• The korean journal of orthodontics
• /
• v.27 no.5 s.64
• /
• pp.781-789
• /
• 1997

The purpose of this study was to evaluate the effects of fluoride relasing orthodontic sealant on the shear bond strength of light-and chemical-cured orthodontic rosins, to compare the shear bond strenth with light-and chemical-cured orthodontic resins, and to identify the changes of shear bond strength by rebonding in vitro. The brackets were divided into eight groups. Each group of metal brackets had different bonding mechanisms with adhesives. Group A : Transbond only Group B : Mono-Lok 2 only Group C : Light cured FluoroBond+Transbond Group D : Light cured FluoroBond+Mono-Lok 2 Group E : Transbond only(rebonded) Group F : Nomo-Lok 2 only(rebonded) Group G : Light cured FluoroBond+Transbond(rebonded) Group H : Light cured FluoroBond+Mono-Lok 2(rebonded) 65 extracted human premolars were prepared for bonding and 65 metal brackets for each group were bonded to prepared enamel surfaces of buccal surfaces as the above prescription. 24 hours bonding after, the Instron universal testing machine was used to test the shear bond strength of metal brackets to enamel. After debonding, same kind of metal brackets for each group were rebonded to prepared enamel surfaces of buccal surfaces to test the shear bond strength at the rebonding to enamel. Statistical analysis of the data was carried out Student's t-test ANOVA test, and Scheffe test using $SPSS/PC^+$ The results were as follows : 1. The order of shear bond strength was Group B(11.84MPa), Group A(10.75MPa), Group, D(9.69MPa), and Group C(9.39MPa)in lst bonded groups. 2. The order of shear bond strength was Group E(7.40MPa), Group G(6.48MPa), Group F(5.89MPa), and Group H(5.15MPa) in rebonded groups. 3. The shear bond strength of chemical cured orthodontic rosins had higher than that of light-cured orthodontic resins in all groups, but there was no statistical significance between groups(P>0.05). 4. In rebonded groups, the shear bond strength of light cured orthodontic rosins had higher than that of chemical cured orthodontic resins, but there was no statistical significance between groups(P>0.05). 5. The shear bond strength of all rebonded groups progressively decreased than that of 1st bonded groups, and there was statistical significance between groups(p<0.05, p<0.001).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.48 no.3
• /
• pp.280-290
• /
• 2021

Color stability of pulp-capping material is considered vital to the final aesthetic result since the material is placed in the coronal area. The purpose of this study was to compare the color stability of various pulp-capping materials by analyzing color change of tooth over time. A cavity was formed in the crown of the extracted premolar, and 4 types of pulp-capping materials were filled. Color assessment was performed with a spectrophotometer at different intervals: before placement; immediately after material placement; 1 day, 1 week, 2 weeks, 4 weeks, 8 weeks, 12 weeks, and 16 weeks after placement. Proroot white MTA^® and TheraCal LC^® showed a significant decrease in the L^* value and an increase in the ∆E^* value over time. In contrast, Biodentine^® and Well-Root^TM PT showed no significant change in the L^* value and maintained a steady ∆E^* value. The application of pulp-capping materials containing bismuth oxide as a radiopacifier may result in a color change of teeth. Long-term color stability of pulp-capping materials should be considered when treating teeth with thin enamel thickness or in aesthetically important area.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.33 no.2
• /
• pp.233-243
• /
• 2006

The aim of this study was to investigate the relationship between the C-factor and shrinkage strain values of composite resin and examine the strain values in different incremental filling techniques. Experiment consisted two aims. First, we compared with strain value in two different C-factors(3.7 and 1.0). Second, we examined the strain values in three different filling techniques. The results of the present study can be summarized as follows : 1. High C-factor groups showed higher contraction stress values than low C-factor groups at 900 sec after polymerization. 2. Hybrid resin showed higher contraction stress values than flowable resin in high C-factor cavities. But contraction stress was not revealed significant difference between hybrid resin and flowable resin in low C-factor cavities (P>0.05). 3. Bulk felling with hybrid resin(Group 1) showed high contraction stress and lining with flowable resin followed hybrid resin (Group 5) showed lower contraction stress. 4. Contraction stress were increased during 900 sec after polymerization in high C-factor groups but decreased gradually after 900 sec. 5. Low C-factor groups showed tight marginal seal between resin and cavity wall but high C-factor groups showed gaps formed between resin and cavity wall in part. On the basis above results, layering techniques in high C-factor cavity showed advantages in reducing contraction stress and gap formation between cavity wall and resin restoration.

• Restorative Dentistry and Endodontics
• /
• v.32 no.6
• /
• pp.491-497
• /
• 2007

The purpose of this study was to compare apical sealing ability of continuous wave canal filling technique according to various heat source plugging depths. Eighty one extracted human premolars with straight root were cleaned and shaped to size 35 using .06 taper rotary NiTi file. After cleansing and shaping, the teeth were divided into 5 groups following the heat source probing depths from the apex; 3, 4, 5, 6 and 7 mm. All specimens were filled using E&Q plus with #35/.06 tapered gutta-percha cone. The positive control teeth were not filled. All teeth were coated with nail varnish except the apical 1 mm around the apical foramen. Negative control teeth were completely sealed include the apical foramen. All specimens were immersed in 1% methylene blue solution for 72 hours. Then the specimens were sectioned horizontally at 1, 2 and 3 mm from the root apex. Each sectioned surface was photographed using a digital camera attached to the stereomicroscope at $12.5{\times}2.5$ fold magnification. All points at 1, 2 and 3 mm were summed as final score of one specimen. Statistical analysis of the collected data was performed. Under the condition of this study. there was no significant difference between the heat source plugging depths of 3, 4, 5, 6 and 7 mm in apical sealing ability. All of apical heat source plugging depth from 3 to 7 mm including Buchanan's protocol -from 5 to 7 mm- seems to be acceptable in clinical application.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.3
• /
• pp.472-480
• /
• 2005

The purpose of this study was to investigate the effective penetration methods of acid etching agents in the pit and fissures on the occlusal surface. Extracted maxillary first and second premolars were divided into 4 groups : to Group I only acid etching agent was applied, to Group II ultrasonic scaler as well as acid etching agent were applied, to Group III after fissurotomy acid etching agent was applied, and to Group IV after fissurotomy the same process performed with Group II. The comparison between the 4 groups by the use of scanning electron microscope showed the results as follows : 1. Comparing each groups with regard to the penetration rate(%) of acid etching agents, Group III and Group IV showed improved penetration rate(%) compared with Group I. Group II made no significant different results from Group I, but had somewhat better penetration rate(%). 2. Comparing each groups with regard to the penetration rate(%) of acid etching agents according to regions within fissures, Group III and Group IV showed more improved penetration rate than Group I in the mesial pit and distal pit. However, no significant difference between each groups was showed in the middle fissure.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.2
• /
• pp.182-190
• /
• 2009

Statement of problem: Microleakage at the occlusal and gingival margin of Class V cavities restored with composite resin has traditionally been considered an obstacle to successful restoration. Purpose: The aim of this study was to assess the effectiveness of three different surface sealants(Fortify, Permaseal and Biscover LV) on the marginal sealing of Class V light-activated composite resin restorations(Z250). Material and methods: Forty noncarious human premolars and molars extracted within a three-month period were selected. Class V cavities with the occlusal margin in enamel and gingival margin in cementum were prepared in both buccal and lingual surfaces. The teeth, randomly assigned in four groups with twenty cavities in each group, were restored with composite resin after applying an adhesive system(Clearfil SE bond). After the finishing and polishing procedures, the restorations were covered with a specific surface sealants, except for the control samples, which were not sealed. After placing restorations, the specimens were thermocycled, and immersed in a 2% methylene blue solution for twenty four hours and sectioned longitudinally. The marginal microleakage was evaluated at the occlusal and gingival interfaces using a microscope and compared among the four groups using ANOVA test and Wilcoxon Rank-Sum test($\alpha$=0.05). Results: Statistical analysis showed that there was significantly less leakage when the surface sealants were used than there was in control group(P<.05). There were no significant differences of microleakage at occlusal and gingival margins among groups. There were no significant differences between microleakage of occlusal and gingival margins in each group. Fortify was not statistically different from control group at the gingival margin(P>.05). Conclusion: Application of surface sealants was an effective method of surface coating in reducing microleakage at occlusal and gingival margins of Class V composite resin restorations. However, it is certain that some microleakage still occurred despite the application of surface sealants, especially gingival margins.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.1
• /
• pp.21-28
• /
• 2009

Purpose: The purpose of this study was to compare the wear characteristics of human enamel opposing 2 heat-pressed ceramics (e.max Press and Empress Esthetic), conventional feldspathic porcelain (Ceramco 3) and type III gold alloy. Material and methods: Intact cusps of extracted premolars were used for enamel specimens. Five disk samples were made for each of two heat-pressed ceramics groups, conventional feldspathic porcelain group and type III gold alloy group. Wear tests were conducted in distilled water using a pin-on-disk tribometer. The amount of enamel wear was determined by weighing the enamel specimens before and after wear tests, and the weight was converted to volumes by average density. The wear tracks were analyzed by scanning electron microscopy and surface profilometer to elucidate the wear characteristics. Results: 1. Ceramco 3 led to the greatest amount of enamel wear followed by Empress Esthetic, e.max Press and type III gold alloy. However, there was no significant difference between Ceramco 3 and Empress Esthetic (P>.05), and there were also no significant differences among Empress Esthetic, e.max Press and type III gold alloy (P>.05). 2. The average surface roughness of e.max Press after wear test was smallest followed by Empress Esthetic and Ceramco 3, but there was no significant difference between Empress Esthetic and Ceramco 3 (P>.05). 3. There were no significant differences among the depth of wear tracks of all the groups (P>.05). The group that showed the largest width of wear track was Ceramco 3 followed by Empress Esthetic, e.max Press and type III gold alloy. However, there was no significant difference between e.max Press and Empress Esthetic (P>.05), and there was also no significant difference between Empress Esthetic and Ceramco 3 (P>.05). Conclusion: Within the limits of this study, heat-pressed ceramics were not more abrasive than conventional feldspathic porcelain.

• Restorative Dentistry and Endodontics
• /
• v.33 no.1
• /
• pp.20-27
• /
• 2008

The purpose of this study was to evaluate the consistency of two electronic apex locators in vitro model. Materials consisted of fifty two extracted premolars and two electronic apex locators; Root ZX (J. Morita, Osaka, Japan) and E-Magic Finder Deluxe (S-Denti. Cheonan, Korea). After access preparation, the teeth were embedded in a saline-mixed alginate model. Canal lengths of each tooth were measured at "0.5" and "Apex" mark of the apex locators, respectively so that each tooth had two measurements from 0.5 and Apex points. The file was fixed at final measurement using a glass ionomer cement. The apical 4 mm from the apex was exposed to measure the distance from the file tip to the major apical foramen of each tooth. Average distances and standard deviations were used to evaluate the consistency. Results showed that all measurements of both Root ZX and E-Magic Finder located the major foramen the range of ${\pm}0.5\;mm$ level. Both apex locators showed better consistency at Apex mark than at 0.5 mark. The average distance of file tip-major foramen was - 0.18 mm at 0.5 mark and - 0.07 mm at Apex mark in Root ZX, - 0.25 mm at 0.5 mark and - 0.02 mm at Apex mark in E-Magic Finder. Standard deviation was 0.21 at 0.5 mark and 0.12 at Apex mark in Root ZX, 0.12 at 0.5 mark and 0.09 at Apex mark in E-Magic Finder.

• Restorative Dentistry and Endodontics
• /
• v.14 no.2
• /
• pp.20-29
• /
• 1989

The purpose of the study is to evaluate the degree of the marginal leakage of class V cavities with 4 brands of esthetic filling materials by means of the dye penetration at the enamel & dentinal margins. 160 cavities of class V were prepared on the buccal & lingual surfaces of 80 extracted premolar teeth, which divided into 4 groups. The four groups of cavities were filled with Durafill$^{(R)}$-Durafill bond$^{(R)}$(KuIzer & Co GmbH), Bisfil M$^{(R)}$-Resin bond$^{(R)}$(BISCO Inc.), Silux$^{(R)}$-Scotchbond$^{(R)}$(3M Co.) and Fuji ionomer$^{(R)}$(type II, G-C Co.) each. All specimens were immersed in 2% methylene blue dye solution for 24 hours at $37^{\circ}C$ after a 30-second thermocycling at $4^{\circ}C$ and $60^{\circ}C$ and longitudinally sectioned with diamond disk into two parts. The results were as follows : 1. At enamel margins, the group filled with Durafill$^{(R)}$-Durafill bond$^{(R)}$, Bisfil M$^{(R)}$-Resin bond$^{(R)}$ and Silux$^{(R)}$-Scotchbond$^{(R)}$ show no significant difference each other(p>0.05), and the above groups show less marginal leakage comparing with the group filled with Fuji ionomer$^{(R)}$(p<0.01). 2. At dentinal margins, the group filled with Silux$^{(R)}$-Scotchbond$^{(R)}$ or Fuji ionomer$^{(R)}$ show less marginal leakage than that with Durafill$^{(R)}$-Durafill bond$^{(R)}$ or Bisfil M$^{(R)}$-Resin bond$^{(R)}$(p<0.01). 3. The enamel margins show less marginal leakage than dentinal margins in all the class V cavities(p<0.01).

• The korean journal of orthodontics
• /
• v.29 no.4 s.75
• /
• pp.483-490
• /
• 1999

Interdental enamel stripping is an usual method for correction of abnormal tooth shape and tooth size discrepancy which is one of the etiologic factors of malocclusion. Clinically it Is useful to correct the minor crowding in anterior teeth and posterior occlusion during finishing stage of orthodontic treatment. But this procedure has risks such as irreversible tooth reduction and remaining roughness of enamel surface can accumulate plaque which can evoke periodontal problem. Even if various methods were introduced to minimize the enamel surface roughness, their evaluation was limited in morphologic differences by scanning electronic microscope(SEM). The purpose of this study was to compare the various interdental enamel stripping method by SEM and to quantify the difference of surface roughness by use of Surfcorder SEF-30D(Kosaka Lab. Ltd.) which can measure the roughness of surface. The stripping methods were divided into mechanical and mechanical-chemical method. Air-rotor stripping and separating strip were used for mechanical stripping and $37\%$ phosphoric acid was used for chemical stripping. The enamel surface roughness after mechanical or mechanical-chemical stripping of interproximal surfaces of premolars which were extracted for orthodontic purpose were measured and compared by means of SEM and $Surfcorder^{\circledR}$, the results were as follows. 1. Enamel surface of primary treated by coarse diamond bur and separating strip groups showed highest value of roughness. 2. To compare the primary treated groups between mechanical and mechanical-chemical method, the latter group showed lower value of roughness remarkably. 3. Mechanical stripping groups which were treated both coarse and fine instrument showed lower value of roughness as much as non treated group. 4. The use of Pumice for final polishing did not show significantly smoothening the stripped enamel surface any more.