In recent years, the construction industry has a tendency to increase of high-rise builidngs. High rise buildings can use limited space efficiently. But High rise buildings have problem that have extremely heavy weight. Various studies are being conducted to reduce the weight of buildings. Although lightweight aggregate is a meterial that can effectively reduce the weight of buildings, the strength of the aggregate itself is weak and the absorption rate is high, so the strength of the ITZ(Interfacial Transition Zone) area is weak. Therefore, it is essential to improve the interfacial area when using lightweight aggregates. In this study, an experiment was conducted to improve the adhesion between the aggregate and cement paste and to strengthen the interfacial area by coating the surface of the lighteight aggregate with Blast Furnace Slag. To confirm the improvement, compressive strength and EIS(Electrochemical Impedance Spectroscopy) measurements were perfromed. Using EIS, the change in electrical resistance of the cement hardened body was confirmed. As a result, it was confirmed that the lightweight aggregate coated on the surface showed highter compressive strength and electrical resistance than the non-coated lightweight aggregate, and that the coating material was filled in the interfacial area and inside the aggregate that helped to strengthen the compresssive strength and higher electrical resistance.

• 콘크리트학회논문집
• /
• 제18권3호
• /
• pp.439-445
• /
• 2006

본 연구는 콘크리트 보강근으로 사용된 단일 FRP 또는 하이브리드 FRP(전기적 특성을 가지고 있는)의 전기저항 변화를 모니터링 함으로써, 콘크리트의 파괴에 대한 자가진단 적용 특성을 검토하기 위해 수행되었다. CFRP(단일형), CRGFRP와 CFAFRP(하이브리드형)의 3종류로 보강된 콘크리트에 휨 하중 재하 단계별로 하중을 가하여 균열 또는 파괴가 발생하기 전후의 탄소섬유의 전기저항 변화를 조사하여, 각 인자의 관계특성(각 하중단계별 전기저항, 변형률, 처짐 등의 변화)을 분석하였다. 그 결과, 콘크리트 인장측 파괴 시 탄소섬유단이 파괴될 때 전기저항은 크게 증가하지만, 그 후 하이브리드 FRP 재료 중 탄소섬유를 보강하고 있던 유리섬유나 아라미드섬유가 나머지 추가 재하 하중에 저항할 수 있어 콘크리트 시험체의 전 파괴단계에까지는 이르지 않았다. 따라서 탄소섬유가 포함된 하이브리트 FRP 보강근은 콘크리트 시험체의 파괴를 사전에 감지할 수 있는 자가진단 재료로서의 적용 및 사용이 가능함을 알 수 있다.

• Composites Research
• /
• 제16권2호
• /
• pp.62-67
• /
• 2003

Microdroplet 시험법과 전기저항 측정을 이용하여 탄소섬유강화 epoxy-AT-PEI 복합재료의 손상 감지능 및 계면물성평가에 대한 연구를 수행하였다. AT-PEI 함량이 증가함에 따라 기지재료의 파괴인성은 증가하였으며, 이로 인한 에너지흡수 메커니즘에 의해서 계면전단강도 역시 증가하였다. Microdroulet 시험에서 순수 에폭시는 취성파괴 현상을 그리고 15 phr AT-PEI의 경우에는 파괴인성의 증가로 인해 연성 파단 현상을 관찰할 수 있었다. 경화 후에 열 수축에 의한 전기저항 변화는 AT-PEI 함량 증가에 따라 증가하였으며. 가변하중 하에서 순수 에폭시에 함침된 탄소섬유의 같은 응력까지의 도달시간과 기울기는 15 phr AT-PEI의 경우보다 더 빠르고 높았다. 경화과정과 가역적인 하중 하에서의 전기저항 측정으로부터 얻은 결과는 기지재료의 파괴인성과 잘 일치하였다.

• 한국지반공학회논문집
• /
• 제24권8호
• /
• pp.25-34
• /
• 2008

연약 지반의 거동 특성 평가를 위하여 전단파 속도와 전기저항을 측정할 수 있는 새로운 압밀셀을 개발하였다. 전단파의 발진과 수신을 위한 벤더엘리먼트는 압밀셀의 상 하부판 및 벽면에 설치하였다. 국부적인 간극비 변화를 평가하기 위하여 이중 쐐기 형식의 전기저항 탐침을 적용하였다. 벤더 엘리먼트와 전기저항 탐침은 나일론 재질의 스크류 안에 고정하였다. 나일론 재질의 스크류는 압밀셀과의 임피던스 차이로 인하여 압밀셀을 통한 파의 직접적 전달을 최소화하며, 고장난 벤더 엘리먼트와 전기저항 탐침을 쉽게 교환하게 해준다. 전기저항-대수 시간 곡선의 기울기 및 전단파 속도의 변화로부터 일차 압밀 시간을 평가하였다. 교란 효과가 적을 경우, 입자 배열은 전단파 속도에 영향을 미치며 이로부터 흙의 고유 이방성을 평가할 수 있었다. 압밀 실험동안 침하량으로 산정한 간극비와 전기저항으로부터 계산된 간극비는 거의 유사한 것으로 나타났다. 본 연구는 전단퐈 속도와 전기저항이 일차 압밀, 고유 이방성, 간극비 등 연약 지반의 압밀 특성 파악을 위한 보완적인 정보를 제공해 줌을 보여준다.

• 센서학회지
• /
• 제15권3호
• /
• pp.199-204
• /
• 2006

Carbon nanotube (CNT) mats grown by thermal chemical vapor deposition on a micromachined substrate with a chrome heater and a diaphragm were investigated as sensing materials of resistive gas sensors for nitrogen dioxide ($NO_{2}$) gas. The aligned CNT mats fabricated into mesh and serpentine shapes by the patterned cobalt catalyst layer. CNT mats showed a p-type electrical resistivity with decreasing electrical resistance upon exposure to $NO_{2}$. All sensors exhibited a reversible response at a thermal treatment temperature of $130^{\circ}C$ for about 5 minutes. The resistance change to $NO_{2}$ of the mesh-shaped CNT mats was larger than that of the serpentine-shaped CNT mats.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제51권10호
• /
• pp.465-472
• /
• 2002

This paper presents a study on the aging and recovery of HTV (high temperature vulcanized) silicone rubber used for outdoor insulators. UV irradiation, corona discharge and water immersion were employed as factors of the artificial aging. The effects of changes derived from these stresses on the tracking and arc resistance of silicone rubber were examined. We have investigated the aging phenomena of HTV silicone rubber by the above stresses using the surface energy calculation with contact angle measurement, solvent-extraction, and surface/volume resistivity and so on. These results showed that UV irradiation and corona discharge lead to nearly the same surface oxidation, but the percentage change of mobile low molecular weight by these stresses was different. Furthermore, the oxidized layer induced under UV irradiation restricted the recovery of hydrophobic surface. Water immersion little lowered hydrophobicity level and leaded to a loss of tracking and arc resistance. The degradation mechanism based on our results was discussed.

• 한국전기전자재료학회논문지
• /
• 제35권4호
• /
• pp.348-352
• /
• 2022

Resistive switching behaviors of a co-sputtered zinc silicate thin film (ZnO and SiO₂ targets) have been investigated. We fabricated an Ag/ZnSiO_x/highly doped n-type Si substrate device by using an RF magnetron sputter system. X-ray diffraction pattern (XRD) indicated that the Zn₂SiO₄ was formed by a post annealing process. A unique morphology was observed by scanning electron microscope (SEM) and atomic force microscope (AFM). As a result of annealing process, 50 nm sized nano clusters were formed spontaneously in 200~300 nm sized grains. The device showed a unipolar resistive switching process. The average value of the ratio of the resistance change between the high resistance state (HRS) and the low resistance state (LRS) was about 106 when the readout voltage (0.5 V) was achieved. Resistance ratio is not degraded during 50 switching cycles. The conduction mechanisms were explained by using Ohmic conduction for the LRS and Schottky emission for the HRS.

• Transactions on Electrical and Electronic Materials
• /
• 제4권5호
• /
• pp.24-27
• /
• 2003

We have been investigated phase-change with temperature and electric field in chalcogenide Ge$_2$Sb$_2$Te$\sub$5/ thin film. T$\sub$c/(crystallization temperature) is confirmed by measuring the resistance with the varying temperature on the hotplate. We have measured I-V characteristics with Ge$_2$Sb$_2$Te$\sub$5/ chalcogenide thin film. It is compared with I-V characteristics after impress the variable pulse. The pulse has variable height and duration.

• 한국섬유공학회:학술대회논문집
• /
• 한국섬유공학회 1998년도 가을 학술발표회논문집
• /
• pp.248-251
• /
• 1998

최근 전자, 의료, 인공지능, 합금, 고분자 등의 여러 분야에 걸쳐 smart 재료에 관한 연구가 흥미롭게 진행되고 있는데, smart 재료의 특성은 Sensor-processor-actuator의 기능을 한 재료 시스템 내에 갖고 있는 경우를 뜻하기 때문에 자기진단, 자기수복기능 및 자기조정기능을 가질 수 있다[1]. (중략)

• Journal of Advanced Marine Engineering and Technology
• /
• 제40권4호
• /
• pp.325-329
• /
• 2016

본 연구에서는 Indium-Tin-Oxide 인쇄 박막의 원격 검출이 가능한 해양오염 방제용 센서로서의 응용 가능성에 대해 연구하였다. 우선 양질의 박막제작을 위한 바인더 비율, Indium-Tin-Oxide 중 주석 농도, 열처리 온도 등의 Indium-Tin-Oxide 인쇄박막 제작 조건을 최적화시켰다. 이를 이용하여 전기저항형 액체 센서를 제작하였고, 센서 동작을 확인하기 위하여 대기 중과 해수 중에서 저항 변화를 확인하였다. 이때 저항 변화의 원인은 전해질 속에서 표면에서 일어나는 환원반응에 의한 것으로 해석하였다. 또한 제작된 센서를 Arduino를 사용하여 작동시키고 취득한 데이터의 원격 검출이 가능함을 확인하였다.