• Korean Journal of Materials Research
• /
• v.3 no.5
• /
• pp.553-561
• /
• 1993

In this study, thr effect of $Bi_2O_3$ and BN addition as grain boundary modifiers on sintering and electrical properties of semiconducting PTCR(Positive Temperature Coefficient of Resistivity) mate rial were analyzed using TMA, XRD and Complex Impedance Spectroscopy method. Bismut.h Ox~de and Boron Nitride were added to Y-doped $BaTiO_3$ respectively. Bismuth sesquioxide up to O.lmol%solubil~ ty limit of $Bi_2O_3$ in Y--$BaTiO_3$ ceramics-retarded densification and grain growth, and further addition mitigated these retardation effects. The resistivity at room temperature increased with increasing amount of $Bi_2O_3$ and thus decreased the PTCR effect, probably due to the $Bi_2O_3$ segregation on the grain boundaries. From the complex ~mpedance pattern, it is known that the grain boundary resisitivity is dominant on the whole resistivity of sample. In the result of applying the defect chemistry, $Bi^{3+} \;and \; Bi^[5+}$ are substituted for Ua and Ti site, respectively. Boron nitride decomposed and formed liquid phase among the $BaTiO_3$ grains. The decomposed com~ ponents made the second phase and existed the tr~ple juntion from the result of EPMA. From the complex impendencc pattern, the gram and grain boundary resistivity were small. The grain size increased with increasing BN contents, and decreased grain boundary resistivity enhanced the PTCR effect.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.2
• /
• pp.56-62
• /
• 2003

Epitaxial $Bi_4Ti_3O_{12}$ films on $SrTiO_3$(100), L$aA1O_3$(100) and MgO(100) were prepared by sol-gel process using metal naphthenate as a starting material. As-deposited films were pyrolyzed at $500^{\circ}C$ for 10 min In air and annealed at $750^{\circ}C$ for 30 min in air. Crystallinity and in-plane alignment of the film were investigated by X-ray diffraction $\theta$-2$\theta$ scan and P scanning. A field emission-scanning electron microscope and an atomic force microscope were used for characterizing the surface morphology and the surface roughness of the film. The film prepared on MgO(100) showed the most poor crystallinity and in-plane alignment, compared to those on the other substrates. While the films on $LaA1O_3$(100) and $SrTiO_3$(100) having high crystallinity and in-plane alignment showed the form of columnar grain growth, the film on MgO(100) which had poor crystallinity showed the form of acicula grain growth.

• Korean Journal of Materials Research
• /
• v.13 no.5
• /
• pp.317-322
• /
• 2003

Bismuth layered structure ferroelectric thin films, $Bi_4$$Ti_3$$O_{12}$ / (BTO) and Nb-doped BTO (BTN) were prepared on the Pt(111)/Ti/$SiO_2$/Si(100) substrates by a sol-gel route. We investigated the Nb-doping effect on the grain orientation and ferroelectric properties. $Nb^{5＋}$ ion substitution for $Ti^{4＋}$ ion in perovskite layers of BTO decreased the degree of c-axis orientation and increased the remanent polarization (2Pr). The fatigue resistance of Nb-doped BTO thin film was shown to be superior to that of BTO, and the leakage current of Nb-doped BTO thin film was decreased about 1 order of magnitude compared with BTO. The improvement of ferroelectric properties with $Nb^{5＋}$ doping in BTO could be attributed to the changes in space charge densities and grain orientation in the thin film.

• Journal of Powder Materials
• /
• v.17 no.4
• /
• pp.289-294
• /
• 2010

For the aim of low-temperature co-fired ceramic microwave components, sintering behavior and microwave properties (dielectric constant ${\varepsilon}_r$, quality factor Q, and temperature coefficient of resonant frequency ${\tau}_f$) are investigated in $Bi_{18}O(Ca_{0.725}Zn_{0.275})_8Nb_{12}O_{65}$ [BCZN] ceramics with addition of $V_2O_5$. The specimens are prepared by conventional ceramic processing technique. As the main result, it is demonstrated that the additives ($V_2O_5$) show the effect of lowering of sintering temperature and improvement of microwave properties at the optimum additive content. The addition of 0.25 wt% $V_2O_5$ lowers the sintering temperature to $890^{\circ}C$ utilizing liquidphase sintering and show the microwave dielectric properties (dielectric constant ${\varepsilon}_r$ = 75, quality factor $Q{\times}f$ = 572 GHz, temperature coefficient of resonance frequency ${\tau}_f\;=\;-10\;ppm/^{\circ}C$). The estimated microwave dielectric properties with $V_2O_5$ addition (increase of ${\varepsilon}_r$, decrease of $Q{\times}f$, shift of ${\tau}_f$ to negative values) can be explained by the observed microstrucure (sintered density, abnormal grain structure) and possibly high-permittivity $Bi_{18}Zn_8Nb_{12}O_{65}$ (BZN) phase determined by X-ray diffraction.

• Korean Journal of Materials Research
• /
• v.17 no.2
• /
• pp.68-72
• /
• 2007

Optimum compositions for piezoelectric properties of $(Bi_{0.5}Na_{0.5})_{(1-x)}Ba_xTiO_3$ ceramics were investigated in the range of $x=0{\sim}0.1$ covering rhombohedral to tetragonal phase regions. No impurity phases other than a perovskite phase were found and the grain size decreased with increasing x. A two-phase coexisting morphotropic phase area rather than boundary dividing rhombohedral and tetragonal phase regions appeared to exist at $x=0.05{\sim}0.08$. As for piezoelectric properties within morphotropic phase compositions, the piezoelectric constant ($d_{33}$) and the electromechanical coupling factor ($K_p$) showed peak values at x=0.065, 192 pC/N and 34%, respectively, indicating x=0.065 as an optimum composition for piezoelectric $(Bi_{0.5}Na_{0.5})_{(1-x)}Ba_xTiO_3$ ceramics.

• Korean Journal of Materials Research
• /
• v.15 no.11
• /
• pp.683-689
• /
• 2005

The structural, piezoelectric and ferroelectric properties of $(1-x)(Bi_{0.5}Na_{0.5})TiO_3$ x=0.00, 0.02, 0.04, 0.06, 0.08, and 0.10) ceramics were investigated. A gradual change in the crystal and microstructures with tile increase of $BaTiO_3$ (BT) concentration was observed. The $(Bi_{0.5}Na_{0.5})TiO_3$ (BNT) samples show unusual properties as ferroelectric relaxer materials. We observed a phase transition in BNT solid solutions with BT having normal ferroelectric phase transition. At room temperature, BNT presents a single phase without the morphotropic phase boundary (MPB). In the case of samples doped with $4\~8 mol\%$ BT, rhombohedral-tetragonal MPB was formed and the piezoelectric properties were improved.

• Korean Journal of Materials Research
• /
• v.16 no.11
• /
• pp.705-709
• /
• 2006

Nb was doped to Pb-free $(Bi_{0.5}Na_{0.5})TiO_3$ (BNT) by a solid state mixing process to form $(Bi_{0.5}Na_{0.5})Ti_{1-x}Nb_xO_3\;(x=0{\sim}0.05)$ (BNTNb) and its doping effects on ferroelectric and piezoelctric properties of BNT were investigated. The BNTNb solid solutions were formed up to x=0.01 with no apparent second phases while grain sizes decreased. As x increased, coercive field ($E_c$) and mechanical quality factor ($Q_m$) decreased but piezoelectric constant ($d_{33}$) increased, which indicates Nb acts as a donor for BNT.

• Korean Journal of Materials Research
• /
• v.18 no.2
• /
• pp.103-106
• /
• 2008

The magneto-transport properties of an individual single crystalline Bi nanowire grown by a spontaneous growth method are reported. A four-terminal device based on an individual 400-nm-diameter nanowire was successfully fabricated using a plasma etching technique that removed an oxide layer that had formed on the surface of the nanowire. Large transverse ordinary magnetoresistance (1401%) and negative longitudinal ordinary magnetoresistance (-38%) were measured at 2 K. It was observed that the period of Shubnikov-de Haas oscillations in transverse geometry was $0.074^{T-1}$, $0.16^{T-1}$ and $0.77^{T-1}$, which is in good agreement with those of bulk Bi. However, it was found that the period of SdH oscillation in longitudinal geometry is $0.24^{T-1}$, which is larger than the value of $0.16^{T-1}$ reported for bulk Bi. The deviation is attributable to the spatial confinement arising from scattering at the nanowire surface boundary.

• Nuclear Engineering and Technology
• /
• v.54 no.3
• /
• pp.1062-1070
• /
• 2022

In the present communication, pure and stable α-Bismuth Oxide (Bi₂O₃) nanoparticles (NPs) were synthesized by low temperature solution combustion method using urea as a fuel and calcined at 500℃. The synthesized sample was characterized by using powder X-ray Diffraction (PXRD), Scanning Electron Microscopy (SEM), Energy dispersive X-ray analysis (EDAX), Transmission Electron Microscopy (TEM), Fourier Transform Infrared Spectroscopy (FTIR) and UV-Visible absorption spectroscopy. The PXRD pattern confirms the formation of mono-clinic, stable and low temperature phase α-Bi₂O₃. The direct optical energy band gap was estimated by using Wood and Tauc's relation which was found to be 2.81 eV. The characterized sample was studied for X-ray/gamma ray shielding properties in the energy range 0.081-1.332 MeV using NaI (Tl) detector and multi channel analyzer (MCA). The measured shielding parameters agrees well with the theory, whereas, slight deviation up to 20% is observed below 356 keV. This deviation is mainly due to the influence of atomic size of the target medium. Furthermore an accurate theory is necessary to explain the interaction of X-ray/gamma ray with the NPs.The present work opens new window to use this facile, economical, efficient, low temperature method to synthesize nanomaterials for X-ray/gamma ray shielding purpose.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.1
• /
• pp.15-19
• /
• 2013

The n-type $Bi_2(Te_{0.9}Se_{0.1})_3$ powders, which were fabricated by melting/grinding method and dispersed with 0.5 vol% $TiO_2$ nanopowders, were hot-pressed in order to investigate the effects of $TiO_2$ dispersion on the thermoelectric properties of the hot-pressed $Bi_2(Te_{0.9}Se_{0.1})_3$. Excellent thermoelectric properties such as a maximum figure-of-merit of $2.93{\times}10^{-3}/K$ and a maximum dimensionless figure-of-merit of 1.02 were obtained for the hot-pressed $Bi_2(Te_{0.9}Se_{0.1})_3$. With dispersion of 0.5 vol% $TiO_2$ nanopowders, the maximum figure-of-merit and the maximum dimensionless figure-of-merit decreased to $2.09{\times}10^{-3}/K$ and 0.68, respectively.