• Journal of the Korean institute of surface engineering
• /
• v.15 no.1
• /
• pp.11-18
• /
• 1982

80% Ni-Permalloy is soft magnetic material with high initial permeability and low magnetic coercive force Hc, and is used to computer memory cores and minirelays of communication e-ngineering. In this paper 80 Permalloy thin film on copper cathode was alloy-deposited from Watts so-lution contatining FeSO4$.$7H2O. The amount of FeSO4$.$7H2O in the solution, pH, temperature of the solution and plating current density were varied as parameters and the resulting comp-osition changes of deposited film were analyzed electrochemically with respect to the parame-ters. From the above procedure electroplating conditions for deposition of 80 Permalloy were est-ablished as following: 17-21 g/$\ell$ of FeSO4$.$7H2O in Watts solution, current density 1.0-2.0 Amp/dm2, pH 2.5-3.0 and temperature range of 50-60$^{\circ}C$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.80-80
• /
• 2018

실리콘 관통전극 (Through Silicon Via, TSV)는 메모리 칩을 적층하여 고밀도의 집적회로를 구현하는 기술로, 기존의 와이어 본딩 (Wire bonding) 기술보다 낮은 소비전력과 빠른 속도가 특징인 3차원 집적기술 중 하나이다. TSV는 일반적으로 도금 공정을 통하여 충전되는데, 고종횡비의 TSV에 결함 없이 구리를 충전하기 위해서 3종의 유기첨가제(억제제, 가속제, 평탄제)가 도금액에 첨가되어야 한다. 이러한 첨가제 중 결함 발생유무에 가장 큰 영향을 주는 첨가제는 평탄제이기 때문에, 본 연구에서는 이미다졸(imidazole) 계열, 이민(imine) 계열, 디아조늄(diazonium) 계열 및 피롤리돈(pyrrolidone) 계열과 같은 평탄제(leveler)의 작용기에 따라 TSV 충전 성능을 조사하였다. TSV 충전 시 관능기의 거동을 규명하기 위해 QCM (quartz crystal microbalance) 및 EQCM (electrochemical QCM)을 사용하여 흡착 정도를 측정하였다. 실험 결과, 디아조늄 계열의 평탄제는 TSV를 결함 없이 충전하였지만 다른 작용기를 갖는 평탄제는 TSV 내 결함이 발생하였다. QCM 분석에서 디아조늄 계열의 평탄제는 낮은 흡착률을 보이지만 EQCM 분석에서는 높은 흡착률을 나타내었다. 즉, 디아조늄 계열의 평탄제는 전기 도금 동안 전류밀도가 집중되는 TSV의 상부 모서리에서 국부적인 흡착을 선호하며 이로 인하여 무결함 충전이 달성된다고 추론할 수 있다.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.3
• /
• pp.242-250
• /
• 2003

Electrodeposition of Ni was carried out on copper substrate from Ni Sulfamate bath by DC and high frequency pulse current. During the electroplating, bath temperature was steady $60^{\circ}C$ , agitation was applied. Morphology and surface roughness of electrodeposits was investigated with the AFM. Crystalline structure of electrodeposits was investigated with XRD. Also, surface electric resistivity was investigated with 4-point probe. The result of crystalline structure by X-ray diffractometer, in the case of DC, <200> direction was dominant growing direction. But in the case of PC, the ratio of <200> direction vs. other direction decreased. As the pulse frequency increased, the enhanced properties of deposits were shown. With increasing frequency, the degree of surface properties increased DC more than that of PC, eg surface morphology, roughness and the degree of compactness of grains. With increasing duty cycle, the surface properties such as the degree of the morphology, roughness and electroconductivity was deteriorated.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.3
• /
• pp.158-165
• /
• 1994

Cu-Cr alloy thin film requires good quality of etching be used for TAB technology. The etched cross sec-tion was clean enough when the etching was performed in 0.1M $FeCl_3$ solution at $50^{\circ}C$. The etching rate was increased with the amount of $KMnO_4$. For enhanced profile of cross section and rate, the spray etchning was found to be superior compared to the immersion etching. A series of experiments were performed to improve the uniformity of the current distribution in electrodeposition onto the substrate with lithographic patterns. Copper was electrodeposited from quiescent-solution, paddle-agitated-solution, and air-bubbled-solution to in-vestigate the effect of the fluid flow. The thickness profile of the specimen measured by profilmetry has the non uniformity at feature scale in quiescent-solution, because of the longitudinal vortex roll caused by the natural convection. However, uniform thickness profile was achieved in paddle-agitated or air bubbled solu-tion.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.2
• /
• pp.120-124
• /
• 2003

This paper describes a MEMS-based micro-fluxgate magnetic sensing element using Ni$\_$0.8/Fe$\_$0.2/ film formed by electroplating. The micro-fluxgate magnetic sensor composed of a thin film magnetic core and micro-structure solenoids for the pick-up and the excitation coils, is developed by using MEMS technologies in order to take advantage of low-cost, small size and lower power consumption in the fabrication. A copper with 20${\mu}$m width and 3${\mu}$m thickness is electroplated on Cr (300${\AA}$) / Au (1500${\AA}$) films for the pick-up (42turn) and the excitation (24turn) coils. In order to improve the sensitivity of the sensing element, we designed the magnetic core into a rectangular-ring shape to reduce the magnetic flux leakage. An electroplated permalloy film with the thickness of 3${\mu}$m is obtained under 2000 gauss to induce magnetic anisotropy. The magnetic core has the high DC effective permeability of ~1,100 and coercive field of ~0.1 Oe. The fabricated sensing element using rectangular-ring shaped magnetic film has the sensitivity of about 150 V/T at the excitation frequency of 2 MHz and the excitation voltage of 4.4 V$\_$p p/. The power consumption is estimated to be 50mW.

• Journal of the Korean institute of surface engineering
• /
• v.18 no.3
• /
• pp.105-115
• /
• 1985

Lead-tin-copper ternary alloy electrodeposition is conducted onto the inner bore surface of plain bearings as an overlay in order to investigate the effect of slot width, current density and fluoboric acid concentration on the uniformity of overlay. The thickness of overlay is analyzed by means of current distribution resulting from the overvoltage of plating bath and the apparent distance between cathode and anode. The result demonstrate that the uniformity of overlay is remarkably dependent of the slot size and current density, but has little bearing on the fluoboric acid concentration over 100g/L. This present study indicates that uniform overlay is obtainable within the tolerable thickness of ${\pm}2{\mu}m$ by using the slot width of 22mm. The surface morphology examination also shows the important role of concentration polarization of the micro-uniformity of overlay. The micro-uniformity has improved at the low concentration polarization which resulted from operating at the low current density and high fluoboric acid concentration. The surface morphology of deposits exhibits the vivid pyramid crystalline in the plating condition of low concentration polarizatio and all deposits have columnar structure parallel to the applied electric field regardless of the electroplating condition used.

• Progress in Superconductivity and Cryogenics
• /
• v.12 no.1
• /
• pp.1-5
• /
• 2010

Silver stabilizing layer of coated conductor has been prepared by dip coating method using organic silver complexes containing 10 wt% silver as a starting material. Coated silver complex layer was dried in situ with hot air and converted to crystalline silver by post heat treatment in flowing oxygen atmosphere. A dense continuous silver layer with good surface coverage and proper thickness of 230 nm is obtained by multiple dip coatings and heat treatments. The film heat treated at $500^{\circ}C$ showed good mechanical adhesion and crystallographic property. The interface resistivity between superconducting YBCO layer and silver layer prepared by dip coating was measured as $0.67\;{\times}\;10^{-13}\;{\Omega}m^2$. Additional protecting copper layer with the thickness of $20\;{\mu}m$ was successfully deposited by electroplating. The critical current measured with the specimen prepared by dip coating and sputtering on same quality YBCO layer showed similar value of ~140 A and proved its ability to replace sputtering method for industrial production of coated conductor.

• Journal of the Korean Electrochemical Society
• /
• v.5 no.3
• /
• pp.153-158
• /
• 2002

The effects of leveler on the copper trench filling were investigated during damascene plating process. To investigate the trench filling effect with the addition of a leveler, a cross-section images of the electroplated trenches with the width of$0.37{\mu}m,\;and\;0.18{\mu}m$ were observed by field emission scanning electron microscope (FE-SEM). Polyethylene glycol(PEG), 3-mercapto-1-propanesulfonic acid and Janus Green B were used as a carrier, an accelerator and a leveler. $0.37{\mu}m$ trenches were superfilled without voids, but there was voids formation in $0.18{\mu}m$ trenches when the leveler was not added into the electrolyte. On the other hand $0.18{\mu}m$ trenches were superfilled without voids with the addition of the leveler due to the reduction growth rate of copper at protrusions and edges, which yield smooth final deposit surface. The leverer effect becomes more significant as the width of trenches becomes smaller when trenches are filed.

• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.1
• /
• pp.55-60
• /
• 2021

In order to produce wearable displays with high adhesion while maintaining flexible characteristics, the adhesive method using electro plating method was carried out. Laser lift-off (LLO) transcription was also used to remove sapphire substrates from LEDs bonded to fibers. Afterwards, the SEM and EDS data of the sample, which conducted the adhesion method using electro plating, confirmed that copper actually grows through the lattice of the fiber fabric to secure the light source and fiber. The adhesion characteristics of copper were checked using Universal testing machine (UTM). After plating adhesion, the characteristics of the LLO transcription process completed and the LED without the transcription process were compared using probe station. The electroluminescence (EL) according to the enhanced current was measured to check the characteristics of the light source after the process. As the current increases, the temperature rises and the bandgap decreases, so it was confirmed that the spectrum shifted. In addition, the change in the electrical characteristics of the samples according to the radius change is confirmed using probe station. The radius strain also had mechanical strength that copper could withstand bending stress, so the Vf variation was measured below 6%. Based on these results, it is expected that it will be applied to batteries, catalysts, and solar cells that require flexibility as well as wearable displays, contributing to the development of wearable devices.

• Korean Journal of Ecology and Environment
• /
• v.44 no.3
• /
• pp.272-279
• /
• 2011

Copper cyanide is a chemical produced in large quantities with 2,500 tonnes being produced in 2006. It is mainly used for electroplating copper, particularly alkali-Cu plate and brass plating. The purpose of this study is to reassess the physicochemical properties and environmental fate of copper cyanide based on reliable data and and to conduct an ecotoxicity test according to the OECD test guidelines as an initial environmental risk assessment (need to state where this was done). Metal containing inorganic substances are not subject to degradation, biodegradation or hydrolysis. Aquatic toxicity tests of copper cyanide were conducted according to OECD test guideline 201, 202 and 203 for green algae, daphnia, and fish, respectively. The following acute toxicity test results were obtained for aquatic species: 0.089 mg $L^{-1}$ (Algae, 72 Hr-$EC_{50}$); 0.21 mg $L^{-1}$ (flea, 48 Hr-$LC_{50}$); 0.62 mg $L^{-1}$ (Fish, 96 Hr-$ErC_{50}$). The chemical possesses properties indicating a hazard for the aquatic environment (acute toxicity in fish, daphnia and algae below 1.0 mg $L^{-1}$). As a result of this study, copper cyanide has become a candidate for detailed risk assessment. Countries that produce this chemical in significant quantities are recommended to perform specific assessments.