In this study, we conducted the hot box tests to compare the changes in thermal insulation for the four types of multi-layer thermal screens by the used period after collecting them from the greenhouses in the field when they were replaced at the end of their usage. The main materials for these four types of multi-layer thermal screens were matt georgette, non-woven fabrics, polyethylene (PE) foam, chemical cotton, etc. These materials were differently combined for each multi-layer thermal screen. We built specimens ($70{\times}70cm$) for each of these multi-layer thermal screens and measured the temperature descending rate, heat transmission coefficient, and thermal resistance for each specimen through the hot box tests. With regard to the material combinations of multi-layer thermal screens, thermal insulation can be increased by applying a multi-layered PE foam. However, it is considered that the multi-layered PE foam significantly less contributes to heat-retaining than chemical wool that forms an air-insulating layer inside multi-layer thermal screens. For the suitable heat-retaining performance of multi-layer thermal screens, basically, materials with the function of forming an air-insulating layer such as chemical cotton should be contained in multi-layer thermal screens. The temperature descending rate, heat transmission coefficient, and thermal resistance of multi-layer thermal screens were appropriately measured through the hot box tests designed in this study. However, in this study, we took into consideration only the four kinds of multi-layer thermal screens due to difficulties in collecting used multi-layer thermal screens. This is the results obtained with relatively few examples and it is the limit of this study. In the future, more cases should be investigated and supplemented through related research.

• Composites Research
• /
• v.26 no.1
• /
• pp.14-20
• /
• 2013

The electrospun PVDF containing CNT was made for fabricating materials of the actuator. The electrochemical and their actuating movement were evaluated for the actuator performance in the electrochemical environment. The actuator (which was fabricated by electrospinning) had some advantages, i.e., good dispersion and flexible properties. In the electrospinning process, the final product would have different forms based on different essential factors. In this work, electrospun nanofibers were aligned by using the drum-type collector, and the morphology was identified via the field emission-scanning electron microscope (FE-SEM). The uniform dispersion of CNT in PVDF nanofiber was observed by electron probe X-ray micro-analysis (EPMA) test. The results of tensile strength and electrical resistivity provided the aligned state. The electrospun CNT/PVDF nanofiber sheet on the aligned direction showed better mechanical and electrical properties than the case of the vertically-aligned direction. The efficiency and electrical capacities of electrospun CNT/PVDF nanofiber sheets were compared with the cast PVDF sheet for actuator application. Electrospun CNT/PVDF nanofiber sheet exhibited much better the case of actuator performance than cast neat PVDF actuator, due to the excellent electrical connecting areas.

• Applied Chemistry for Engineering
• /
• v.31 no.3
• /
• pp.310-316
• /
• 2020

Terpene-modified phenolic resins were used to improve the tires wet traction related to the driving safety and also rolling resistance related to fuel efficiency. In this work, alpha-pinene, beta pinene, and delta limonene resins, which constitute different basic structures of terpene-modified phenolic resins, were individually added to the tread compounds of tires and their physical properties were compared with those of the alkyl phenol resin compounds. Alkyl phenolic resins showed no significant difference in tangent delta from terpene-modified phenolic resins at 0 ℃, which is related to wet traction, but showed higher tangent delta at 80 ℃, which is related to rolling resistance, indicating smaller fuel efficiency improvement effects. Among the terpene-modified phenolic resins, beta pinene one showed improved wet traction and fuel efficiency compared to those of other resins. Delta limonene resin showed the best wet traction improvement effect, and alkyl phenolic resins showed relatively high tensile strength and abrasion property. All terpene-modified resins exhibited better rolling resistance than those of alkyl phenolic ones so that they can be said to have better fuel efficiency improvement effects and also to improve other properties compared to those of blanks. Terpene-modified phenolic resins could be used when mixing tire compounds referring to the properties of the phenolic resins revealed in this work, which could result in preparing compounds with improved wet traction and rolling resistance.

• Analytical Science and Technology
• /
• v.5 no.1
• /
• pp.79-82
• /
• 1992

A bipolar pulse conductometric detector has been developed for continuous on-line monitroring of the flowing sample streams. The conductometric detector was fast and easy to use due to the free of interferences by serial or parallel capacitances. The performance of the bipolar pulse conductometric detector was tested using dummy cells with $10^1{\sim}10^8$ ohm resistance range and found a linear response with a 0.01% relative standard deviation. The possible applications of the bipolar pulse conductometric detector was discussed.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.4
• /
• pp.61-68
• /
• 2019

As the pollution of water resources deteriorates due to industrialization and urbanization, it is difficult to supply clean water through a water treatment method using chlorine. Therefore, the introduction of advanced water treatment facilities using ozone is on the increase. However, epoxy which is used as waterproofing and anticorrosives and stainless steel used in conventional waterproofing and anti-corrosive methods have deteriorated because of the strong oxidizing power of ozone, causing problems such as leaking. Moreover, it even causes the durability degradation of a concrete. Therefore, in this study, metal spraying system was used as the means of constructing a metal panel with excellent ozone resistance and chemical resistance which is an easier method than an existing construction method. Ozone resistance was evaluated in accordance with the type of metal sprayed coatings to develop a finishing method which can prevent the concrete structure of water treatment facilities from deterioration. Furthermore, electrochemical stability in actual sewage treatment plant environment was evaluated. Experimental results showed that Ti has superior ozone resistance after spraying and the electrochemical stability in the sewage treatment plant environment showed that Ti has the highest polarization resistance of $403.83k{\cdot}{\Omega}{\cdot}cm^2$, which ensures high levels of durability.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.6
• /
• pp.29-36
• /
• 2015

In this study, to examine the use of sulfur polymer as a coating agent for concrete, durability and hazard evaluations were performed. The result of the evaluation indicated that the chemical resistance of the coating agent for concrete was outstanding against acidic, base, and alkaline solutions. The evaluation of the bond strength after an accelerated weathering test depending on the mixing condition indicated that the most outstanding strength characteristic was obtained when silica powder and fly ash were mixed at the same time. The bond strength exceeded 1 MPa in every mixing condition even after the repeated hot and cold treatment of the coating agent specimen for concrete, and the SFS mix proportion showed the highest bond strength. The examination of the accelerated carbonation and chloride ion penetration resistance of the concrete coated with the coating agent indicated that the specimen coated with the coating agent using silica powder as a filler showed the most outstanding durability. When a fish toxicity test was performed to examine the hazard of the use of the functional polymer as a coating agent for concrete, the functional polymer was found to have no effect on the organisms. When the chemical resistance, freezing and thawing resistance, carbonation, and chloride ion penetration resistance of the coating agent were considered, substituting silica powder and fly ash as the fillers of the functional polymer by 20%, respectively, was the optimal level in the range of this study.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.1
• /
• pp.89-96
• /
• 2023

In this paper, a ferrosilicon by-product was evaluated to confirm the feasibility of recycling it as supplementary cementitious material of ordinary Portland cement in concrete. Three different levels of replacement ratio (10 %, 20 % and 30 % of total binder) were applied to find which is the most beneficial to be used as a binder. Ferrosilicon concrete was initially assessed at setting time and compressive strength. Durability was evaluated by the resistance to chloride penetration test(RCPT) and alkali-silica reaction(ASR) with a comparison to silica fume concrete due to their similarity in chemical composition. The porosimetry and X-ray diffraction analysis along with energy dispersive X-ray spectroscopy give information on the microstructural characteristics of the ferrosilicon concrete. It was found that 10 % ferrosilicon concrete has higher strength while 20 %, 30 % have lower strength than OPC concrete. However, chemical resistance to chloride attack is higher when replacement is increased. Compared to silica fume, the durability of ferrosilicon might be less efficient however, it is obviously beneficial than OPC. High SiO₂ content in ferrosilicon results in producing more C-S-H gel which could make denser pore structure. Most of the risk of alkali silica reaction to silicate binders through length change tests was less than 0.2 %, and both mortar using ferrosilicon and silica fume showed better resistance to alkali silica reaction as the substitution rate increased.Reuse of industrial waste rather than producing highly refined additives might reduce environmental load during manufacture and save costs.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.6
• /
• pp.281-289
• /
• 1998

This study has been performed to test the flowability and filling ability of high flowing concrete as well as distribution of aggregate and pore of core specimen, heat of hydration, compressive strength and core strength of concrete. In addition, the resistance to chloride ion penetration and chemical solutionof concrete was tested in order to evaluate the resistance to sea water of concrete and its application of high flowing concrete using blended low heat cement in the field of Seohae Grand Bridge. The properties of high flowing concrete with blended low heat cement were compared with ordinary 25-240-15 concrete using Type V cement. As the results of this study, the flowability and filling ability of high flowing concrete with blended low heat cement is satisfied without vibration. Though the cement content of high flowing concrete with blended low heat cement was 400kg/m$^2$, the rising temperature of it was relatively lower than that of the ordinary 25-240-15 concrete with Type V cement. Also, the compressive of high flowing concrete with blended low heat cement is similar to that of the ordinary 25-240-15 concrete with Type V cement.

• Korean Chemical Engineering Research
• /
• v.54 no.3
• /
• pp.305-309
• /
• 2016

Recently, there are many efforts focused on development of more economical non-fluorinated membranes for PEMFCs (Proton Exchange Membrane Fuel Cells). In this study, to test the durability of sPEEK MEA (Membrane and Electrode Assembly), ADT (Accelerated Degradation Test) of MEA degradation was done at the condition that membrane and electrode were degraded simultaneously. Before and after degradation, I-V polarization curve, hydrogen crossover, electrochemical surface area, membrane resistance and charge transfer resistance were measured. Although the permeability of hydrogen through sPEEK membrane was low, sPEEK membrane was weaker to radical evolved at low humidity and OCV condition than fluorinated membrane such as Nafion. Performance after MEA degradation for 144 hours and 271 hours were reduced by 15% and 65%, respectively. It was showed that the main cause of rapid decrease of performance after 144 hours was shorting due to Pt/C particles in the pinholes.

• Korean Chemical Engineering Research
• /
• v.50 no.4
• /
• pp.749-753
• /
• 2012

In present work, anode support for micro-tubular SOFC was fabricated with outer diameter of 3 mm and characterized with microstructure, mechanical properties and gas permeability. The microstructure of surface and cross section of a porous anode support were analyzed by using SEM (Scanning Electron Microscope) image. The gas permeability and the mechanical strength of anode support was measured and analysed by using differential pressure at the flow rates of 50, 100, 150 cc/min. and using universal testing machine respectively. The unit cell composed of NiO-YSZ, YSZ, YSZ-LSM/LSM/LSCF was fabricated and operated with reaction temperature and fuel flow rate and showed maximum power density of $1095mW/cm^2$ on the condition of $800^{\circ}C$. The performance of single cell for micro-tubular SOFC increased with the increasing the reaction temperature due to the decrement of ohmic resistance of cell by the increment of the ionic conductivity of electrolyte through the evaluation of electrochemical impedance analysis for single cell with reaction temperature.