THE EFFECTS OF FLUORIDE RELEASING ORTHODONTIC SEALANT ON THE SHEAR BOND STRENGTH Of LIGHT-AND CHEMICAL-CURED ORTHODONTIC RESINS

불소가 유리되는 교정용 전색제가 광중합형 및 화학중합형 교정용 접착제의 전단결합강도에 미치는 영향

The purpose of this study was to evaluate the effects of fluoride relasing orthodontic sealant on the shear bond strength of light-and chemical-cured orthodontic rosins, to compare the shear bond strenth with light-and chemical-cured orthodontic resins, and to identify the changes of shear bond strength by rebonding in vitro. The brackets were divided into eight groups. Each group of metal brackets had different bonding mechanisms with adhesives. Group A : Transbond only Group B : Mono-Lok 2 only Group C : Light cured FluoroBond+Transbond Group D : Light cured FluoroBond+Mono-Lok 2 Group E : Transbond only(rebonded) Group F : Nomo-Lok 2 only(rebonded) Group G : Light cured FluoroBond+Transbond(rebonded) Group H : Light cured FluoroBond+Mono-Lok 2(rebonded) 65 extracted human premolars were prepared for bonding and 65 metal brackets for each group were bonded to prepared enamel surfaces of buccal surfaces as the above prescription. 24 hours bonding after, the Instron universal testing machine was used to test the shear bond strength of metal brackets to enamel. After debonding, same kind of metal brackets for each group were rebonded to prepared enamel surfaces of buccal surfaces to test the shear bond strength at the rebonding to enamel. Statistical analysis of the data was carried out Student's t-test ANOVA test, and Scheffe test using $SPSS/PC^+$ The results were as follows : 1. The order of shear bond strength was Group B(11.84MPa), Group A(10.75MPa), Group, D(9.69MPa), and Group C(9.39MPa)in lst bonded groups. 2. The order of shear bond strength was Group E(7.40MPa), Group G(6.48MPa), Group F(5.89MPa), and Group H(5.15MPa) in rebonded groups. 3. The shear bond strength of chemical cured orthodontic rosins had higher than that of light-cured orthodontic resins in all groups, but there was no statistical significance between groups(P>0.05). 4. In rebonded groups, the shear bond strength of light cured orthodontic rosins had higher than that of chemical cured orthodontic resins, but there was no statistical significance between groups(P>0.05). 5. The shear bond strength of all rebonded groups progressively decreased than that of 1st bonded groups, and there was statistical significance between groups(p<0.05, p<0.001).

본 연구는 교정치료를 위해 최근에 발거된 소구치 65개를 대상으로 발거직후 부착된 이물질을 제거하고 생리식염수에 담구어 보관한 후 법랑질을 퍼미스 및 $38\%$ 인산으로 표면 처리하고 불소가 유리되는 교정용 전색제로는 광중합형 FluoroBond, 광중합 접착제로는 Transbond, 화학중합 접착제로는 Mono-Lok 2를 선정하여 1차 부착 및 재부착시의 전단결합강도를 만능강도시험기로 측정함으로서, 치아우식 예방 및 진행 억제효과를 지닌 불소가 유리되는 교정용 전색제가 광중합형 및 화학중합형 교정용 접착제의 전단결합강도에 미치는 영향과 재부착에 의한 전단결합강도의 변화를 규명하고, 광중합형 접착제와 화학중합형 접착제 사이의 전단결합강도를 비교하여 다음의 결론을 얻었다. 1. 1차부착에 의한 전단결합강도의 크기는 Mono-Lok2군(11.84MPa), Trans bond군(10.75MPa), Light cured FluoroBond+Mono-Lok 2군(9.69MPa), Light cured FluoroBond+Transbond군(9.39MPa)순이었다. 2. 재부착에 의한 전단결합강도의 크기는 Transbond군(7.40MPa), Light cured FluoroBond+Transbond군(6.48MPa), Mono-Lok 2군(5.89MPa), Light cured FluoroBond+Mono-Lok 2군(5.15MPa)순이었다. 3. 불소가 유리되는 교정용 전색제를 적용한군과 적용하지 않은 군 모두에서 화학중합형 접착제가 광중합형 접착제보다 높은 전단결합강도를 보였으나 통계학적으로 유의한 차이는 없었다(p>0.05). 4. 불소가 유리되는 교정용 전색제를 적용한군과 적용하지 않은 군 모두에서 재부착된 광중합형 접착제가 재부착된 화학중합형 접착제보다 높은 전단결합강도를 보였으나 통계학적으로 유의한 차이는없었다(p>0.05). 5. 1차 부착된 군에 비해 재부착된 모든 군에서 전단결합강도가 현저하게 감소되었으며, 통계학적으로 유의한 차이를 보였다(p<0.05 p<0.001). 이상의 결론을 종합해볼 때 임상적으로 브라켓의 전단결합강도에 경향을 미치지 않는 불소가 유리되는 교정용 전색제를 치아 협면에 적용하여 불소의 유리에 의한 치아우식 예방 및 억제효과를 기대하는 것이 필요할 것으로 생각된다.