• Clean Technology
• /
• v.16 no.2
• /
• pp.132-139
• /
• 2010

The Cu-Mn mixed oxide catalysts with different molar ratios of Cu/(Cu+Mn) prepared by co-precipitation method have been investigated in CO oxidation at $30^{\circ}C$. The catalysts used in this study were characterized by X-ray Diffraction (XRD), $N_2$ sorption, X-ray photoelectron spectroscopy (XPS), and $H_2$-temperature programmed reduction $(H_2-TPR)$ to correlate with catalytic activities in CO oxidation. The $N_2$ adsorption-desorption isotherms of Cu-Mn mixed oxide catalysts showed a type 4 having pore range of 7-20 nm and BET surface area was increased from 17 to $205\;m^2{\cdot}g^{-1}$ with increasing of Mn content. The XPS analysis showed the surface oxidation state of Cu and Mn represented $Cu^{2+}$and the mixture of $Mn^{3+}$ and $Mn^{4+}$, respectively. Among the catalysts studied here, Cu/(Cu+Mn) = 0.5 catalyst showed the highest activity at $30^{\circ}C$ in CO oxidation and the catalytic activity showed a typical volcano-shape curve with respect to Cu/(Cu+Mn) molar ratios. The water vapor showed a prohibiting effect on the efficiency of the catalyst which is due to the competitive adsorption of carbon monoxide on the active sites of catalyst surface and finally the formation of hydroxyl group with active metals.

• Journal of the Korean Electrochemical Society
• /
• v.15 no.4
• /
• pp.216-221
• /
• 2012

Electrochemical reduction of carbon dioxide has been widely studied by many scientists and researchers. Recently, the production of formic acid, which is expensive but highly useful liquid material, is receiving a great attention. However, difficulties in the electrochemical reduction process and analyzing methods impede the researches. Therefore, it is important to design an adequate system, develop the reduction process and establish the analyzing methods for carbon dioxide reduction to formic acid. In this study, the production of formic acid through electrochemical reduction of carbon dioxide was performed and concentration of the product has been analyzed. Large scale batch cell with proton exchange membrane was used in the experiment. The electrochemical experiment has been performed using a series of metal catalysts. Linear sweep voltammetry (LSV) and chronoamperometry were performed for carbon dioxide reduction and electrochemical analysis using silver chloride and platinum electrode as a reference electrode and counter electrode, respectively. The concentration of formic acid generated from the reduction was monitored using high performance liquid chromatography (HPLC). The results validate the appropriateness and effectiveness of the designed system and analyzing tool.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.22 no.2
• /
• pp.451-457
• /
• 1998

This paper describes a modelling method for SCR(selective catalystic reduction) system in refuse incineration plant. We consider the SCR system as a single input and single output system. For modelling the SCR system, an auto regressive exogeneous(ARX) modelling method is used. In this case, we should design the white noise input for modelling and put it on the system as an input$(NH_3)$, and take an outlet NOx as an output. From these two relations, we design the ARX model with 45 second delay time and transform to a discrete system with sampling time of 0.5 second. Using the obtained SCR model, we verify that the outlet NOx is deeply related with stoker`s moving in boiler of refuse incineration plant.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.06a
• /
• pp.331-334
• /
• 2007

탄소나노튜브는 화학적 안정성과 고전도성을 갖는 동시에 높은 비표면적을 지니고 있다. 이와 같은 특정으로 염료감응형태양전지의 상대전극으로 사용 가능이 기대되어 지고 있으나, 아직 성공적인 연구가 발표되고 있지 않다. 많은 연구자들이 CNT 자체만으로 원하는 효과를 얻지 못하고 있기 때문에, CNT 조작(가공)을 통해 CNT 특성을 올리고자 노력하였다. 그러나 본 연구에서, 가공하지 않은 CNT powder를 이용하여 paste를 제조하고 doctro-blade법으로 코팅하여 CNT counter electrode를 제조하여 DSSC의 상대전극으로써의 적용 가능성을 조사 해 보았다. 제조된 CNT counter electrode에 대한 CNT 자체만의 전기화학적 특성을 측정하였다. 그리고 DSSC 에 직접 적용하여 전지의 광전특성을 측정하였다. 그 결과 탄소나노튜브의 고전도성 특성과 넓은 비표면적 특성에 의해 상대전극의 전해질/전극계변에서의 전해질의 산화환원 반응에 대한 촉매 작용을 향상시키고, 상대전극 표변에서의 전자전달 속도를 높여 염료감응형 태양전지의 효율을 높이는 것으로 확인되어졌다.

• Journal of the Korean Chemical Society
• /
• v.48 no.2
• /
• pp.151-155
• /
• 2004

The self-assembled mololayers(SAMs)were prepared with cysteine(cys) and subsequently coupled with dopamine(dopa) containing quinone functionality on the gold modified electrodes. The SAMs annealed in ethanol for 6 hours gave a better shaped cyclic voltammogram which had a 0.28 V of formal potential and same redox potential in 0.1M phosphate buffer(pH=7.10). The electrodes were employed to determine concentration of HADH with the result that calibration curve exhibited an excellent correlation(${\geq}$ 0.993) for the concentrations ranging up to 5.0${\times}10^{-4}$ M.

• Journal of ILASS-Korea
• /
• v.22 no.2
• /
• pp.96-102
• /
• 2017

In order to reduce the NOx, SCR technology is most suitable. In this study, we focused on studying the injector part of urea-SCR system. When stoichiometric 1 mole of urea is injected, 2 moles of $NH_3$ are created. $NH_3$ causes a SCR reaction by reacting with NOx. However, urea is decomposed by the side reaction of coming out HNCO, deposit formation is formed. In this study, it was to design a nozzle that can spray the optimal spray flow rate. Test nozzle used in this experiment is efferverscent type. The result of the experiment, liquid flow rate was confirmed to be that they are dominated by the exit orifice diameter. The area ratio is defined by ratio of the area of exit orifice hole and that of aerorator. The droplet size was measured by varying the area ratios. In addition, it was also confirmed that there is no change of the liquid flow rate and air flow rate to change the aerorator at the same exit orifice. Further, It was confirmed that the droplet size was relatively uniform even though the area ratio was different. Finally, there is little change in the SMD that air flow rate increases in 0.3 or more ALR.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.318.2-318.2
• /
• 2013

기존의 염료감응형 태양전지(Dye Sensitized Solar Cells; DSSCs)는 최대 효율 11~12%의 광전변환효율을 가지고 있다. 이러한 한계를 극복하기 위해서 광흡수 층 최적화, 상대전극의 촉매성 증대, 전해질의 산화 환원 반응 최적화 등의 많은 연구가 이루어지고 있다. 본 연구에서는 DSSCs의 광전변환효율을 증가시키고자 기존의 투명전극 및 기판으로 사용되는 FTO(Fluor-doped Tin Oxide)를 GZO(Gallium-doped Zinc Oxide)를 사용하여 투명전극기판에 따른 계면 저항, 전류손실 등 DSSCs에 미치는 영향을 분석하였다. 본 연구에 사용된 FTO는 ${\sim}7{\Omega}/{\square}$의 면저항과 80%이상의 투과도를 갖고 있으나 Ion-Sputtering 법으로 증착된 GZO는 열처리 과정을 통하여 $3{\sim}4{\Omega}/{\square}$의 면 저항을 나타내고 80%이상의 우수한 투과도를 가지고 있다. 이러한 두 기판의 특성 비교를 위해, UV-Visble Spectrophotometer를 사용하여 광학적 특성을 분석하고, SEM(Scanning Electron Microscope), AFM(Atomic Force Microscope)를 사용하여 표면 특성을 평가하였다. 또한 전기적 특성을 분석하기 위하여 4-Point-probe를 이용하여 면 저항을 측정하였고, DSSCs의 효율 및 Fill Factor를 분석하기 위하여 Solar Simulator의 I-V measurement를 이용하였다.

• Journal of the Korean Society of Visualization
• /
• v.19 no.1
• /
• pp.62-67
• /
• 2021

Selective catalytic reduction(SCR) is an exhaust gas reduction device to remove nitro oxides (NOx). SCR operation of ship can be controlled through valves for minimizing economic loss from SCR. Valve in SCR-high pressure (HP) system is directly connected to engine exhaust and operates in high temperature and high pressure. Long-term thermal deformation induced by engine heat weakens the sealing of the valve, which can lead to unexpected failures during ship sailing. In order to prevent the unexpected failures due to long-term valve thermal deformation, a failure prediction system using autoregressive integrated moving average (ARIMA) was proposed. Based on the heating experiment, virtual data mimicking temperature range around the SCR-HP valve were produced. By detecting abnormal temperature rise and fall based on the short-term ARIMA prediction, an algorithm determines whether present temperature data is required for failure prediction. The signal processed by the data collection algorithm was interpolated for the failure prediction. By comparing mean average error (MAE) and root mean square error (RMSE), ARIMA model and suitable prediction instant were determined.

• Resources Recycling
• /
• v.13 no.5
• /
• pp.28-36
• /
• 2004

The extraction of platinum group metals such as Pt, Pd and Rh from spent automobile catalyst has been investigated by leaching in HCl solutions using $HNO_3$ or NaOCl as a oxidant. The effect of type and amount of oxidant, reaction time and pulp density on the extraction of platinum group metals was examined. Platinum group metals were recovered by the cementation method using aluminum as a reducing agent. The extraction ratio was higher when NaOCl was used as a oxidant. The optimum leaching conditions were obtained to be: HCl 8 M, the amount of NaOCl 1.4 mole, leaching temperature $90^{\circ}C$, leaching time 180 minutes, pulp density 400g/L. Under the optimum conditions, the extraction of Pt, Pd and Rh were 96.1%, 93.6% and 77.3%, respectively. With the addition of 2.0g of aluminum which corresponds to 28 equivalent the reduction were 98% for Pt. 98.8% for Pd and 65.3% for Rh, respectively.

• Journal of the Microelectronics and Packaging Society
• /
• v.25 no.4
• /
• pp.105-109
• /
• 2018

We studied graphene synthesis to porous Cu to improve the characteristics of carbon dioxide reduction of cu. Cu powders were formed through Thermal Chemical Vapor Deposition(TCVD) to Porous Cu/Graphene structures synthesized with graphene. As a result of electrochemical experiments using a 0.1 M $KHCO_3$ electrolyte at an applied potential of -1.0 V to -1.4 V, the current density of Porous Cu/Graphene was 1.8 times higher than that of Porous Cu. As a result of evaluating the product, CO and $H_2$ were generated to Porous Cu electrode. On the other hand, the product of porous Cu/Graphene produced CO, $CH_4$ and $C_2H_4$. It is considered that the graphene causes longer carbon dioxide adsorption time, which means that the intermediates formed during the reaction remain on the electrode surface for a longer time. As a result, it can be concluded that the production reaction of the C2 compound could be continuously performed.