• Corrosion Science and Technology
• /
• 제20권3호
• /
• pp.118-128
• /
• 2021

The oxide layer in samples taken from an irradiated Zr-2.5Nb pressure tube from a CANDU-PHWR reactor was analyzed using electron probe microanalysis (EPMA). The examined tube had been exposed to temperatures ranging from 264 to 306 ℃ and a neutron fluence of 8.9 × 10²¹ n/cm² (E > 1 MeV) for the maximum 10 effective full-power years in a nuclear power plant. Measuring oxide layer thickness generally employs optical microscopy. However, in this study, analysis of the oxide layer from the irradiated pressure tube components was undertaken through X-ray image mapping obtained using EPMA. The oxide layer characteristics were analyzed by X-ray image mapping with 256 × 256 pixels using EPMA. In addition, the slope of the oxide layer was measured for each location. A particular advantage of this study was that backscattered electrons and X-ray image mapping were obtained at a magnification of 9,000 when 20 kV volts and 30 uA of current were applied to radiation-shielded EPMA. The results of this study should usefully contribute to the study of the oxide layer properties of various types of metallic materials irradiated by high radiation in nuclear power plants.

• Corrosion Science and Technology
• /
• 제20권6호
• /
• pp.466-474
• /
• 2021

A wet type scrubber for merchant vessel uses super austenitic stainless steels with pitting resistance equivalent number (PREN) of 40 or higher for operation in a harsh corrosive environment. However, it is expensive due to a high nickel content. Thus, electrochemical behavior and cavitation erosion characteristics of UNS S32750 as an alternative material were investigated. Microstructure analysis revealed fractions of ferritic and austenitic phases of 48% and 52%, respectively, confirming the existence of ferritic matrix and austenitic island. Potentiodynamic polarization test revealed damage at the interface of the two phases because of galvanic corrosion due to different chemical compositions of ferritic and austenitic phases. After a cavitation test, a compressive residual stress was formed on the material surface due to impact pressure of cavity. Surface hardness was improved by water cavitation peening effect. Hardness value was the highest at 30 ㎛ amplitude. Scanning electron microscopy revealed wave patterns due to plastic deformation caused by impact pressure of the cavity. The depth of surface damage increased with amplitude. Cavitation test revealed larger damage caused by erosion in the ferritic phase due to brittle fracture derived from different strain rate sensitivity index of FCC and BCC structures.

• Corrosion Science and Technology
• /
• 제20권6호
• /
• pp.412-425
• /
• 2021

Because austenitic stainless steel causes localized corrosion such as pitting and crevice corrosion in environments containing chlorine, corrosion resistance is improved by surface treatment or changes of the alloy element content. Accordingly, research using cyclic potentiodynamic polarization experiment to evaluate the properties of the passivation film of super austenitic stainless steel that improved corrosion resistance is being actively conducted. In this investigation, the electrochemical properties of austenitic stainless steel and super austenitic stainless steel were compared and analyzed through cyclic potentiodynamic polarization experiment with varying temperatures. Repassivation properties were not observed in austenitic stainless steels at all temperature conditions, but super austenitic stainless steels exhibited repassivation behaviors at all temperatures. This is expressed as α values using a relational formula comparing the localized corrosion rate and general corrosion rate. As the α values of UNS S31603 decreased with temperature, the tendency of general corrosion was expected to be higher, and the α value of UNS N08367 increased with increasing temperatures, so it is considered that the tendency of localized corrosion was dominant.

• Corrosion Science and Technology
• /
• 제20권6호
• /
• pp.484-490
• /
• 2021

Instrumented indentation testing has been widely used for residual stress measurement. The Knoop indentation is mainly selected for determining anisotropic mechanical properties and non-equibiaxial residual stress. However, the measurement of equibiaxial stress state and compressive residual stress on a specimen surface using Knoop indentation is neither fully comprehended nor unavailable. In this study, we investigated stress conversion factors for measuring Knoop indentation on equibiaxial stress state through indentation depth using finite element analysis. Knoop indentation was conducted for specimens to determine tensile and compressive equibiaxial residual stress. Both were found to be increased proportionally according to indentation depth. The stress field beneath the indenter during each indentation test was also analyzed. Compressive residual stress suppressed the in-plane expansion of stress field during indentation. In contrast, stress fields beneath the indenter developed diagonally downward for tensile residual stress. Furthermore, differences between trends of stress fields at long and short axes of Knoop indenter were observed due to difference in indenting angles and the projected area of plastic zone that was exposed to residual stress.

• Corrosion Science and Technology
• /
• 제20권6호
• /
• pp.391-402
• /
• 2021

In this investigation, the electrochemical characteristics of superaustenitic and general austenitic stainless steels were compared by conducting potentiodynamic polarization experiment with varying temperatures in natural seawater solution. From the result of the potentiodynamic polarization experiment, the corrosion rate of UNS S31603 was found to be 17 times faster than that of UNS N08367 under the most severe corrosion conditions. The relationship between the corrosion rate by maximum damage depth and the corrosion rate by the corrosion current density was expressed as α value for each stainless steel. The α value of UNS S31603 under all temperature conditions was higher than that of UNS N08367 under similar conditions. This means that UNS S31603 is more prone to localized corrosion than UNS N08367. UNS S31603 expressed pitting type damages under all temperature conditions as shown by SEM analysis results. The pitting damage rapidly grew at the relatively poor grain boundaries. Damage on UNS N08367 was not clearly represented at 30 ℃ and 60 ℃, and slight intergranular corrosion damage was observed on the entire surface at 90 ℃.

• Corrosion Science and Technology
• /
• 제21권2호
• /
• pp.158-169
• /
• 2022

The objective of this study was to investigate the electrochemical behavior and damage degree of metal surface under different conditions by performing a potentiodynamic polarization experiment using an electropolishing solution for UNS S31603 based on initial delay time and surface roughness (parameters). A second anodic peak occurred at initial delay time of 0s and 100s. However, it was not discovered at 1000s and 3600s. This research referred to an increase in current density due to hydrogen oxidation reaction among various hypotheses for the second anodic peak. After the experiment, both critical current density and corrosion current density decreased when the initial delay time (immersion time) was longer. As a result of surface analysis, characteristics of the potentiodynamic polarization behavior were similar with roughness, although the degree of damage was clearly different. With an increase in surface roughness value, the degree of surface damage was precisely observed. As such, electrochemical properties were different according to the immersion time in the electropolishing solution. To select electropolishing conditions such as applied current density, voltage, and immersion time, 1000s for initial delay time on the potentiodynamic polarization behavior was the most appropriate in this experiment.

• Corrosion Science and Technology
• /
• 제21권6호
• /
• pp.445-453
• /
• 2022

SiO_x was prepared from a mixture of Si and SiO₂ via high-energy ball milling as a negative electrode material for Li-ion batteries. The molar ratio of Si to SiO₂ as precursors and the milling time were varied to identify the synthetic condition that could exhibit desirable anode performances. With an appropriate milling time, the material showed a unique microstructure in which amorphous Si nanoparticles were intimately embedded within the SiO₂ matrix. The interface between the Si and SiO₂ was composed of silicon suboxides with Si oxidation states from 0 to +4 as proven by X-ray photoelectron spectroscopy and electrochemical analysis. With the addition of a conductive carbon (Super P carbon black) as a coating material, the SiO_x/C manifested superior specific capacity to a commercial SiO_x/C composite without compromising its cycle-life performance. The simple mechanochemical method described in this study will shed light on cost-effective synthesis of high-capacity silicon oxides as promising anode materials.

• Corrosion Science and Technology
• /
• 제21권2호
• /
• pp.147-157
• /
• 2022

Electrochemical characteristics and damage behavior of 6061-T6 aluminum alloy used as a battery housing material for electric vehicles were investigated in solution simulating the acid rain environment with chloride concentrations. Potentiodynamic polarization test was performed to analyze electrochemical characteristics. Damage behavior was analyzed through Tafel analysis, measurement of damage area, weight loss, and surface observation. Results described that corrosion current density was increased rapidly when chloride concentration excceded 600 PPM, and it was increased about 7.7 times in the case of 1000 PPM compared with 0 PPM. Potentiodynamic polarization experiment revealed that corrosion damage area and mass loss of specimen increased with chloride concentrations. When chloride concentration was further increased, the corrosion damage area extended to the entire surface. To determine damage tendency of pitting corrosion according to chloride concentration, the ratio of damage depth to width was calculated. It was found that the damage tendency decreased with chloride concentrations. Thus, 6061-T6 aluminum alloy damage becomes larger in the width direction than in the depth direction when a small amount of chloride is contained in an acid rain environment.

• Corrosion Science and Technology
• /
• 제21권1호
• /
• pp.9-20
• /
• 2022

The aim of this paper is to study corrosion inhibition of Aluminum with Capparis decidua extract. The study was performed in a 1.0 M solution of hydrochloric acid (HCl) and was monitored both by measuring mass loss and by using electrochemical and polarization methods. A scanning electron microscopy (SEM) technique was also applied for surface morphology analysis. The results revealed high inhibition efficiency of Capparis decidua extract. Our data also determined that efficiency is governed by temperature and concentration of extract. Optimum (88.2%) inhibitor efficiency was found with maximum extract concentration at 45 o C. The results also showed a slight diminution of aluminum dissolution when the temperature is low. Based on the Langmuir adsorption model, Capparis decidua adsorption on the aluminum surface shows a high regression coefficient value. From the results, the activation enthalpy (∆H#) and activation entropy (∆S#) were estimated and discussed. In conclusion, the study clearly shows that Capparis decidua extract acted against aluminum corrosion in acidic media by forming a protective film on top of the aluminum surface.

• Corrosion Science and Technology
• /
• 제22권2호
• /
• pp.115-122
• /
• 2023

This study aimed to elucidate causes of corrosion of heat transport pipes and air vents installed under a manhole of heat transport facilities and suggest effective anticorrosive measures by applying paints or adhesive tapes. It was found that air vent corrosion was attributed to corrosion under insulation caused by the inflow of water and the enrichment of chloride ions. The infiltrated water caused a hydrolysis of polyurethane foam (PUF) insulation by concentrating chloride ions at the interface between a pipe and the PUF. As insulator deteriorated, more chloride ions were eluted as confirmed by ion chromatograph (IC) analysis. As an effective method to prevent air vent corrosion, different types of paints and adhesive tapes with higher corrosion resistance on chloride ions were applied and environmental resistance tests were performed with those samples. Based on environmental test results of samples exposed to 10% HCl solution, it was revealed that a wax tape was the most adequate from a viewpoint of stability at operating condition, environmental resistance, surface treatment, and field applicability.