• The korean journal of orthodontics
• /
• v.27 no.3 s.62
• /
• pp.493-502
• /
• 1997

This study was conducted to evaluate the tensile bond strength by bonding the dental bracket with Super-bond after treating the surface of dental Nickel-Chromium alloy with sandblasting, sandblasting & tin-plating, respectively, and tin-plating. 10 pieces of Nickel-Chromium alloys with brackets bonded with Super-bond without their surface treatment were sampled as a control group, 20 pieces of Nickel-Chromium alloy brackets bonded with Super-bond after treating them with sandblasting as group I, 20 pieces of Nickel-Chromium alloys tin-plated and bonded with Super-bond after sandblasting as group II, and then 20 pieces of alloys with brackets bonded with Super-bond after tin-plating as group III. The result of those examination and comparison is summarized as follows: 1. Group I showed the mean tensile bond strength of $14.41{\pm}2.24MPa$ which was highest among 4 groups, followed by group III($13.59{\pm}.51MPa$), group II($12.27{\pm}.45MPa$), and control group($10.50{\pm}1.57MPa$), respectively. However, it was shown that there was no statistically significant difference between group I and III, group III and II, and group II and control group(p>0.05). 2. The main failure pattern of those brackets showed that $70\%$ of the control group had an adhesive failure at the bracket-Superbond interface, and $30\%$ at the Nickel-Chromium alloy-Superbond interface, while other groups did the adhesive failure at the bracket-Superbond interface. 3. When examined under SEM, it was shown that adhesives were mostly attached to the surface of the Nickel-Chromium alloy for all groups while a considerable quantity of adhesives were attached to the bracket base. Then, those samples treated only with sandblasting showed the most even and remarkable roughness of their surface.

• The Journal of Korean Academy of Prosthodontics
• /
• v.53 no.4
• /
• pp.295-300
• /
• 2015

Purpose: The aim of this study was to evaluate the shear bond strength between Ni-Cr alloy and composite resin using universal adhesive systems coMPared to conventional method using metal primers. Materials and methods: For this study, a total of 120 cast commercial Ni-Cr alloy (Vera Bond 2V) disks were embedded in acrylic resin, and their surfaces were smoothed with silicon carbide papers and airborne-particle abrasion. Specimens of each metal were divided into 6 groups based on the combination of metal primers (Metal primer II, Alloy primer, Metal & Zirconia primer, MKZ primer) and universal adhesive systems (Single Bond Universal, All Bond Universal). All specimens were stored in distilled water at $37^{\circ}C$ for 24 hours. Shear bond strength testing was performed with a universal testing machine at a cross head speed of 1 m/min. Data (MPa) were analyzed using one-way ANOVA and the post hoc Tukey's multiple comparison test (${\alpha}$=.05). Results: There were significant differences between Single Bond Universal, All Bond Universal, Metal Primer II and Alloy Primer, MKZ Primer, Metal & Zirconia Primer (P<.001). Conclusion: Universal Adhesive system groups indicated high shear bond strength value bonded to Ni-Cr alloy than that of conventional system groups using primers except Metal Primer II. Within the limitations of this study, improvement of universal adhesive systems which can be applied to all types of restorations is recommended especially non-precious metal alloy. More research is needed to evaluate the effect of silane inclusion or exclusion in universal adhesive systems.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.4
• /
• pp.685-695
• /
• 2004

The aim of this study was to evaluate the resistance to degradation and to compare the wear resistance characteristics of four composite resins in an alkaline solution. The resistance to degradation was evaluated on the basis of mass loss(%), degradation depth(${\mu}m$), Si loss(ppm) and wear depth. The brands studied were Heliomolar flow, Filtek supreme, Point4, Tetric flow. The results were as follows: 1. The sequence of the mass loss was in descending order by Heliomolar flow, Filtek supreme, Point4, Tetric flow. There was significant differences among the materials except Heliomolar flow and Filtek supreme. 2. The sequence of the degree of degradation layer depth was in descending order by Filtek supreme, Heliomolar flow, Tetric flow, Point4. There were significant differences among the materials except Heliomolar flow and Tetric flow. 3. The sequence of Si loss was in descending order by Filtek supreme, Heliomolar flow, Point4, Tetric flow. There were significant differences among the materials except Point 4 and Tetric flow. 4. The sequence of maximum wear depth was in descending order by Heliomolar flow, Point4, Fillet supreme, Tetric flow and there was increasing wear depth on soaking in 0.1N NaOH solution. 5. When observed with SEM, destruction of bonding between matrix and filler was observed and when observed with CLSM, the depth of degradation layer of specimen surface was observed. There results indicate that wear and hydrolytic degradation could be considered to be evaluation factors of composite resins.

• Korean Journal of Dental Materials
• /
• v.44 no.1
• /
• pp.61-68
• /
• 2017

This study evaluated the effects of various cleaning methods on the shear bond strength of zirconia ceramics after saliva contamination. Eighty zirconia disk specimens were divided into 8 groups. All groups were treated with one coat of MDP primer. All specimens (except the negative control) were contaminated with human saliva on the zirconia surface. The positive control went through the bonding procedure immediately after contamination without any cleaning procedure. With the exception of control groups, the remaining six groups were rinsed with water and either applied with MDP recoating (WATER+MDP) or without MDP recoating (WATER). While some were cleaned with a Ivoclean with MDP recoating (IVOCLEAN+MDP) or not applied with MDP recoating(IVOCLEAN), others were cleaned with a 1% NaOCl solution with MDP recoating (NaOCl+MDP) or without MDP recoating (NaOCl). The shear bond strength of all specimens were measured after being stored in distilled water at $37^{\circ}C$ for 24 hours. The data was analyzed statistically by an analysis of ANOVA, Tukey's post hoc test and Student's t-test was used to compare the shear bond strength according to the re-coating of MDP after the cleaning procedure. The positive control group showed the lowest shear bond strength value, and the WATER group and NaOCl group showed no significant difference when compared to the positive control group. The IVOCLEAN group showed significantly higher shear bond strength when compared to Water group and NaOCl group but not with the group of negative control. After rinsing with water or the NaOCl solution, the comparison of the single coating of MDP and re-coating of MDP showed different shear bond strengths but there was no significant difference to the negative control. After rinsing with Ivoclean, there was no significant difference to the negative control regardless of the recoating of MDP. In conclusion, the shear bond strength was affected by the cleansing procedure and Ivoclean was found to be effective regardless of the re-coating of MDP. When water or the NaOCl solution is used to remove surface contaminants, the re-coating of MDP provides a positive effect on cementation.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.4
• /
• pp.93-99
• /
• 2019

The purpose of this study was to investigate the bond strength between PEKK(Polyetherketoneketone) and Sinfony(3M ESPE, Seefeld, Germany) the dental composite resin by proposing the three representative surface treatment methods and evaluate to see if they affect the bond strength between two materials. A total of 30 PEKK($Pekkton^{(R)}$ Ivory, $Cendres+M{\acute{e}}taux$, Bienne, Switzerland) specimens were prepared, embedded in acrylic resin, polished(P 1200 grid) to surface, and each group was divided into 10 specimens. After then, by the surface treatment method, it classified into three groups(n=10) such as Air abrasion group(PN), applying Single Bond Universal(3M ESPE) after Air abrasion(PB), applying OPAQUE(3M ESPE) after Air abrasion(PO). Then, veneering was performed by using Sinfony(3M ESPE, Seefeld, Germany). All completed specimens were allowed to rest in a $37^{\circ}C$ water bath for 24 hours. Shear bond strength of each group was measured and fracture patterns were classified. Statistic analysis was performed with One-way ANOVA followed by post hoc Scheffe tast (p<.05). Statistical analysis was performed using the SPSSWIN 21.0 program. As a result of one-way ANOVA, the average value of PB group was $27.67{\pm}4,18MPa$ and it was shown as the highest bond strength, PN and PO were $20.43{\pm}1.70$ and $19.8{\pm}4.77MPa$ each, and these were relatively low(F=18.4, P<.001), and as the post-test the Scheffe test was conducted and verified (p<.05). After examining the scheffe test, it was showed significant differences as PB>PO, PB>PN(p<.001). Through this study, in order to enhance the bonding force between PEKK and the composite resin, perform the Air abrasion and surface treatment by using Single Bond Universal(3M ESPE) is recommended, and as coMPared with other studies. And it is assumed that the increase of the application time of the Air abrasion affects the increase of the shear bond strength. Thus, further research is required.

• The Journal of Korean Academy of Prosthodontics
• /
• v.46 no.2
• /
• pp.148-156
• /
• 2008

Statement of problems: Self-etch adhesives exhibit some clinical benefits such as ease of manipulation and reduced technique-sensitivity. Nevertheless, some concern remains regarding the bonding effectiveness of self-etch adhesives to enamel, in particular when so-called 'mild' self-etch adhesives are employed. This study compared the microtensile bond strengths to ground enamel of the two-step self-etch adhesive Clearfil SE Bond (Kuraray) to the three-step etch-and- rinse adhesive Scotchbond Multi-Purpose (3M ESPE) and the one-step self-etch adhesive iBond (Heraeus Kulzer). Purpose: The purpose of this study was to determine the effect of a preceding phosphoric acid conditioning step on the bonding effectiveness of a two-step self-etch adhesive to ground enamel. Material and methods: The two-step self-etch adhesive Clearfil SE Bond non-etch group, Clearfil SE Bond etch group with prior 35% phosphoric acid etching, and the one-step self-etch adhesive iBond group were used as experimental groups. The three-step etch-and-rinse adhesive Scotchbond Multi-Purpose was used as a control group. The facial surfaces of bovine incisors were divided in four equal parts cruciformly, and randomly distributed into each group. The facial surface of each incisor was ground with 800-grit silicon carbide paper. Each adhesive group was applied according to the manufacturer's instructions to ground enamel, after which the surface was built up using Light-Core (Bisco). After storage in distilled water at $37^{\circ}C$ for 1 week, the restored teeth were sectioned into enamel beams approximately 0.8*0.8mm in cross section using a low speed precision diamond saw (TOPMET Metsaw-LS). After storage in distilled water at $37^{\circ}C$ for 1 month, 3 months, microtensile bond strength evaluations were performed using microspecimens. The microtensile bond strength (MPa) was derived by dividing the imposed force (N) at time of fracture by the bond area ($mm^2$). The mode of failure at the interface was determined with a microscope (Microscope-B nocular, Nikon). The data of microtensile bond strength were statistically analyzed using a one-way ANOVA, followed by Least Significant Difference Post Hoc Test at a significance level of 5%. Results: The mean microtensile bond strength after 1 month of storage showed no statistically significant difference between all adhesive groups (P>0.05). After 3 months of storage, adhesion to ground enamel of iBond was not significantly different from Clearfil SE Bond etch (P>>0.05), while Clearfil SE Bond non-etch and Scotchbond Multi-Purpose demonstrated significantly lower bond strengths (P<0.05), with no significant differences between the two adhesives. Conclusion: In this study the microtensile bond strength to ground enamel of two-step self-etch adhesive Clearfil SE Bond was not significantly different from three-step etch-and-rinse adhesive Scotchbond Multi-Purpose, and prior etching with 35% phosphoric acid significantly increased the bonding effectiveness of Clearfil SE Bond to enamel at 3 months.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.45 no.2
• /
• pp.185-194
• /
• 2018

The objective of this study was to compare the shear bonding strength of zirconia after cleaning the crown contaminated by saliva or blood and determine the effect of thermocycling. 180 specimens were embedded in acrylic resin. 20 Specimens in the positive control group were bonded with resin cement without contamination. 20 Specimens in the negative control group were washed with water for 20 seconds and then dried for 10 seconds. 120 Specimens contaminated by saliva or blood were cleaned by using three cleaning methods: 37% phosphoric acid gel, commercial cleanse, and 2.5% NaOCl. All samples were bonded with resin cement and divided into two subgroups: One was not aged, and the other was tested with 30,000 thermocycling. In both groups contamination by saliva and blood, no statistically significant difference was not found in control, groups cleansed by commercial cleanser and 2.5% NaOCl. When the groups cleansed with water and 37% phosphate gel were compared with the control, significantly low shear bond strength was shown. Thermocycling group showed statistically significantly low shear bond stress compared to the groups without thermocycling. When zirconia was contaminated by saliva or blood, its original shear bond strength could be obtained if it was cleaned with commercial cleanser or 2.5% NaOCl.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.25 no.3
• /
• pp.225-235
• /
• 2009

A common procedure of restoration of endodonticlly treated tooth with fiber-reinforced post is followed by core build-up after post cementation. However, this technique is complex and time-consuming. The aim of this study was to compare fracture strength of premolar, restored with various methods of core fabrications on fiber-reinforced posts and casting metal restoration. Forty five freshly extracted human mandibular premolars were obtained and devided into 5 groups acconding to the type of post and methods of core build-up. In Group A, D.T. $Light-post^{(R)}$ were cemented with $DUO-LINK^{TM}$ and then $LIGHT-CORE^{TM}$ was used for core restoration. In Group B, D.T. $Light-post^{(R)}$ and $DUO-LINK^{TM}$ were used for cementing in the postspace, and $DUO-LINK^{TM}$ was used again for core restoration. In Group C, $Light-post^{(R)}$ bonding and the core build-up were performed simultaneously by using $DUO-LINK^{TM}$. In Group D, $LuxaPost^{(R)}$ was bonded by using $LuxaCore^{(R)}-Dual$. Again, $LuxaCore^{(R)}-Dual$ was used for core restoration. In Group E, $LuxaPost^{(R)}$ bonding and the core build-up were performed simultaneously by using $LuxaCore^{(R)}-Dual$. Axial reduction was formed parallelly as possible and 45 degree bevel was made at buccal occlusal surface. Crowns were fabricated and cemented. Each tooth was embedded in self-curing acrylic resin to the level of 2mm below the CEJ. Specimens were fixed on universal testing machin such that the axis of the tooth was at 45 degree inclination to the horizontal plane, and compressive force was applied at a crosshead speed of 1mm/min until failure occurred. The mean fracture strength was the highest in group A followed by descending order in group B, D, E and C. However, there were no statistically significant differences between groups with regard to the fracture strength. The type of the post or build-up methods of the core does not seem to influence the fracture strength.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.25 no.4
• /
• pp.361-374
• /
• 2009

For successful osteogenesis around the implants, interaction between implant surface and surrounding tissue is important. Biomechanical bonding and biochemical bonding are considered to influence the response of adherent cells. But the focus has shifted surface chemistry. The purpose of this study is to evaluate the MC3T3-E1 osteoblast like cell responses of magnesium (Mg) ion implanted titanium surface produced using a plasma source ion implantation method. Commercially pure titanium disc was used as substrates. The discs were prepared to produce four different surface, A: Machine turned surface, B: Mg implanted surface, C: sandblasted surface, D: sandblasted and Mg implanted surface. MC3T3 El osteoblastic like cells were cultured on the disc specimens. Cell adhesion, proliferation, differentiation, and synthesis of extracellular matrix were evaluated. The cell adhesion morphology was evaluated by SEM. RT PCR assay was used for assessment of cell adhesion, proliferation and differentiation. ALP activity was measured for cell differentiation. The results of this study were as follows: 1. SEM showed that cell on Mg ion groups was more proliferative than that of non Mg ion groups. On the machine turned surface, cell showed some degree of contact guidance in aligning with the machining grooves. 2. In RT PCR analysis, osteonectin and c-fos mRNA were more expressed on sandblasted and Mg ion implanted group. 3. ALP activity was not significantly different among all groups. Within the limitations of this study, the following conclusions were drawn: It might indicate Mg ion implanted titanium surface induce better bone response than non Mg ion groups.

• The korean journal of orthodontics
• /
• v.34 no.5 s.106
• /
• pp.439-447
• /
• 2004

The purpose of this study was to investigate the influence of water, saliva and blood contamination on the bonding strength of metal brackets with a self-etching primer/adhesive to enamel. Ninety-six extracted human teeth were divided into four groups. The brackets were bonded to enamel with a self- etching primer (3M/Unitek Dental Products. Monorovia California) according to one of four protocols. The teeth were bonded in a dry condition (group D) or in contamination with distilled water (group W), artificial saliva (group S). or fresh human blood (group B) Shear bond strengths were tested using an Instron Universal testing machine. After debonding. bracket and tooth surfaces were examined with a stereomicroscope. In each group, four samples were selected and examined with a Scanning electron microscope of the prepared enamel surface and resin-enamel interlace. The results obtained were summarized as follows: Shear bond Strength if group D $(15.22{\pm}2.86MPa)$ and W $(15.20{\pm}3.85 MPa)$ Were higher than in group B$(12.56{\pm}2.94MPa)$ (p<0.05). There were no statistical differences in the shear bond strengths between groups D. W and S (p>0.05). There was a tendency to have less residual adhesive remaining on the enamel surfaces of group B than group D. The SEW morphology of group D and W showed a more roughened etching pattern than group S and B. Water or saliva contamination on bending of orthodontic brackets with Transbond plus self etching primer had almost no influence on bond strength In this study, the blood contaminated group showed the lowest bond strength, but it was above the clinically acceptable bond strength (5.9-7.8 MPa, Reynold, 1975). The results of this study suggest that acceptable clinical bond strengths can be obtained in wet conditions when self-etching adhesives are used.