site than the late sericite.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.406-407
• /
• 2006

This paper describes the ohmic contact formation between a TiW film as a contact material deposied by RF magnetron sputter and polycrystalline 3C-SiC films deposied on thermally grown Si wafers. The specific contact resistance (${\rho}_c$) of the TiW contact was measured by using the C-TLM. The contact phase and interfacial reaction between TiW and 3C-SiC at high-temperature were also analyzed by XRD and SEM. All of the samples didn't show cracks of the TiW film and any interfacial reaction after annealing. Especially, when the sample was annealed at $800^{\circ}$ for 30min., the lowest contact resistivity of $2.90{\times}10^{-5}{\Omega}cm^2$ was obtained due to the improved interfacial adhesion.

• Journal of Korea Foundry Society
• /
• v.40 no.5
• /
• pp.129-133
• /
• 2020

The outcomes of solution annealing and stress corrosion cracking in cold-worked 316L austenitic stainless steel have been studied using x-ray diffraction (XRD) and the slow strain rate test (SSRT) technique. The good compatibility with a high-temperature water environment allows 316L austenitic stainless steel to be widely adopted as an internal structural material in light water reactors. However, stress corrosion cracking (SCC) has recently been highlighted in the stainless steels used in commercial pressurized water reactor (PWR) plants. In this paper, SCC and inter granular cracking (IGC) are discussed on the basis of solution annealing in a chloride environment. It was found that the martensitic contents of cold-worked 316L stainless steel decreased as the solution annealing time was increased at a high temperature. Moreover, mode of SCC was closely related to use of a chloride environment. The results here provide evidence of the vital role of a chloride environment during the SCC of cold-worked 316L.

• Journal of the Korean Ceramic Society
• /
• v.51 no.4
• /
• pp.271-277
• /
• 2014

To overcome the limitations of the solid oxide fuel cells (SOFCs) due to the high temperature operation, there has been increasing interest in proton conducting fuel cells (PCFCs) for reduction of the operating temperature to the intermediate temperature range. In present work, the perovskite $BaCe_{0.85-x}Zr_xY_{0.15}O_{3-\delta}$ (BCZY, x = 0.1, 0.3, 0.5, and 0.7) were synthesized via solid state reaction (SSR) and adopted as an electrolyte materials for PCFCs. Powder characteristics were examined using X-ray diffraction (XRD), thermogravimetric analysis (TGA) and Brunauer, Emmett and Teller (BET) surface area analysis. Single phase BCZY were obtained in all compositions, and chemical stability was improved with increasing Zr content. Anode-supported cell with $Ni-BaCe_{0.55}Z_{0.3}Y_{0.15}O_{3-\delta}$ (BCZY3) anode, BCZY3 electrolyte and BCZY3-$Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-\delta}$ (BSCF) composite cathode was fabricated and electrochemically characterized. Open-circuit voltage (OCV) was 1.05 V, and peak power density of 370 ($mW/cm^2$) was achieved at $650^{\circ}C$.

• Corrosion Science and Technology
• /
• v.7 no.3
• /
• pp.139-144
• /
• 2008

The results of microstructure observations of the $Al_2O_3$ scale formed on a Fe-Cr-Al steel during high temperature oxidation in the $SO_2$ atmosphere are presented. Morphology of the scale has been studied by SEM and TEM techniques. Phase and chemical compositions have been studied by EDX and XRD techniques. The alumina oxide is a primary component of the scale. TEM observations showed that the scale was multilayer. The entire surface of the scale is covered with "whiskers", which look like very thin platelets and have random orientation. The cross section of a sample shows, that the "whiskers" are approximately $2{\mu}m$ high, however the compact scale layer on which they reside is $0.2{\mu}m$ thick. The scale layer was composed mainly of small equiaxial grains and a residual amount of small columnar grains. EDX analysis of the scale surface showed that the any sulfides were found in the formed outer and thin inner scale layer. A phase analysis of the scale formed revealed that it is composed mainly of the $\theta-Al_2O_3$ phase and a residual amount of $\alpha-Al_2O_3$.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.52 no.6
• /
• pp.241-248
• /
• 2003

$Bi_{1.84}Pb_{0.34}Sr_{1.91}Ca_{2.03}Cu_{3.06}O_{10+\delta}$ high $T_{c}$ superconductors containing Ag as an additive were fabricated by a solid-state reaction method. The superconducting properties, such as the structural characteristics, the critical temperatures, the grain size and the image of mapping on the surface were investigated. Samples with Ag and Au of 50 wt% each were sintered at various temperature(820~$850^{\circ}C$). The structural characteristics, the microstructure of surface and the critical temperature with respect to the each samples were analyzed by XRD and SEM, EDS and four-prove methode respectively. The critical temperature showed the result which the Ag additive samples are higher than Au additive samples. The microstructure of the surface showed the tendency which the Ag additive samples become more minuteness than Au additive samples.

• Journal of Sensor Science and Technology
• /
• v.15 no.6
• /
• pp.386-390
• /
• 2006

This paper describes the ohmic contact formation of polycrystalline 3C-SiC films deposited on thermally grown Si wafers. In this work, a TiW (titanium tungsten) film as a contact material was deposited by RF magnetron sputter and annealed with the vacuum process. The specific contact resistance (${\rho}_{c}$) of the TiW contact was measured by using the C-TLM (circular transmission line method). The contact phase and interfacial reaction between TiW and 3C-SiC at high-temperature as also analyzed by XRD (X-ray diffraction) and SEM (scanning electron microscope). All of the samples didn't show cracks of the TiW film and any interfacial reaction after annealing. Especially, when the sample was annealed at $800^{\circ}$ for 30 min., the lowest contact resistivity of $2.90{\times}10{\Omega}cm^{2}$ was obtained due to the improved interfacial adhesion. Therefore, the good ohmic contact of polycrystalline 3C-SiC films using the TiW film is very suitable for high-temperature MEMS applications.

• Macromolecular Research
• /
• v.11 no.2
• /
• pp.122-127
• /
• 2003

A glass-like carbon was fabricated using furan resin. The influence of heat treatment temperature during fabrication process on the chemical and micro-structural changes was studied by various analytical and spectroscopic methods including TGA, FT-IR, CHN, TEM and XRD. The chemical resistance properties of the fabricated glass-like carbon were also investigated. It has been found that the heat-treated samples at higher temperature up to 2600 $^{\circ}C$ in $N_2$ atmosphere had little weight loss, small amounts of functional groups, and high carbon content. The fabricated glass-like carbons upon heat treatment at 2600 $^{\circ}C$ showed an amorphous stage without any grain growth and/or reconstruction of structure. The glass-like carbon had much better chemical resistance than the artificial graphite, and exhibited a high chemical resistance due to its low surface areas, minimum impurities, and low graphite crystallites.

• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.696-700
• /
• 2002

The Ti-aluminide intermetallic compound was formed from high purity elemental Ti and Al foils by self-propagating, high-temperature synthesis(SHS) in hot press. formation of $TiAl_3$ at the interface between Ti and Al foils was controlled by temperature, pressure, heating rate, and so on. According to the thermal analysis, it is known in this study that the heating rate is the most important factor to form the intermetallic compound by this SHS reaction. The V layer addition between Al and Ti foils increased SHS reaction temperatures. The fully dense, well-boned inter-metallic composite($TiA1/Ti_3$Al) sheets of 700 m thickness were formed by heat treatment at $1000^{\circ}C$ for 10 hours after the SHS reaction of alternatively layered 10 Ti and 9 Al foils with the V coating layer. The phases and microstructures of intermetallic composite sheets were confirmed by EPMA and XRD.