• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.5
• /
• pp.15-23
• /
• 2021

In this paper, service life for RC(Reinforced Concrete) substructure subjective to carbonation was evaluated through deterministic and probabilistic method considering field investigation data and Design Code(KDS 14 20 40). Furthermore changes in service life with increasing COV(Coefficient of Variation) and equivalent safety index meeting the same service life were studied. From the investigation, the mean and its COV of cover depth were evaluated to 70.0 ~ 90.0 mm and 0.2, respectively. With intended failure probability of 10.0 % and 70 mm of cover depth, service life decreased to 137 years, 123 years, and 91 years with increasing COV of 0.05, 0.1, and 0.2, respectively. In the case of 80 mm of cover depth, it changes to 179 years, 161 years, and 120 years with increasing COV. The equivalent safety index meeting the same service life from deterministic method showed 1.66 ~ 3.43 for 70 mm of cover depth and 1.61 ~ 3.24 for 80 mm of cover depth, respectively. The various design parameters covering local environment and quality condition in deterministic method yields a considerable difference of service life, so that determination of design parameters are required for exposure conditions and parameter variation.

• Resources Recycling
• /
• v.27 no.6
• /
• pp.59-67
• /
• 2018

Efflorescence is a white deposit of powders in the surface of cement concrete which can also occur in geopolymers. Efflorescence occurs when sodium ions in alkali activator react with atmospheric carbon dioxide to form sodium carbonate components. In this study, we investigated whether the secondary efflorescence can be reduced by controlling the Na/Al mole ratio or by changing the curing temperature and heat curing time in fly ash-based geopolymers. The 28 days compressive strength in geopolymers having Na/Al ratio of 1.0 was higher than geopolymers having Na/Al ratio of 0.8. The strength increased with the increasing curing temperature and longer heat curing time. On the other hand, efflorescence was lower when the curing temperature was high and the heat curing time was longer in the geopolymers having Na/Al ratio of 1.0. The geopolymers having Na/Al ratio of 0.8 showed accelerated efflorescence occurrence than the geopolymers having Na/Al ratio of 1.0. In order to reduce the occurrence of the secondary efflorescence of fly ash-based geopolymers, it will be advantageous to maintain the Na/Al ratio at 1.0, increase the curing temperature, and lengthen the heating curing time.

• Journal of the Korean GEO-environmental Society
• /
• v.19 no.12
• /
• pp.59-64
• /
• 2018

The damages to the reinforced earth retaining wall are divided into the front wall, foundation, drainage and upper slope. Damage of reinforced earth retaining wall is mainly caused by damage caused by drainage problem in the field. Recently, damage caused by snow removal materials have been occurred. Recently, the amount of snow removal materials used in winter is increasing due to abnormal weather. This chlorides degrades the concrete structure, where the reinforced earth retaining wall was no exception. There has recently been a case in which the front wall of the reinforced earth retaining wall deteriorates due to the chlorides introduced into the back filling portion through the drainage passage. Therefore, in this study, the cause of damages of reinforced earth retaining wall constructed in bridge abutment was analyzed, and an analytical study was conducted on the countermeasure. As a result, it was found that chlorides, which was introduced through the drainage system in the expansion joint of the bridge shift part or the upper structure, is infiltrated into the back part of the reinforced earth retaining wall and damaged. Therefore, it is suggested to improve the drainage system and restored the stiffness of the front wall.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.21 no.5
• /
• pp.717-733
• /
• 2019

In this study, lining thickness distribution and its behind state (particularly, its void state) were analyzed using the GPR survey data performed on three currently operating NATM tunnels. Results of GPR analysis showed that void areas were mostly detected between concrete lining and primary support, particularly, near the crown of the tunnels. The lining thickness in the left-hand side of the tunnel was different from that of the right-hand side by 8.6~253.5 mm when measured in transverse direction. It was also found that longitudinal cracks were prevailed in the area lining thickness was sharply changed. Longitudinal thickness distribution at the crown was also studied and tested by performing 3 goodness-of-fit tests in order to find the most suitable thickness distribution. Normal distribution (or similar distribution) fit most suitably to the measured data if the measured average thickness was larger than designed one; Gamma and/or Inverse Gauss distribution fit to the measured data reasonably well if the measured average thickness was less than the designed value of thickness. Since actual lining thickness can be a potential index when assessing the state and safety of the unreinforced NATM tunnel lining, measuring of the lining thickness with GPR survey might be needed rather than assuming the thickness is always constant and same with the designed value.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.1
• /
• pp.130-137
• /
• 2019

Precast concrete (PC) structure is one of the type of the structures which is made in a facility prior to installing it to a construction field. The contact surfaces between two PC structures should be treated for obtaining enough binding force by inducing prestressing force. However, in the many cases, the contact surface causes the crack and leakage of water. These cracks and water leakage can cause the corrosion of the rebar, and the corrosion of the rebar can severely reduce the long-term durability. In this study, the SMA wire connector is suggested to solve the problem with the contact surfaces between two PC structures. The pull-out resistance of the suggested SMA wire connector is evaluated by conducting the tests to find the effect of the number of wires, shape of connector part, and shape memory effect. As a result of this study, the empirical formula is suggested to estimate the pull-out resistance related with the effects of the shape of the connector, shape memory effect, and the adhesive force. The validity between the estimated pull-out resistance and the measured value is confirmed.

• Journal of the Korean Geotechnical Society
• /
• v.35 no.9
• /
• pp.15-28
• /
• 2019

Long-term allowable compressive Loads of PHC piles were analyzed based on qualification tests results by 17 small and medium PHC pile producing companies and product specifications by 6 major and 17 small and medium PHC pile producing companies. At the present stage, an average long-term allowable compressive load of PHC pile was designed at 70% level from current design data, and safety factor of 4.0 was applied to long-term allowable compressive loads of PHC pile despite of its excellent quality. Most quality standards of PHC pile are specified at KS F 4306. But compressive strength test method of spun concrete is specified at KS F 2454. As a result of analyzing quality test data supplied by each manufacturer, all quality test results showed higher performances than standard values. Therefore, it was considered that the capacity of PHC pile can be used up to the maximum allowable compressive load of PHC pile when PHC pile is designed.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.21 no.1
• /
• pp.1-29
• /
• 2019

Related to the previous paper on the typical crack pattern of tunnel lining with NATM, the characteristic defects in reinforced cement concrete lining of NATM tunnel have analyzed with the precise inspection with safety and diagnosis (PISD) by KISTEC. Depending on the reinforcing materials, steel rebar, steel fiber, and glass fiber have been implemented to reinforcing lining in various NATM tunnel constructions. Reinforcing lining with rebar are prevailed on NATM tunnel to countermeasure the weak geological circumstances, to pursuit the economical tunnel sections, and to resist the risk of tunnel deterioration. By the special act on the safety control of public facilities, the reinforced NATM tunnels for more than 1 km length are scrutinized closely to characterize defects; crack, reinforcement exposure, and lack of lining. Crack resistance by reinforcing is shown in comparison with the normalized crack to the length of tunnel. Typical exposed reinforcements in lining have exemplified with various sections. The lack of lining due to the mal-construction, spalling, fire, earthquake and leaching has been analyzed. The cause and mechanism with the field inspections and other studies has also been verified. Detailed cases are selected by the above concerns as well as the basic information from FMS (Facilities Management System). Likewise the previous paper, this study provides specialized defects in reinforced lining of NATM and it can be widely used in spreading the essential technics and reporting skills. Furthermore, it would be advised and amended for the detail guideline of Safety Diagnosis and PISD (tunnel).

• Journal of the Korean GEO-environmental Society
• /
• v.12 no.5
• /
• pp.51-57
• /
• 2011

Generally, ready-mixed concrete(RMC) gets hardened by time, so the remaining concrete in the drum should be cleaned. But if the RMC waste water generated from this is discharged to soil without any treatment, the strong alkaline elements and heavy metals affect water and ecosystem pollution. Although about 10 to 15% of water used for cleaning in the RMC factory is discharged to soil or river, the concrete report of this affecting soil pollution has not been sufficient. Hence, in this study it was analyzed the extraction of cleaning water from RMC factories all over the country and heavy metal and pH components remaining in soil when this is penetrated to various soils having water permeability. The specimens used for the experiment are weathering soil and soils having different particle size, and it is made to be penetrated to those for 24 hours while fixed thickness of the layer is maintained. Cleaning water is divided into that before deposition treatment(sludge water) and that after deposition treatment(upper water) to be penetrated into soil, and according to the result of penetrating sludge water to soil, Cu and Mn, Fe, and Zn were found to be remained over 23 to 90%. However, it is analyzed that in upper water having deposition treatment, Cu and Mn remain as 60% or more only in weathering soil.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.42 no.6
• /
• pp.825-836
• /
• 2022

Micropiles can be used to support additional load in extended building structures. However, their use brings about a risk of exceeding the bearing capacity of existing piles. In this study, pre-compression was applied to distribute the load of an existing building to micropiles, and an indoor loading test was performed to confirm the structural applicability of a wedge-type anchorage device designed to improve its capacity. According to the test results, the maximum strain of the anchorage device was 0.63 times that of the yield strain, and the amount of slip generated at the time of anchorage was 0.11 mm, satisfying structural standards. In addition, using MIDAS GTS, a geotechnical finite element analysis software, the effect of the size of the pre-compression, the thickness of the soil layer, and the ground conditions around the tip on the reaction force of the existing piles and micropiles were analyzed. From the numerical analysis, as the size of the pre-compression load increased, the reaction force of the existing pile decreased, resulting in a reduction rate of up to 36 %. In addition, as the soil layer increased by 5 m, the reduction rate decreased by 4 %, and when the ground condition at the tip of the micropile was weathered rock, the reduction rate increased by 14 % compared with that of weathered soil.

• Journal of the Korean Geotechnical Society
• /
• v.23 no.8
• /
• pp.159-169
• /
• 2007

The behavior of fiber-reinforced cemented sands (FRCS) was studied to improve a brittle failure mode observed in cemented sands. Nak-dong River sand was mixed with ordinary Portland cement and a Polyvinyl alcohol (PVA) fiber. A PVA fiber is widely used in concrete and cement reinforcement. It has a good adhesive property to cement and a specific gravity of 1.3. A PVA fiber has a diameter of 0.1 mm that is thicker than general PVA fiber for reinforced cement. Clean Nak-dong River sand, cement and fiber at optimum water content were compacted in 5 layers giving 55 blows per layer. They were cured for 7 days. Cemented sands with a cement/sand ratio of 4% were fiber-reinforced at different locations and tested for unconfined compression tests. The effect of fiber reinforcement form and distribution on strength was investigated. A specimen with evenly distributed fiber showed two times more strength than not-evenly reinforced specimen. The strength of fiber-reinforced cemented sands increases as fiber reinforcement ratio increases. A fully reinforced specimen was 1.5 times stronger than a specimen reinforced at only middle part. FRCS behavior was controlled not only by a dosage of fiber but also by fiber distribution methods or fiber types.