• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.9
• /
• pp.807-811
• /
• 2003

We investigated the electrical characterisitics of T $a_2$ $O_{5}$ (tantalum pentoxide) film and Ti-O/T $a_2$ $O_{5}$ film deposited on $Al_2$ $O_3$based substrate. Ta (tantalum) electrode and $Al_2$ $O_3$ substrate was used for the purpose of simplifying the manufacturing process in IPD's (integrated passive devices). Dielectric materials (T $a_2$ $O_{5}$ and Ti-O/T $a_2$ $O_{5}$ films) deposited on Ta/Ti/A $l_2$ $O_3$ were annealed at 700 $^{\circ}C$ for 60 sec. in vacuum. The XRD results showed that as-deposited T $a_2$ $O_{5}$ film possessed amorphous structure, which was transformed to crystallines by rapid thermal heat treatment. We compared the lnJ- $E^{{\frac}{1}{2}}$, C-V, C-F of both as-deposited and annealed dielectric thin films deposited on Ta bottom electrode. From this results, we concluded that the leakage current could be reduced by introducing Ti-O buffer layer and conduction mechanisms of T $a_2$ $O_{5}$ and Ti-O/T $a_2$ $O_{5}$ could be interpreted appropriately by Schottky emission effect.

• Korean Journal of Crystallography
• /
• v.11 no.2
• /
• pp.95-101
• /
• 2000

Ferroelectric SrBi2Ta2O9 (SBT) thin films of Pt/Ti/SiO2 electrode were fabricated using a sintered SBT target with various Bi2O3 content by rf magnetron sputtering. Good hysteresis loop characteristics were observed in the SBT thin films deposited with 50mol% excess Bi target. SBT thin films crystallized from 650℃ however, good hysteresis loop can be obtained in the film annealed above 700℃. pt/TiO2/SiO2 and Pt/SiO2 electrodes were also used to investigate the Pt electrode dependence of SBT thin films. SBT thin films showed random oriented polycrystalline structure and similar morphology regardless of electrodes with quite different surface morphology. A 0.2㎛ thick SBT film annealed at 750℃ exhibited the remanent polarization (2Pr) of μC/㎠ and coercive voltage(Vc) of 1V at an applied voltage of 5V.

• Progress in Superconductivity and Cryogenics
• /
• v.23 no.2
• /
• pp.1-5
• /
• 2021

We have investigated the electrical transport properties of polycrystalline tantalum nitride (TaN_x) films. Various compositions of tantalum (nitride) thin films have been deposited on SiO₂ substrates by reactive DC magnetron sputtering while changing the ratio of nitrogen partial pressure. The substrate temperature was maintained at 283 K during deposition. X-ray diffraction analyses indicated the presence of α-Ta and β-Ta phases in the Ta film deposited in pure argon atmosphere, while fcc-TaN_x phases appeared in the sputtering gas mixture of argon and nitrogen. The N/Ta atomic ratio in the film increased ranging from 0.36 to 1.07 for nitrogen partial pressure from 7 to 20.7%. The superconducting transition temperatures of the TaN_x thin films were measured to be greater than 3.86 K with a maximum of 5.34 K. The electrical resistivity of TaN_x thin film was in the range of 177-577 𝜇Ωcm and increased with an increase in nitrogen content. The upper critical filed at zero temperature for a TaN_0.87 thin film was estimated to exceed 11.3 T, while it showed the lowest T_c = 3.86 K among the measured superconducting TaN_x thin films. We try to explain the behavior of the increase of the residual resistivity and the upper critical field for TaN_x thin films with the nitrogen content by using the combined role of the intergrain Coulomb effect and disorder effect by grain boundaries.

• Korean Journal of Materials Research
• /
• v.9 no.5
• /
• pp.509-514
• /
• 1999

Interest in the integrated capacitors, which make it possible to reduce the size of and to obtain improved electrical performance of an electronic system, is expanding. In this study, $Ta_2$O\ulcorner thin film capacitors for MCM integrated capacitors were fabricated on a Upilex-S polymer film by DC magnetron reactive sputtering and the effects of low temperature annealing at various atmospheres and substrate surface morphology on the capacitor characteristics were discussed. The low temperature($150^{\circ}C$) annealing produced improved capacitor yield irrespective of the annealing at mosphere. But the leakage current of the $O_2$-annealed film was larger than that of any other films. This is presumably mosphere. But the leakage current of the $O_2$-annealed film was larger than that of any other films. This is presumably due to the change of the $Ta_2$O\ulcorner film surface by oxygen, which was explained by conduction mechanism study. Leakage current and breakdown field strength of the capacitors fabricated on the Upilex-S film were 7.27$\times$10\ulcornerA/$\textrm{cm}^2$ and 1.0 MV/cm respectively. These capacitor characteristics were inferior to those of the capacitors fabricated on the Si substrate but enough to be used for decoupling capacitors in multilayer package. Roughness Analysis of each layer by AFM demonstrated that the properties of the capacitors fabricated on the polymer film were affected by the surface morphology of the substrate. This substrate effect could be classified into two factors. One is the surface morphology of the polymer film and the other is the surface morphology of the metal bottom electrode determined by the deposition process. Therefore, the control of the two factors is important to obtain improved electrical of capacitors deposited on a polymer film.

• Journal of the Korean Ceramic Society
• /
• v.40 no.12
• /
• pp.1165-1169
• /
• 2003

The Ta$_2$O$_{5}$ thin film was deposited on Si-(III) and glass substrate with the change of Ar:O$_2$ gas flow rate in the assist ion gun by the Dual ion-Beam Sputtering (DIBS). As the $O_2$ gas flow of the assist ion gun was decreased, the deposition rate of the thin films decreased. The refractive index was fixed (2.11, at 1550 nm) without regarding to $O_2$ gas flow of the range 3∼12 sccm in assist ion gun. The condition of Ar:O$_2$=3:12 was formatted stoichiometry composition of Ta$_2$O$_{5}$ and the ms roughness was small (0.183 nm).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.71-74
• /
• 1996

Ta$_2$O$_{5}$ film ale recognized as promising capacitor dielectric for future DRAM\`s. The electrical properties of Ta$_2$O$_{5}$films greatly depend on the heating condition. In the practical fabrication process, several annealing process, such as the annealing of Al in H$_2$(about 40$0^{\circ}C$) and reflow of BPSG (borophosphosilicate glass) film in $N_2$(about 80$0^{\circ}C$), exist after deposition of Ta$_2$O$_{5}$ film. In this paper, we describe the temperature effect on the electrical properties of W/Ta$_2$O$_{5}$/Si structure. The thin film of Ta$_2$O$_{5}$ and tungsten have been deposited on p-si(100) wafer using the sputtering system. The heating temperature was varied from 500 to 90$0^{\circ}C$ in $N_2$for 30min and The degree of temperature is 100\`C. In a log(J/E$^2$) Vs 1/E plot of typical I-V data, we find a linear relationship for the temperature of 500, $600^{\circ}C$ and as deposition. This could indicate Fowler-Nordheim tunneling as the dominant mode of current transports. However, we can not find a linear relationship for the temperature above $700^{\circ}C$. This could not indicate Fowler-Nordheim tunneling as the dominant mode of current transport. The high frequency (1MHz) capacitance-voltage (C-V) of W/Ta$_2$O$_{5}$/Si Capacitor were investigated on the basis of shift in the threshold voltage and dielectric constant. The magnitude of the threshold voltage and dielectric constant depends on the heating temperature, and increases with heating temperature.temperature.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.276-276
• /
• 2014

High-performance, fully-transparent, and top-gated oxide thin-film transistor (TFT) was successfully fabricated with Ta2O5 high-k gate dielectric on a glass substrate. Through a self-passivation with the gate dielectric and top electrode, the top-gated oxide TFT was not affected from H2O and O2 causing the electrical instability. Heat-treated InSnO (ITO) was used as the top and source/drain electrode with a low resistance and a transparent property in visible region. A InGaZnO (IGZO) thin-film was used as a active channel with a broad optical bandgap of 3.72 eV and transparent property. In addition, using a X-ray diffraction, amorphous phase of IGZO thin-film was observed until it was heat-treated at 500 oC. The fabricated device was demonstrated that an applied electric field efficiently controlled electron transfer in the IGZO active channel using the Ta2O5 gate dielectric. With the transparent ITO electrodes and IGZO active channel, the fabricated oxide TFT on a glass substrate showed optical transparency and high carrier mobility. These results expected that the top-gated oxide TFT with the high-k gate dielectric accelerates the realization of presence of fully-transparent electronics.

• Journal of the Korean Vacuum Society
• /
• v.8 no.3A
• /
• pp.224-230
• /
• 1999

$SrBi_{2x}Ta_2O_9$ (SBT) thin films were prepared on platinized silicon substrates by MOD process, and their ferroelectric and leakage current characteristics were investigated. The grain size of the MOD derived SBT films increased with increasing the BI/Ta mole ration. Although the SBT films with x of 0.8~1.2 were composed of the equiaxed grains, the elongated grains were also observed for the SBT films with x of 1.4 and 1.6. The SBT film with x of 1.2 exhibited the optimum ferroelectric properties of 2PR : 9.79 $\muC/\textrm{cm}^2$ and Ec : 24.2kV/cm at applied voltage of 5V. The leakage current density of the SBT films increased with increasing the BI/Ta mole ratio. With post annealing process, 2Pr and $E_c$of the SBT film with x of 1.2 increases 11.3 $\muC/\textrm{cm}^2$ and 39.6kV/cm, respectively. decrement of the leakage current density by post annealing process increased remarkably with increasing the Bi/ta mole ratio, and the SBT film with x=1.6 exhibited the lowest leakage current density after post annealing process.

• Korean Journal of Materials Research
• /
• v.1 no.4
• /
• pp.229-235
• /
• 1991

A new electrode material for $Ta_2O_5$ capacitor was developed to obtain both high dielectric constant and improved electrical properties for use in DRAM. High leakage current and low breakdown field of as-deposited $Ta_2O_5$ film on Si is due to the reduction of $Ta_2O_5$ by silicon at $Ta_2O_5$/electrode interface. $Dry-O_2$ anneal improves the electrical properties of $Ta_2O_5$ capacitor with Si electrode, but it thickens the interfacial oxide and lowers the dielectric constant, subsequently. $Ta_2O_5$ capacitor with TiN exectrode shows better electrical properties and higher dielectric constant than post heat treated $Ta_2O_5$ film on Si. No interfacial oxide layer at $Ta_2O_5$/TiN interface suggests that there\`s no Interaction between $Ta_2O_5$ and electrode. TiN is a adequate electrode material for $Ta_2O_5$ capacitor.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.51 no.5
• /
• pp.185-190
• /
• 2002

Capacitor material utilized in the downsizing passive devices and dynamic random access memory(DRAM) requires the physical and electrical properties at given area such as capacitor thickness reduction, relative dielectric constant increase, low leakage current and thermal stability. Common capacitor materials, $SiO_2$, $Si_3N_4$, $SiO_2$/$Si_3N_4$,TaN and et al., used until recently have reached their physical limits in their application to several hundred angstrom scale capacitor. $Ta_2O_{5}$ is known to be a good alternative to the existing materials for the capacitor application because of its high dielectric constant (25 ~35), low leakage current and high breakdown strength. Despite the numerous investigations of $Ta_2O_{5}$ material, there have little been established the clear understanding of the annealing effect on capacitance characteristic and conduction mechanism, design and fabrication for $Ta_2O_{5}$ film capacitor. This study presents the structure-property relationship of reactive-sputtered $Ta_2O_{5}$ MIM capacitor structure processed by annealing in a vacuum. X-ray diffraction patterns skewed the existence of amorphous phase in as-deposited condition and the formation of preferentially oriented-$Ta_2O_{5}$ in 670, $700^{\circ}C$ annealing. On 670, $700^{\circ}C$ annealing under the vacuum, the leakage current decrease and the enhanced temperature-capacitance characteristic stability. and the leakage current behavior is stable irrespective of applied electric field. The results states that keeping $Ta_2O_{5}$ annealed at vacuum gives rise to improvement of electrical characteristics in the capacitor by reducing oxygen-vacancy and the broken bond between Ta and O.