• 센서학회지
• /
• 제28권2호
• /
• pp.101-105
• /
• 2019

ZnS substrates with excellent transmittance in the mid-infrared region ($3-5{\mu}m$) were prepared using hot pressing instead of conventional chemical vapor deposition (CVD). Diamond-like carbon(DLC) was coated on either one or both sides of the ZnS substrates to improve their mechanical properties and transmittance. More specifically DLC was coated using CVD with an Ar and $C_2H_2$ mixed gas, and Ge was used as the bonding layer. During CVD, the bias voltage was fixed to 500 V and analyzed by Fourier transform infrared spectroscopy (FT-IR), nanoindenter, scanning electron microscope and energy dispersive spectrometry. Results of hardness analysis using the nanoindenter, showed that DLC coating increased from 5.9 to 17.7 GPa after deposition. The FT-IR spectroscopy results showed that, in the mid-infrared region ($3-5{\mu}m$), the average transmittance of the samples with DLC coating on one and both sides increased by approximately 6% and approximately 11.2% respectively. In conclusion, the DLC coating improved the durability and transmittance of the ZnS substrates.

• 한국정밀공학회지
• /
• 제27권12호
• /
• pp.28-32
• /
• 2010

Technical demands for aspheric glass lens formed in market increases its application from simple camera lens module to fiber optics connection module in optical engineering. WC is often used as a metal core of the aspheric glass lens, but the long life time is issued because it fabricated in high temperature and high pressure environment. High hard thin film coating of lens core increases the core life time critically. Diamond Like Carbon(DLC) thin film coating shows very high hardness and low surface roughness, i.e. low friction between a glass lens and a metal core, and thus draw interests from an optical manufacturing industry. In addition, DLC thin film coating can removed by etching process and deposit the film again, which makes the core renewable. In this study, DLC films were deposited on the SiC ceramic core. The process variable in FVA(Filtered Vacuum Arc) method was the substrate bias-voltage. Deposited thin film was evaluated by raman spectroscopy, AFM and nano indenter and measured its crystal structure, surface roughness, and hardness. After applying optimum thin film condition, the life time and crystal structure transition of DLC thin film was monitored.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제52권8호
• /
• pp.325-329
• /
• 2003

Effects of thermal treatment on the structural properties of diamond-like carbon (DU) films were examined. The DLC films were deposited by using a modified filtered cathodic vacuum arc (FCVA) deposition system and by varying the negative substrate bias voltage, deposition time, and nitrogen flow rate. Thermal treatment on DLC films was performed using a rapid thermal annealing (RTA) process at $600^{\circ}C$ for 2min. Raman spectroscopy, x-ray photoemission spectroscopy (XPS), atomic force microscope (AFM), and surface profiler were used to characterize the I$_{D}$I$_{G}$ intensity ratio, sp$^3$ hybrid carbon fraction, internal stress, and surface roughness. It was found for all the deposited DLC films that the RTA-treatment results in the release of internal compressive stress, while at the same time it leds to the decrease of sp$^3$ fraction and the increase of I$_{D}$I$_{G}$ intensity ratio. It was also suggested that the thermal treatment effect on the structural property of DLC films strongly depends on the diamond-like nature (i.e., sp$^3$ fraction) of as-deposited film.ed film.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제40회 동계학술대회 초록집
• /
• pp.496-496
• /
• 2011

A very simple and cost-effective method for fabrication of SiOx-incorporated diamond-like carbon (DLC) thin films at a preparation temperature of less than $200^{\circ}C$ was developed. Since DLC coating can be prepared not under vacuum but atmospheric conditions without any carrier gas flow, not only wafers but also powderic substrates can be used for DLC coating. Formation of DLC coating could result in appearance of superhydrophobic behaviors, which was sustained in a wide range of pH (1~14). DLC-coated surfaces selectively interacted with toluene in a toluene/water mixture. These results imply that our preparation method of the DLC coating can be useful in many application fields such as creating self-cleaning surfaces, and water and air purification filters.

• 한국진공학회지
• /
• 제8권2호
• /
• pp.165-171
• /
• 1999

Diamond-like carbon(DLC) films were synthesized using the rf-plasma CVD technique with the addition of small amounts of nitrogen and oxygen to a gas mixture of $CH_4$ and $H_2$. The gas flow ratio of $CH_4$ to $H_2$ was 2.4:1, and 3% , 13.6% of nitrogen were added to the gas mixture of $CH_4$ and $H_2$ for the deposition of DLC films. The film stress tended to decrease as the nitrogen concentration increased from 3% to 13.6%, probably due to the decrease of the number of the interlink between carbon atoms. The residual stress tended to slightly decrease when 3% of oxygen was added. Scratch tests were performed to investigate the adhesion between the DLC films and the Ti intelayer after pretreating the TiN surface with direct hydrogen plasma. The adhesion was enhanced by adding nitrogen and oxygen to the $CH_4$ and $H_2$ gas mixture. The adhesion for the 3% nitrogen addition was better than that for the 13.6% nitrogen addition. The Vicker's hardness of the DLC films was measured to be 1100Hv.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2007년도 춘계학술대회 논문집
• /
• pp.17-18
• /
• 2007

• 한국표면공학회지
• /
• 제36권1호
• /
• pp.27-33
• /
• 2003

Pulsed magnetron sputtering of graphite target was employed for deposition of diamond-like carbon (DLC) films. Time-resolved probe measurements of magnetron discharge plasma have been performed. It was shown that the pulsed magnetron discharge plasma density ($∼10^{17}$ $m^{-3}$ ) is close to that of vacuum arc cathode sputtering of graphite. Raman spectroscopy was sed to examine DLC films produced at low ( $U_{sub}$ / < 1 kV) pulsed bias voltages applied to the substrate. It has been shown that maximum content of diamond-like carbon in the coating (50-60%) is achieved at energy per deposited carbon atom of $E_{c}$ =100 eV. In spite of rather high percentage of $sp^3$-bonded carbon atoms and good scratch-resistance, the films showed poor adhesion because of absence of ion mixing between the film and the substrates. Electric breakdowns occurring during the deposition of the insulating DLC film also thought to decrease its adhesion.

• 한국재료학회지
• /
• 제10권7호
• /
• pp.459-463
• /
• 2000

순수한 동적 결합반응이고 전하 누적이 없는 이온 임플란테이션, 새로운 재료 개발 등에 음이온을 직접 사용하는 새로운 연구가 진행되고 있으며, 이러한 관점에서 새로운 고체상의 Cs이온 법이 실험실 규모로 연구되고 있다. 본 논문에서는 음이온 Cs gun으로 DLC 박막을 실리콘 위에 제조하였다. 이 시스템은 가스가 필요없으므로, 고 진공에서 증착이 일어난다. C(sup)-빔 에너지는 80~150eV 사이에서 조절이 우수하였다. Raman 분석결과 박막의 DLC 지수, 즉$sp^3$비율은 이온 에너지 증가에 따라 증가하였으며, 미소 경도값 또한 7에서 14GPa로 증가하였다. DLC박막의 표면 평균거칠기(Ra)는 ~1$\AA$정도로 아주 매끈하였으며, 불순물이 내재되지 않는 박막을 얻을 수 있었다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.214-214
• /
• 2013

Diamond like carbon(DLC) 박막은 고경도, 저마찰, 내스크래치 특성을 요구하는 표면기술 응용분야에 널리 사용되며, 대면적 저가 코팅 방법 개발 및 물성 조절 기술이 요구된다. 본 연구에서는 Filtered Vacuum Arc (FVA)를 통해 증착되는 Hydrogen-free DLC 박막의 밀착력 제어를 위한 증착시 기판 전압에 따른 증착 및 밀착력 특성을 분석하였다. 기판전압이 0~-150 V 까지 변화함에 따른 스크래치 테스트 결과를 통해 최적 증착 조건을 도출하였다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 춘계학술발표강연 및 논문개요집
• /
• pp.242-242
• /
• 2003

DLC(Diamond-Like Carbon)는 높은 경도, 내마모성, 화학적 안정성, 생체친화성 및 열전도율이 우수하여 VTR 헤드드럼, CRT Gun, Video Tape, 인공골절, 면도날 등에 널리 사용되고 있다. 에어컨용 Al 냉각핀은 높은 냉각성능의 향상으로 인한 전기절전 효과와 내부식성 및 친수성 등이 요구된다. DC-Sputtering법에 의한 에어컨용 알루미늄 냉각핀에 인가전압의 변화 (300V, 500V, 600V)와 증착시간 (3시간, 5시간 증착)의 변화에 따른 DLC 박막을 합성하여 AFM, XRD 및 Raman spectroscopy 측정을 통하여 분석하고, Micro Vickers Hardness 및 Roughness 등을 측정하였다.