• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2007.06a
• /
• pp.536-539
• /
• 2007

BSCCO am films fabricated by using the evaporation method at various substrate temperatures, Tsub and ozone gas pressures $PO_3$. Despite setting the composition of thin film Bi2223, Bi2201, Bi2212 and Bi2223 phase were appeared. It was confirmed the obtained field of stabilizing phase was represented in the diagonal direction of the right below end in the Arrhenius plot of temperature of the substrate and $PO_3$, and it was distributed in the rezone. The XRD peak of the generated film continuously changed according to the substrate temperature. This demonstrates the existence of mixed crystal composition where the phases of Bi2201, Bi2212 and Bi2223 are mixed in the crystal structure; and the single-phase film of each phase exist in a very rezone of temperature and gas pressure.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2003.05a
• /
• pp.615-618
• /
• 2003

This paper presents Bi thin films have been fabricated by atomic layer-by-layer deposition and co-deposition at an IBS method. The growth rates of the films was set in the region from 0.17 to 0.27 nm/min. MgO(l00) was used as a substrate. In order to appreciate stable existing region of Bi 2212 phase with temperature and ozone pressure, the substrate temperature was varied between 655 and 820 $^{\circ}C$ and the highly condensed ozone gas pressure(PO$_3$) in vacuum chamber was varied between 2.0$\times$10$^{-6}$ and 2.3$\times$10$^{-5}$ Torr. Bi 2212 phase appeared in the temperature range of 750 and 795$^{\circ}C$ and single phase of Bi 2201 existed in the lower region than 785 $^{\circ}C$. Whereas, PO$_3$ dependance on structural formation was scarcely observed regardless of the pressure variation. And high quality of c-axis oriented Bi 2212 thin film with T$_{c}$(onset) of about 90 K and T$_{c}$(zero) of about 45 K is obtained. Only a small amount of CuO in some films was observed as impurity, and no impurity phase such as CaCuO$_2$ was observed in all of the obtained films.lms.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.11
• /
• pp.997-1002
• /
• 2002

BSCCO thin films are fabricated by an ion beam sputtering method, and sticking coefficients of the respective elements are evaluated. The sticking coefficient of Bi element in BSCCO film formation was observed to show a unique temperature dependence; it was almost a constant value of 0.49 below about 730$^{\circ}C$ and decreased linearly over about 730$^{\circ}C$ In contrast, Sr and Ca, displayed no such remarkable temperature dependence. This behavior of the sticking coefficient was explained consistently on the basis of the evaporation and sublimation processes of Bi$\sub$2/O$\sub$3/. It was concluded that Bi(2212) thin film constructs from the partial melted Bi(2201) phase with the aid of the liquid phase of Bi$\sub$2/O$\sub$3/.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.252-255
• /
• 2002

BSCCO thin films are fabricated by an ion beam sputtering method, and sticking coefficients of the respective elements are evaluated. The sticking coefficient of Bi element in BSCCO film formation was observed to show a unique temperature dependence; it was almost a constant value of 0.49 below about $730^{\circ}C$ and decreased linearly over about $730^{\circ}C$. In contrast, Sr and Ca, displayed no such remarkable temperature dependence. This behavior of the sticking coefficient was explained consistently on the basis of the evaporation and sublimation processes of $Bi_{2}O_{3}$. It was concluded that Bi(2212) thin film constructs from the partial melted Bi(2201) phase with the aid of the liquid phase of $Bi_{2}O_{3}$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.327-328
• /
• 2005

Bi-system thin films are prepared by ion beam sputtering technique. Three phases of Bi-2201, Bi-2212 and Bi-2223 appear as stable ones in spite of the conditions for thin film fabrication of Bi-2212 and Bi-2223 compositions, depending on substrate temperature($T_{sub}$) and ozone pressure($PO_3$). It is found out that these phases show similar $T_{sub}$ and $PO_3$ dependence, and that the stable regions of these phases are limited within very narrow temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.05b
• /
• pp.98-101
• /
• 2005

BSCCO thin films fabricated by using the evaporation method. As a result, although the composition of Bi2212 was set up, the phase of Bi2201, Bi2212 and Bi2223 was formed. The formation area of these stable phases is indicated as inclined line in the direction of the right lower end from the Arrhenius plot of the substrate temperature-oxidation gas pressure, and are distributed in very small area. The activation energy for the phase transformation from the Bi2201 to the Bi2212 is estimated in terms of the Avrami equation.

• Transactions on Electrical and Electronic Materials
• /
• v.2 no.1
• /
• pp.12-15
• /
• 2001

Bi-2212 and Bi-2223 thin films are prepared by IBS(ion beam sputtering) technique. Three phases of Bi-2201, Bi-2212 and Bi-2223 appear as stable ones in spite of the conditions for thin film fabrication of Bi-2212 and Bi-2223 compositions, depending on substrate temperature (T $_{sub}$) and ozone pressure(PO$_3$). It is found out that these phases are limited within very narrow temperature.e.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.11
• /
• pp.1029-1034
• /
• 2003

The Bi$_2$Sr$_2$Ca$_{n}$Cu$_{n+1}$ O$_{x}$, superconducting thin films arc fabricated by using the sputtering and evaporation method. Because we confirmed the sticking ratio of Bi element in the Bi$_2$Sr$_2$Ca$_{n}$Cu$_{n+1}$ O$_{x}$ superconducting thin film fabricated by using the sputtering method was much lower than the expected value, to get the enough number of the flakes of Bi, faraday cup was used to evaporate Bi clement. As a result of the fabrication, Bi 2201 and Bi 2212 single phases could be made by the optima of deposition condition. And we confirmed the sticking coefficient of Bi element was clearly related to the temperature change of the substrate and the generation of Bi22l2 phase

• Bulletin of the Korean Chemical Society
• /
• v.16 no.6
• /
• pp.484-489
• /
• 1995

The synthesis of new bismuth-barium containing members of layered cuprates with 2201 type structure was reported. By solution calorimetry the formation enthalpies for Bi2MLaCuO6.5 (M=Ba, Ba0.5Sr0.5, Sr) were obtained. Crucial influence of partial oxygen pressure and size of lanthanoid on stability of layered cuprates was shown. Electronic states of variable valence atoms were studied by voltammetry of solids.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.1218-1221
• /
• 2004

Bi2212 superconducting thin films fabricated by using the ion Beam Sputtering Method. As a result, although the composition of Bi2212 was set up, the phase of Bi2201, Bi2212 and Bi2223 was formed. The formation area of these stable phases is indicated as inclined line in the direction of the right lower end from the Arrhenius plot of the substrate temperature-oxidation gas pressure, and are distributed in very small area. The activation energy for the phase transformation from the Bi2201 to the Bi2212 is estimated in terms of the Avrami equation.