A Study on Properties of Waste Wood-Plastic Composite Panels

폐목재-플라스틱을 이용한 복합패널의 특성 연구

  • Received : 2004.09.30
  • Accepted : 2004.12.03
  • Published : 2004.12.30

Abstract

Waste wood-plastic composite panels are made on different hot press molding conditions, and tested for apparent density, water absorption, expansion in thickness and flexural strength. From the test results, regardless of molding temperature and molding time, the apparent density of the composite panels is increased with an increase in the molding pressure, while their water absorption is decreased with an increase in the molding pressure. The flexural strength of the composite panels is markedly increased with increasing molding pressure, molding temperature and molding time, and tends to become nearly constant at a molding temperature of $120^{\circ}C$ and a molding time of 15min.

본 연구에서는 가연성 건설폐기물인 폐목재와 폐발포폴리스티렌의 유효이용을 목적으로 열압성형법에의한 폐목재-플라스틱 복합패널을 제조하였다. 전열프레스를 이용하여 다양한 성형조건하에서 복합패널 공시체를 제조하였으며, 그 겉보기 밀도, 흡수율, 흡수에 의한 두께 팽창률, 휨강도 등에 관한 일련의 실험을 행하였다. 폐목재-플라스틱 복합패널의 밀도는, 성형 온도 및 성형 시간에 관계없이, 성형 압력의 증가에 따라 높아지는 반면, 그 흡수율의 성형압력의 증가에 따라 작아진다. 복합패널의 흡수에 의한 두께 팽창률은, 성형 조건에 관계없이, 모두 1.2~2.0%의 범위에 있어, 높은 치수 안정성을 보인다. 복합패널의 휨강도는, 성형 온도 $120^{\circ}C$, 성형 시간 15min에서 일정하게 되는 경향이 있으며, 성형 온도 및 성형 시간에 관계없이, 성형 압력의 증가에 따라 현저하게 증가한다. 중합 반응과 성형을 동시에 하는 리액션프로세싱인 이 방법은, 그 제조 공정이 간단하고, 또한, 결합재로서 폐발포폴리스티렌 용액을, 골재로서 폐목재 칩을 이용하기 때문에, 공업 생산성이 있는 건설 발생 폐목재 및 폐발포폴리스티렌의 리사이클 방법으로서 지극히 유효하다고 생각된다.

Keywords