• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1993년도 추계학술대회 논문집
• /
• pp.144-148
• /
• 1993

This paper is a study on electromagnetic wave absorption properties for the composition ratio of Ni-Zn-Fe$_2$O$_4$. Li-Zn-Fe$_2$O$_4$was composed of Fe$_2$O$_3$ 48∼51mo1%, LiO 18 ∼22mo1%, ZnO 34∼27mo1%. and sintering was carried out at 1200$^{\circ}C$. Through the experiments, the resonance phenomenon occured at low frequence range for high permeability, and vice versa. Specialy, In the case of Fe$_2$O$_3$49mol%, NiO 20mo1%, ZnO 3lmol% ,and the matching thickness was 10mm , the absorbing bandwith was 0.35 ∼0.95GHz. Also, In the case of Fe$_2$O$_3$51mo1%. NiO 22mo1%, ZnO 27mol%, we could get the absorbing bandwith of 0.45∼1.2GHz when the matching thickness was 6mm. Therefore. it is proved that electromagnetic wave absorbers with the above bandwidth range can be fabricated successful1y.

• 한국자기학회지
• /
• 제5권1호
• /
• pp.21-26
• /
• 1995

비화학양론 조성의 니켈-아연 페라이트 소결체 시편에서 투자율과 유전율을 체계적으로 변화 시킴에 따라 전파흡수특성에 미치는 영향을 조사하였다. ${(Ni_{0.5}Zn_{0.5}O)}_{1-x}(Fe_{2}O_{3})_{1+x}$ 시편은 일반적인 세라믹 제조공정에 의해 제조 하였다. 본 연구에서는 니켈-아연 페 라이트에서 ${\alpha}-Fe_{2}O_{3}$ 함량을 변화시킴에 따라 복수투자율과 복소유전율의 조절 방안 을 조사하였다. 철과잉량의 효과는 유전상수 증가였으며 철결핍량의 효과는 ${\mu}_{r}"$ 감소이었다. 니켈-아연 페라이트에서 ${\alpha}-Fe_{2}O_{3}$ 함량 변화에 따라 정합주파수와 정합두께 조절이 가능함을 제시하였다.

• 대한금속재료학회지
• /
• 제50권10호
• /
• pp.769-774
• /
• 2012

Mg-x wt% $Fe_2O_3-y$ wt% Ni samples were prepared by reactive mechanical grinding in a planetary ball mill, and their hydrogen-storage properties were investigated and compared. Activations of $Mg-5Fe_2O_3-5Ni$ was completed after one hydriding (under 12 bar $H_2$) - dehydriding (in vacuum) cycle at 593 K. At n = 2, $Mg-5Fe_2O_3-5Ni$ absorbed 3.43 wt% H for 5 min, 3.57 wt% H for 10 min, 3.76 wt% H for 20 min, and 3.98 wt% H for 60 min. Activated $Mg-10Fe_2O_3$ had the highest hydriding rate, absorbing 2.99 wt% H for 2.5 min, 4.86 wt% H for 10 min, and 5.54 wt% H for 60 min at 593 K under 12 bar $H_2$. Activated $Mg-10Fe_2O_3-5Ni$ had the highest dehydriding rate, desorbing 1.31 wt% H for 10 min, 2.91 wt% H for 30 min, and 3.83 wt% H for 60 min at 593 K under 1.0 bar $H_2$.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.139.1-139.1
• /
• 2016

Multiferroic materials are of great interest because of its potential applications in the design of devices combining magnetic, electronic and optical functionalities. Among various multiferroic materials, $BiFeO_3$(BFO) is known to be one of the intensively focused mainly due to the possibility of multiferroism at device working temperature (> $200^{\circ}C$). However, leakage current and weak polarization resulting from oxygen deficiency and crystalline defect should be resolved. Furthermore the magnetic ordering of pure BFO mainly prefers to have antiferromagnetic coupling. Up to now many attempts have been performed to improve the ferromagnetic and the ferroelectric properties of BFO by doping. In this work, we investigated the effects of Ni substitution on the multiferroism of bulk BFO. Four BFO samples (a pure BFO and three Ni-doped BFO's; $BiFe_{0.99}Ni_{0.01}O_3$, $BiFe_{0.98}Ni_{0.02}O_3$ and $BiFe_{0.97}Ni_{0.03}O_3$) were synthesized by the standard solid-state reaction and rapid sintering technique. The XRD results reveal that Ni atoms are substituted into Fe-sites and give rise to phase transition of cubic to rhombohedal. By using vibrating sample magnetometer and standard ferroelectric tester, the multiferroic properties at room temperature were characterized. We found that the magnetic moment of Ni-doped BFO turned out to be maximized for 3% of Ni dopant.

• 한국주조공학회지
• /
• 제25권2호
• /
• pp.73-79
• /
• 2005

Effects of Cr and Ni addition on damping capacity, mechanical property, and corrosion resistance of Fe-17%Mn martensitic alloy have been studied. Martensite start temperature($M_{S}$) of the alloy decreases linearly with increasing Cr and Ni contents up to 15%. The damping capacity decreases gradually from 27 to 22% in specific damping capacity(SDC) with increasing Cr and Ni contents from zero to 10%, and decreases rapidly with further Cr and Ni content in Fe-17%Mn alloy. The tensile strength of the alloy maintains a level of 60 $kgf/mm^{2}$ regardless of Cr content with an elongation of 20 to 25%. But, in case of Fe-17%Mn-x%Ni alloy, the tensile strength decreased rapidly with the Ni content of above 10% because of austenite morphology. Immersion test in 5% NaCl solution leads to the result that the corrosion resistance of the alloy becomes excellent above 10% Cr. From the above results, it is concluded that the optimum Cr content to improve the mechanical property and corrosion resistance of the alloy in 5%NaCl solution with a lesser decrease in damping capacity is about 10%. In the case of 5% $H_{2}SO_{4}$ condition, the Fe-17%Mn-10%Ni is an optimum alloy.

• Journal of Magnetics
• /
• 제19권2호
• /
• pp.111-115
• /
• 2014

X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and vibrating sample magnetometry (VSM) were used to investigate the influence of Ni ions on the structural, electronic, and magnetic properties of nickel-ferrites ($Ni_xFe_{3-x}O_4$). Spinel $Ni_xFe_{3-x}O_4$ ($x{\leq}0.96$) samples were prepared as polycrystalline thin films on $Al_2O_3$ (0001) substrates, using a sol-gel method. XRD patterns of the nickel-ferrites indicate that as the Ni composition increases (x > 0.3), a structural phase transition takes place from cubic to tetragonal lattice. The XPS results imply that the Ni ions in $Ni_xFe_{3-x}O_4$ substitute for the octahedral sites of the spinel lattice, mostly with the ionic valence of +2. The minority-spin d-electrons of the $Ni^{2+}$ ions are mainly distributed below the Fermi level ($E_F$), at around 3 eV; while those of the $Fe^{2+}$ ions are distributed closer to $E_F$ (~1 eV below $E_F$). The magnetic hysteresis curves of the $Ni_xFe_{3-x}O_4$ films measured by VSM show that as x increases, the saturation magnetization ($M_s$) linearly decreases. The decreasing trend is primarily attributable to the decrease in net spin magnetic moment, by the $Ni^{2+}$ ($2{\mu}_B$) substitution for octahedral $Fe^{2+}$ ($4{\mu}_B$) site.

• 대한전자공학회논문지SD
• /
• 제44권2호
• /
• pp.1-6
• /
• 2007

본 연구에서는 모양으로 유도된 자기 이방성을 가진 $Ni_{80}Fe_{20}/SiO_2$ laminates 다층막의 자기적 성질을 조사 하였다. 다층막은 rf 다이오드 스퍼터링 시스템을 이용하여 개개의 $Ni_{80}Fe_{20} 와 $SiO_2$ (at%) 합금 타겟들로부터 Si 또는 upilex 기판에 적층하였다. 여러 가지 개수(N)의 이중층으로 구성된 $Ni_{80}Fe_{20}/SiO_2$ laminates 가 적층되었다. 사진식각기술을 사용하여 타원형 어레이 패턴을 가진 $Ni_{80}Fe_{20}/SiO_2$ laminates 가 제작 되었다. 자기적 성질은 B-H 히스테리시스 그래프와 고주파 permeameter를 사용하여 상온에서 측정 되었다. 다층막에서 도메인 reversal 시 발견된 몇 개의 스텝들은 자성체 박막 사이에 존재하는 coupling 때문으로 사료된다. 내재하는 intrinsic 일축 자기 이방성 field는 N이 증가하면 증가한다. 전체 자기 이방성 field의 실험값은 계산된 값과 잘 일치 하였다. 본 연구에서는 소형의 타원형 어레이를 가진 다층막의 laminate 구조체를 이용하여 더 큰 일축 자기 이방성을 유도하고 그 결과 laminate의 동작 주파수를 극대화시키고자 하였다.

• Journal of Magnetics
• /
• 제10권4호
• /
• pp.133-136
• /
• 2005

The NiMn/NiFe bilayer structure which was short time annealed in order to induce unidirectional anisotropy were studied as a function of annealing temperature. The maximum exchange bias field of NiMn/NiFe bilayer was presented at $250^{\circ}C$ after short time annealing process with no external field. The appearance of exchange bias was due to phase transformation of NiMn layer. In plane angular dependence of a resonance field distribution which measured by FMR was analysed as a combined effect of unidirectional anisotropy and uniaxial anisotropy. The resonance field and the line width from FMR measurement were also analysed with annealing temperature.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 춘계학술발표강연 및 논문개요집
• /
• pp.45-45
• /
• 2003

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 2004년도 요약집 춘계학술발표대회
• /
• pp.377.2-377.2
• /
• 2004