• Journal of Wetlands Research
• /
• v.26 no.2
• /
• pp.139-146
• /
• 2024

Various injection materials, such as asphalt-based injection materials, urethane-based injection materials, cement- based injection materials, and acrylic-based injection materials, are used for the repair of aged conduits and underground structures with cracks. In this study, research was conducted on an environmentally friendly acrylic- based leak repair material that exhibits good curing properties even in humid conditions and stability in temperature fluctuations. To compare the performance of the improved acrylic leak repair material with the existing acrylate injection material, experiments were conducted using KS standard methods, including underwater length change rate tests, underwater leakage resistance tests, and chemical performance tests. The comparative experiments revealed that the improved acrylic leak repair material showed no changes in shrinkage due to humidity, temperature variations, or chemical reactions compared to the existing acrylate injection material. In the underwater resistance test, the improved acrylic leak repair material did not show any leakage. Additionally, to assess the environmental impact of the improved acrylic leak repair material, acute fish toxicity tests and acute oral toxicity tests were conducted, and the results showed no mortality and no specific concerns with the test specimens. The experimental results led to the conclusion that the improved acrylic leak repair material is considered to be superior in performance, environmentally safe, and harmless to the human body. Based on various experimental results, it is inferred that the improved acrylic leak repair material is suitable for use as a repair material for cracks in manholes and underground structures compared to the existing acrylate repair material. This study aims to propose valuable data for future technological development by evaluating the applicability of acrylic leak repair materials.

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 1997.11a
• /
• pp.171-176
• /
• 1997

본 연구에서는 노후화 된 구조물을 효과적으로 보강할 수 있는 방법에 대해 휨 거동을 중심으로 그 성능을 규명하고자 하였다. 연구에 채택된 보강재료로는 현재 시공의 간편성과 보강된 부재 단면의 최소화로 최근에 각광을 받고 있는 섬유접착 보강재료 중에서 탄소섬유쉬트(CFS)와 아라미드섬유쉬트(AFS) 접착공법을 선택하였으며, 현재 상용중인 보강단면을 채택하여 보수ㆍ보강을 실시하였다. 그리고, 보강효과를 실험을 통하여 비교ㆍ분석함으로써 합리적인 보수ㆍ보강공법을 위한 선택의 폭을 넓히고, 현재 활발히 진행중인 국내 보수ㆍ보강의 체계화를 위한 기초적인 자료를 얻고자 한다. (중략)

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.7
• /
• pp.39-45
• /
• 2017

In this study, permeable repair materials mainly composed of silicate - based inorganic materials(SIM), which are easily available domestically, were prepared as a basic study for the development of permeable repair materials using SIM. SIM were compared and examined for their performance as repair materials by selecting a product group which has many cases of use in foreign countries. The SIM used were mainly composed of sodium, potassium and lithium silicate. Performance evaluation of SIM was performed by absorption and penetration, compression and adhesion, rapid chloride ion penetration, rapid freezing and thawing, and chemical resistance test. According to the test results, SIM showed effective performance in all areas, mainly because SIM permeates into the interior of the capillary and has a dense internal microstructure. Therefore, it can be used variously to improve the durability of concrete based on the results of this experiment.

• Journal of the Korea Concrete Institute
• /
• v.16 no.1 s.79
• /
• pp.88-93
• /
• 2004

The objective of this study was to investigate applicability of epoxy injection method to cracked RC beams and structural behavior of repaired RC beams considering pre-loading conditions. For this purpose, five test beams were fabricated under two experimental variables. The main variables of this experimental study were pre-loading conditions and repair methods. The two pre-loading conditions were selected as $70\%$ and $90\%$ of nominal strength and the repair methods were to repair the cracked RC beams under free loading after crack and sustained loading. The comparative study was executed to evaluate effects of pre-loading conditions on the structural behavior of the cracked RC beams after crack-repair. The strains of reinforcement and concrete and deflections of beams at each loading step were measured and evaluated. As the results of this study, repair methods have much influence on structural behavior of epoxy injected RC beams and epoxy injection method for cracks of RC structures is appeared to be efficient.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.496-502
• /
• 2017

The purpose of this study is to investigate the applicability of surface-wave techniques for the evaluation of the crack-repairing performance of an epoxy injection method in concrete. In this study, box-shaped concrete specimens with four different crack depths were made with identical mix proportions. The specimens with different crack depths were completely repaired using the same epoxy injection method. The spectral energy transmission ratio of surface waves is used as an index to differentiate the effects of crack depth and crack-repairing performance. The decrease of spectral energy transmission ratio in accordance with the increase of crack depth was identified before repairing. Furthermore, the spectral energy transmission ratio increased after the crack-repairing process in all specimens. The spectral energy transmission ratio is considered as a great indicator for estimating the crack-repairing performance of the epoxy injection method; the ratio was recovered up to almost 95% of the uncracked condition.

• Journal of the Korea Concrete Institute
• /
• v.19 no.1
• /
• pp.39-46
• /
• 2007

In this study, for the establishment of the performance evaluation methods and the quality control standards of durability recovery method, the quantitative exposure data by long term exposure test under the coast and normal atmosphere is accumulated and analyzed. Investigating and evaluating the result of exposure test during 30 months of exposure age under the coastal and normal atmosphere environment, carbonation depth and chloride-ion penetration depth very little penetrated than cover depth. It seems reasonable to conclude that main cause of Corrosion of reinforcing bar are chloride-ion and macro cell from the result of corrosion area and corrosion velocity. Therefore, it is considered to be applied as the fundamental data on the performance evaluation and quality control standards of repair material and method through continuous exposure test in the future.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.633-636
• /
• 2008

Concrete structures are occur many various deteriorations in the course of time and many efforts have progressed to improve on performance of concrete. The purpose of this study is to evaluate the durability of latex modified mortar in order to repair concrete structure which are happened deterioration. In this study, we tested plastic shrinkage, drying shirnkage, repeated freezing and thawing, permeability and resistance of chemical solution. Latex modified mortar and two kinds of sprayed polymer mortar used on durability test. As a result of test, latex modified repair mortar was exhibited durablilty improvement compared to the conventional sprayed polymer mortars. It is judged the fact that latex modified mortar have no problem in site application but additionally many research will be necessary.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.2
• /
• pp.75-86
• /
• 2012

This paper presents some research results on the shrinkage characteristics and frost resistance before and after cracking of FR-ECC(Fire Resistance-Engineered Cementitious Composite). Also, a waterstop performance and exfoliating resistance of multi-layer lining specimens using FR-ECC and flexural performance of beam member by repaired FR-ECC are estimated in this paper. Experimental results indicate that the plastic shrinkage crack and length change ratio of FR-ECC have been reduced as compared with that of the existing repair mortar, and that its crack resistance on the dry shrinkage is improved under the confining stress. As well as FR-ECC has been great in the frost resistance and its tensile properties under the cracked state have been not reduced by freezing and thawing reaction. In addition, beam member by repaired FR-ECC have been increased in the flexural properties such as initial crack moment, yeild moment, and its crack width has been controled in a stable by the frexural failure.

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 2003.10a
• /
• pp.378-383
• /
• 2003

콘크리트 구조물은 여러 가지 원인에 의해 손상을 입거나 시간이 지남에 따라 노후화가 진행된다. 이와 같이 손상을 입거나 노후화가 진행된 구조물은 그 내구성능이 저하되어 계속 사용하기 위해서는 보수를 하거나 보강해야만 한다. 구조물을 보수하거나 보강하는 것은 구조물의 수명을 크게 연장하는 일로 여러 가지의 경제적인 효과가 있기 때문에 이에 대한 연구와 공법 개발 등이 활발히 이루어지고 있다.(중략)

• Information and Communications Magazine
• /
• v.6 no.1
• /
• pp.62-68
• /
• 1989