• Korean Journal of Materials Research
• /
• v.30 no.2
• /
• pp.81-86
• /
• 2020

MoO₃ metal oxide nanostructure was formed by hydrothermal synthesis, and a perovskite solar cell with an MoO₃ hole transfer layer was fabricated and evaluated. The characteristics of the MoO₃ thin film were analyzed according to the change of hydrothermal synthesis temperature in the range of 100 ℃ to 200 ℃ and mass ratio of AMT : nitric acid of 1 : 3 ~ 15 wt%. The influence on the photoelectric conversion efficiency of the solar cell was evaluated. Nanorod-shaped MoO₃ thin films were formed in the temperature range of 150 ℃ to 200 ℃, and the chemical bonding and crystal structure of the thin films were analyzed. As the amount of nitric acid added increased, the thickness of the thin film decreased. As the thickness of the hole transfer layer decreased, the photoelectric conversion efficiency of the perovskite solar cell improved. The maximum photoelectric conversion efficiency of the perovskite solar cell having an MoO₃ thin film was 4.69 % when the conditions of hydrothermal synthesis were 150 ℃ and mass ratio of AMT : nitric acid of 1 : 12 wt%.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.8
• /
• pp.474-478
• /
• 2017

We report on thin-film transistors based on $TiO_x$ pre-annealed by femtosecond laser pulses. A 30-nm thick $TiO_x$ active channel layer was initially deposited by an ALD system. The $TiO_x$ semiconducting films were annealed by irradiation with a femtosecond laser (power: $3W/cm^2$) for 5, 25, and 50s. Atomic force microscopy images revealed that the surface of a $TiO_x$ film without femtosecond laser pre-annealing was relatively rough, while after annealing with femtosecond laser pulses, the surface of the $TiO_x$ films became smooth. With increasing radiation time, the surrounding gas atmosphere could have a larger impact on the $TiO_x$ surface; meanwhile, the thin-film roughness decreased. Thin-film transistors with $TiO_x$ active channels pre-annealed at 50s exhibited good transfer characteristics and an on-to-off current ratio of ${\sim}10^3$.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.3
• /
• pp.102-108
• /
• 2008

In this paper, the LiF and polymer thin film as passivation layer have been evaporated on green OLED devices. HDPE, polyacenaphthylene, polytetrafluoroethylene, poly(2,6-dimethyl-1,4-pheneylene oxide), poly sulfone and poly(dimer-acid-co-alkyl poly-amine) have been used as polymer materials. The optical transmittance of evaporated polymer thin film was very good as an above 90% in visible range. The morphology of polymer thin film was measured by AFM. As a result of the measurement average roughness($R_a$) value of the polysulfone was very low as 2.2 nm. The green OLED devices with a structure of ITO/HIL/HTL/EML/Buffer/Al in series of various passivation films were fabricated and analyzed. It was observed that an OLED device with LiF as first passivation film has shown the good electrical and optical property, and all kind of polymer films did not influence on the I-V-L characteristics and the life time of OLED devices. Therefore, we found that polymer layer played a key role as a buffer layer between the inorganic passivation layers to relieve the stress of the inorganic layers.

• Journal of the Korean Ceramic Society
• /
• v.54 no.3
• /
• pp.249-256
• /
• 2017

We design Ge-Al multilayer assemblies as anode materials for Li-ion batteries, in which Ge and Al thin films are alternately deposited by a radio sputtering method. By sandwiching Ge layers between Al layer, the cyclability, rate capability, and capacity of Ge are improved significantly. The success of the Ge-Al multilayer is attributed to the Al films. To maintain the integrity of electrical contact, Al acts as an elastic layer, which can expand or shrink with the Ge film upon lithiation or delithiation. In addition, the presence of the Al film on the surface can prevent direct contact of Ge and electrolyte, thereby reducing the growth of a SEI layer. Importantly, with high electrical and ionic conductivities, the Al film provides efficient electrical and ionic routes for electrons and Li-ions to access the Ge film, promoting a high specific capacity and high rate capability for Ge.

• Current Photovoltaic Research
• /
• v.2 no.1
• /
• pp.1-7
• /
• 2014

We developed a method of growing thin Si film at $600^{\circ}C$ by hot wire CVD using a very thin large-grained poly-Si seed layer for thin-film Si solar cells. The seed layer was prepared by crystallizing an amorphous Si film by vapor-induced crystallization using $AlCl_3$ vapor. The average grain size of the p-type epitaxial Si layer was about $20{\mu}m$ and crystallographic defects in the epitaxial layer were mainly low-angle grain boundaries and coincident-site lattice boundaries, which are special boundaries with less electrical activity. Moreover, with a decreasing in-situ boron doping time, the mis-orientation angle between grain boundaries and in-grain defects in epitaxial Si decreased. Due to fewer defects, the epitaxial Si film was high quality evidenced from Raman and TEM analysis. The highest mobility of $360cm^2/V{\cdot}s$ was achieved by decreasing the in-situ boron doping time. The performance of our preliminary thin-film solar cells with a single-side HIT structure and $CoSi_2$ back contact was poor. However, the result showed that the epitaxial Si film has considerable potential for improved performance with a reduced boron doping concentration.

• Korean Journal of Materials Research
• /
• v.16 no.8
• /
• pp.490-496
• /
• 2006

ITO monolayer and ITO/Ag/ITO multilayer thin films are prepared by D.C. magnetron sputtering method. Ag layer was inserted for applying ITO to a flexible substrate at low temperature. Carrier concentration and carrier mobility of ITO and ITO/Ag/ITO thin films were measured, the transmittance of them also was done. The amorphous phase was confirmed to be combined in addition to (400) and (440) peaks from XRD result of ITO thin film. As the substrate temperature increased, the preferred orientation of (400) appeared. From the result of application of Ag layer at room temperature, the growth of columnar structure was inhibited, and the amorphous phase formed mostly. The ITO/Ag/ITO thin film represented the transmittance of above 80% when the thickness of Ag layer was 50 ${\AA}$, and the concentration of carrier increased up to above 10 times than that of ITO thin film. Finally, since very low resistance of 3.9${\Omega}/{\square}$ was observed, the effective application of low temperature process is expected to be possible for ITO thin film.

• Proceedings of the KIEE Conference
• /
• 2002.06a
• /
• pp.49-51
• /
• 2002

In this thesis, Josephson junction using high-Tc superconducting multi-layer thin film has been fabricated by on-axis RF magnetron sputtering method. And, the characterizations were performed by X-ray diffraction, SEM and the measuring system of critical current density. The physical properties of multi-layer superconducting thin films were also analyzed with the measured results. To fabricate the multi-layer superconducting thin films, the optimum partial pressure of Argon and Oxgen and the temperature of substrate were measured. Also, YBaCuO thin film was grown on MgO and $SrTiO_3$ substrates by rf-sputtering and LGO thin film of 30 A was epitaxially grown on the YBaCuO thin film as a josephson junction with the same condition. The schottky barrier at the contact surface between YBaCuO/LGO and YBaCuO/Au and the energy gap of 0.5 ${\sim}$ 0.6 mV in Nb were observed from the dI/dV-V of YBaCuO/LGO/Au/Nb and YBaCuO/Au/Nb.

• Journal of the Semiconductor & Display Technology
• /
• v.16 no.4
• /
• pp.1-4
• /
• 2017

Encapsulation of organic based devices is essential issue due to easy deterioration of organic material by water vapor. Atomic layer deposition (ALD) is a promising solution because of its low temperature deposition and quality of the deposited film. Moisture permeation has a mechanism to pass through defects, Thin Film Encapsulation using inorganic / organic / inorganic hybrid film has been used as promising technology. $Al_2O_3$ / Polymer / $Al_2O_3$ multilayer film has shown excellent environmental protection characteristics despite of thin thicknesses of the films.

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.1
• /
• pp.24-27
• /
• 2009

N-doped ZnO thin films were deposited on n-type Si(100) and homo-buffer layer, and undoped ZnO thin film was also deposited on homo-buffer layer by RF magnetron sputtering method. After deposition, all films were in-situ annealed at $800^{\circ}C$ for 5 minutes in ambient of $O_2$ with pressure of 10Torr. X -ray diffraction shows that the homo-buffer layer is beneficial to the crystalline of N-doped ZnO thin films and all films have preferable c-axis orientation. Atomic force microscopy shows that undoped ZnO thin film grown on homo-buffer layer has an evident improvement of smoothness compared with N-dope ZnO thin films. Hall-effect measurements show that all ZnO films annealed at $800^{\circ}C$ possess p-type conductivities. The undoped ZnO film has the highest carrier concentration of $1.145{\times}10^{17}cm{-3}$. The photoluminescence spectra show the emissions related to FE, DAP and many defects such as $V_{Zn}$, $Zn_O$, $O_i$ and $O_{Zn}$. The p-type defects ($O_i$, $V_{Zn}$, and $O_{Zn}$) are dominant. The undoped ZnO thin film has a better p-type conductivity compared with N-doped ZnO thin film.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.87-87
• /
• 2010

We report a new patterning technique of inorganic materials by using thin-film transfer printing (TFTP) with atomic layer deposition. This method consists of the atomic layer deposition (ALD) of inorganic thin film and a nanotransfer printing (nTP) that is based on a water-mediated transfer process. In the TFTP method, the Al2O3 ALD growth occurs on FTS-coated PDMS stamp without specific chemical species, such as hydroxyl group. The CF3-terminated alkylsiloxane monolayer, which is coated on PDMS stamp, provides a weak adhesion between the deposited Al2O3 and stamp, and promotes the easy and complete release of Al2O3 film from the stamp. And also, the water layer serves as an adhesion layer to provide good conformal contact and form strong covalent bonding between the Al2O3 layer and Si substrate. Thus, the TFTP technique is potentially useful for making nanochannels of various inorganic materials.