• Korean Journal of Materials Research
• /
• v.8 no.7
• /
• pp.579-583
• /
• 1998

Silicide layer structures, agglomeration of silicide layers, and dopant redistributions for the Co/Ti bilayer sputter-deposited on the P-doped polycrystalline Si substrate and subjected to rapid thermal annealing were investigated and compared with those on the single Si substrate. The $CoSi_2$ phase transition temperature is higher and agglomeration of the silicide layer occurs more severely for the Co/Ti bilayer on the doped polycrystalline Si substrate than on the single Si substrate. Also, dopant loss by outdiffusion is much more significant on the doped polycrystalline Si substrate than on the single Si substrate. All of these differences are attributed to the grain boundary diffusion and heavier doping concentration in the polycrystalline Si. The layer structure after silicidation annealing of Co/ Tildoped - polycrystalline Si is polycrystalline CoSi,/polycrystalline Si, while that of Co/TiI( 100) Si is Co- Ti- Si/epi- CoSi,/(lOO) Si.

• Journal of the Korean Ceramic Society
• /
• v.35 no.5
• /
• pp.505-511
• /
• 1998

The silicide formation mechanisms of Co/Hf and Co/Nb bilayer on (100) Si have been investigated. We ob-served that crystallographic orientationso f the 500$^{\circ}C$ formed cobalt silcides were different each other with the varying intermediate layers. Epitaxial and non-epitaxial CoSi2 formed simultaneously in Co/Hf/(100Si. While only non-epitaxial CoSi2 formed in Co/Nb/(100) Si. The reason why the crystallographic orientation of CpSi2 is different for those two systems seemed to be relate to the formation and decomposition of stable reaction barriers at high temperature. The stable reaction barrier formed at high temperature could control the uniform diffusion of Co atoms which enables epitaxial growth of CoSi2.

• Korean Journal of Materials Research
• /
• v.6 no.12
• /
• pp.1192-1198
• /
• 1996

배선 재료나 salicide 트랜지스터에 적용될 것으로 기대되는 Cu 배선과 Co 단일층 및 Co/Ti 이중층을 사용하여 형성된 코발트 실리사이드간의 열적 안정성에 대하여 조사하였다. 40$0^{\circ}C$열처리후 Cu3Si 막이 CoSi2층과 Si 기판 사이에 형성되었는데, 이것은 Cu 원자의 확산에 기인한 것이다. $600^{\circ}C$에서의 열처리 후에 형성된 최종막의 구조는 각각 Cu/CoSi2/Cu3Si/Si과 TiO2/Co-Ti-Si 합금/CoSi2/Cu3Si/Si였으며, 상부에 형성된 TiO2층은 산소 오염에 의한 것으로 밝혀졌다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.1
• /
• pp.62-72
• /
• 1996

The interface formation and reaction-product morphology between SiC and thin metal films were studied at temperatures between 550 and $1450^{\circ}C$ for various times. The typical reaction layer sequence was CoSi/CoSi+C/CoSi/CoSi+C/ $\cdots$ /SiC reaction at 1050 and $1250^{\circ}C$ for 2 h, while $Ni_2Si/Ni_2Si+C/Ni_2Si/Ni_2Si+C/ {\cdots} /SiC$ at 950 and 105$0^{\circ}C$ for 2 h. Carbon precipitated preferentially on the outer surface and crystallized as graphite above $1450^{\circ}C$ for SiC/Co reaction zone and $1250^{\circ}C$ for SiC/Ni. The mechanism of the periodic band structure formation with carbon precipitation behaviour was discussed in terms of thermodynamic considerations.

• Korean Journal of Materials Research
• /
• v.6 no.8
• /
• pp.779-785
• /
• 1996

Thin $700^{\circ}C$films were formed through layer inversion of Co/Nb bilayer during rapid thermal annealing(RTA). The Nb interlayer seems to effectively prevent over-consumption of Si and to control the silicidation reaction by forming Co-Nb intermetallic compounds and removing the native oxide formed on Si substrate which interferes the uniform Co-Si interaction. The final layer structure of the Co/Nb bilayer after $700^{\circ}C$ RTA was found to be ${Nb}_{2}{O}_{3}$/${Co}_{2}$Si.CoSi/${NbCo}_{x}$/Nb(O, C)/${CoSi}_{2}$/ Si. The layer inversion and the formation of a stable CoSi, phase occurred above $700^{\circ}C$, and the Nb silicides were not found at any annealing temperature. These may be due to the formation of very stable Co-Nb intermetallic compounds and Nb oxides which limit the moving of Co and Si.

• Korean Journal of Materials Research
• /
• v.5 no.3
• /
• pp.324-332
• /
• 1995

전자빔 증착법을 사용하여 Ti과 Co를 Si(100) 단결정, 다결정 Si 및 Si$O_{2}$기판에 증착한 후 90$0^{\circ}C$에서 20초 급속 열처리하여, Co/Ti 이중박막으로부터의 실리사이드화 반응을 조사하였다. 단결정 시편의 경우 Ti의 두께를 5~6mm로 최소화함으로서 두께가 균일하고 기판과의 계면이 평탄하며 비저항이 낮고 열적 안정성이 높은 Co$Si_{2}$ 에피박막을 형성할 수 있었다. 그러나 다결정 시편에는 두께와 계면이 불균일하고 열적으로도 불안정한 다결정의 Co$Si_{2}$와 그 위에 두개의 Co-Ti-Si혼합층이 형성되었다. 한편 Si$O_{2}$ 우에 증착된 Co/Ti은 열처리를 하여도 확산하지 않고 그대로 남아 있어서, Co/Ti 이중박막의 Si$O_{2}$와의 반응성이 미약함을 보여 주었다.

• Korean Journal of Materials Research
• /
• v.11 no.8
• /
• pp.641-646
• /
• 2001

The $CoSi_2$ layers have been in-situ grown on undoped poly-Si by the reactive chemical vapor deposition of $Co({\Eta}^5-C_5H_5)(CO)_2$ at $650^{\circ}C$ and their thermal stabilities have been investigated in the temperature range of 800 to $1000^{\circ}C$. The $CoSi_2$ layer grown by the in-situ method had grains with large area of (111) plane, while grains with little area of (111) plane appeared on the $CoSi_2$ layer grown by the conventional two-step method where $CoSi_2$ formed first and transformed to $CoSi_2$. The thermal stability of the $CoSi_2$ layer grown by the in- situ process was improved by more than $100^{\circ}C$ higher than that of the $CoSi_2$ layer grown by the conventional two-step process. The $CoSi_2$ layer grown in situ on a large-grained Poly-Si was stable up to $950^{\circ}C$. The effect of stability improvement by the in situ growth was more pronounced when the grain sizes of the poly-Si substrate were small. The improved thermal stability of the in-situ grown $CoSi_2$ layer could be mainly due to the formation of a uniform $CoSi_2$ layer with the $CoSi_2$ grains, which are in the form of epitaxial-like growth on the each poly-Si grains, causing a reduction of the interfacial energy of the system.

• Journal of the Korean Magnetics Society
• /
• v.17 no.4
• /
• pp.147-151
• /
• 2007

We have investigated the half-metallicity and magnetism for the Heusler ferromagnet $Co_2$ZrSi interfaced with semiconductor ZnTe along the (001) plane by using the full-potential linearized augmented plane wave (FLAPW) method. We considered low types of possible interfaces: ZrSi/Zn, ZrSi/Te, Co/Zn, and Co/Te, respectively. From the calculated density of states, it was found that the half-metallicity was lost at all the interfaces, however for the Co/Te system the value of minority spin density of states was close to zero at the Fermi level. These facts are due to the interface states, appeared in the minority spin gap in bulk $Co_2$ZrSi, caused by the changes of the coordination and symmetry and the hybridizations between the interface atoms. At the Co/Te interface, the magnetic moments of Co atoms are 0.68 and $0.78{\mu}_B$ for the "bridge" and "antibridge" sites, respectively, which are much reduced with respect to that ($1.15{\mu}_B$) of the bulk $Co_2$ZrSi. In the case of Co/Zn, Co atoms at the "bridge" and "antibridge" sites have magnetic moments of 1.16 and $0.93{\mu}_B$, respectively, which are almost same or slightly decreased compared to that of the bulk $Co_2$ZrSi. On the other hand, for the ZrSi/Zn and ZrSi/Te systems, the magnetic moments of Co atoms at the sub-interface layers are in the range of $1.13{\sim}1.30\;{\mu}_B$, which are almost same or slightly increased than that of the bulk $Co_2$ZrSi.

• Journal of the Korean Vacuum Society
• /
• v.7 no.3
• /
• pp.208-213
• /
• 1998

Silicidation of the Co/Ti/Si bilayer system in which Ti is used as epitaxy promoter for $CoSi_2$has recently received much attention. The Co/Ti bilayer on the spacer oxide of gate electrode must be thermally stable at high temperatures for a salicide transistor to be fabricated successfully. In the $SiO_2$substrate was rapid-thermal annealed. The Sheet resistances of the Co/Ti bilayer increased substantially after annealing at $600^{\circ}C$, which is due to the agglomeration of the Co layer to reduce the interface energy between the Co layer and the $SiO_2$substrate. In the bilayer system insulating Ti oxide stoichiometric Ti oxide and silicide were not found after annealing.

• Korean Journal of Materials Research
• /
• v.13 no.1
• /
• pp.1-5
• /
• 2003

Uniform polycrystalline $CoSi_2$layers have been grown in situ on a polycrystalline Si substrate at temperature near $625^{\circ}C$ by reactive chemical vapor deposition of cyclopentadienyl dicarbonyl cobalt, Co(η$^{5}$ -C$_{5}$ H$_{5}$ )(CO)$_2$. The growth behavior and thermal stability of $CoSi_2$layer grown on polycrystalline Si substrates were investigated. The plate-like CoSi$_2$was initially formed with either (111), (220) or (311) interface on polycrystalline Si substrate. As deposition time was increasing, a uniform epitaxial $CoSi_2$layer was grown from the discrete $CoSi_2$plate, where the orientation of the$ CoSi_2$layer is same as the orientation of polycrystalline Si grain. The interface between $CoSi_2$layer and polycrystalline Si substrate was always (111) coherent. The growth of the uniform $CoSi_2$layer had a parabolic relationship with the deposition time. Therefore we confirmed that the growth of $CoSi_2$layer was controlled by diffusion of cobalt. The thermal stability of $CoSi_2$layer on small grain-sized polycrystalline Si substrate has been investigated using sheet resistance measurement at temperature from $600^{\circ}C$ to $900^{\circ}C$. The $CoSi_2$layer was degraded at $900^{\circ}C$. Inserting a TiN interlayer between polycrystalline Si and $_CoSi2$layers improved the thermal stability of $CoSi_2$layer up to $900^{\circ}C$ due to the suppression of the Co diffusion.