• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2004.05a
• /
• pp.174-178
• /
• 2004

본 논문에서는 P-type (100)Si 기판위에 RF magnetron sputtering법으로 완충층용 MgO 박막을 $500\AA$ 증착한 후 제작된 MgO/Si 기판위에 BST 박막을 증착하였다. 증착 시 기판온도는 $400^{\circ}C$ 작업가스 $AR:O_2:=80:20$, 작업진공 10mtorr에서 RF 파워를 25W, 50W, 75W로 변화하면서 증착하여 최적의 RF 파워조건을 확립하였다. XRD 측정결과 25W에서 증착된 BST 박막은 배향성이 보이지 않는 비정질 형태로 성장되었고 50W에서 증착된 박막의 결정특성이 가장 양호하였다. I-V측정결과 모든 샘플에서 $\pm150KV/cm$에서 $10^{-7}A/\textrm{cm}^2$이하의 양호한 누설전류특성을 나타내었고 C-V측정 결과 역시 50W에서 증착된 BST 박막의 비유전율이 약 305로서 가장 우수한 특성을 보여주었다.

• Korean Journal of Materials Research
• /
• v.4 no.4
• /
• pp.401-405
• /
• 1994

The chemical composition and electrical properties were investigated for epitaxially crystallized $(Ba_{0.5}Sr_{0.5})Tio_3$ (BST) films deposited on Pt and $YBa_Cu_3O_{7-x}$(YBCO) electrodes by laser ablation technique. The crystalline quality of the heteroepitaxial BST films deposited on Pt bottom electrode was found to be better than that of BST film on YBCO electrode by the RBS analysis. Films deposited at $600^{\circ}C$ on Pt electrode showed a dielectric constant of 320 and a dissipation factor of 0.023 at 100kHz. Leakage current density of BST films on Pt electrode was smaller than that on YBCO bottom electrode. Their leakage current density was about 0.8$\mu \; A/ \textrm{cm}^2$ at an applied electric field of 0.15MV/cm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.121-124
• /
• 1999

The (Ba,Sr)TiO$_3$[BST] thin film were fabricated on the Pt/Ti/SiO$_2$/Si substrate by RF sputtering technique. The structural properties of the BST thin films were investigated with deposition time and substrate temperature by XRD. In the case of the BST thin films which has the deposition thin of 20 min, second phases and BST (111) peaks were increased with increasing the temperature of substrate. The capacitance of the BST thin film (deposition time of 20 min.) was decreased with the substrate temperature and was 1500pF with applied voltage of 1V.

• Korean Journal of Materials Research
• /
• v.4 no.4
• /
• pp.453-458
• /
• 1994

$(Ba_{0.5}Sr_{0.5)/TiO_3$(BST) thin films were prepared for the application of 256 Mb DRAM by RF magnetron sputtering. The crystallinity of BST thin films increased with increasing deposition tempera lure. The composition of thin films was $(Ba_{0.48}Sr_{0.48)/TiO_{2.93}$ Pt/Ti barrier layer suppressed the diffusion of Si into BST layer. The films showed a dielectric constant of 320 and a dissipation factor of 0.022 at 100 kHz. the change of capacitance of the films with applied voltage was small, showing paraelectric property. The charge storage density and leakage current density were 40fC/$\mu \textrm{m}^{2}$ and 0.8$\mu A/\textrm{cm}^2$, respectively at a field of 0.15 MV/cm. The BST films obtained by RF magnetron sputtering appeared to be potential thin film capacitors for 256 Mb DRAM application.

• Journal of the Korean Vacuum Society
• /
• v.11 no.3
• /
• pp.135-140
• /
• 2002

In this paper, We deposited the BST thin-film on p-type (100)Si, (100)MgO and MgO/Si substrates respectively using RF magnetron sputtering method. After the BST thin-fil m was deposited, we performed RTA(rapid thermal anneal) at $600^{\circ}C$, oxygen atmosphere and 1 min. In the XRD measurement, we observed the (110) $Ba_{0.5}Sr_{0.5}TiO_3$ main peak in all samples and the peak intensity increased after post annealing. Then we manufactured a capacitor using Al Electrode and measured I-V, C-V. In C-V measurement result values for each substrate, dielectric constant was calculated 120 (bare Si), 305(MgO/Si), 310(MgO) respectively. A leakage current density was present less than 1 $\mu\textrm{A/cm}^2$ at applied fields below 0.3 MV/cm. In conclusion we confirmed that MgO/Si substrates give good results for BST thin-film deposition.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.36D no.6
• /
• pp.44-51
• /
• 1999

The electrical conduction mechanism of high dielectric $(Ba,Sr)TiO_3$ (BST) thin film capacitor, which is the promising cell capacitor for high density DRAM, was investigated in low field region (<0.2MV/cm). It is known that the current in the low field region consists of dielectric relaxation current and leakage current. The current-time (I-t) measurement technique under the constant voltage was used for extracting successfully each current component. The conduction mechanism of the BST capacitor was deduced from the dependency of the current on the measurement temperature, strength of electric field, the polarity of applied electric field and post annealing process. From these results, it was suggested that the dielectric relaxation current and the leakage current are originated from the redistribution of internally trapped electron by hopping process and Pool-Frenkel conduction mechanism, respectively. It was also concluded that traps causing these two current components are due to oxygen vacancies within the BST film.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.16 no.3 s.94
• /
• pp.253-259
• /
• 2005

In this paper, BaSrTiO$_{3}$(BST) thin film tunable interdigital capacitor using low cost silicon substrate instead of expensive single-crystalline substrate is presented. The tunable capacitor in which BST thin film is deposited by PLD has operation frequency and applied bias up to 4 GHz and 50 V, respectively. The maximum tunability in capacitance is found to be 30$\%$, for an applied field of 5 kV/cm at a bias of 50 V. Therefore, it has been shown that the BST microwave tunable capacitor can be integrated onto Si substrate.

• Journal of the Korean Ceramic Society
• /
• v.38 no.5
• /
• pp.492-498
• /
• 2001

Ba$_{0.5}$Sr$_{0.5}$TiO$_3$타겟을 이용 Pt/Ti/SiO/Si 기판 위에 R.F magnetron sputtering 방법으로 BST 박막을 증착하여 다양한 열처리 조건에 따른 BST 박막의 전기적 성질(정전용량, 누설전류)에 대해 박막의 결정성과 미세구조의 연관성에 대하여 연구하였다. BST 박막의 유전상수는 grain size에 영향 받으며, 열처리 온도가 증가할수록 유전상수는 증가함을 보였고 온도에 따른 누설전류는 저전압 영역에서는 Hopping conduction, 고전압 영역에서는 Schottky conduction mechanism을 따르는 것으로 나타났다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.2
• /
• pp.60-66
• /
• 2001

($Ba_x$$Sr_{1-x}$)$TiO_3$ (x=0.9, 0.7, 0.5) thin films were prepared on ITO-coated glass by sol-gel method. Perovskite phase formation temperature of BST thin films seemed to be higher than $600^{\circ}C$. Peaks of perovskite phase shift to high diffraction angles as the Sr/(Ba+Sr) ratio was increased, due to the smaller ionic size of $Sr^{2+}$ than $Ba^{2+}$ . As a heating temperature was increased, the grain became coarser. And as Sr/(Ba + Sr) ratio was increased, the grain became finer. Dielectric constants of the BST(50/50) thin film are higher and dielectric losses of that are lower than those of the others. Dielectric constant and dielectric loss of the BST(50/50) thin film were 652 and 0.042 at 1kHz, respectively.

• Journal of the Microelectronics and Packaging Society
• /
• v.3 no.1
• /
• pp.33-40
• /
• 1996

MOD법에 의해 BST박막을 제조하고 전기적 특성을 측정함으로써 마이크로 회로에 적용가능성을 타진하였다. MOD 공정의 선구물질로서 barium neodecanoate, strontium 2-ethylhexanoate 및 titanium dimethoxy 야-2-ethylheanoate를 합성하였다, 합성된 선구물 질들을 Ba0.5Sr0.5TiO3가 되도록 화학양론적으로 혼합하여 공통용매인 p-xylene에 녹인다음 기판위에 spin coating 방법으로 박막을 형성하여 건조하고 소성하였다. 사용된 기판은 ITO/glass, Pt/SiO2/Si, Pt/Ti/SiO2/Si 및 Pt foil을 사용하였다. 소성 속도를 빨리했을 경우 소성속도를 느리게 했을때에 비하여 훨씬 균일하고 치밀한 박막을 얻을수 있었다, 여러 가 지 제조조건의 변화에 따른 유전상수 I-V 특성 및 C-V 측성 등의 전기적 특성을 측정하고 고찰하였다.