• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.4
• /
• pp.143-148
• /
• 2019

We have successfully fabricated high aspect-ratio GaN-based nanowires on Si substrates using molecular beam epitaxy (MBE) system for high-efficiency hydrogen generation of photoelectrochemical water splitting. Scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX) demonstrated that p-GaN:Mg and p-InGaN nanowires were grown vertically on the substrate with high density. Furthermore, it was also confirmed that the emission wavelength of p-InGaN nanowire can be adjusted from 552 nm to 590 nm. Such high-aspect ratio p-InGaN nanowire structure will be a solid foundation for the realization of ultrahigh-efficiency photoelectrochemical water splitting through sunlight.

• Journal of the Korean Vacuum Society
• /
• v.18 no.2
• /
• pp.102-107
• /
• 2009

We investigated optical emission of oxygen plasma discharged by 13.56 MHz radio frequency (rf) by using optical emission spectroscopy (OES). Experimental measurement is done at a range of oxygen flow rate of 1$\sim$20 seem, rf power of 25$\sim$250 W, and orifice 3 and 5 mm in diameter. When oxygen plasma was generated, typical emission spectra for oxygen plasma were observed regardless of diameter of orifice. Strong atomic emission lines are observe at 776.8 an 843.9 nm, corresponding to the $3p^{5}P-3s^{5}S^{0}$ and $3p^{3}P-3s^{3}S^{0}$ transitions, respectively. The emission intensity of line at 776.8 and 843.9 nm increased with increasing the oxygen flow rate and rf power. The increasing rate of emission intensity of 776.8 nm line was larger than that of 843.9 nm line. When the diameter of orifice was 3 mm, the oxygen plasma was more stably generated than orifice 5 mm in diameter.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.170.1-170.1
• /
• 2015

안티모니 (Sb)를 기반으로 한 제2형 초격자 (Type II superlattice, T2SL)구조 적외선 검출기 연구는 2000년대 들어 Sb 계열의 화합물 반도체 성장 기술이 발전함에 따라 HgCdTe (MCT), InSb, 양자우물 적외선 검출기 (QWIP)를 대체할 수 있는 고성능의 양자형 적외선 검출 소재로 부상하였으며, 현재 전 세계적으로 활발한 연구가 진행되고 있다. 특히, 기존의 양자형 적외선 검출소자에 비해 전자의 유효질량이 상대적으로 커서 밴드 간의 투과전류가 줄어들 뿐만 아니라, 전자와 정공이 서로 다른 물질 영역에 분포하여 Auger 재결합률을 효과적으로 줄일 수 있어 상온 동작이 가능한 소재로 주목을 받고 있다. 또한, T2SL 구조는 초격자를 구성하는 물질의 두께나 조성 변화를 통한 밴드갭 변조가 용이하여 단파장에서 장파장 적외선에 이르는 광범위한 파장 대역에서 동작이 가능할 뿐만 아니라 구조적 변화를 통해 이중 대역을 동시에 검출 할 수 있는 차세대 적외선 열영상 소자로 알려져 있다. 본 연구에서는 분자선 에피택시(MBE)법을 이용하여 300 주기의 InAs/GaSb (10/10 ML) 제2형 초격자 구조를 성장하여 적외선 검출소자를 제작하였다. 제2형 초격자 구조를 구성하는 물질계에 p-type dopant인 Be을 이용하여 각각 도핑 농도가 다른 시료를 성장하였다. 이때 p-type 도핑 농도는 각각 $1/5/10{\times}10^{15}cm^{-3}$로 변화를 주었다. 성장된 시료의 구조적 특성 분석을 위해 고분해능 X선 회절 (High resolution X-ray diffraction, HRXRD)법을 이용하였으며, 초격자 한 주기의 두께가 6.2~6.4 nm 로 설계된 구조와 동일하게 성장됨을 확인 하였으며, 1차 위성피크의 반치폭은 30~80 arcsec로 우수한 결정성을 가짐을 확인하였다. 적외선 검출을 위한 $410{\times}410{\mu}m^2$ 크기의 단위 소자 공정을 진행하였으며 이때 적외선의 전면 입사를 위해 소자 위에 $300{\mu}m$의 윈도우 창을 제작하였다. 단위 소자의 측벽에는 표면 누설 전류가 흐르는데 이를 방지하기 위해서 표면보호막을 증착하였다. 적외선 검출 소자의 전기적 특성 평가를 위해 각각의 시료의 암전류 (dark current)와 파장별 반응 (spectral response)을 온도별로 측정하여 비교 및 분석하였다.

• Journal of the Korean Vacuum Society
• /
• v.15 no.2
• /
• pp.223-230
• /
• 2006

We have investigated the characteristics of hydrogen (H) plasma treated quantum dot infrared photodetectors (QDIPs). The structure used in this study consists of 3 stacked, self assembled $In_{0.5}Ga_{0.5}As/GaAs$ QD layer separated by GaAs barrier layers that were grown by molecular beam epitaxy. Optical characteristics of QDIPs, such as photoluminescence (PL) spectra and photocurrent spectra, have been studied and compared with each other for the as grown and H plasma treated QDIPs. H plasma treatment, resulted in the splitting of PL peak, which can be attributed to the redistribution of the size of QDs. The activation energies estimated from the temperature dependence of integrated PL intensity for as grown and H plasma treated QDIPs are found to be in good agreement with those determined from corresponding peaks of photocurrent spectra. It is also noted that photocurrent is detected up to 130 K for the H plasma treated QDIP, suggesting the future possibility for the development of infrared photodetectors with high temperature operation.

• Journal of the Korean Vacuum Society
• /
• v.16 no.5
• /
• pp.371-376
• /
• 2007

We have investigated the lasing characteristics of the InGaAs quantum dot laser diode (QD-LD) and InGaAs quantum well laser diode (QW-LD) operated at the 980 nm wavelength range. The 980-nm lasers are used as a pumping source for a erbium-doped fiber amplifier (EDFA) and it shows high efficiency in long-haul optical fiber network. We have compared the threshold current density, the characteristic temperature, the optical power and the internal efficiency of QD-LD and QW-LD under a pulsed current condition. The QD-LD shows superior performances to the QW-LD. Further optimization of a LD structure is expected to the superior performances of a QD-LD.

• Journal of the Korean Vacuum Society
• /
• v.18 no.5
• /
• pp.352-357
• /
• 2009

The InAs multi-quantum dots (MQDs) solar cell and InGaAs multi-quantum wells (MQWs) solar cell to cover 1.1 eV and 1.3 eV were designed by 1D poisson, respectively. The MQDs and MQWs of 5, 10, 15 layers were grown by molecular beam epitaxy. The photo luminescence results showed that the 5 period stacked MQDs have the highest intensity at around 1.1 eV with 57.6 meV full width at half maximum (FWHM). Also we can observe 10 period stacked MQWs peak position which has highest intensity at 1.31 eV with 12.37 meV FWHM. The density and size of QDs were observed by reflection high energy electron diffraction pattern and atomic force microscope. Futhermore, AlGaAs/GaAs sandwiched tunnel junctions were modified according to the width of GaAs layer on p-type GaAs substrates. The structures with GaAs width of 30 nm and 50 nm have backward diode characteristics. In contrast, tunnel diode characteristics were observed in the 20 nm of that of sample.

• Journal of the Korean Vacuum Society
• /
• v.22 no.6
• /
• pp.313-320
• /
• 2013

The $AlAs_xSb_{1-x}$ step-graded buffer (SGB) layer was grown on the Silicon (Si) substrate to overcome lattice mismatch between Si substrate and $Al_{0.3}Ga_{0.7}As$/GaAs multiple quantum wells (MQWs). The value of root-mean-square (RMS) surface roughness for 5 nm-thick GaAs grown on $AlAs_xSb_{1-x}$ step-graded buffer layer was ~1.7 nm. $Al_{0.3}Ga_{0.7}As$/GaAs MQWs with AlAs/GaAs short period superlattice (SPS) were formed on the $AlAs_xSb_{1-x}$/Si substrate. Photoluminescence (PL) peak at 10 K for the $Al_{0.3}Ga_{0.7}As$/GaAs MQW structure showed relatively low intensity at ~813 nm. The RMS surface roughness of the $Al_{0.3}Ga_{0.7}As$/GaAs MQW structure was ~42.9 nm. The crystal defects were observed on the cross-sectional transmission electron microscope (TEM) images of the $Al_{0.3}Ga_{0.7}As$/GaAs MQW structure. The decrease of PL intensity and increase of RMS surface roughness would be due to the formation of the crystal defects.

• Journal of the Korean Vacuum Society
• /
• v.19 no.3
• /
• pp.211-216
• /
• 2010

The luminescence properties of $In_{0.5}Ga_{0.5}As/In_{0.5}Al_{0.5}As$ multiple quantum wells (MQWs) grown on $In_{0.5}Al_{0.5}As$ buffer layers have been studied by using photoluminescence (PL) and time-resolved PL measurements. A$1-{\mu}m$ thick $In_{0.5}Al_{0.5}As$ buffer layers were deposited on a 500 nm thick GaAs layer, followed by the deposition of the InGaAs/InAlAs MQWs. In order to investigate the effects of InAlAs buffer layer on the optical properties of the MQWs, four different temperature sequences are used for the growth of InAlAs buffer layer. The growth temperature for InAlAs buffer layer was varied from 320^{\circ}C to $580^{\circ}C$. The MQWs consist of three $In_{0.5}Ga_{0.5}$As wells with different well thicknesses (2.5 nm, 4.0 nm, and 6.0 nm thick) and 10 nm thick $In_{0.5}Al_{0.5}$As barriers. The PL spectra from the MQWs with InAlAs layer grown at lower temperature range ($320-580^{\circ}C$) showed strong peaks from 4 nm QW and 6 nm QW. However, for the MQWs with InAlAs buffer grown at higher temperature range ($320-480^{\circ}C$), the PL spectra only showed a strong peak from 6 nm QW. The strongest PL intensity was obtained from the MQWs with InAlAs layer grown at the fixed temperature of $480^{\circ}C$, while the MQWs with buffer layer grown at higher temperature from $530^{\circ}C$ to $580^{\circ}C$ showed the weakest PL intensity. From the emission wavelength dependence of PL decay times, the fast and slow decay times may be related to the recombination of carriers in the 4 nm QW and 6 nm QW, respectively. These results indicated that the growth temperatures of InAlAs layer affect the structural and optical properties of the MQWs.