• 한국표면공학회지
• /
• 제43권6호
• /
• pp.278-282
• /
• 2010

In this research, the friction and wear characteristic behaviors of coating materials of TiAlN and CrAlN were investigated. The wear test was conducted in air and un-lubricated state using the reciprocating friction wear tester. Temperature were 50 and $120^{\circ}C$, and load were 3, 7, and 11 kgf for tests. By comparing the coefficient of friction and observing the wear microstructure, the friction and wear characteristic behaviors of TiAlN and CrAlN coating layers on SKD61 were investigated. The coefficient of friction of CrAlN coating was lower than that of TiAlN at all conditions. Therefore, CrAlN was suggested to be more advantageous coating than TiAlN for the extrusion mold of aluminum.

• 한국분말재료학회지
• /
• 제27권5호
• /
• pp.406-413
• /
• 2020

Ti_0.5Al_0.5N/CrN nano-multilayers, which are known to exhibit excellent wear resistances, were prepared using the unbalanced magnetron sputter for various periods of 2-7 nm. Ti_0.5Al_0.5N and CrN comprised a cubic structure in a single layer with different lattice parameters; however, Ti_0.5Al_0.5N/CrN exhibited a cubic structure with the same lattice parameters that formed the superlattice in the nano-multilayers. The Ti_0.5Al_0.5/CrN multilayer with a period of 5.0 nm exceeded the hardness of the Ti_0.5Al_0.5N/CrN single layer, attaining a value of 36 GPa. According to the low-angle X-ray diffraction, the Ti_0.5Al_0.5N/CrN multilayer maintained its as-coated structure up to 700℃ and exhibited a hardness of 32 GPa. The thickness of the oxidation layer of the Ti_0.5Al_0.5N/CrN multilayered coating was less than 25% of that of the single layers. Thus, the Ti_0.5Al_0.5N/CrN multilayered coating was superior in terms of hardness and oxidation resistance as compared to its constituent single layers.

• 한국표면공학회지
• /
• 제50권5호
• /
• pp.339-344
• /
• 2017

Highly corrosion resistance performance of CrAlSiN coatings were obtained by applying ultrathin $Al_2O_3$ thin films using atomic layer deposition (ALD) method. CrAlSiN coatings were prepared on Cr adhesion layer/SUS304 substrates by a hybrid coating system of arc ion plating and high power impulse magnetron sputtering (HiPIMS) method. And, ultrathin $Al_2O_3$ passivation layer was deposited on the CrAlSiN/Cr adhesion layer/SUS304 sample to protect CrAlSiN coatings by encapsulating the whole surface defects of coating using ALD. Here, the high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and energy dispersive X-ray spectrometry (EDX) analysis revealed that the ALD $Al_2O_3$ thin films uniformly covered the inner and outer surface of CrAlSiN coatings. Also, the potentiodynamic and potentiostatic polarization test revealed that the corrosion protection properties of CrAlSiN coatings/Cr/SUS304 sample was greatly improved by ALD encapsulation with 50 nm-thick $Al_2O_3$ thin films, which implies that ALD-$Al_2O_3$ passivation layer can be used as an effect barrier layer of corrosion.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2014년도 추계학술대회 논문집
• /
• pp.21-21
• /
• 2014

$CrN/Al_2O_3/CrN$ 다층 코팅을 HIPIMS와 ALD간 하이브리드 코팅법을 통해 형성하였다. ALD를 통해 CrN 층에 도입한 $Al2O_3$층의 두께 및 위치가 $CrN/Al_2O_3/CrN$ 다층 코팅층의 미세구조, 표면 거칠기, 기계적 특성 및 화학적 특성에 미치는 영향에 대해 조사하였다. 전체 공정시간은 거의 변화시키지 않고도, ALD를 이용한 $Al2O_3$층의 삽입에 의하여 기계적/화학적 특성이 크게 개선될 수 있음을 확인하였으며, 개선된 특성에 대한 원인에 대해 조사하였다.

• 한국세라믹학회지
• /
• 제54권6호
• /
• pp.511-517
• /
• 2017

With different working pressures and substrate biases, Cr-Al-N coatings were deposited by hybrid physical vapor deposition (PVD) method, consisting of unbalanced magnetron (UBM) sputtering and arc ion plating (AIP) processes. Cr and Al targets were used for the arc ion plating and the sputtering process, respectively. Phase analysis, and composition, binding energy, and microstructural analyses were performed using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and field emission scanning electron microscopy (FESEM), respectively. Surface droplet size of Cr-Al-N coatings was found to decrease with increasing substrate bias. A decrease of the deposition rate of Cr-Al-N films was expected due to the increase of substrate bias. The coatings were grown with textured CrN phase and (111), (200), and (220) planes. X-ray diffraction data show that all Cr-Al-N coatings shifted to lower diffraction angles due to the addition of Al. The XPS results were used to determine the $Cr_2N$, CrN, and (Cr,Al)N binding energies. The compositions of the Cr-Al-N films were measured by XPS to be Cr 23.2~36.9 at%, Al 30.1~40.3 at%, and N 31.3~38.6 at%.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2014년도 추계학술대회 논문집
• /
• pp.192-192
• /
• 2014

TiN, Ti(C,N), TiAlSiN, TiZrAlN, TiAlCrSiN 박막을 제조한 후, 이 들의 고온산화 특성을 SEM, EPMA, TGA, TEM, AES 등을 이용하여 조사하고, 산화기구를 제안하였다. 산화속도, 생성되는 산화물의 종류와 분포는 박막의 조성, 산화온도, 산화시간에 따라 변하였다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.53-54
• /
• 2013

Nano-multilayered CrAlSiN films consisting of crystalline CrN nanolayers and amorphous AlSiN nanolayers were deposited by cathodic arc plasma deposition. Their oxidation characteristics were studied between 600 and $1000^{\circ}C$ for up to 70 h in air. During their oxidation, the amorphous AlSiN nanolayers crystallized. The formed oxides consisted primarily of $Cr_2O_3$, ${\alpha}-Al_2O_3$, $SiO_2$. The outer $Al_2O_3$ layer formed by outward diffusion of Al ions. Simultaneously, an inner ($Al_2O_3$, $Cr_2O_3$)-mixed layer formed by the inward diffusion of oxygen ions. $SiO_2$ was present mainly in the lower part of the oxide layer due to its immobility. The CrAlSiN films displayed good oxidation resistance, owing to the formation of oxide crystallites of $Cr_2O_3$, ${\alpha}-Al_2O_3$, and amorphous $SiO_2$.

• 한국세라믹학회지
• /
• 제56권1호
• /
• pp.49-55
• /
• 2019

$Ti_{0.33}Al_{0.67}N/CrN$ nano-multilayers, which are known to have excellent wear resistance, were prepared using an unbalanced magnetron sputter to have various periods of 2-5 nm. $Ti_{0.33}Al_{0.67}N$ had a hexagonal structure in a single layer, but converted to a cubic structure by forming a multilayer with CrN, which has a cubic structure. Thus, $Ti_{0.33}Al_{0.67}N$ formed a superlattice in the multilayer. The $Ti_{0.33}Al_{0.67}/CrN$ multilayer with a period of 2.5 nm greatly exceeded the hardness of the $Ti_{0.33}Al_{0.67}N$ and the CrN single layer, reaching 39 GPa. According to the low angle X-ray diffraction results, the $Ti_{0.33}Al_{0.67}N/CrN$ multilayer maintained its as-coated structure to a temperature as high as $700^{\circ}C$ and exhibited hardness of 30 GPa. The thickness of the oxide layer of the $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating was less than one-tenth of those of the single layers. Thus, $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating had hardness and oxidation resistance far superior to those of its constituent single layers.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.161-161
• /
• 2012

결정질 TiCrN과 AlSiN 나노층이 교대로 구성하는 나노 다층 TiAlCrSiN 박막은 음극 아크 플라즈마 증착법에 의해 증착되었다. 나노 다층 TiAlCrSiN 박막의 산화특성들은 $600{\sim}1000^{\circ}C$사이에서 대기 중 최대 70시간동안 연구 되었다. 형성된 산화물들은 주로 $Cr_2O_3$, ${\alpha}-Al_2O_3$, $SiO_2$ 그리고 rutile-$TiO_2$들로 구성되었다. 나노 다층 TiAlCrSiN 박막이 산화하는 동안, 가장 바깥쪽의 $TiO_2$층은 Ti 이온의 외부확산에 의해, 외부 $Al_2O_3$층은 Al이온의 외부확산에 의해 형성되었다. 동시에, 내부($Al_2O_3$, $Cr_2O_3$) 혼합층과 가장 안쪽의 $TiO_2$층은 산소이온의 내부확산에 의해 형성되었다.

• 한국표면공학회지
• /
• 제31권3호
• /
• pp.157-164
• /
• 1998

Effects of alloying elements on the pitting behavior of Ti-Al intermetalic compounds in the electrolytic soution containing Cl- were investigated through electrochemical tets and corrosion morphologies. Corrosion potential increased in the case of Cr addition to Ti-48%Al, whereas it decreased in the case of Si and B addition. The simultaneous addition of Cr and Si increased passive current density and decrosion corrosion potential. The passive current density of N addtion was higher than that of B addition in H2SO4 solution. With the addition of alloying elements, The pitting resistance decreased in order of TiAl>TiAlSi>TiAlN>TiAlB>TiAlCr and whin siumultaneous addition, it decreased in order of TiAlCrSi>TiAlCrBN>TiAlCrrN. The surface merohology after pitting test showed that the TiAl coataining Si had for fewer pits than that containing Cr and N simultaneously.