• Korean Journal of Materials Research
• /
• v.13 no.6
• /
• pp.360-364
• /
• 2003

$Sr_{l}$ $\pm$x/$Bi_{2}$ $\pm$y/$Ta_2$ $O_{9}$ and $Sr_{l}$ $\pm$$Bi_{x}$ $2\pm$y$Nb_2$$O_{9}$ ceramics were prepared by a solid state reaction method. X-ray diffraction analysis indicated that single-phase of Bi-layered perovskite was obtained. According to Sr/Bi content ratio, Curie temperature( $T_{c}$), electromechanical factor($K_{p}$ ) and mechanical quality factor($Q_{m}$ ) were measured. The Curie temperature of SBN(SBT) rose from $414^{\circ}C$(314$^{\circ}C$) to $494^{\circ}C$(426$^{\circ}C$) when Sr/Bi content ratio was increased. In the case of Sr/Bi content ratio = 0.55/2.3, the maximum value of the mechanical quality factor $Q_{m}$ of SBT and SBN were obtained 3320 and 1010, respectively.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.621-627
• /
• 1996

$SrBi_{2x}TaO_9$ ferroelectric thin films were prepared on platinized silicon substrates using MOD proces, and crystallization behavior of the films was investigated with variation of the annealing temperature and Bi content x. Crystalline phase of bismuth layered perovskite structure was formed even by baking the films at $800^{\circ}C$ for 5 minutes in air, and was not changed by annealing at temperatures raning from $700^{\circ}C$ to $900^{\circ}C$ for 1 hour in oxygen ambient. When $SrBi_{2x}TaO_9$ thin films ($0.8\lex\ie1.6$) were annealed at $800^{\circ}C$, Preferred orientation of the films along c-axis was observed with $x\ge1.2$. With increasing Bi content x, surface morphology of the films was changed from equiaxed grains to elongated grains.

• The Korean Journal of Ceramics
• /
• v.6 no.3
• /
• pp.219-223
• /
• 2000

The ferroelectric SBT films were deposited on Pt/Ti/SiO$_2$/Si substrates by liquid injection metalorganic chemical vapor deposition (MOCVD) with single-mixture solution of Sr[Ta(OEt)$_5$(dmae)]$_2$and Bi(C$_6$ 6/H$_5$)$_3$. The Sr/Ta and Bi/Ta ratio in SBT films depended on deposition temperature and mol ratio of precursor in the single-mixture solution. At the substrate temperature of 40$0^{\circ}C$, Sr/Ta and Bi/Ta ratio were close to 0.4 and 1 at precursor mol ratio of 0.5~1.0, respectively. As-deposited film was amorphous. However, after annealing at 75$0^{\circ}C$ for 30 min in oxygen atmosphere, the diffraction patterns indicated polycrystalline SBT phase. The remanent polarization (Pr) and coercive field (Ec) of SBT film annealed at 75$0^{\circ}C$ were 4.7$\mu$C/$\textrm{cm}^2$ and 115.7kV/cm at an applied voltage of 5V, respectively. The SBT films annealed at 75$0^{\circ}C$ showed practically no polarization fatigue up to 10$^10$ switching cycles.

• Korean Journal of Materials Research
• /
• v.7 no.5
• /
• pp.381-385
• /
• 1997

PEMOCVD에 의해서 SrBi$_{2}$Ta$_{2}$O$_{9}$밥막이 낮은 온도에서 성공적으로 Pt/Ti/SiO$_{2}$Si위에 증착되었다. 5$50^{\circ}C$에서 증착된 200nm박막은 치밀하고 작은 결정립을 보였으며 3V의 인가전압하에서 이력곡선은 포화되기 시작하였다. 3V에서 박막은 잔류분극 (P$_{r}$)과 항전계(E$_{c}$)는 각각 15$\mu$/$\textrm{cm}^2$과 50kV/cm이었다. 6V bipolar square pulse의 피로측정에서 박막은 1.0x$10^{11}$cycles까지 피로 현상을 보이지 않았다. PEMOCVD에 의해서 5$50^{\circ}C$에서 증착된 SBT박막은 비휘발성 기억소자에 충분히 활용할 수 있다.다.

• Proceedings of the KIEE Conference
• /
• 1999.11d
• /
• pp.867-869
• /
• 1999

In this study, $SrBi_{2}Ta_{2}O_{9}$(SBT) thin films were etched as a function of $SF_6$/Ar gas mixing ratio in magnetically enhanced inductively coupled plasma(MEICP) system fer a fixed rf power, dc-bias voltage, and chamber pressure. The etch rate of SBT thin film was $1500{\AA}/min$ and the selectivities of photoresist (PR) and $SiO_2$ to SBT thin film were 0.48 and 0.62, respectively when the samples were etched at a rf power of 600W, a dc-bias voltage of -150V, a chamber pressure of 10 mTorr and a gas mixing ratio of $SF_6/(SF_6+A)$=0.1. In order to examine the chemical reactions on the etched surface, X-ray photoelectron spectroscopy(XPS) and secondary ion mass spectrometry(SIMS) were done.

• The Korean Journal of Ceramics
• /
• v.6 no.2
• /
• pp.110-115
• /
• 2000

$SrBi_2Ta_2O_9$ thin films were deposited at room temperature on the usual (111) oriented Pt bottom electrodes using r.f. magnetron sputtering, and then post-annealed at 650-$800^{\circ}C$ for 30min in oxygen flow. Low temperature processing which shows the preferred oriented SBT thin films was obtained by controlling the sputtering pressure and/or Sr content in target. The orientation and grain growth behavior of SBT thin films were dependent on Sr contents in films. With increasing the excess Bi content up to 50% in SBT thin films, it was possible to lower the onset temperature of grain growth. The c-axis preferred oriented SBT thin films were well-grown under the condition of low post-annealing($650^{\circ}C$) by lowering post-annealing pressure. After $10^{11}$ switching cycles, no polarization degradation was observed in both preferred oriented SBT capacitors.

• Korean Journal of Materials Research
• /
• v.7 no.6
• /
• pp.505-509
• /
• 1997

FRAM(Ferroelectric Random Access memory)에의 응용을 위해 rf magnetron sputtering법을 이용하여 SrB $i_{2}$T $a_{2}$ $O_{9}$(SBT)박막을 증착하였다. 사용된 기판은 Pt/Ti/Si $o_{2}$Si이었으며 50$0^{\circ}C$에서 증착한 후 80$0^{\circ}C$의 산소 분위기 하에서 1시간 동안 열처리하였다. 증착시 증착 압력을 변화시켜 가면서 이에 따른 특성의 변화를 고찰하였다. 박막내의 Bi와 Sr의 부족을 보상하기 위해 20mole%의 Bi $O_{2}$와 30mole%의 SrC $O_{3}$를 과잉으로 넣어 타겟을 제조후 사용하였고 박막들의 두께는 300nm의 두께를 가지며 증착압력에 따라 다른 미세 구조르 보였다. 10mtorr에서 증착한 박막의 조성은 S $r_{0.6}$B $i_{3.8}$Ta/ sub 2.0/ $O_{9.0}$이었다. 이 SBT 박막의 잔류 분극(2 $P_{r}$)과 보전계(2 $E_{c}$)값은 각각 인가 전압 5V에서 18.5 $\mu%C/$\textrm{cm}^2$과 150kV/cm이었고, signal/noise비는 3V에서 4.6을 나타내었다. 5V의 bipolar pulse하에서 $10^{10}$cycle까지 피로 현상이 나타나지 않았으며, 누설 전류 밀도는 133kV/cm에서 약 1x$10^{-7A}$$\textrm{cm}^2$의 값을 보였다.을 보였다.

• 한국초전도학회:학술대회논문집
• /
• v.10
• /
• pp.165-168
• /
• 2000

We fabricated ramp-edge Josephson junctions with barriers formed by interface treatments instead of epitaxially grown barrier layers. A low-dielectric Sr$_2$AlTaO$_6$(SAT) layer was used as an ion-milling mask as well as an insulating layer for the ramp-edge junctions. An ion-milled YBa$_2$Cu$_3$O$_{7-x}$ (YBCO)-edge surface was not exposed to solvent through all fabrication procedures. The barriers were produced by structural modification at the edge of the YBCO base electrode using high energy ion-beam treatment prior to deposition of the YBCO counter electrode. We investigated the effects of high energy ion-beam treatment, annealing, and counter electrode deposition temperature on the characteristics of the interface-controlled Josephson junctions. The junction parameters such as T$_c$, I$_c$c, R$_n$ were measured and discussed in relation to the barrier layer depending on the process parameters.

• The Korean Journal of Ceramics
• /
• v.6 no.3
• /
• pp.276-279
• /
• 2000

Ferroelectric properties of $SrBi_2TaNbO_9$ (SBTN) thin films were changed by the amount of Bi content in SBTN. We suggested that the addition of excess Bi into the films could be accomplished by heat-treating $SBTN/Bi_2O_3/SBTN$ heterostructure fabricated by r.f. magnetron sputtering method. Excess Bi composition was controlled by the thickness of the sandwiched $Bi_2O_3$ from 0 to $400\;\AA$. When the SBTN thin films were inserted by $400\;{\AA}\;Bi_2O_3$ layer, $Bi_2Pt$ phase was formed as a second phase in SBTN films, resulting in poor ferroelectric properties. The onset temperature for hysteresis loop can be reduced by heat treating $SBTN/Bi_2O_3/SBTN$ heterostructure. The films with $SBTN/Bi_2O_3(100\;{\AA})/SBTN$ hetero-structure followed by annealing at $650^{\circ}C$ for 30 min show 2Pr and Ec of $5.66\;{\mu}C/\textrm{cm}^2$ and 54 kV/cm, respectively.

• Journal of the Korean Ceramic Society
• /
• v.25 no.6
• /
• pp.639-644
• /
• 1988

The physical and dielectric properties of complex perovskite compound Sr(Mg1/3Nb1/3)O3-Ba(Mg1/3Nb2/3)O3-Ba(Mg1/3Ta2/3)O3(BMT) system were investigated as a function of composition. As the mole ratio of BMN was increased, lattice parameter ratio c/a was slightly increased, and density was increased in SMN-BMN system. However, in BMN-BMT system, lattice parameter ratio c/a and density were decreased with increasing the mole ratio of BMN. Dielectric constant, dielectric loss at $25^{\circ}C$ and 100kHz, and temperature coefficient of resonant frequency, the dependence of temperature in capacitance were increased with increasing the mole ratio of BMN in SMN-BMN-BMT system. These result can be explained according to the degree of order=disorder and dielectric constant.