• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.4
• /
• pp.23-29
• /
• 2000

We demonstrate the fabrication method of high-density and high-quality solder bump solving a copper (Cu) cross-contamination in Si-LSI laboratory. The Cu cross-contamination is solved by separating solder-bump process by two steps. Former is via-formation process excluding Cu/Ti under ball metallurgy (UBM) layer sputtering in Si-LSI laboratory. Latter is electroplating process including Ti-adhesion and Cu-seed layers sputtering out of Si-LSI laboratory. Thick photoresist (PR) is achieved by a multiple coating method. After TiW/Al-electrode sputtering for electroplating and via formation in Si-LSI laboratory, Cu/Ti UBM layer is sputtered on sample. The Cu-seed layer on the PR is etched during Cu-electroplating with low-electroplating rate due to a difference in resistance of UBM layer between via bottom and PR. Therefore Cu-buffer layer can be electroplated selectively at the via bottom. After etching the Ti-adhesion layer on the PR, Sn/Pb solder layer with a composition of 60/40 is electroplated using a tin-lead electroplating bath with a metal stoichiometry of 60/40 (weight percent ratio). Scanning electron microscope image shows that the fabricated solder bump is high-uniformity and high-quality as well as symmetric mushroom shape. The solder bumps with even 40/60 $\mu\textrm{m}$ in diameter/pitch do not touch during electroplating and reflow procedures. The solder-bump process of high-uniformity and high-density with the Cu cross-contamination free in Si-LSI laboratory will be effective for electronic microwave application.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.235-237
• /
• 2007

In this paper, fabrication of Sn-3.0Ag-0.5Cu solder bumping having accurate composition and behavior of intermetallic compounds(IMCs) growth at interface between Sn-Ag-Cu bumps and Cu substrate were studied. The ternary alloy of the Sn-3.0Ag-0.5Cu solder was made by two binary(Sn-Cu, Sn-Ag) electroplating on Cu pad. For the manufacturing of the micro-bumps, photo-lithography and reflow process were carried out. After reflow process, the micro-bumps were aged at $150^{\circ}C$ during 1 hr to 500 hrs to observe behavior of IMCs growth at interface. As a different of Cu contents(0.5 or 2wt%) at Sn-Cu layer, behavior of IMCs was estimated. The interface were observed by FE-SEM and TEM for estimating of their each IMCs volume ratio and crystallographic-structure, respectively. From the results, it was found that the thickness of $Cu_3Sn$ layer formed at Sn-2.0Cu was thinner than the thickness of that layer be formed Sn-0.5Cu. After aging treatment $Cu_3Sn$ was formed at Sn-0.5Cu layer far thinner.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.24 no.12
• /
• pp.1120-1127
• /
• 2013

In this paper, novel chip-on-chip(CoC) flip-chip bump structures using chip-on-wafer(CoW) process technology are proposed, designed and fabricated, and their microwave frequency responses are analyzed. With conventional bumps of Cu pillar/SnAg and Cu pillar/Ni/SnAg and novel Polybenzoxazole(PBO)-passivated bumps of Cu pillar/SnAg, Cu pillar/Ni/SnAg and SnAg with the deposition option of $2^{nd}$ Polyimide(PI2) layer on the wafer, 10 kinds of CoC samples are designed and their frequency responses up to 20 GHz are investigated. The measurement results show that the bumps on the wafers with PI2 layers are better for the batch flip-chip process and have average insertion loss of 0.14 dB at 18 GHz. The developed bump structures for chips with fine-pitch pads show similar or slightly better insertion loss of 0.11~0.14 dB up to 18 GHz, compared with that of 0.13~0.17 dB of conventional bump structures in this study, and we find that they could be utilized in various microwave packages for high integration density.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.99-102
• /
• 2003

Reactions between 48Sn-52In solder and under bump metallurgies(UBM) such as 100nm $Ti/8{\mu}m$ Cu and 300nm Al/400nm Ni(V)/400nm Cu have been investigated, and the shear strength of 48Sn-52In solder bumps on each UBM has been evaluated. While intermetallic compounds with two different morphologies were continuously thickened on Ti/Cu with repeating the reflow process, the intermetallics on Al/Ni(V)/Cu spalled into the solder with increasing the number of reflow times. The solder bumps on Ti/Cu exhibited higher shear strength than those on Al/Ni(V)/Cu.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2013.05a
• /
• pp.841-842
• /
• 2013

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2011.06a
• /
• pp.757-758
• /
• 2011

• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.750-760
• /
• 2002

In this study, three solders, Sn-37Pb, Sn-3.5Ag, and Sn-3.8Ag-0.7Cu were screen printed on both electroless Ni/Au and OSP metal finished micro-via PCBs (Printed Circuit Boards). The interfacial reaction between PCB metal pad finish materials and solder materials, and its effects on the solder bump joint mechanical reliability were investigated. The lead free solders formed a large amount of intermetallic compounds (IMC) than Sn-37Pb on both electroless Ni/Au and OSP (Organic Solderabilty Preservatives) finished PCBs during solder reflows because of the higher Sn content and higher reflow temperature. For OSP finish, scallop-like $Cu_{6}$ /$Sn_{5}$ and planar $Cu_3$Sn intermetallic compounds (IMC) were formed, and fracture occurred 100% within the solder regardless of reflow numbers and solder materials. Bump shear strength of lead free solders showed higher value than that of Sn-37Pb solder, because lead free solders are usually harder than eutectic Sn-37Pb solder. For Ni/Au finish, polygonal shaped $Ni_3$$Sn_4$ IMC and P-rich Ni layer were formed, and a brittle fracture at the Ni-Sn IMC layer or the interface between Ni-Sn intermetallic and P-rich Ni layer was observed after several reflows. Therefore, bump shear strength values of the Ni/Au finish are relatively lower than those of OSP finish. Especially, spalled IMCs at Sn-3.5Ag interface was observed after several reflow times. And, for the Sn-3.8Ag-0.7Cu solder case, the ternary Sn-Ni-Cu IMCs were observed. As a result, it was found that OSP finished PCB was a better choice for solders on PCB in terms of flip chip mechanical reliability.

• Korean Journal of Materials Research
• /
• v.18 no.1
• /
• pp.45-50
• /
• 2008

Microstructural evolution and the intermetallic compound (IMC) growth kinetics in an Au stud bump were studied via isothermal aging at 120, 150, and $180^{\circ}C$ for 300hrs. The $AlAu_4$ phase was observed in an Al pad/Au stud interface, and its thickness was kept constant during the aging treatment. AuSn, $AuSn_2,\;and\;AuSn_4$ phases formed at interface between the Au stud and Sn. $AuSn_2,\;AuSn_2/AuSn_4$, and AuSn phases dominantly grew as the aging time increased at $120^{\circ}C,\;150^{\circ}C,\;and\;180^{\circ}C$, respectively, while $(Au,Cu)_6Sn_5/Cu_3Sn$ phases formed at Sn/Cu interface with a negligible growth rate. Kirkendall voids formed at $AlAu_4/Au$, Au/Au-Sn IMC, and $Cu_3Sn/Cu$ interfaces and propagated continuously as the time increased. The apparent activation energy for the overall growth of the Au-Sn IMC was estimated to be 1.04 eV.

• Advances in materials Research
• /
• v.1 no.1
• /
• pp.83-92
• /
• 2012

The effect of under-bump-metallization (UBM) on electromigration was investigated at temperatures ranging from $135^{\circ}C$ to $165^{\circ}C$. The UBM structures were examined: 5-${\mu}m$-Cu/3-${\mu}m$-Ni and $5{\mu}m$ Cu. Experimental results show that the solder joint with the Cu/Ni UBM has a longer electromigration lifetime than the solder joint with the Cu UBM. Three important parameters were analyzed to explain the difference in failure time, including maximum current density, hot-spot temperature, and electromigration activation energy. The simulation and experimental results illustrate that the addition 3-${\mu}m$-Ni layer is able to reduce the maximum current density and hot-spot temperature in solder, resulting in a longer electromigration lifetime. In addition, the Ni layer changes the electromigration failure mode. With the $5{\mu}m$ Cu UBM, dissolution of Cu layer and formation of $Cu_6Sn_5$ intermetallic compounds are responsible for the electromigration failure in the joint. Yet, the failure mode changes to void formation in the interface of $Ni_3Sn_4$ and the solder for the joint with the Cu/Ni UBM. The measured activation energy is 0.85 eV and 1.06 eV for the joint with the Cu/Ni and the Cu UBM, respectively.

• Proceedings of the KWS Conference
• /
• 2001.10a
• /
• pp.156-158
• /
• 2001