• 한국표면공학회지
• /
• 제41권3호
• /
• pp.88-93
• /
• 2008

Ir-Re thin films with Ti interlayer were deposited onto the tungsten carbide substrate by ion beam assisted DC magnetron sputtering. The Ir-Re films were prepared with targets of having two atomic percent of 7:3 and 5:5. The microstructure and surface analysis of the specimen were conducted by using SEM, XRD and AFM. Mechanical properties such as hardness and adhesion strength of Ir-Re thin film also were examined. The interlayer of pure titanium was formed with 100 nm thickness. The film growth of Ir-30at.%Re was faster than that of Ir-50at.%Re in the same deposition conditions. Ir-Re thin films consisted of dense and columnar structure irrespective of the different target compositions. The values of hardness and adhesion strength of Ir-30at.%Re thin film coated on WC substrate were higher than those of Ir-50at.%Re thin film.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2001년도 추계학술발표회 초록집
• /
• pp.35-35
• /
• 2001

agnesium Oxide (MgO) with a NaCI structure is well known to exhibit high secondary electron emission, excellent high temperature chemical stability, high thermal conductance and electrical insulating properties. For these reason MgO films have been widely used for a buffer layer of high $T_c$ superconducting and a protective layer for AC-plasma display panels to improve discharge characteristics and panel lifetime. Up to now MgO films have been synthesized by lE-beam evaporation, Molecular Beam Epitaxy (MBE) and Metalorganic Chemical Vapor Deposition (MOCVD), however there have been some limitations such as low film density and micro-cracks in films. Therefore magnetron sputtering process were emerged as predominant method to synthesis high density MgO films. In previous works, we designed and manufactured unbalanced magnetron source with high power density for the deposition of high quality MgO films. The magnetron discharges were sustained at the pressure of O.lmtorr with power density of $110W/\textrm{cm}^2$ and the maximum deposition rate was measured at $2.8\mu\textrm{m}/min$ for Cu films. In this study, the syntheses of MgO films were carried out by unbalanced magnetron sputtering with various $O_2$ partial pressure and specially target power densities, duty cycles and frequency using pulsed DC power supply. And also we investigated the plasma states with various $O_2$ partial pressure and pulsed DC conditions by Optical Emission Spectroscopy (OES). In order to confirm the relationships between plasma states and film properties such as microstructure and secondary electron emission coefficient were analyzed by X-Ray Diffraction(XRD), Transmission Electron Microscopy(TEM) and ${\gamma}-Focused$ Ion Beam (${\gamma}-FIB$).

• 열처리공학회지
• /
• 제22권3호
• /
• pp.143-148
• /
• 2009

We have fabricated Ti metal films on Cu wire substrates by using a RF magnetron sputtering method at different RF powers (0, 30 and 60 W) in a high vacuum, and we have investigated the thin film characteristics and resistivity. The ion bombardment effect is increased by the method to superimpose RF power to DC power applied to two poles of the base; thus, the thin film is deposited at sputtering gas pressures below 1 Pa. Moreover, the thin film formation of the multilayer structure becomes possible by gradually injecting the RF power, and the thin film quality is improved.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제40회 동계학술대회 초록집
• /
• pp.402-402
• /
• 2011

이번 연구에서는 DC magnetron sputtering을 이용하여 타겟의 각도 변화를 주어 각도 변화에 따른 원자의 거동분석에 대해 수행하였다. 타겟의 각도가 증가할수록 비저항이 증가하고 있으며 40도의 각도의 약 600 nm의 두께에서 $5.5{\times}10^{-4}{\Omega}cm$로 나타났으며, 가시광선 영역에서 88%의 투과도를 보이는데 이는 타겟 각도에 따라 Ar 이온으로부터 나온 입자들에 의해서 플라즈마가 형성되면서 플라즈마 산란이 발생한 것으로 보며, 특히 비저항 감소와 달리 이동도 및 농도가 감소하는 형태를 보이는데 이는 Hall 측정을 통해 알 수 있다. 타겟 각도 변화는 결정 성장 방해에 영향을 주어 결정 크기는 감소하면서 스트레스로 인한 FWHM 증가가 이를 입증해 주고 있다.

• E2M - 전기 전자와 첨단 소재
• /
• 제10권7호
• /
• pp.700-705
• /
• 1997

Transparent conducting indium tin oxide (TC-ITO) thin films are deposited on soda lime glass by a dc magnetron sputtering technique having the unbalanced-magnet structure in order to improve the electrical/material characteristics and to avoid the surface damages. The material properties are measured by the x-ray diffractometer (XRD) and atomic force microscope (AFM). The (400) peak as the preferred orientation of <100> direction for ITO thin films is stabilized with the increase of substrate temperature. The surface roughness estimated by AFM 3D image at the substrate temperature of 40$0^{\circ}C$ is extremely uniform. The best resistivity of ITO films (5500 $\AA$ thick) at 40$0^{\circ}C$ is about 1.3$\times$10$^{-4}$ $\Omega$cm on the position of 4 cm from substrate center.

• 한국진공학회지
• /
• 제8권3A호
• /
• pp.245-248
• /
• 1999

Recently low resistance of gate line or data line is required for large screen size TFT-LCD panels. As a result, lower resistance Al-alloy is currently reviewed extensively and the resistivity is required smaller than 10$\mu\Omega$cm. In this paper, Al-Nd and Al-Zr thin film were deposited on glass substrated by D.C. magnetron sputtering system under various condition. Its properties were characterized by SEM, AFM, XRD and 4-point-probe. The optimal condition was $120^{\circ}C$, 125W, 0.4Pa, 30sccm (Ar) and $350^{\circ}C$, 20min. annealing. At that condition the resistivity of Al-Zr(0.9%wt.) is about 4$\mu\Omega$cm.

• 전력전자학회논문지
• /
• 제18권6호
• /
• pp.593-600
• /
• 2013

The asymmetric pulsed DC reactive magnetron sputtering system is widely used for the high quality plasma sputtering process such as a thin film deposition. In asymmetric pulsed DC power supply a reverse voltage is applied to the target periodically to minimize arc discharging effect. When sputtering in the mid-frequency range (20-350 kHz), the periodic target voltage reversals suppress arc formation at the target and provide long-term process stability. Thus, high quality, defect-free coatings of these materials can now be deposited at competitive rates. In this paper, a new style asymmetric pulsed DC power supply including mid-transformer is presented. In the proposed, an energy recovery circuit is adopted to reduce the mutual inductance of the transformer. As a result, the system dynamics of the voltage control loop is increased highly and the non-linear voltage boosting effect of the conventional system is removed. This work was proved through simulation and laboratory based experimental study.

• 한국결정성장학회지
• /
• 제14권4호
• /
• pp.145-150
• /
• 2004

We have investigated the structural, electrical and optical properties of Al-doped ZnO (AZO) thin films grown on glass substrate by pulsed DC magnetron sputtering as functions of pulse frequency and substrate temperature. A highly c-axis oriented AZO thin film is grown in perpendicular to the substrate when pulse frequency of 30 kHz and substrate temperature of $400^{\circ}C$ was applied. Under this optimized growth condition, the resistivity of AZO thin films exhibited $7.40\times 10^{-4}\Omega \textrm{cm}$. This indicated that the decrease of film resistivity resulted from the improvement of film crystallinity. The optical transmittance spectra of the films showed a very high transmittance of 85∼90 % in the visible wavelength region and exhibited the absorption edge of about 350 nm. The results show the potential application for transparent conductivity oxide (TCO) thin films.

• Transactions on Electrical and Electronic Materials
• /
• 제17권6호
• /
• pp.351-354
• /
• 2016

The mechanical properties of ITO films such as adhesion and internal stress are very important for the commercial application of solar cell devices. We report high quality pulsed DC magnetron sputtered ITO films deposited on silicon and glass substrates with low resistivity and high transmittance for various working pressures ranging from 0.96 to 3.0 mTorr. ITO films showed the lowest resistivity of $2.68{\times}10^{-4}{\Omega}{\cdot}cm$, high hall mobility of $46.89cm^2/V.s$, and high transmittance (>85%) for the ITO films deposited at a low working pressure of 0.99 mTorr. The ITO films deposited at a low working (0.96 mTorr) pressure had both amorphous and polycrystalline structures and were found to have compressive stress while the ITO films deposited at higher temperature than 0.99 mTorr was mixture of amorphous and polycrystalline and was found to have tensile stress.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.319-320
• /
• 2009

In this study, high-quality Al-N doped p-type ZnO thin films were deposited on n-type Si (100) wafer or Si coated with buffer layer by DC magnetron sputtering in the mixture of $N_2$ and $O_2$ gas. The target was ceramic ZnO mixed with $Al_2O_3$ (2 wt%). The p-type ZnO thin film showed higher carrier concentration $2.93\times10^{17}cm^{-3}$, lower resistivity of $5.349\;{\Omega}cm$ and mobility of $3.99\;cm^2V^{-1}S^{-1}$, respectively. According to PL spectrum, the Al donor energy level depth ($E_d$) of Al-N codoped p-type ZnO film was reduced to about 51 meV, and the N acceptor energy level depth ($E_a$) was reduced to 63 meV, respectively.