• Journal of the Korean Wood Science and Technology
• /
• v.17 no.1
• /
• pp.3-11
• /
• 1989

This study was carried out to investigate the physical and mechanical properties. durability of adhesive bond and paint film for the basic data which were required to determine the suitability as a raw material for furniture the laminated veneer lumber (LVL) with pitch pine (Pinus rigida Mill). The results obtained were as follows; 1) The proper pressing time for making the LVL was over 45 second per milimeter of LVL thickness. 2) The bending strength of the LVL was lower than that of the solid wood but the compressive strength of the LVL was similar to that of the solid wood. The strength increased with the decrease of veneer thickness. 3) The impact bending absorbed energy of the LVL was 0 to 0.3 kg.m/$cm^2$ in the direction of parallel to the grain. The energy of the LVL was lower than that of the solid wood (0.68 kg.m/$cm^2$). 4) In warm water soaking and cold-dry tests, delamination of adhered layers surface crack, swelling, and color change were not found when the hot pressing time was over 45 second per milimeter of LVL thickness. As a result of soak under vacuum test shrinkage in the direction of parallel to the grain was about -1.0 percent and. was about 3.0 percent in the direction of the perpendicular to the grain. 6) The film cacks on the LVL's surface after the wet and cold-dry test were not found at all. 7) In the use of the LVL for interior decoration it was considered that the surface of the LVL be overlaid crossly with fancy veneers of birch and paulownia, etc. This cross overlayirg methods have resulted in few cracks on the fancy veneer.

• Journal of Biomedical Engineering Research
• /
• v.25 no.2
• /
• pp.157-163
• /
• 2004

Nitrogen ion implantation and ion plating techniques were applied for improvement of the wear resistance of metallic implant materials. In this work, the wear dissolution behaviour of a nitrogen ion implanted super stainless steel (S.S.S, 22Cr-20Ni-6Mo-0.25N) was compared with those of S.S.S, 316L SS and TiN coated 316L SS. The amounts of Cr and Ni ions worn-out from the specimens were Investigated using an electrothermal atomic absorption spectrometry. Furthermore, the Ti(Grade 2) disks were coated with TiN, ZrN and TiCN by use of low temperature arc vapor deposition and the wear resistance of the coating layers was compared with that of titanium. The chemical compositions of the nitrogen ion implanted and nitride coated layers were examined with a scanting auger electron spectroscopy. It wat observed that the metal ions released from the nitrogen ion implanted S.S.S surface were significantly reduced. From the results obtained, it was shown that the nitrogen ion implanted zone obtained with 100 KeV ion energy was easily removed within 200,000 revolutions from a wear dissolution testing under a similar load condition when applied to artificial hip joint. The remarkable improvement in wear resistance weir confirmed by the nitrides coated Ti materials and the wear properties differ greatly according to the chemical composition of the coating layers. for specimens with the same coating thickness of about 3$\mu\textrm{m}$, TiCN coated Ti showed the highest wear resistance. However, after removing the coating layers, the wear rates of all nitrides coated Ti reverted to their normal rates of below 10,000 revolutions from Ti-disk-on-disk wear testing under the same load condition. From the results obtained, it is suggested that the insufficient depth of the 100 Kel N$\^$＋/ ion implanted zone and of the nitrides coated layers of 3$\mu\textrm{m}$ are subject to restriction when used as frictional parts of load bearing implants.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.6
• /
• pp.37-43
• /
• 2017

This review investigates the basic principle of physical interactions and failure mechanisms introduced in the materials and inner parts of semiconducting components under electromagnetic pulses (EMPs). The transfer process of EMPs at the semiconducting component level can be explained based on three layer structures (air, dielectric, and conductor layers). The theoretically absorbed energy can be predicted by the complex reflection coefficient. The main failure mechanisms of semiconductor components are also described based on the Joule heating energy generated by the coupling between materials and the applied EMPs. Breakdown of the P-N junction, burnout of the circuit pattern in the semiconductor chip, and damage to connecting wires between the lead frame and semiconducting chips can result from dielectric heating and eddy current loss due to electric and magnetic fields. To summarize, the EMPs transferred to the semiconductor components interact with the chip material in a semiconductor, and dipolar polarization and ionic conduction happen at the same time. Destruction of the P-N junction can result from excessive reverse voltage. Further EMP research at the semiconducting component level is needed to improve the reliability and susceptibility of electric and electronic systems.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.1
• /
• pp.23-34
• /
• 2015

Recently a new damper system with Kogome truss structure was developed and its mechanical properties were verified based on the laboratory test. This paper presents a Kagome truss damper external connection method for seismic strengthening of RC frame structural system. The Kagome external connection method, proposed in this study, consisted of building structure, Kagome damper and support system. The method is capable of reducing earthquake energy on the basis of the dynamic interaction between external support and building structures using Kagome damper. The pseudo-dynamic test, designed using a existing RC frame apartment for pilot application of LH corporation, was carried out in order to verify the seismic strengthening effects of the proposed method in terms of the maximum load carrying capacity and response ductility. Test results revealed that the proposed Kagome damper method installed in RC frame enhanced conspicuously the strength and displacement capacities, and the method can resist markedly under the large scaled earthquake intensity level.

• International Journal of Highway Engineering
• /
• v.20 no.1
• /
• pp.87-95
• /
• 2018

PURPOSES : A geo-grid pavement, e.g., a stress-absorbing membrane interlayer (SAMI), can be applied to an asphalt-overlay method on the existing surface-pavement layer for pavement maintenance related to reflection cracking. Reflection cracking can occur when a crack in the existing surface layer influences the overlay pavement. It can reduce the pavement life cycle and adversely affect traffic safety. Moreover, a failed overlay can reduce the economic value. In this regard, the objective of this study is to evaluate the bonding properties between the rigid pavement and a SAMI by using the direct shear test and the pull-off test. The predicted fractural energy functions with the shear stress were determined from a numerical analysis of the moving average method and the polynomial regression method. METHODS : In this research, the shear and pull-off tests were performed to evaluate the properties of mixtures constructed using no interlayer, a tack-coat, and SAMI with fabric and without fabric. The lower mixture parts (describing the existing pavement) were mixed using the 25-40-8 joint cement-concrete standard. The overlay layer was constructed especially using polymer-modified stone mastic asphalt (SMA) pavement. It was composed of an SMA aggregate gradation and applied as the modified agent. The sixth polynomial regression equation and the general moving average method were utilized to estimate the interlayer shear strength. These numerical analysis methods were also used to determine the predictive models for estimating the fracture energy. RESULTS : From the direct shear test and the pull-off test results, the mixture bonded using the tack-coat (applied as the interlayer between the overlay layer and the jointed cement concrete) had the strongest shear resistance and bonding strength. In contrast, the SAMI pavement without fiber has a strong need for fractural energy at failure. CONCLUSIONS : The effects of site-reflection cracking can be determined using the same tests on cored specimens. Further, an empirical-mechanical finite-element method (FEM) must be done to understand the appropriate SAMI application. In this regard, the FEM application analy pavement-design analysis using thesis and bonding property tests using cored specimens from public roads will be conducted in further research.

• The Korean Journal of Food And Nutrition
• /
• v.11 no.3
• /
• pp.323-328
• /
• 1998

This study was to investigate regularity of breakfast and food habits of commuting local college students. The regularly breakfast eating rate was found to be 32.9% in man and 26.5% in woman. The mean score of food habits was pretty low, 36.7 out of minimum possible score 12 and maximum 60. The mean score of nutrition attitude was 58.1 out of minimum possible score 18 and maximum 90. This survey showed that skipping breakfast or irregularity of breakfast led to overeating, high fat diet, lot of alcohol and imbalanced diet. It was known that breakfast was the most important among three meals. But having balanced breakfast daily was very difficult according to loss of appetite and busy schedule early in the morning. I suggested carbohydrate food, protein food, and vitamin & mineral food items desirable for nutritionally balanced, easily digestible, tasteful, quick and easily cooking breakfast menu. It was recommended to choose on item out of each of three food categories considering calory(1/3 of daily recommended calory intake for breakfast).

• Journal of radiological science and technology
• /
• v.36 no.4
• /
• pp.263-271
• /
• 2013

The decrease of bone mineral density gives rise to the outbreak of osteopenia and makes the possibility of a bone fracture. It makes health problems in society. It's very important to prevent osteopenia in advance. Also it's critical to prevent and take care of it in adolescent because it's the most developing period comparing to middle ages because that bone mineral density decreases. There are genetic, physical and enviromental factors that affect bone mineral density. Recently, a lifestyle and eating habits are also changing as the society atmosphere is gradually doing. This study have shown that 134 women and 75 men was chosen and responded to the survey of measuring bone mineral density and investigating a lifestyle. The measure of bone mineral density is to use Dual energy X-ray absorptiometry(DEXA) and check femoral neck and lumbar spine. Also questionaries was required to pre-made survey about their lifestyles. Analysis of data was done with SPSS program. Multiple regression analysis was used for the relation of bone mineral density, the heigths and BMI. The sample of Groups are checked for drinking, smoking or excercising about differences by t-test. The results of the experiments were; first, there is statistically significant differences in the comparisons between BMD and BMD. But there isn't any special correlation between drinking, smoking and BMD. Secondly, bone mineral density becomes low related to an intake of caffeine. Particularly, this is statically significant on women. Also there is statically significant correlation between femoral neck and quantity of motion for both men and women. Third, there is significant relation between eating habits and bone mineral density on women's lumbar spine. However, there is no significant relation between men's lumbar spine and women's one. Therefore, to prevent osteopenia, it's good to abstain from intaking caffeine within an hour after a meal. In addition, it's helpful to walk or run regularly and have a balanced meal.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.29 no.5A
• /
• pp.565-575
• /
• 2009

In recent years, there have been numerous explosion-related accidents due to military and terrorist activities. Such incidents caused not only damages to structures but also human casualties, especially in urban areas. To protect structures and save human lives against explosion accidents, better understanding of the explosion effect on structures is needed. In an explosion, the blast load is applied to concrete structures as an impulsive load of extremely short duration with very high pressure and heat. Generally, concrete is known to have a relatively high blast resistance compared to other construction materials. However, normal strength concrete structures require higher strength to improve their resistance against impact and blast loads. Therefore, a new material with high-energy absorption capacity and high resistance to damage is needed for blast resistance design. Recently, Ultra High Strength Concrete(UHSC) and Reactive Powder Concrete(RPC) have been actively developed to significantly improve concrete strength. UHSC and RPC, can improve concrete strength, reduce member size and weight, and improve workability. High strength concrete are used to improve earthquake resistance and increase height and bridge span. Also, UHSC and RPC, can be implemented for blast resistance design of infrastructure susceptible to terror or impact such as 9.11 terror attack. Therefore, in this study, the blast tests are performed to investigate the behavior of UHSC and RPC slabs under blast loading. Blast wave characteristics including incident and reflected pressures as well as maximum and residual displacements and strains in steel and concrete surface are measured. Also, blast damages and failure modes were recorded for each specimen. From these tests, UHSC and RPC have shown to better blast explosions resistance compare to normal strength concrete.

• Journal of Nutrition and Health
• /
• v.49 no.5
• /
• pp.347-357
• /
• 2016

Purpose: This study investigated bone mineral density and nutritional state according to consumption of milk in Korean postmenopausal women who drink coffee. Methods: Using the 2008~2009 Korean National Health & Nutrition Examination Survey data, a total of 1,373 postmenopausal females aged 50 yrs and over were analyzed after excluding those with diseases related to bone health. According to coffee and/or milk consumption, subjects were divided into four groups: coffee only, both coffee & milk, milk only, and none of the above. All data were processed after application of weighted values and adjustment of age, body mass index, physical activity, drinking, and smoking using a general linear model. For analysis of nutrient intake and bone density, data were additionally adjusted by total energy and calcium intake. Results: The coffee & milk group had more subjects younger than 65 yrs and higher education, urban residents, and higher income than any other group. The coffee only group showed somewhat similar characteristics as the none of the above group, which showed the highest percentage of subjects older than 65 and in a lower education and socio-economic state. Body weight, height, body mass index, and lean mass were the highest in coffee & milk group and lowest in the none of the above group. On the other hand, the milk only group showed the lowest values for body mass index and waist circumference, whereas percent body fat did not show any difference among the groups. The coffee and milk group showed the highest bone mineral density in the total femur and lumbar spine as well as the highest nutritional state and most food group intakes, followed by the milk only group, coffee only group, and none of the above group. In the assessment of osteoporosis based on T-score of bone mineral density, although not significant, the coffee and milk group and milk only group, which showed a better nutritional state, included more subjects with a normal bone density, whereas the none of the above group included more subjects with osteoporosis than any other group. Conclusion: Bone mineral density in postmenopausal women might not be affected by coffee drinking if their diets are accompanied by balanced food and nutrient intake including milk.