• Journal of the Korean Vacuum Society
• /
• v.17 no.2
• /
• pp.156-159
• /
• 2008

The electrical characteristic of SiGe-on-SOI (SGOI) wafer with different Ge concentration were evaluated by pseudo-MOSFET. Epitaxial SiGe layers was grown directly on top of SOI with Ge concentrations of 16.2, 29.7, 34.3 and 56.5 at.%. As Ge concentration increased, leakage current increased and threshold voltage shifted from 3 V to 7 V in nMOSFET, from -7 V to -6 V in pMOSFET. The interface states between buried oxide and top of Si was significantly increased by the rapid thermal annealing (RTA) process, and so the electrical characteristic of SGOI wafer degraded. On the other hand, additional post RTA　annealing (PRA) showed that it was effective in decreasing the interface states generated by RTA processes and the electrical characteristic of SGOI wafer enhanced higher than initial state.

• Journal of the Korean Magnetics Society
• /
• v.15 no.1
• /
• pp.25-29
• /
• 2005

Magnetic properties of YIG films grown by solid phase epitaxy (SPE) was measured as a function of temperature with focus on magneto-crystalline and perpendicular magnetic anisotropy. Perpendicular magnetic anisotropy was not induced in the SPE YIG films annealed at low temperature by relaxing residual stress through formation of dislocation. On the contrary the films annealed at high temperature showed perpendicular magnetic anisotropy which shows very low density of dislocation. Perpendicular magnetic anisotropy field decreased linearly up to a high temperature of $230^{\circ}C$ above which magneto-crystalline anisotropy disappeared. Coercivity also decreased linearly with temperature up 세 $230^{\circ}C$. Magneto-crystalline anisotropy of perpendicular anisotropy induced epitaxial (111) YIG films can be measured using $H_k=4K_1/3M_s$. Temperature behavior of initial susceptibility can be successfully explained by Hopkinson effects. Curie temperature of YIG films grown on GGG substrate with high paramagnetic susceptibility can be easily measured using the results.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.68-68
• /
• 2000

펄스레이저 증착법(이하 PLD)을 이용하여 마이크로파 유전체 소자 및 절연 산화막으로의 응용을 위한 MgTiO3 박막을 다양한 기판상에서 증착하였다. 사파이어 기판에 (a,c-plane Al2O3) 성장된 MgTiO3 박막은 에피텍셜 성장(epitaxial growth)이 되었으며, SiO2/Si 및 Pt/Ti/Si 기판위세 성장된 MgTiO3 박막의 경우 003방향으로 배향(oriented) 되었다. MgTiO3 박막은 450~75$0^{\circ}C$까지 기판온도를 변화시키면서 증착시켰으며, 증착시 산소분압은 50~200 mTorr로 변화시켰다. PLD 증착시 타켓에 조사된 레이저 에너지 밀도는 약 2J/cm2였으며, MgTiO3 박막 증착후 200Torr O2 분위기에서 상온까지 1$0^{\circ}C$/min 의 속도로 냉각시켰다. 사파이어 c-plane 상에서 일머나잇(ilminite) MgTiO3 구조가 55$0^{\circ}C$ 에피텍셜 성장하는 것을 관찰할 수 있었으며, 사파이어 a-plane 상에서는 MgTiO3 구조가 $650^{\circ}C$ 이상부터 110방향으로 배향되며 성장하였다. $600^{\circ}C$ 이상에서 c-축으로 배향된 구조를 갖고 있었다. 증착된 MgTiO3 박막의 조성분석(stoichio metric analysis)을 위해 RBS 분석을 수행하여, 증착에 이용된 타켓과 동일한 조성을 갖는 MgTiO3 박막이 성장된 것을 확인할 수 있었다. 사파이어 기판상에 증착된 MgTiO3 박막은 가시영역에서 투명하였으며, 약 270nm 파장을 갖는 영역에서 급격한 흡수단을 보였다. 이때의 MgTiO3 박막은 AFM 분석을 통해 약 0.87mn rms roughness 값을 갖는 매우 평탄한 표면구조를 갖고 있는 것을 확인하였다. MIM(Pt/MgTiO3/Pt) 구조의 캐패시터를 형성시켜 MgTiO3 박막의 유전특성(dielectric properties)을 관찰하였다. PLD로 성장된 MgTiO3 박막의 유전율(relative dielectric constant)은 약 22였으며, 1MHz에서 약 1.5%의 유전손실(dielectirc loss) 값을 보였다. 또한 이때 MgTiO3 박막은 낮은 유전분산값을 보였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.490-490
• /
• 2011

Graphene, hexagonal network of carbon atoms forming a one-atom thick planar sheet, has been emerged as a fascinating material for future nanoelectronics. Huge attention has been captured by its extraordinary electronic properties, such as bipolar conductance, half integer quantum Hall effect at room temperature, ballistic transport over ${\sim}0.4{\mu}m$ length and extremely high carrier mobility at room temperature. Several approaches have been developed to produce graphene, such as micromechanical cleavage of highly ordered pyrolytic graphite using adhesive tape, chemical reduction of exfoliated graphite oxide, epitaxial growth of graphene on SiC and single crystalline metal substrate, and chemical vapor deposition (CVD) synthesis. In particular, direct synthesis of graphene using metal catalytic substrate in CVD process provides a new way to large-scale production of graphene film for realization of graphene-based electronics. In this method, metal catalytic substrates including Ni and Cu have been used for CVD synthesis of graphene. There are two proposed mechanism of graphene synthesis: carbon diffusion and precipitation for graphene synthesized on Ni, and surface adsorption for graphene synthesized on Cu, namely, self-limiting growth mechanism, which can be divided by difference of carbon solubility of the metals. Here we present that large area, uniform, and layer controllable graphene synthesized on Cu catalytic substrate is achieved by acetylene-assisted CVD. The number of graphene layer can be simply controlled by adjusting acetylene injection time, verified by Raman spectroscopy. Structural features and full details of mechanism for the growth of layer controllable graphene on Cu were systematically explored by transmission electron microscopy, atomic force microscopy, and secondary ion mass spectroscopy.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.53-53
• /
• 2011

This paper describes results for surface and bulk characterization of the most promising thin film solar cell material for high performance devices, (Ag,Cu) (In,Ga) Se2 (ACIGS). This material in particular exhibits a range of exotic behaviors. The surface and general materials science of the material also has direct implications for the operation of solar cells based upon it. Some of the techniques and results described will include scanning probe (AFM, STM, KPFM) measurements of epitaxial films of different surface orientations, photoelectron spectroscopy and inverse photoemission, Auger electron spectroscopy, and more. Bulk measurements are included as support for the surface measurements such as cathodoluminescence imaging around grain boundaries and showing surface recombination effects, and transmission electron microscopy to verify the surface growth behaviors to be equilibrium rather than kinetic phenomena. The results show that the polar close packed surface of CIGS is the lowest energy surface by far. This surface is expected to be reconstructed to eliminate the surface charge. However, the AgInSe2 compound has yielded excellent atomic-resolution images of the surface with no evidence of surface reconstruction. Similar imaging of CuInSe2 has proven more difficult and no atomic resolution images have been obtained, although current imaging tunneling spectroscopy images show electronic structure variations on the atomic scale. A discussion of the reasons why this may be the case is given. The surface composition and grain boundary compositions match the bulk chemistry exactly in as-grow films. However, the deposition of the heterojunction forming the device alters this chemistry, leading to a strongly n-type surface. This also directly explains unpinning of the Fermi level and the operation of the resulting devices when heterojunctions are formed with the CIGS. These results are linked to device performance through simulation of the characteristic operating behaviors of the cells using models developed in my laboratory.

• Korean Journal of Materials Research
• /
• v.4 no.2
• /
• pp.136-142
• /
• 1994

Epitaxial TiSiz films have been grown by UHV deposition of Ti on atomically clean Si(ll1)- orientated substrates. The Ti film of 50$\AA$ was deposited on the reconstructed Si(ll1) surface at room temperature. The sample was annealed up to $800^{\circ}C$ in $100^{\circ}C$ increments. The structure of the TiSiL films have been identified as the C49 metastable phase by electron diffraction patterns. Scanning electron microscopy( SEM) shows three different types of Tiksilicide island morphologies. The individual island structures are single crystal and are considered to be epitaxy with different crystallographic orientations. The orientational relationships of the $TiSi_{2}$ islands is given by [ 172 1 C49 $TiSi_{2}$//[110] Si and (021) C49 $TiSi_{2}$// (111)Si.

• Korean Journal of Materials Research
• /
• v.9 no.9
• /
• pp.878-882
• /
• 1999

Structural properties of $Al_xGa_1-_xN$ epilayers grown on (0001) sapphire substrate by plasma induced molecular beam epitaxy are investigated in the range of AlN molar fraction from 0.16 to 0.76. The AlN molar fraction estimated by X-ray diffraction agrees well with that of Rutherford backscattering spectroscopy, showing a good linear relationship. The uniform Auger electron microscopy depth profile and linear dependence of average atomic concentration of all the constituents of AlGaN epilayers on AlN molar fraction imply that the epitaxial growth of $Al_xGa_1-_xN$ layers with variation of AlN molar fraction is well controlled without the compositional fluctuation in depth of the epilayer. It is observed by atomic force microscopy that the surface grain shape of $Al_xGa_1-_xN$ epilayer changes from roundish to coalesced one with increasing AlN molar fraction.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.2
• /
• pp.68-72
• /
• 2009

We report on the growth of $CuCrO_2$ films using pulsed laser deposition and their structural and electrical transport properties. $CuCrO_2$ thin films were doped with 5 at% Mg for p-type properties. Epitaxial films of $CuCr_{0.95}Mg_{0.05}O_2$ were grown on c-plane sapphire substrates. The effects of growth temperature and oxygen pressure on film properties were investigated. The main phase of delafossite $CuCr_{0.95}Mg_{0.05}O_2$ was appeared above the growth temperature of $600^{\circ}C$. The thin film grown at $500^{\circ}C$ showed the highest conductivity, reaching 19.6 S/cm while higher growth temperatures over $500^{\circ}C$ led to lower conductivity; the thin film grown at $700^{\circ}C$ showed 0.02 S/cm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.182-185
• /
• 2002

자기정렬구조의 실리콘-게르마늄 이종접합 트랜지스터에서 $f_{max}$를 높이기 위한 방안으로 베이스의 저항 값을 감소시키고자 외부 베이스에 실리콘 및 실리콘-게르마늄 박막을 저온에서 선택적으로 성장할 수 있는 방법을 연구하였다. RPCVD를 이용하여 $SiH_{2}Cl_{2}$과 $GeH_{4}$를 소스 가스로 하고 HCI을 첨가하여 선택성을 향상시킴으로써 $675\sim725^{\circ}C$의 저온에서도 실리콘 및 실리콘-게르마늄의 선택적 에피성장이 가능하였다. 고온 공정에 주로 이용되는 $SiH_{2}Cl_{2}$를 이용한 실리콘 증착은 $675^{\circ}C$에서 열분해가 잘 이루어지지 않고 HCl의 첨가에 의한 식각반응이 동시에 진행되어 실리콘 기판에서도 증착이 진행되지 않으나 $700^{\circ}C$ 이상에서는 HCI을 첨가한 경우에 한해서 선택성이 유지되면서 실리콘의 성장이 이루어졌다, 반면 실리콘-게르마늄막은 실리콘에 비해 열분해 온도가 낮고 GeO를 형성하여 잠입시간을 지연하는 효과가 있는 게르마늄의 특성으로 인해 선택성이나 증착속도 모두에서 유리하였으나 실리사이드 공정시에 표면으로 게르마늄이 석출되는 현상 등의 저항성분이 크게 작용하여 실리콘-게르마늄막 만으로는 외부 베이스에의 적용은 적절하지 않았다. 그러나 실리콘막을 실리콘-게르마늄막 위에 Cap 층으로 증착하거나 실리콘막 만으로 외부 베이스에 선택적으로 증착하여 베이스의 저항을 70% 가량 감소시킬 수 있었다.

• Journal of the Korean Chemical Society
• /
• v.39 no.1
• /
• pp.1-6
• /
• 1995

The surface of a sapphire substrate used for hetero-epitaxy was chemically polished in a mixture of $H_3PO_4\;and\;H_2SO_4$ solution. The extent of etching for various crystal orientations was found to be dependent on the etching time at $315{\pm}2^{\circ}C$ and at the composition of $H_2SO_4 : H_3PO_4$=3 : 1. In addition, the etching rates of the substrates were investigated in the mixture of $H_2SO_4 : H_3PO_4$=3 : 1 by volume and in the temperature range of 280~320$^{\circ}C$. From the plot of log R against 1/T, the activation penergy ($(E_a)$) was found to be in the order of $({\bar1}012) > (10{\bar1}0) > (11{\bar2}0) > (0001)$ plane. After removing the surface layers of the sapphire with (0001), $({\bar1}012),\;(10{\bar1}0)\;and\;(11{\bar2}0)$ plane by a thickness of 64.6, 46.5, 16.2 and 5.1 ${\mu}m$, respectively, the morphology of the resulting surface was observed by SEM.