• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.121-124
• /
• 1999

The (Ba,Sr)TiO$_3$[BST] thin film were fabricated on the Pt/Ti/SiO$_2$/Si substrate by RF sputtering technique. The structural properties of the BST thin films were investigated with deposition time and substrate temperature by XRD. In the case of the BST thin films which has the deposition thin of 20 min, second phases and BST (111) peaks were increased with increasing the temperature of substrate. The capacitance of the BST thin film (deposition time of 20 min.) was decreased with the substrate temperature and was 1500pF with applied voltage of 1V.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.5
• /
• pp.265-269
• /
• 2000

$(Ba, Sr)TiO_3$thin films were etched with a magnetically enhanced inductively coupled plasma (MEICP) at different CF4/Ar gas mixing ratios. Experimental was done by varying the etching parameters such as rf power, dc bias and chamber pressure. The maximum etch rate of the BST films was $1800{AA}/min$ under $CF_4/(CF_4+Ar)$ of 0.1, 600 W/350 V and 5 mTorr. The selectivity of BST to Pt and PR was 0.6, 0.7, respectively. X-ray photoelectron spectroscopy (XPS) results show that surface reaction between Ba, Sr, Ti and C, F radicals occurs during the (Ba, Sr)TiO3 etching. To analyze the composition of surface residue after the etching, films etched with different CF_4/Ar$ gas mixing ratio were investigated using XPS and secondary ion mass spectroscopy (SIMS).

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.2
• /
• pp.111-115
• /
• 2000

$BaTIO_3$ thin films were prepared on (100) $BaTIO_3$ substrates by coating- pyrolysis process using metal-organic compounds of Ba and Ti. The amorphous films prefired at $450^{\circ}C$were crystallized above $700^{\circ}C$ under oxygen partial pressure of $2\times 10^{-4}$. The lattice parameters of the perpendicular axis for the $BaTIO_3$ thin films heat-treated below $800^{\circ}C$ were closer to a value of cubic $BaTIO_3$, whereas those above $800^{\circ}C$ were closer to a value of tetragonal BaTiG. The results of XRD P scan and pole-figure analyses indicated that BaTiO, thin films have an epitaxial relationship with the $SrTiO_3$ substrates. The $BaTIO_3$thin films annealed at$800^{\circ}C$ showed the surface with island-like grains about 0.4$mu \textrm{m}$ and the cross section of 0.8 $mu \textrm{m}$ thickness with granular grains.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.11a
• /
• pp.50-50
• /
• 1996

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1879-1881
• /
• 1999

(Ba,Sr)$TiO_3$[BST] thin films were fabricated on Pt/Ti/$SiO_2$/Si substrate by RF sputtering. We investigated the effects of substrate temperature on the structural and dielectric properties of BST thin films. Increasing the substrate temperature, barium multi titanate phases were decreased, and BST (100), (200) peaks were increased. The relative dielectric constant and dielectric loss of the BST thin films at the substrate temperature of $500^{\circ}C$ were 300 and 0.018, respectively at l[kHz]. In all films, the dielectric constants decreased. Dielectric losses increased as increasing the frequency. The switching voltage was 5V of the BST thin films at the substrate temperature of $500^{\circ}C$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.8
• /
• pp.852-858
• /
• 2004

An alkoxide-based sol-gel method was used to fabricate $Ba_{0.6}Sr_{0.4}TiO_{3}$thin films doped by Bi from 5 to 20 mol% on a Pt/Ti/$SiO_2$/Sisubstrate. The structural and dielectric properties of BST thin films were investigated as a function of Bi dopant concentration. The dielectric properties of the Bi doped BST films were strongly dependent on the Bi contents. The dielectric constant and dielectric loss of the films decreased with increasing Bi content. However, the leakage current density of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_{3}$ thin film showed the lowest value of 5.13$\times 10^{-7} A/{cm}^2$ at 5 V. The figure of merit (FOM) reached a maximum value of 32.42 at a 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_{3}$thin films. The dielectric constant, loss factor, and tunability of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}Tio_{3}$ thin films were 333, 0.0095, and 31.1%, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.51-54
• /
• 2000

In this paper, $Ba_{0.5}$Sr$_{0.5}$TiO$_3$ thin films were prepared on Pt/Ti/SiO$_2$/Si substrate by RF magnetron sputtering method. We investigated effect of deposition conditions (especially RF input power) on structural properties of BST thin films. Deposit conditions of BST films were set working gas ratio, Ar:O$_2$= 70 : 30, working pressure 10mTorr, and RF input power 25W, 50W, 75W and 100W. Post-annealing using rapid thermal annealing(RTA) performed at 45$0^{\circ}C$, 55$0^{\circ}C$, $650^{\circ}C$, and 75$0^{\circ}C$ in oxigen ambient for 60 sec, respectively. The structural properties of BST films on Pt/Ti/SiO$_2$/Si substrate analysed by X-ray diffraction(XRD).).).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.565-568
• /
• 2004

An alkoxide-based sol-gel method was used to fabricate $Ba_{0.6}Sr_{0.4}TiO_3$ thin films doped by Bi from 5 to 20 mol% on a Pt/Ti/SiO2/Si substrate. The structural and dielectric properties of BST thin films were investigated as a function of Bi dopant concentration. The dielectric properties of the Bi doped BST films were strongly dependent on the Bi contents. The dielectric constant and dielectric loss of the films decreased with increasing Bi content. However, the leakage current density of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin film showed the lowest value of 5.13 10-7 at 5 V. The figure of merit (FOM) reached a maximum value of 32.42 at a 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin films. The dielectric constant, loss factor, and tunability of the 10 mol% Bi doped $BBa_{0.6}Sr_{0.4}TiO_3$ thin films were 333,0.0095, and 31.1%, respectively.

• Journal of the Korean Ceramic Society
• /
• v.40 no.2
• /
• pp.198-205
• /
• 2003

$Ba_{0.66}Sr_{0.34}TiO_3$ thin films and seed-layers were deposited on $Pt/Ti/SiO_2/Si$substrate by R.F. magnetron sputtering method. Effects of various substrate temperature conditions on electrical properties (such as capacitance and leakage current) of BST thin films were studied. The effect of seed-layer was also studied. When seed-layer was inserted between BST and Pt, the crystallization of the BST thin films was considerably improved and the processing temperature was lowered. Compared to the pure BST thin films, dielectric constant, dielectric loss, and leakage current of BST thin films deposited on the seed-layer were considerably improved. It could be revealed that electrical properties are influenced by the substrate temperatures of BST thin films and are enhanced by the seed-layer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.04a
• /
• pp.309-313
• /
• 1997

(Ba$_{x}$Sr$_{l-x}$)TiO$_3$(BST) thin fi1ms with various Ba/Sr ratios were deposited on Pt(80nm)/SiO$_2$(100nm)/Si by RF magnetron sputtering. BST thin films which have x=0.6, 0.5, 0.4 were studied dielectric properties with temperature variation. The frequency was used from 100Hz to 1MHz for measuring dielectric constant. The measurement conditions of dielectric constant with Temperature Variation were 1KHz and 2$0^{\circ}C$. As a result, the dielectric constant of BST thin film was about 425 and loss factor was 0.013. Also, with increasing Temperature, the dielectric constants of BST thin films were gradually decreased.sed.