MARGINAL SEALING OF AMALGAM RESTORATIONS USING DENTIN BONDING ADHESIVES

아말감수복시 상아질접착제가 변연봉쇄에 미치는 영향

The purpose of this study was to evaluate microleakage of etched and non-etched amalgam restorations lined with dentin bonding system primer and adhesives. Class V amalgam preparations were made in 100 extracted human premolars divided into 10 groups with 10 teeth each. SEM was taken to assess the dentin/amalgam interface. The results were as follows; 1. At the occlusal and gingival margins, all experimental groups showed lower leakage value than unlined group(p<0.05) The $Copalite^{(R)}-lined$ group showed higher leakage value than other experimental groups(p<0.05). 2. In all experimental groups, the gingival margin showed higher leakage value than the occlusal margin. 3. There were no significant difference between non-etching and etching groups, primer only and primer & adhesive groups, primer & adhesive and self-priming adhesive groups(p>0.05). 4. On the SEM observation, continuous gaps were observed in the unlined and $Copalite^{(R)}-lined$ groups, but the gaps were filled with primer or adhesive layer in other experimental groups.

고동아말감수복시 프라이머 및 상아질접착제의 변연봉쇄효과를 비교검토하기 위하여 발거된 소구치 100개의 치아 협면에 5급 와동을 형성하고 대조군과 실험군으로 나누어 $Copalite^{(R)}$와 프라이머 및 상아질접착제를 적용하였다. 고동아말감합금인 $Luxalloy^{(R)}$로 충전한후 변연누출의 정도를 측정하고 주사전자현미경을 이용해 치질과 아말감과의 경계면을 관찰하여 다음과 같은 결론을 얻었다. 1. 교합측과 치은측에서 실험군은 모두 대조군보다 유의하게 적은 변연누출을 보였다(p<0.05). $Copalite^{(R)}$를 적용한 군은 나머지 실험군에 비해 많은 변연누출을 보였다(p<0.05). 2. 모든 실험군의 변연누출은 치은측이 교합측보다 많았다. 3. 산부식 처리, 프라이머 적용후 접착제사용 및 프라이머와 접착제의 혼합사용이 변연누출에 영향을 미치지 못하였다(p>0.05). 4. 주사전자현미경 소견에서는 대조군과 $Copalite^{(R)}$를 적용한 군에서 아말감과 와동벽사이에 연속적인 틈이 관찰되었으나, 나머지 실험군에서는 틈이 프라이머나 접착제층으로 채워져 있었다. 이상의 결과로 보아 고동 아말감합금의 사용시에 프라이머나 상아질접착제가 변연누출방지에 효과적이며, $Copalite^{(R)}$는 변연누출방지에 비효율적이다.