• Journal of the Korea Institute of Building Construction
• /
• v.17 no.5
• /
• pp.393-401
• /
• 2017

This study presents an evaluation of basic properties of light weight mortar with expanded polystyrene bead(EPB) and waste expanded polystyrene(WEP) by varying replacement rations. In order to evaluate the basic properties of the light weight mortar with EPB and WEP, unit weight, compressive strength, flexural strength, water absorption ratio, thermal conductivity and distribution of polystyrene (EPB and WEP) in hardened mortar were performed. As a result, unit volume, compressive strength, bending strength, water absorption and thermal conductivity of light weight mortar were increased, but area distribution of polystyrene decreased with increasing the replacement ratio of WEP.

• Journal of the Korea Concrete Institute
• /
• v.16 no.1 s.79
• /
• pp.54-60
• /
• 2004

This study deals with the setting behavior of polystyrene mortars using waste expanded polystyrene(EPS) solution-based binders. The binders for polystyrene mortars are made by mixing crosslinking agent with EPS solutions prepared by dissolving EPS in styrene. Polystyrene mortars are prepared with various EPS concentrations of EPS solutions and crosslinking agent contents, subjected to a dry curing, and tested for working life, peak exotherm temperature and 10h-length change. From the test results, He working lives of polystyrene mortars are shortened with raising EPS concentration of EPS solution and crosslinking agent content. Low-shrinkage or non-shrinkage polystyrene mortars could be obtained by adjusting EPS concentration of EPS solution and crosslinking agent content.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.250-251
• /
• 2017

In study, the lightweight insulation mortar is produced with more than 50,000tons of waste each year, but it is difficult to treat with the degradable composite material and the recycling ratio is still 50%. the lightweight insulation mortar is manufactured by using the ratio of expanded polystyrene and pulverized expanded polystyrene.

• Journal of the Korea Organic Resources Recycling Association
• /
• v.12 no.4
• /
• pp.85-94
• /
• 2004

Waste wood-plastic composite panels are made on different hot press molding conditions, and tested for apparent density, water absorption, expansion in thickness and flexural strength. From the test results, regardless of molding temperature and molding time, the apparent density of the composite panels is increased with an increase in the molding pressure, while their water absorption is decreased with an increase in the molding pressure. The flexural strength of the composite panels is markedly increased with increasing molding pressure, molding temperature and molding time, and tends to become nearly constant at a molding temperature of $120^{\circ}C$ and a molding time of 15min.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.221-222
• /
• 2016

The replacement ratio of waste EPS was varied, and its effect on compressive strength and absorption capacity was investigated. According to the experimental results, The 28th day compressive strengths for the W/C 50% specimens were 17.5~21.2MPa, which was relatively low compared to the 13.6~22.2MPa of the W/C 70%.

• Journal of the Korea Concrete Institute
• /
• v.13 no.1
• /
• pp.30-37
• /
• 2001

Generally, polymer mortar made with unsaturated polyester(UP) resin has a high curing shrinkage. This is an inadequate as repair material and construction products that have been widely used for years recently. To overcome these problems, polymer researchers and engineers have used shrinkage-reducing additives, which are usually specific thermoplastic polymers. The objective of this study is to evaluate the effects of shrinkage-reducing additive on the curing shrinkage and strengths of UP mortar. UP mortars are prepared with expanded polystyrene(EPS) ratio in styrene monomer(SM), (EPS/PS, PS=EPS+SM), and the ratio of total polystyrene resin(PS) to UP resin, (PS/UP). And it is tested for viscosity of UP resin, slump-flow, working life, flexural and compressive strengths, and curing shrinkage tests. From the test results, viscosity of resin for UP mortar increases with increasing PS content. Curing shrinkage of UP mortar is considerably smaller than that of plain UP mortar, nevertheless, reduction in the strengths is not recognized according to adding PS resin. In this study, we can obtain the optimum mix proportions of UP mortar using PS resin which made of waste expanded polystyrene.

• Journal of the Korea Organic Resources Recycling Association
• /
• v.12 no.4
• /
• pp.95-104
• /
• 2004

A styrene solution of waste expanded polystyrene with a crosslinking agent and an initiator was used as a binder for waste wood-plastic composite panels. The waste wood-plastic composite panels are prepared with various binder contents and filler-binder ratios by using a hot press molding method. The apparent density of the composite panels is increased with increasing binder content and filler-binder ratio, while their water absorption and expansion in thickness are decreased with increasing binder content and filler-binder ratio. The maximum flexural strength and wet flexural strength of the composite panels are obtained at a binder content of 35% and a filler-binder ratio of 0.8. Decreases in the flexural strengths of the composite panels due to water immersion at 20 and $100^{\circ}C$ are hardly recognized at binder contents of 30% or more.

• Applied Chemistry for Engineering
• /
• v.17 no.3
• /
• pp.321-326
• /
• 2006

Thermal degradation of styrene dimer fraction (SDF, main compound: 47 wt% of 1,3-diphenylpropane), 5~15% of total products produced during decomposition of waste expanded polystyrene (WEPS) was investigated. Reaction condition of $360^{\circ}C$, and 152 kPa to 202 kPa was an optimum for high pressure degradation. Under this operating condition, the yield of oil was 73.8% and the selectivities to Ben, Tol, EB, SM, and AMS were 0.4, 30.9, 15.0, 19.6, and 4.2%, respectively. Non-catalytic fixed bed continuous degradation was conducted at reaction temperatures of $510{\sim}610^{\circ}C$ and contact time ranges of 2~24 min, where the yield was increased by increasing of reaction temperature and contact time. A $Cr_2O_3$ catalyst showed the highest activity and SM yield among acid, base, and redox catalysts. The conversion of 74.6% and the yield of Ben, Tol, EB, SM, and AMS were 0.4, 21.6, 9.7, 17.9, and 3.5%, respectively at $560^{\circ}C$ and contact time of 24 min. It is thought that styrene is converted to EB and other secondary products throughout the formation of diradicals of styrene.