Setting Behavior of Polystyrene Mortars with Elapsed Curing Time

폴리스티렌 모르타르의 양생재령에 따른 경화거동

  • Choi Nak-Woon (Research Center of Industrial Technology, Chonbuk National University) ;
  • Kim Han-Sang (Dept. of Civil Engineering, Kansas State University)
  • 최낙운 (전북대학교 공업기술연구센터) ;
  • 김한상 (켄사스주립대학교 토목공학과)
  • Published : 2004.02.01

Abstract

This study deals with the setting behavior of polystyrene mortars using waste expanded polystyrene(EPS) solution-based binders. The binders for polystyrene mortars are made by mixing crosslinking agent with EPS solutions prepared by dissolving EPS in styrene. Polystyrene mortars are prepared with various EPS concentrations of EPS solutions and crosslinking agent contents, subjected to a dry curing, and tested for working life, peak exotherm temperature and 10h-length change. From the test results, He working lives of polystyrene mortars are shortened with raising EPS concentration of EPS solution and crosslinking agent content. Low-shrinkage or non-shrinkage polystyrene mortars could be obtained by adjusting EPS concentration of EPS solution and crosslinking agent content.

발포폴리스티렌(EPS)의 효율적인 재활용 기술개발의 일환으로서 폐 발포폴리스티렌을 중합성 모노머인 스티렌에 용해한 고분자 용액에 가교제, 개시제, 촉진제 등을 첨가하여 상온 중합성 결합재를 개발하였으며 이를 이용한 폴리스티렌 모르타르를 제조하여 그 중요한 경화특성인 사용가능시간, 건조양생재령에 따른 발열온도 및 길이변화 거동에 미치는 폐 발포폴리스티렌 용액농도 및 TMPTMA 첨가량의 영향에 대해서 검토하였다. EPS용액을 이용한 결합재 및 폴리스티렌 모르타르의 사용가능시간은 EPS용액 농도 및 TMPTMA 첨가율의 증가에 따라서 짧아지며, 또한 폴리스티렌 모르타르의 경화에 따른 길이변화는 EPS용액 농도 및 TMPTMA 첨가율에 크게 영향을 받는데 이를 적절히 조절하여 경화특성을 제어함으로써 저수축 혹은 무수축 폴리스티렌 모르타르의 제조가 가능하다는 것을 검증하고 있다.

Keywords

References

  1. Kukacka, L. E., Fontana, J, and Steinberg, M, 'Polymer Concrete Materials for Use in Geothermal Energy Processes,' Proceedings of the Second Intermational Congress on Polymers in Concrete, The University of Texas at Austin, Austin, USA, Oct. 1978, pp.105-119
  2. 大擴嘉彦, 'スチレンを結合材と したレジンコンクリ-トの 製造法及びその性吠', 昭和52年度日本建築學書大書學術證 演梗漑集(中國), 構造系, No.257, Oct. 1977, pp.297-288
  3. 卒野徹, 'ァクリル系ポリマ-コンクリ-トの特性と應用', ポリマ-ダイジェスト, Vol.35, No.5, May 1983, pp.25-43
  4. 山崎竹博, 宮川邦彦, 渡辺明,'補强されたレジンコンクリ一ト の便化收縮応力算定こ關する實驗', 土木學營論文報告集, No.318, Feb. 1982, pp.127-137
  5. 최낙훈, 소양섭, '폴리스티렌 모르타르의 강도특성', 대한건축학회 학술발표논문집, 단국대학교, Vol.23, No.1, Apr. 2003, pp.247-250
  6. Ohama, Y. and Demura, K, 'Apparatus for Measuring the Length Change of Polymer (or Resin) Concrete,' The journal. of the College of Engineering of Nihon University, Series A, Vol.20, Mar. 1979, pp.47-50
  7. Moriyoshi, A, Omata, F., Kawakami, M, Tokushige, H. and Ohama, Y., "Stresses and Stains of Resin Mortar during Setting,' Polymers in Concrete, Proceedings of the 2nd East Asia Symposiun on Polymers in Concrete, College of Engineering, Nihon University, Koriyama, Japan, May 1997, pp.353-362
  8. 鶴駱禎二, '新訂高分子合成反庶', 日刊工業新聞社, 東京, Sep. 1977, pp.10-24
  9. Billmeyer, F. W., 'Textbook of Polymer Science-Second Edition,' John Wiley & Sons, New York, USA, 1971, pp.291-293
  10. 崔沿涯, 大賓嘉彦, '廢發池ぽリスチレンを用いたポリマ- そルタルの可使時間疋び張さ性淡に疋ぼす開始劑춻び促 劑の影響', セメント·コンクリ-ト論文集, NO.56, Feb. 2003, pp.727-732
  11. McNerey, M. T., 'Research in Progress: Rapid AilWeather Pavement Repair with Polymer Concrete,' Applications of Polymer Concrete, American Concrete Institute(SP69), Detroit, Nov. 1981, pp.93-105
  12. 携澤業一郎, 'ポリエステル樹指ハンドブック', 日刊工業 新聞社, 東京, Jun. 1988, pp.258-260