• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.2
• /
• pp.26-33
• /
• 2016

The alkali-slag-red mud(ASRC) cement belongs to clinker free cementitious material, which is made from alkali activator, blast-furnace slag(BFS) and red mud in designed proportion. This study is to investigate strength and pore characteristics of alkali-activated slag cement(NC), clinker free cementitious material, and ordinary portland cement(C) mortars using polymer according to red mud content. The results showed that the hardened alkali-activated slag-red mud cement paste was mostly consisted of C-S-H gel, being very fine in size and extremely irregular in its shape. So the hardened ASRC cement paste has lower total porosity, less portion of larger pore and more portion of smaller pore, as compared with those of hardened portland cement paste, and has higher strength within containing 10 wt.(%) of alkali-activated slag cement(NC) substituted by red mud.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.3
• /
• pp.267-275
• /
• 2018

This study is to investigate the effect of various temperature and humidity conditions on the strength and efflorescence of alkali activated slag cement(AAS) using the red mud. As a result of examining the strength and efflorescence characteristics of AAS mixed with red mud according to the curing conditions, The compressive strength and flexural strength were the highest at 28 days, but the absorption rate, efflorescence area and soluble $Na^+$ elution were lowest in standard wet curing compared to the air curing, high temperature curing and low temperature curing.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.2
• /
• pp.130-137
• /
• 2018

In the construction industry, research on alkali activated cement using fly ash or blast furnace slag fine powder has been published in Korea and abroad as a way to reuse industrial byproducts without using cement at all and to obtain economical effects at the same time. the purpose of this paper is to evaluate the effect of the ratio and coefficient of hydration ratio and lime saturation degree on the strength of alkali activated slag cement by chemical quantitative analysis of alkali activated slag cement used in the management of existing portland cement. as a result, it was confirmed that the ratio and coefficient of hydration ratio and lime saturation are all within a certain range.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.3
• /
• pp.261-268
• /
• 2017

Red mud is an inorganic by-product obtained from the mineral processing of alumina from Bauxite ores. A highly alkali inorganic waste product with a pH level over 11, red mud in its original state negatively impacts the ecosystem, so appropriate treatment is necessary. The development of alkali activated slag-red mud cement can be a representative study aimed at recycling the strong alkali of the red mud as a construction material. However, Alkali-activated binders that use sodium activators have been reported to be more vulnerable to efflorescence. Therefore, in this study, the compressive strength, pore characteristics, water absorption, elution characteristics, and efflorescence properties of alkali-activated slag cement mortar were assessed according to their red mud substitution ratio.

• Journal of Korean Society of Environmental Engineers
• /
• v.29 no.7
• /
• pp.801-809
• /
• 2007

Fly ash and blast furnace slag are an industrial by-product that can be alkali-activated to yield adhesive and cementitious materials, whose production is less energy-intensive and emits less $CO_2$ than ordinary Portland cement manufacture. A laboratory investigation was carried out to evaluate the effect of alkali-activating conditions on compressive strength of fly ash/slag cement and the acid corrosion resistance of this cement. Two alkali activator solution, NaOH and waterglass + NaOH solutions, were used. Waterglass concentration was the factor that gave the highest compressive strength in all tests. The next significant factor was the NaOH concentration, followed by curing temperature. Acid corrosion resistance of FC(fly ash cement) and FSC(fly ash/slag cement), such as sulfuric$(H_2SO_4)$ and hydrochloric acid(HCl), was for better than Portland cement(PC).

• Cement Symposium
• /
• no.29
• /
• pp.82-87
• /
• 2002

• Cement Symposium
• /
• no.32
• /
• pp.202-207
• /
• 2005

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.3
• /
• pp.276-283
• /
• 2016

Red mud is an inorganic by-product produced from the mineral processing of alumina from Bauxite ores. the development of alkali-activated slag-red mud cement can be a representative study aimed at recycling the strong alkali of the red mud as a construction material. This study is to investigate the optimum water content, compressive strength, moisture absorption coefficient and efflorescence of alkali-activated slag-red mud soil pavement according to the recycling fine aggregate content. The results showed that the optimum water content, moisture absorption coefficient and efflorescence area of alkali-activated slag-red mud soil pavement increased but the compressive strength of that decreased as the recycled fine aggregate content increased.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.4
• /
• pp.321-329
• /
• 2016

The use of ternary blended cement consisting of Portland cement, granulated blast-furnace slag (GGBFS) and fly ash has been on the rise to improve marine concrete structure's resistance to chloride attack. Therefore, this study attempted to investigate changes in chloride attack resistibility of concrete through NT Build 492-based chloride migration experiments and test of concrete's ability to resist chloride ion penetration under ASTM C 1202(KS F 2271) when 1.5-2.0% of alkali-sulfate activator (modified alkali sulfate type) was added to the ternary blended cement mixtures (40% ordinary Portland cement + 40% GGBFS + 20% fly ash). Then, the results found the followings: Even though the slump for the plain concrete slightly declined depending on the use of the alkali-sulfate activator, compressive strength from day 2 to day 7 improved by 17-42%. In addition, the coefficient from non-steady-state migration experiments for the plain concrete measured at day 28 decreased by 36-56% depending on the use of alkali-sulfate. Furthermore, total charge passed according to the test for electrical indication of concrete's ability to resist chloride ion penetration decreased by 33-62% at day 7 and by 31-48% at day 28. As confirmed in previous studies, reactivity in the GGBFS and fly ash improved because of alkali activation. As a result, concrete strength increased due to reduced total porosity.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.1
• /
• pp.47-54
• /
• 2017

Cement industry is typical carbon-emission industry. If the industrial by-products(granulated blast-furnace slag (GGBFS), fly ash, etc.) are used a large amount, it might be able to reduce cement consumption and mitigate carbon emissions. In this case, however, decrease of early strength is relatively large. Therefore, there is a limitation in increase of the amount of substitute. Considering these circumstances, it would be a good solution to reduce carbon emissions in cement industry to improve the performances of mixed cement through proper alkali-activation in Portland blended cement using GGBFS or fly ash. Therefore, this study prepared concrete in ready-mixed concrete manufacturing facilities with an addition of a binder which used 2.0% modified alkali sulfate activator after mixing Portland cement, GGBFS and fly ash in the ratio of 4:4:2 and assessed its basic properties. The results found the followings: The use of modified alkali-sulfate activator slightly reduced slump and shortened setting time. As a result, bleeding capacity decreased while early strength improved. In addition, there is no big difference in carbonation resistance. It appears that there should be continued experiments and analyses on the related long-term aged specimens.