• 대한금속재료학회지
• /
• 제46권11호
• /
• pp.762-769
• /
• 2008

Hydrogenated amorphous silicon(a-Si : H) layers, 120 nm and 50 nm in thickness, were deposited on 200 $nm-SiO_2$/single-Si substrates by inductively coupled plasma chemical vapor deposition(ICP-CVD). Subsequently, 30 nm-Ni layers were deposited by E-beam evaporation. Finally, 30 nm-Ni/120 nm a-Si : H/200 $nm-SiO_2$/single-Si and 30 nm-Ni/50 nm a-Si:H/200 $nm-SiO_2$/single-Si were prepared. The prepared samples were annealed by rapid thermal annealing(RTA) from $200^{\circ}C$ to $500^{\circ}C$ in $50^{\circ}C$ increments for 30 minute. A four-point tester, high resolution X-ray diffraction(HRXRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), and scanning probe microscopy(SPM) were used to examine the sheet resistance, phase transformation, in-plane microstructure, cross-sectional microstructure, and surface roughness, respectively. The nickel silicide on the 120 nm a-Si:H substrate showed high sheet resistance($470{\Omega}/{\Box}$) at T(temperature) < $450^{\circ}C$ and low sheet resistance ($70{\Omega}/{\Box}$) at T > $450^{\circ}C$. The high and low resistive regions contained ${\zeta}-Ni_2Si$ and NiSi, respectively. In case of microstructure showed mixed phase of nickel silicide and a-Si:H on the residual a-Si:H layer at T < $450^{\circ}C$ but no mixed phase and a residual a-Si:H layer at T > $450^{\circ}C$. The surface roughness matched the phase transformation according to the silicidation temperature. The nickel silicide on the 50 nm a-Si:H substrate had high sheet resistance(${\sim}1k{\Omega}/{\Box}$) at T < $400^{\circ}C$ and low sheet resistance ($100{\Omega}/{\Box}$) at T > $400^{\circ}C$. This was attributed to the formation of ${\delta}-Ni_2Si$ at T > $400^{\circ}C$ regardless of the siliciation temperature. An examination of the microstructure showed a region of nickel silicide at T < $400^{\circ}C$ that consisted of a mixed phase of nickel silicide and a-Si:H without a residual a-Si:H layer. The region at T > $400^{\circ}C$ showed crystalline nickel silicide without a mixed phase. The surface roughness remained constant regardless of the silicidation temperature. Our results suggest that a 50 nm a-Si:H nickel silicide layer is advantageous of the active layer of a thin film transistor(TFT) when applying a nano-thick layer with a constant sheet resistance, surface roughness, and ${\delta}-Ni_2Si$ temperatures > $400^{\circ}C$.

• 한국진공학회지
• /
• 제17권6호
• /
• pp.528-537
• /
• 2008

ICP-CVD를 사용하여 수소화된 비정질 실리콘(a-Si:H)을 60 nm 또는 20 nm 두께로 성막 시키고, 그 위에 전자총증착장치(e-beam evaporator)를 이용하여 30 nm Ni 증착 후, 최종적으로 30 nm Ni/(60 또는 20 nm a-Si:H)/200 nm $SiO_2$/single-Si 구조의 시편을 만들고 $200{\sim}500^{\circ}C$ 사이에서 $50^{\circ}C$간격으로 40초간 진공열처리를 실시하여 실리사이드화 처리하였다. 완성된 니켈실리사이드의 처리온도에 따른 면저항값, 상구조, 미세구조, 표면조도 변화를 각각 사점면저항측정기, HRXRD, FE-SEM과 TEM, SPM을 활용하여 확인하였다. 60 nm a-Si:H 기판 위에 생성된 니켈실리사이드는 $400^{\circ}C$이후부터 저온공정이 가능한 면저항값을 보였다. 반면 20 nm a-Si:H 기판 위에 생성된 니켈실리사이드는 $300^{\circ}C$이후부터 저온공정이 가능한 면저항값을 보였다. HRXRD 결과 60 nm 와 20 nm a-Si:H 기판 위에 생성된 니켈실리사이드는 열처리온도에 따라서 동일한 상변화를 보였다. FE-SEM과 TEM 관찰결과, 60 nm a-Si:H 기판 위에 생성된 니켈실리사이드는 저온에서 고저항의 미반응 실리콘이 잔류하고 60 nm 두께의 니켈실리사이드를 가지는 미세구조를 보였다. 20 nm a-Si:H 기판위에 형성되는 니켈실리사이드는 20 nm 두께의 균일한 결정질 실리사이드가 생성됨을 확인하였다. SPM 결과 모든 시편은 열처리온도가 증가하면서 RMS값이 증가하였고 특히 20 nm a-Si:H 기판 위에 생성된 니켈실리사이드는 $300^{\circ}C$에서 0.75 nm의 가장 낮은 RMS 값을 보였다.