• Journal of Adhesion and Interface
• /
• v.23 no.3
• /
• pp.94-99
• /
• 2022

Ternary phased graphene/silica/EVOH nanocomposite coating materials were prepared via sol-gel process and solution blending process. From both SEM observations and XRD analysis, the exfoliated structure and dispersion state of graphene nanosheets and silica particles in the nanocomposites as well as the intercalated and exfoliated structure of the prepared graphene oxide were confirmed. The incorporation of GrO and silica at appropriate content resulted in remarkable improvement in oxygen barrier property of the ternary phased nanocompoiste-coated BOPP films, compared with that of binary(silica/EVOH) phased nanocomposite coating films, however, at excess amount of GrO and silica, very slight variation was observed due to incomplete exfoliation, dispersion of graphene tactoids, and formation of micro cracks in the silica clusters. In addition, the transparency of nanocomposite-coated film was investigated by measuring the light transmittance as a function of GrO contents, suggesting the possibility for the application of food packaging films.

• Polymer(Korea)
• /
• v.36 no.4
• /
• pp.536-541
• /
• 2012

The effects of silica content were studied on UV curing characteristics and defect formations in imprinted patterns of hundreads nanometer size for the photo-curable imprinting composites with silica particles. An increase in elasticity and a decrease in shrinkage were observed with an increase in silica content in the imprinting resin which was UV cured at room temperature. However, the patterned nano-pillars were stuck together with neighboring nano-pillars if the amount of silica is more than 7 wt%. This can be ascribed to the increased viscosity of imperfectly cured resin due to the obstruction of the photo-reaction by silica particles. Addition of silica to the imprinting resin is useful in enhancing the strength of the cured resin although it is difficult to get good imprinted patterns for the resin with more than 7 wt% of silica due to the reduction of photo-reaction conversion.

• Resources Recycling
• /
• v.16 no.5
• /
• pp.41-45
• /
• 2007

Tetramethylorthosilicate (TMOS) and silica nanopowder were synthesized from the waste silicon sludge containing 15% weight of silicon powder. TMOS, a precursor of silica nanopowder, was firstly prepared from the waste silicon sludge by catalytic chemical reaction. The maximum recovery of the TMOS was 100% after 5 hrs regardless of reaction temperature above $130^{\circ}C$. But the initial reaction rate became faster while the reaction temperature was higher than $150^{\circ}C$. As the methanol feedrate Increased from 0.8 ml/min to 1.4 ml/min, the yield of reaction was not varied after 3 hrs. Then, silica nanopowder was synthesized from the synthesized TMOS by flame spray pyrolysis. The morphology of as-prepared silica nanopowder was spherical and non-aggregated. The average particle diameters ranged from 9 nm to 30 nm and were in proportional to the precursor feed rate, and precursor concentration.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.2
• /
• pp.166-173
• /
• 2019

In this paper, the reaction properties of silica source in the accelerated curing conditions using autoclave and the fundamental properties of inorganic Micro Defect Free(MiDF) concrete using silica source are studied. Studies show that Si ions elution rate from silica source in autoclave curing is higher in amorphous source. In tap water conditions, solids which is source after autoclaved curing show a higher mass reduction in amorphous materials, which is attributed to the higher elution rate of ion. In $Ca(OH)_2$ solution conditions, amorphous materials show higher mass increase, due to increase in C-S-H minerals. From experiment for influence on the properties of MiDF concrete by using nano silica materials, the specimen with silica fume shows an increase in compressive strength and a decrease in absorption depending on replacement rate up to 5.5%, while nano silica with amorphous phase and high-fineness shows a decrease in compressive strength and decrease in the water absorption. The specimen with nano silica increases the pore below 10,000nm, but reduces pore between 10,000 and 100,000nm. The above results show that the porosity and absorption rate of MiDF concrete can be reduced by using amorphous nano-size silica. However, to reduce the pore of 50 to 10,000nm, better dispersion of nano material in the cement matrix will be necessary. We will focus on the this item in the next research.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.12 no.1
• /
• pp.33-39
• /
• 2024

In this study, the basic properties of cement paste with varying replacement ratio of micro-silica and fumed silica were analyzed to determine the suitability of nanomaterials for use as concrete admixtures. Referring to the ultra-high strength mix, the fluidity of cement paste was evaluated according to the nanomaterial replacement rate and the compressive strength characteristics were compared and analyzed. The related properties of the reactive nanomaterials to the cement hydrate were analyzed using SEM and EDS to observe the microstructure and identify the components of the hydration product. The reactive nanomaterials used in this study had tap densities between 0.061 and 0.264 g/cm³, which were lower than SF. Micro silica exhibited excellent compressive strength properties with increasing replacement ratio, but fumed silica, unlike micro white, obtained excellent compressive strength at replacement ratio of 0.01~0.1 %. The same trend was observed in the hydration characterization.

• Elastomers and Composites
• /
• v.44 no.1
• /
• pp.34-40
• /
• 2009

New coupling agent or surface modified agent (9-decenoic acid) was used to enhance the compatibility between silica and polystyrene in silica/polystyrene hybrid nanocomposite, synthesized by in situ miniemulsion polymerization. Composites contain well dispersed nanosize silica particles. Related tests and analyses confirmed the success of synthesis. Functionalization of silica by 9-decenoic acid and silica on the polystyrene was confirmed by FTIR. TGA showed presence and amount of silica in final latex. The glass transition temperature of the hybrid nanocomposite was increased with the silica amount. SEM and TEM analysis showed the spherical morphology of PS and composite with an average diameter of 55 nm. The presence of silica within composite was confirmed by EDS attached to the existing TEM.

• Proceedings of the KAIS Fall Conference
• /
• 2007.05a
• /
• pp.273-275
• /
• 2007

본 논문은 실리카 코팅 자성 나노입자를 이용한 새로운 DNA의 정제에 관한 것으로 기존의 negative-charged polyanion 형태의 수지 및 실리카 멤브레인 기술을 이용한 제품의 단점인 저속, 고비용의 정제방법을 개선할 수 있는 새로운 정제법을 기술한 것이다.

• Membrane Journal
• /
• v.24 no.4
• /
• pp.301-310
• /
• 2014

In this study, the silica nanoparticles were considerably chosen to improve a dimensional stability, proton transport and electrochemical performance of the resulting inorganic-organic nanocomposite membranes. For this purpose, hydrophobic silica (Aerosil$^{(R)}$ 812, Degussa) and hydrophilic silica (Aerosil$^{(R)}$ 380, Degussa) nanoparticles were, respectively, introduced into a Sulfonated poly(arylene ether sulfone) (SPAES) polymer matrix. The $SiO_2$ particles are evenly dispersed in a SPAES matrix by the aid of a non-ionic surfactant (Pluronics$^{(R)}$ L64). A $SiO_2$ content plays an important role in membrane microstructures and membrane properties such as proton conductivity and water uptake. Therefore, to study nanocomposite membranes with excessive amount of silica, the content of silica nanoparticles were increased up to 5 wt%. Interestingly, a hydrophobic $SiO_2$ containing nanocomposite membrane showed better electrochemical performance (29% higher than pristine SPAES) despite of low proton conductivity due to its adhesive properties with a catalyst layer in a single cell test. All the silica-SPAES membranes exhibited better performance than a pristine SPAES membrane.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.3
• /
• pp.269-275
• /
• 2022

In this study, the setting time and compressive strength of cement paste composites applied with nano-micro pozzolanic binders were experimental analyzed. The pozzolanic binder was reduced initial and final setting time and the compressive strength was increased. Micro silica was effective in decrease the initial setting and final setting time and impressing the compressive strength. When two or more cement binders were used, the using of silica fume and a small amount of nano silica at reduced the setting time to 62-64 % to OPC cement and the compressive strength was increased to 117 %. A small amount of mixing the nano silica was effect to pore filling and pozzolanic activation. However, the addition of a chemical admixture should be considered when mixing table design because pozzolanic binders high specific surface area causes a decrease in cement composites flow.

• Polymer(Korea)
• /
• v.34 no.1
• /
• pp.1-7
• /
• 2010

To enhance the transport properties of gas separation membrane, we prepared 6FDA-6FpDA based polyimide membrane with PMMA-graft-silica nanoparticles. The silica was grafted PMMA which is miscible with 6FDA-based polyimide after surface treatment by 3-methacryloxypropyltrimethoxysilane ($\gamma$-MPS). The untreated silica/6FDA-6FpDA membrane showed greater permeability and less selectivity than PMMA-g-silica/6FDA-6FpDA due to its low dispersion. The transport properties of PMMA-g-silica/6FDA-GFpDA membrane were measured as a function of filler concentration. These membranes were evaluated using pure gases (He, $O_2$, $N_2$, $CO_2$). The increase in permeation was attributed to changes in the free volume distribution until 1 wt%. After 1 wt%, the permeability was decreased by excess silica which decreased effective area in polymer matrix. The selectivity was decreased with increasing permeability on the whole. However, the selectivity of $CO_2$ showed more enhance value.