• Restorative Dentistry and Endodontics
• /
• v.24 no.4
• /
• pp.570-577
• /
• 1999

Intuitively, higher bond strengths should result in less leakage. However, the relationship between bond strengths and microleakage value is complex and not clearly understood. The purpose of this study was to evaluate the relationship between tensile bond strengths and microleakage values in the same restorations to understand the behavior of resin bonding to tooth structure. One-hundred and twenty enamel or dentin specimens from freshly extracted bovine mandibular incisors were used. The specimen was treated with 32% phosphoric acid for 15 seconds and rinsed for 20 seconds. the teeth were divided into four groups by means of wet bonding technique or dry bonding. One-Step$^{TM}$ adhesive were applied to the specimen. The specimens were immersed in 2% methylene blue solution for 7 days, and tensile bond strength and microleakage were measured. The results were as follows: 1. Significant negative correlation was found between bond strengths and micro leakage values. Hence, higher bond strengths seem to be associated with lower microleakage, and vice versa (r=-0 50, p<0.05). 2. The Enamel/Wet group showed significantly higher bond strength than Enamel/Dry one, and Dentin/Wet group showed higher strength than Dentin/Dry one (p<0.05). 3. Microleakage was significantly less ill wet bonding than in dry one at dentin (p<0.05), however, there was no significant difference between wet and dry bonding at enamel (p>0.05).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.1
• /
• pp.57-68
• /
• 2002

The purpose of this study was to evaluate microleakage of etched and non-etched amalgam restorations lined with dentin bonding system primer and adhesives. Class V amalgam preparations were made in 100 extracted human premolars divided into 10 groups with 10 teeth each. SEM was taken to assess the dentin/amalgam interface. The results were as follows; 1. At the occlusal and gingival margins, all experimental groups showed lower leakage value than unlined group(p<0.05) The $Copalite^{(R)}-lined$ group showed higher leakage value than other experimental groups(p<0.05). 2. In all experimental groups, the gingival margin showed higher leakage value than the occlusal margin. 3. There were no significant difference between non-etching and etching groups, primer only and primer & adhesive groups, primer & adhesive and self-priming adhesive groups(p>0.05). 4. On the SEM observation, continuous gaps were observed in the unlined and $Copalite^{(R)}-lined$ groups, but the gaps were filled with primer or adhesive layer in other experimental groups.

• Restorative Dentistry and Endodontics
• /
• v.32 no.5
• /
• pp.437-444
• /
• 2007

The purpose of this study was to compare the marginal microleakage of different 2-step adhesive systems in Class V cavities prepared with different diamond points. Forty Class V cavities were prepared with two different (coarse or fine) diamond points on cervical third of extracted molars. The occlusal and gingival margin of cavities was located in enamel and dentin, respectively. They were divided into one of four equal groups (n = 10) and ; Group 1-prepared with coarse diamond point (EX-41), restored with Single Bond and Z 250, Group 2-prepared with fine diamond piont (TF-21F), restored with Sing)e Bond and Z 250, Group 3-prepared with coarse diamond point (EX-41), restored with Clearfil SE Bond and Clearfil AP-X, Group 4-prepared with fine diamond point (TF-21F), restored with Clearfil SE Bond and Clearfil AP-X. Specimens were thermocycled, immersed in a 2% methylene blue solution for 24 hours, and bisected longitudinally. They were observed leakages at enamel and dentinal margins. Data were analyzed using Mann-Whitney and Wilcoxon signed ranked test. In this study, marginal microleakage or Single Bond was not affected by type of diamond points. But Clearfil SE Bond showed higher marginal microleakage at both enamel and dentinal margin when Class V cavity was prepared with coarse diamond point.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.4
• /
• pp.619-627
• /
• 2008

The objective of this study was to compare the microleakage of five adhesive systems in the enamel and dentin of permanent teeth. Class V cavity preparations with occlusal margins in enamel and gingival margins in dentin were prepared on both buccal and lingual surfaces of 25 extracted human molar teeth. The tested adhesives were: Adper Scotchbond Multi-purpose Plus Adhesive (SM), Adper Single bond 2 (SB), Clearfil SE Bond (SE), Adper Prompt L-Pop (PL) and G-Bond (GB). The results were as follows: 1. At the enamel margins, PL showed the highest leakage value(0.85), and others showed values of SB(0.55), GB(0.50), SM(0.35) and SE(0.25) in decreasing order. There were statistically significant differences in PL vs. SM and PL vs. SE(p<0.05). 2. At the dentin margins, GB showed the highest leakage value(2.10), and others showed values of SE(1.45), PL(1.40), SB(1.05), SM(0.70) in decreasing order. There were statistically significant differences in GB vs. SB and GB vs. SM(p<0.05). 3. Dentin margins showed high dye penetration rate than enamel margins in all material tested groups and there were statistically significant differences for SE, PL and GB.

• Restorative Dentistry and Endodontics
• /
• v.34 no.6
• /
• pp.477-483
• /
• 2009

The purpose of this study was to compare the microleakage of low and high viscosity flowable resins in class V cavities applied with 1-step adhesives. Forty Class V cavities were prepared on the cervices of buccal and lingual surfaces of extracted molar teeth and divided into four groups (n=8). Cavities were restored with AQ Bond Plus /Metafil Flo $\alpha$, G-Bond/ UniFil LoFlo Plus (Low flow groups), AQ Bond Plus/Metafil Flo and G-Bond/UniFil Flow (High flow group), respectively. Specimens were immersed in a 2% methylene blue solution for 24 hours, and bisected longitudinally. They were observed microleakages at the enamel and dentinal margins. In conclusion, the low viscosity flowable resins showed lower marginal microleakage than do the high vis cosity flowable resins in class V cavities.

• Restorative Dentistry and Endodontics
• /
• v.27 no.4
• /
• pp.394-402
• /
• 2002

2급 복합레진 수복 와동의 치은 변연이 상아질 상에 있을 때 유동성 레진 이장의 유무와 두께가 미세누출에 미치는 영향을 알아보기 위해 본 실험을 시행하였다. 60개의 발거된 대구치의 근, 원심면에 각각 협설측 3mm, 치은벽 깊이 1mm의 2급 와동을 형성하고 치은 변연은 법랑-백아 경계에서 약 1mm 하방에 위치 시켰다. 모든 와동을 32% 인산으로 15초 처리 및 30초 수세 후 Prime & Bond$^{\circledR}$ NT 상아질 접착제를 적용하였고, Tetric Ceram(TC), Tetric Flow(TF)를 이용하여 다음의 6가지 군으로 나누어 수복하였다. (1) TC로 수평 적층 충전, (2) TC로 수직 적층 충전, (3) 0.5-1mm두께로 TF 이장 후 TC로 수평적층 충전, (4) 0.5-1mm 두께로 TF 이장 후 TC로 수직 적층 충전, (5) 2-3mm 두께로 TF 이장 후 TC로 수평적층 충전, (6) 2-3mm두께로 TF이장 후 TC로 수직 적층 충전. 충전된 시편을 37$^{\circ}C$ 100% humidity에서 24시간 보관하고 5$^{\circ}C$와 55$^{\circ}C$에서 500회의 열순환을 실시하여 치은 변연의 0.5mm 외부에 nail varnish를 도포 하여 2% methylene blue 용액에 12시간 침잠시켰다. 시편을 아크릴릭 레진에 매몰하여 수복물의 중앙에서 종절단 한 후 입체현미경하에서 색소의 침투도를 관찰하여 다음과 같은 결과를 얻었다. 유동성 레진의 이장을 시행한 군과 하지 않은 군간에 미세누출은 유의차를 보이지 않았다(p>0.05) 유동성 레진의 두께에 따른 미세누출의 차이는 나타나지 않았다(p>0.05) 경사면 충전법을 시행한 군에서는 유동성 레진을 이장한 군들이 이장하지 않은 군보다 유의하게 많은 누출을 보였다(p<0.05). 수평적층 충전법을 시행한 군에서는 유동성 레진 이장이 미세누출에 유의한 차이를 보이지 않았다(p>0.05).

• Restorative Dentistry and Endodontics
• /
• v.30 no.5
• /
• pp.363-371
• /
• 2005

This study investigated the effect of thickness of flowable resin lining on marginal leakage in class II composite restorations. 80 experimental teeth were prepared with class II preparations with enamel margin or dentin margin. Each group was devided into four groups according to flowable resin lining thickness ; Control group - no flowable resin lining, Group 1 - 0.5 mm flowable resin lining, Group 2 - 1 mm flowable resin lining, Group 3 - 2 mm flowable resin lining. The cavities were restored using Scotchbond Multi-Purpose adhesive system, Filtek Flow and Filtek Z 250 composite resin. Following one day storage in distilled water, the restored teeth were thermocycled for 500 cycles and immersed in $2\%$ methylene blue for 24 hours. The results of this study were as follows : 1. Ranking of mean microleakage scores at the enamel margins was Group 1 < Control = Group 2 < Group 3. The microleakage of Group 3 was significantly higher than that of Control, Group 1 and Group 2 (p < 0.05). 2. Ranking of mean microleakage scores at the dentin margins was Group 1 < Group 2 < Control < Group 3. The microleakage of Group 3 was significantly higher than that of Control, Group 1 (p < 0.05) 3. Compared with microleakage between the enamel and dentin margins, enamel margin group were significantly lower than dentin margin group.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.30 no.2
• /
• pp.272-285
• /
• 2003

This study was conducted to observe the microscopic structures of cavities formed after ablation of primary teeth, permanent teeth, enamel and dentin in using a bur and cavities formed after ablation using laser and the following results were obtained after comparing the effects of ablation. Using a #330 bur and Er:YAG laser irradiated at 150 mJ, 200 mJ, 250 mJ and 300 mJ all at the frequency of 5 Hz, 1 mm enamel and dentin samples were ablated and the ablation time was measured. In order to measure the surfaces ablated, 5 each of primary teeth and permanent teeth were ablated using a #330 bur and Er:YAG laser at 150 mJ, 200 mJ, 250 mJ and 300 mJ for 1 sec and the cross section and vertical section were observed. The following results were obtained : 1. Cutting time of Er:YAG laser was longer than that of conventinal high-speed bur regardless of teeth type. 2. Cutting on enamel, Cutting time of conventional high-speed bur in deciduous teeth was longer than in permanent teeth(P<0.05). But Er:YAG laser was not showed any difference between the deciduous and permanent teeth(P>0.05). 3. Cutting on dentin, Cutting time of conventional high-speed bur in permanent teeth was longer than deciduous teeth. Er:YAG laser of 150 mJ, 5 Hz in permanent teeth was longer than in deciduous teeth(p<0.05). But laser of other power did not showed mean difference. 4. The cavity surface treated with the convetional high-speed bur revealed a relatively flat appearance, almost covered with a debris-like smear layer. Cavity wall showed striped appearance because of blade of bur. 5. The cavity surface treated by the Er:YAG laser system was irregular or rough surface with the absence charring, carbonization, or cracking of the dentin. In addition, there was an absence of a smear layer. Cavity floor was round and relatively smooth. According to these results, cutting time of Er:YAG laser was almostly same in permanent and deciduous teeth, but more effective in dentin than enamel. Cutting the sample, Er:YAG laser was needed more time than conventional bur. But SEM findings suggested that laser device produced favorable surface characteristic(i.e, no smear layer, irregular surface, cracking).

• Restorative Dentistry and Endodontics
• /
• v.26 no.4
• /
• pp.263-272
• /
• 2001

The aim of this study was to investigate the influence of four different light curing modes on the marginal leakage of Class V composite resin restoration. Eighty extracted human premolars were used. Wedge-shaped class Y cavities were prepared on the buccal surface of the tooth with high-speed diamond bur without bevel. The cavities were positioned half of the cavity above and half beyond the cemento-enamel junction. The depth, height, and width of the cavity were 2 mm, 3 mm and 2 mm respectively. The specimens were divided into 4 groups of 20 teeth each. All the specimen cavities were treated with Prime & Bond$^{R}$ NT dental adhesive system (Dentsply DeTrey GmbH, Germany) according to the manufacturer's instructions and cured for 10 seconds except group VI which were cured for 3 seconds. All the cavities were restored with resin composite Spectrum$^{TM}$ TPH A2 (Dentsply DeTrey GmbH, Germany) in a bulk. Resin composites were light-cured under 4 different modes. A regular intensity group (600 mW/${cm}^2$, group I) was irradiated for 30 s, a low intensity group (300 mW/${cm}^2$, group II) for 60 s and a ultra-high intensity group (1930 mW/${cm}^2$, group IV) for 3 s. A pulse-delay group (group III) was irradiated with 400 mW/${cm}^2$ for 2 s followed by 800 mW/${cm}^2$ for 10 s after 5 minutes delay. The Spectrum$^{TM}$ 800 (Dentsply DeTrey GmbH, Germany) light-curing units were used for groups I, II and III and Apollo 95E (DMD, U.S.A.) was used for group IV. The composite resin specimens were finished and polished immediately after light curing except group III which were finished and polished during delaying time. Specimens were stored in a physiologic saline solution at 37$^{\circ}C$ for 24 hours. After thermocycling (500$\times$, 5-55$^{\circ}C$), all teeth were covered with nail varnish up to 0.5 mm from the margins of the restorations, immersed in 37$^{\circ}C$, 2% methylene blue solution for 24 hours, and rinsed with tap water for 24 hours. After embedding in clear resin, the specimens were sectioned with a water-cooled diamond saw (Isomet$^{TM}$, Buehler Co., Lake Bluff, IL, U.S.A.) along the longitudinal axis of the tooth so as to pass the center of the restorations. The cut surfaces were examined under a stereomicroscope (SZ-PT Olympus, Japan) at ${\times}$25 magnification, and the images were captured with a CCD camera (GP-KR222, Panasonic, Japan) and stored in a computer with Studio Grabber program. Dye penetration depth at the restoration/dentin and the restoration/enamel interfaces was measured as a rate of the entire depth of the restoration using a software (Scion image, Scion Corp., U.S.A.) The data were analysed statistically using One-way ANOVA and Tukey's method. The results were as follows : 1. Pulse-Delay group did not show any significant difference in dye penetration rate from other groups at enamel and dentin margins (p>0.05) 2. At dentin margin, ultra-high intensity group showed significantly higher dye penetration rate than both regular intensity group and low intensity group (p<0.05). 3. At enamel margin, there were no statistically significant difference among four groups (p>0.05). 4. Dentin margin showed significantly higher dye penetration rate than enamel margin in all groups (p<0.05).

• Restorative Dentistry and Endodontics
• /
• v.32 no.4
• /
• pp.327-334
• /
• 2007

The purpose of this study was to evaluate the effect of burs on microleakage of Class V resin restorations when a self-etching primer adhesive was used. Forty Class V cavities were prepared with four different cutting burs on extracted third molars, and divided into one of four equal groups (n = 10); Group 1-plain cut carbide bur (no. 245), Group 2-cross cut carbide bur (no. 557), Group 3-fine diamond bur (TF-21F), Group 4-standard diamond bur (EX-41). The occlusal and gingival margin of cavities was located in enamel and dentin, respectively. Cavities were treated with Clearfil SE Bond and restored with Clearfil AP-X. Specimens were thermocycled, immersed in a 2% methylene blue solution for 24 hours, and bisected longitudinally. They were observed leakages at enamel and dentinal margins. Data were analyzed using Mann-Whitney and Wilcoxon signed ranked test. The results of this study were as follows; 1. At enamel margin, microleakage of group 4 was statistically higher than those of group 1, 2 and 3 (p < 0.01). 2. At dentinal margin, microleakage of group 4 was statistically higher than group 3 (p < 0.01), but group 1 and 2 were not statistically different with group 3 and 4. 3. Enamel microleakage was statistically higher than dentinal microleakage in group 1, 2 and 3 (p < 0.05), but statistical difference between the microleakage of enamel and dentinal margin was not in Group 4. In conclusion, the use of coarse diamond bur showed high microleakage at both enamel and dentinal margin when Clearfil SE Bond was used in class V cavity.