Basic Properties of Waste Wood-Plastic Composite Panels by Hot Press Molding Method

열압 성형법에 의한 폐목재-플라스틱 복합패널의 기초적 성질

A styrene solution of waste expanded polystyrene with a crosslinking agent and an initiator was used as a binder for waste wood-plastic composite panels. The waste wood-plastic composite panels are prepared with various binder contents and filler-binder ratios by using a hot press molding method. The apparent density of the composite panels is increased with increasing binder content and filler-binder ratio, while their water absorption and expansion in thickness are decreased with increasing binder content and filler-binder ratio. The maximum flexural strength and wet flexural strength of the composite panels are obtained at a binder content of 35% and a filler-binder ratio of 0.8. Decreases in the flexural strengths of the composite panels due to water immersion at 20 and $100^{\circ}C$ are hardly recognized at binder contents of 30% or more.

본 연구에서는 가연성 건설폐기물 재활용의 일환으로, 폐발포폴리스티렌의 스티렌 용액에 가교제 및 개시제를 첨가하여 제조한 결합재와, 폐목재 칩을 이용하여, 폐목재-플라스틱 복합패널을 제조하였다. 전열 프레스를 이용하여 다양한 결합재량 및 충전재-결합재 비를 갖는 복합패널 공시체를 제조하였으며, 그 겉보기 밀도, 흡수율, 흡수에 의한 팽창률, 휨강도, 내수성 등에 관한 일련의 실험을 행하였다. 폐목재-플라스틱 복합패널의 겉보기밀도는 결합재량 및 충전재-결합재비의 증가에 따라 증대하며, 그 휨강도 및 습윤 휨강도는, 결합재량 35%, 충전재-결합재비 0.8에 있어서 최대치에 이른다. 흡수율 및 흡수에 의한 두께 팽창률은, 결합재량 및 충전재-결합재비의 증가에 따라 현저하게 감소한다. 결합재량 30%이상의 경우, 충전재-결합재비에 관계없이, 복합패널의 24h 상온 수중($20^{\circ}C$) 침지 및 2h 끓는 물중($100^{\circ}C$)＋1h상온 수중($20^{\circ}C$) 침지에 의한 휨강도의 감소는 거의 발생하지 않으며, 높은 내수성을 발현한다.