• Transactions on Electrical and Electronic Materials
• /
• v.18 no.1
• /
• pp.55-57
• /
• 2017

Amorphous oxide thin film transistors (TFTs) were fabricated with 0.5 wt% silicon doped zinc tin oxide (a-0.5SZTO) thin film deposited by radio frequency (RF) magnetron sputtering. In order to investigate the effect of annealing treatment on the electrical properties of TFTs, a-0.5SZTO thin films were annealed at three different temperatures ($300^{\circ}C$, $500^{\circ}C$, and $700^{\circ}C$ for 2 hours in a air atmosphere. The structural and electrical properties of a-0.5SZTO TFTs were measured using X-ray diffraction and a semiconductor analyzer. As annealing temperature increased from $300^{\circ}C$ to $500^{\circ}C$, no peak was observed. This provided crystalline properties indicating that the amorphous phase was observed up to $500^{\circ}C$. The electrical properties of a-0.5SZTO TFTs, such as the field effect mobility (${\mu}_{FE}$) of $24.31cm^2/Vs$, on current ($I_{ON}$) of $2.38{\times}10^{-4}A$, and subthreshold swing (S.S) of 0.59 V/decade improved with the thermal annealing treatment. This improvement was mainly due to the increased carrier concentration and decreased structural defects by rearranged atoms. However, when a-0.5SZTO TFTs were annealed at $700^{\circ}C$, a crystalline peak was observed. As a result, electrical properties degraded. ${\mu}_{FE}$ was $0.06cm^2/Vs$, $I_{ON}$ was $5.27{\times}10^{-7}A$, and S.S was 2.09 V/decade. This degradation of electrical properties was mainly due to increased interfacial and bulk trap densities of forming grain boundaries caused by the annealing treatment.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1999.06a
• /
• pp.419-431
• /
• 1999

InP, III-V binary compound semiconductor, single crystal was grown by VGF (vertical gradient freeze) method using quartz ampoule and its electrical optical properties were investigated. Phosphorous powders were put in the bottom of quartz ampoule and Indium metal changed in conical quartz crucible hat was attached at the upper side position inside the quartz ampoule. It was vacuous under the pressure of 10-5 Torr and sealed up. In metal in the quartz crucible was melted at 1070$^{\circ}C$ and phophorous sublimated at 450$^{\circ}C$, there after it was diffused in In melt and so InP composition was formed. By cooling the InP composition melt (2$^{\circ}C$∼5$^{\circ}C$/hr of cooling rate) in range of 1070$^{\circ}C$∼900$^{\circ}C$, InP crystal was grown. the grown InP single crystals were investigated by X-ray analysis and polarized optical microscopy. Electrical properties of them were measured by Van der Pauw method. At the cooling rate of 2$^{\circ}C$/hr, its direction was (111), quality of the ingot ws better upper side of the ingot than lower. It was found that the InP crystals were n-type semiconductor and the carrier concentration, electron mobility and relative resistivity were 1015∼1016/㎤, 2x103∼3x104$\textrm{cm}^2$/Vsec and 2x10-1∼2x10-3Ωcm in the range of 150K∼300K, respectively.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.98.2-98.2
• /
• 2010

$CuInS_2$ thin films were synthesized by sulfurization of Cu/In Stacked elemental layer deposited onto glass Substrates by vacuum furnace annealing at temperature 200[$^{\circ}C$]. And structural and electrical properties were measured in order to certify optimum conditions for growth of the ternary compound semiconductor $CuInS_2$ thin films with non-stoichiometry composition. $CuInS_2$ thin film was well made at the heat treatment 200[$^{\circ}C$] of SLG/Cu/In/S stacked elemental layer which was prepared by thermal evaporator, and chemical composition of the thin film was analyzed nearly as the proportion of 1 : 1 : 2. Physical properties of the thin film were investigated at various fabrication conditions substrate temperature, annealing and temperature, annealing time by XRD, FE-SEM and hall measurement system. At the same time, carrier concentration, hall mobility and resistivity of the thin films was $9.10568{\times}10^{17}$ [$cm^{-3}$], 312.502 [$cm^2/V{\cdot}s$] and $2.36{\times}10^{-2}$ [${\Omega}{\cdot}cm$], respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.1
• /
• pp.12-16
• /
• 2020

Indium tin oxide (ITO) films were prepared onto transparent polyimide (PI) substrates by RF magnetron sputtering at room temperature. The deposited ITO films were heat-treated at various temperatures (50, 100, 150, and 200℃). The effect of post heat-treatment temperature on structural, electrical and optical properties of ITO films were investigated. It was found that the as-deposited ITO films were amorphous and the degree of crystallinity and the grain size increased with an increasing heat-treatment temperature, which led to the increase in carrier concentration and mobility. The electrical resistivity of as-deposited ITO films was 2.73 × 10^-3 Ω·cm. With the heat-treatment temperature increasing from 50 to 200℃, the electrical resistivity decreased from 2.93 × 10^-3 to 1.21 × 10^-4 Ω·cm. The average transmittance (400~800 nm) of the ITO deposited PI substrates was decreasing with post heat-treatment temperature and was above 81 % for the temperatures 50~150℃ and decreased considerably to 78 % at 200℃.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.2
• /
• pp.114-120
• /
• 2012

In this research, we prepared Ga doped zinc oxide(ZnO:Ga, GZO) targets each difference sintering temperature $700^{\circ}C$, $800^{\circ}C$, and doping rate 1 wt.%, 2 wt.%, 3 wt.%. The characteristics of thin film on glass substrates which deposited by facing target sputtering in pure Ar atmosphere are reported. Ga doped zinc oxide film is attracted material through low resistivity, high transmittance, etc. When prepared target powder's structure was investigated by scanning electron microscope, densification and coarsening by driving force was observed. For each ZnO:Ga films with a $Ga_2O_3$ content of 3 wt.% at input power of 45W, the lowest resistivity of $9.967{\times}10^{-4}{\Omega}{\cdot}cm$ ($700^{\circ}C$) and $9.846{\times}10^{-4}{\Omega}{\cdot}cm$ ($800^{\circ}C$) was obtained. the carrier concentration and mobility were $4.09{\times}10^{20}cm^{-3}$($700^{\circ}C$), $4.12{\times}10^{20}cm^{-3}$($800^{\circ}C$) and $15.31cm^2/V{\cdot}s(700^{\circ}C)$, $12.51cm^2/V{\cdot}s(800^{\circ}C)$, respectively. And except 1 wt.% Ga doped ZnO thin film, average transmittance of these samples in the range 350-800 nm was over 80%.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.143-143
• /
• 2010

In this study, we demonstrate that ZnO deposited onto $SiO_2$ substrates by magnetron sputtering produces p-type ZnO at higher $O_2$ pressure and n-type ZnO at lower $O_2$ pressure. We also report the effect of hydrogen peroxide ($H_2O_2$) on the stability of undoped ZnO thin films. The films were immersed in 30% $H_2O_2$ for 1 min at $30^{\circ}C$ and annealed in $O_2$at $450^{\circ}C$. The carrier concentration, mobility. and conductivity were measured by a Hall effect measurement system. The Hall measurement results for ZnO films untreated with $H_2O_2$ but annealed in $O_2$ indicate that oxygen fraction greater than ~0.5 produces undoped p-type ZnO films, whereas oxygen fraction less than ~0.5 produces undoped n-type ZnO films. This is attributed to the fact that the oxygen vacancies ($V_o$) decrease and the oxygen interstitials ($O_i$) or zinc vacancies ($V_{Zn}$) increase with increasing oxygen atoms incorporated into ZnO films during deposition and $O_2$ post-annealing.

• Korean Journal of Crystallography
• /
• v.1 no.1
• /
• pp.19-28
• /
• 1990

6H-SiC is a promising material (Eg=3.0eV) for blue light-emitting doide and high-temperature semiconducting device. In the experiment, single crystals of a-SiC have been grown by the sublimation method to fabricate blue light~emitting diode. During the growth of a-SiC single crystals, a temperature Vadient, yonh temperature and pressure ranges were kept 44℃/cm , 1800-1990℃ and 50-1000 mTorr, respectively. Single crystals obtained in Acheson furnace were used as seed crystals. Polarizing microscopy and back-reflection X-ray Laue diffraction showed that the a-SiC crystal was epitaxially and on the seed crytal. It was found by XRD analysis that when other growth conditions were the same, a-SiC was grown at the temperature above 1840℃ and 3C-SiC was gown at lower temperature or under low supersaturation of vapor. The carrier type. concentration and mobility were measured be hole(p-type), 7.6x1014cm-3 and 19cm2V-1sec-1, respectively, by van der Pauw method.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.12
• /
• pp.961-965
• /
• 2010

In this study, we investigated the optical, electrical, and structural properties of the IGZO($In_2O_3:Ga_2O_3:ZnO$=1:9:90 wt.%) thin films prepared by RF-magnetron sputtering system under various substrate temperatures. All of the IGZO thin films shows an average transmittance of over the 80% in visible range. Most of all, deposited IGZO thin film at $100^{\circ}C$ substrate temperature have ZnO (002) of main growth peak and 17.02 nm of increased grains. And also IGZO thin film have low resistivity($1.35{\times}10^{-3}\;\Omega{\cdot}cm$), high carrier concentration($6.62{\times}10^{20} cm^{-3}$) and mobility($80.1 cm^2$/Vsec). IGZO thin film have 2.08 mV at surface potential of electric force microscopy(EFM). We suggest that pre-annealing at $100^{\circ}C$ can be applied for improving optical, electrical and structural properties.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.398.1-398.1
• /
• 2014

The $Cu_2ZnSnSe_4$ (CZTSe) thin films solar cell is one of the next generation candidates for photovoltaic materials as the absorber of thin film solar cells because it has optimal bandgap (Eg=1.0eV) and high absorption coefficient of $10^4cm^{-1}$ in the visible length region. More importantly, CZTSe consists of abundant and non-toxic elements, so researches on CZTSe thin film solar cells have been increasing significantly in recent years. CZTSe thin film has very similar structure and properties with the CIGS thin film by substituting In with Zn and Ga with Sn. In this study, As-deposited CZTSe thin films have been deposited onto soda lime glass (SLG) substrates at different deposition condition using Pulsed Laser Deposition (PLD) technique without post-annealing process. The effects of deposition conditions (deposition time, deposition temperature) onto the structural, compositional and optical properties of CZTSe thin films have been investigated, without experiencing selenization process. The XRD pattern shows that quaternary CZTSe films with a stannite single phase. The existence of (112), (204), (312), (008), (316) peaks indicates all films grew and crystallized as a stannite-type structure, which is in a good agreement with the diffraction pattern of CZTSe single crystal. All the films were observed to be polycrystalline in nature with a high (112) predominant orientation at $2{\theta}{\sim}26.8^{\circ}$. The carrier concentration, mobility, resistivity and optical band gap of CZTSe thin films depending on the deposition conditions. Average energy band gap of the CZTSe thin films is about 1.3 eV.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.5
• /
• pp.193-197
• /
• 2005

Highly c-axis oriented Zinc oxide (ZnO) films were successfully deposited at room temperature by oxygen ion-assisted pulsed filtered vacuum arc. The effect of oxygen gas ratio ($O_{2}/O_{2}+Ar$ on the preferred orientation, surface morphology and resistivity of the ZnO films were investigated. Highly crystalline ZnO films with (002) orientation were obtained at over $13\%$ of oxygen gas ratio. Increasing oxygen gas ratio up to $80\%$ was found to improve crystallinity of the films. From hall measurements, it was found that the film has n-type characteristic and carrier concentration and its mobility were closely related with oxygen gas ratio. Minimal resistivity of $3.6{\times}10^{-3}{\Omega}{\cdot}cm$ was obtained in the range of $20\%$ to $40\%$ of oxygen gas ratio.