• 폴리머
• /
• 제35권6호
• /
• pp.565-573
• /
• 2011

Poly(methyl methacrylate)/aluminum hydroxide(PMMA/AH) 컴포지트의 기계적 강도를 향상시키기 위해 그래핀 산화물(GO)을 충전제로 사용하여 나노컴포지트를 제조하였다. GO는 흑연을 Hummers법으로 산화한 후 열처리에 의해 박리시켜 제조하였다. PMMA/AH 컴포지트 매트릭스와의 계면혼화성을 향상시키기 위해 산소 플라즈마를 사용하여 노출 시간을 0분에서 70분까지 변화를 주어가며 GO 표면을 개질시켰다. 노출 시간이 50분까지 증가함에 따라 산소 플라즈마 처리한 GO를 충전제로 사용한 나노컴포지트는 PMMA/AH 컴포지트에 비해 굴곡강도, 굴곡탄성률, Rockwell 경도, Barcol 경도, Izod 충격강도 모두 현저히 증가하였다. 적절한 조건에서 산소 플라즈마 처리된 GO는 PMMA/AH 컴포지트 매트릭스와의 계면접착력이 매우 우수함을 파단면 모폴로지로부터 확인하였다. 하지만 GO의 함량이 0.07 phr 이상으로 증가하면 충전제의 분산이 균일하지 못하여 나노컴포지트의 기계적 강도는 오히려 감소하는 경향을 나타내었다.

• 한국표면공학회지
• /
• 제56권1호
• /
• pp.104-114
• /
• 2023

Three dimensional (3D) porous structures consisting of Cu@CoO core-shell-type nano-dendrites were synthesized and tested as the anode materials in lithium secondary batteries. For this purpose, first, the 3D porous films comprising Cu@Co core-shell-type nano-dendrites with various thicknesses were fabricated through the electrochemical co-deposition of Cu and Co. Then the Co shells were selectively anodized to form Co hydroxides, which was finally dehydrated to get Cu@CoO nanodendrites. The resulting electrodes exhibited very high reversible specific capacity almost 1.4~2.4 times the theoretical capacity of commercial graphite, and excellent capacity retention (~90%@50^th cycle) as compared with those of the existing transition metal oxides. From the analysis of the cumulative irreversible capacity and morphology change during charge/discharge cycling, it proved that the excellent capacity retention was attributed to the unique structural feature of our core-shell structure where only the thin CoO shell participates in the lithium storage. In addition, our electrodes showed a superb rate performance (70.5%@10.8 C-rate), most likely due to the open porous structure of 3D films, large surface area thanks to the dendritic structure, and fast electron transport through Cu core network.

• 폴리머
• /
• 제36권3호
• /
• pp.251-261
• /
• 2012

폴리(메틸메타크릴레이트)(PMMA) 매트릭스를 갖는 인조대리석의 기계적 강도를 향상시키기 위해 그래핀 산화물 플레이크(GOF)를 충전제로 사용하여 나노컴포지트를 제조하였다. 충전제로 사용한 GOF는 흑연을 Hummers법으로 산화한 후 열처리에 의해 박리시켜 제조하였다. PMMA 매트릭스와의 계면혼화성을 향상시키기 위하여 다양한 산소:불소 조성의 함산소불소화 처리로 GOF 계면을 개질시켰다. 산소함량 50% 이상에서 함산소불소화 처리한 GOF를 충전제로 사용한 나노컴포지트는 기존 인조대리석에 비해 굴곡강도, 굴곡탄성률, Rockwell경도, Barcol경도, Izod충격강도 모두 현저히 증가하였다. 적절히 함산소불소화 처리된 GOF는 PMMA 매트릭스와의 계면접착력이 우수함을 파단면의 모폴로지로부터 확인하였다. 하지만 GOF 충전제의 함량이 0.07 phr 이상으로 증가하면 충전제의 분산이 균일하지 못하여 인조대리석의 기계적 강도는 오히려 감소하는 경향을 나타내었다.

• 한국표면공학회지
• /
• 제46권2호
• /
• pp.68-74
• /
• 2013

For the coating of diamond films on WC-Co tools, a buffer interlayer is needed because Co catalyzes diamond into graphite. W and Ti were chosen as candidate interlayer materials to prevent the diffusion of Co during diamond deposition. W or Ti interlayer of $1{\mu}m$ thickness was deposited on WC-Co substrate under Ar in a DC magnetron sputter. After seeding treatment of the interlayer-deposited specimens in an ultrasonic bath containing nanometer diamond powders, $2{\mu}m$ thick nanocrystalline diamond (NCD) films were deposited at $600^{\circ}C$ over the metal layers in a 2.45 GHz microwave plasma CVD system. The cross-sectional morphology of films was observed by FESEM. X-ray diffraction and visual Raman spectroscopy were used to confirm the NCD crystal structure. Micro hardness was measured by nano-indenter. The coefficient of friction (COF) was measured by tribology test using ball on disk method. After tribology test, wear tracks were examined by optical microscope and alpha step profiler. Rockwell C indentation test was performed to characterize the adhesion between films and substrate. Ti and W were found good interlayer materials to act as Co diffusion barriers and diamond nucleation layers. The COFs on NCD films with W or Ti interlayer were measured as less than 0.1 whereas that on bare WC-Co was 0.6~1.0. However, W interlayer exhibited better results than Ti in terms of the adhesion to WC-Co substrate and to NCD film. This result is believed to be due to smaller difference in the coefficients of thermal expansion of the related films in the case of W interlayer than Ti one. By varying the thickness of W interlayer as 1, 2, and $4{\mu}m$ with a fixed $2{\mu}m$ thick NCD film, no difference in COF and wear behavior but a significant change in adhesion was observed. It was shown that the thicker the interlayer, the stronger the adhesion. It is suggested that thicker W interlayer is more effective in relieving the residual stress of NCD film during cooling after deposition and results in stronger adhesion.

• 폴리머
• /
• 제36권5호
• /
• pp.656-661
• /
• 2012

케이지 구조의 POSS-$NH_3{^+}$를 이용하여 팔라듐 입자들의 자기 조직화로 인한 구조가 제어된 Pd-POSS 나노입자를 제조하였다. 또한 흑연을 강산과 산화제를 이용하여 산화된 그래핀 옥사이드(GO)를 합성한 후 얻어진 GO와 NaBH4와의 반응을 통하여 그래핀을 제조하였다. 합성된 그래핀과 acrylic acid와 라디칼 중합 반응을 통하여 그래핀 표면에 poly(acrylic acid)(PAA)가 결합된 PAA-grafted graphene을 얻었다. Pd-POSS와 PAA-grafted graphene을 이용한 나노복합체는 POSS-$NH_3{^+}$로 인하여 양전하를 띠는 Pd-POSS 나노입자와 PAA로 인하여 음전하를 띠는 PAA-grafted graphene와의 정전기적 인력을 이용하여 제조하였다. Pd-POSS 나노입자가 PAA로 치환된 그래핀 표면에 정전기적 인력으로 결합되어 있고, 나노복합체의 열적 안정성은 PAA와 PAA-grafted graphene 보다 우수한 것을 확인할 수 있었다. 제조된 Pd-POSS/PAA-grafted graphene 나노복합체의 구조 및 형태와 열적 안정성은 FE-SEM, AFM, TEM, EDX, FTIR과 TGA를 통하여 분석하였다.

• 공업화학
• /
• 제22권2호
• /
• pp.138-143
• /
• 2011

열처리 온도에 따른 탄소섬유의 전자파 차폐특성을 알아보고자 전기방사법을 이용하여 나노섬유를 제조하고 1073, 1323, 1873, 2573 K의 온도 조건에서 열처리 공정을 실시하여 서로 다른 탄소 결정화도를 갖는 PAN계 탄소섬유를 제조하였다. 장방출 주사전자현미경을 통하여 제조된 섬유의 표면 형상을 조사하였고 열처리 온도에 따른 탄소섬유의 결정화도를 Raman 분석을 통하여 확인하였다. 또한 결정화도에 따른 전기전도성을 알아보고자 4-탐침법을 이용하여 표면저항을 측정하고 전기전도성을 계산하였으며, 회로망 분석기를 이용하여 800~4500 MHz의 주파수 영역에서 S-parameter를 측정하고 유전율 및 투자율, 그리고 전자파 차폐 특성을 조사하였다. 2573 K에서 제조된 탄소섬유의 경우 Raman 분석을 통하여 Ig/Id 값이 2.66으로 1323 K에서 제조된 탄소섬유의 1.08에 비해 2.4배 증가하여 결정화도가 향상됨을 확인하였고 전기전도성 또한 54.7 S/cm로 약 6배의 향상을 확인하였다. 유전율 실수부에서는 평균 20의 수치를 보여 1323 K에서 제조된 탄소섬유와 비교하여 약 4배의 향상을 보였다. 결과적으로 열처리 온도에 따른 탄소의 결정화도 향상에 의해 전자파 차폐 성능이 평균 41.7 dB로 약 10 dB이 향상되었음을 확인하였다.