To improve the etch rate of $Si_3N_4$ thin film, $H_2SiF_6$ is added to increase etching rate by more than two times. $SiO_3H_2$ is gradually added to obtain a selectivity of 170: 1 at 600 ppm. Moreover, when $SiO_3H_2$ is added, the etching rate of the $SiO_2$ thin film increases in proportion to the radius of the wafer. In $Si_3N_4$ thin film, there is no difference in the etching rate according to the position. However, in the $SiO_2$ thin film, the etching rate increases in proportion to the radius. At the center of the wafer, the re-growth phenomenon is confirmed at a specific concentration or above. The difference in etch rates of $SiO_2$ thin films and the reason for regrowth at these positions are interpreted as the result of the flow rate of the chemical solution replaced with fresh solution.
(PDDA/$SiO_2$) thin films that consisted of positively charged poly (diallyldimethylammonium chloride) (PDDA) and negatively charged $SiO_2$ nanoparticles were fabricated on a glass substrate by an applying voltage layer-by-layer (LBL) self-assembly method. In this study, the microstructure and optical properties of the (PDDA/$SiO_2$) thin films coated on glass substrate were measured as a function of the applied voltage on the Pt electrodes. When 1.0 V was applied to a Pt electrode in a PDDA and $SiO_2$ solution, the thickness of the $(PDDA/SiO_2)_{10}$ thin film increased from 79 nm to 166 nm. The surface roughness also increased from 15.21 nm to 33.25 nm because the adsorption volume of the oppositely charged PDDA and $SiO_2$ solution increased. Especially, when the voltage was applied to the Pt electrode in the $SiO_2$ solution, the thickness increase of the (PDDA/$SiO_2$) thin film was larger than that obtained when using the PDDA solution. The refractive index of the fabricated (PDDA/$SiO_2$) thin film was ca. n = 1.31~1.32. The transmittance of the glass substrate coated by (PDDA/$SiO_2$)6 thin film with a thickness of 106 nm increased from ca. 91.37 to 95.74% in the visible range.
JSTS:Journal of Semiconductor Technology and Science
/
제2권3호
/
pp.164-169
/
2002
This paper mainly discusses the hard breakdown of 2.2-nm-thick $SiO_2$ films. It is shown that the hard breakdown event of a 2.2-nm-thick $SiO_2$ film greatly depends on the applied electric field. It is strongly suggested that the local weak spots created by applying a low initial stress to a 2.2-nm-thick $SiO_2$film resist the onset of hard breakdown. In other words, it is anticipated that the stored electrostatic energy is fast dissipated by trap-assisted tunneling in 2.2-nm-thick $SiO_2$ film. Consequently, it is strongly suggested that 2.2-nm-thick $SiO_2$ films are intrinsically quite robust.
$Si_3N_4/SiO_2/Si_3N_4$/Si 판위에 MgO 박막을 성장하여 MgO 단결정과 결정배향성이 유사한 초전형 적외선 센서용 기판을 제작하였다. RF 마그네트론 스퍼터링법으로 MgO 박막을 성장하였고, 그 위에 Pt 하부전극과 PLT 박막을 성장시킨 후 c축 배향성을 조사하였다. $500^{\circ}C$의 기판온도와 30 mTorr의 분위기 압력 및 160 W의 RF power에서 성장된 MgO 박막이 단결정 MgO가 가지는 배향성 정도의 우수한 a축 배향성을 보였고, 그 위에 성장된 PLT 박막은 MgO 단결정 기판위에 성장된 것과 거의 회절강도 변화가 유사한 c축 배향성을 보였다.
Effects of Na2SiO3 concentration added into 0.1 M NaOH + 0.05 M NaF solution on the formation behavior and properties of PEO films on AZ91 Mg alloy were investigated under 1200 Hz of alternating current (AC) by voltage-time curves, in-situ observation of arc generation behavior and measurements of film thickness, surface roughness and micro vickers hardness. In the absence of Na2SiO3 in the 0.1 M NaOH + 0.05 M NaF solution, about 4 ㎛ thick PEO film was formed within 1 min and then PEO film did not grow but white spots were formed by local burning. Addition of Na2SiO3 up to 0.2 M caused more increased formation voltage and growth of PEO film with uniform generation of arcs. Addition of Na2SiO3 from 0.2 M to 0.4 M showed nearly the same voltage-time behavior and uniform arc generation. Addition of Na2SiO3 more than 0.5 M resulted in a decrease of formation voltage and non-uniform arc generation due to local burning. PEO film growth rate increased with increasing added Na2SiO3 concentration but maximum PEO film thickness was limited by local burning if added Na2SiO3 concentration is higher than 0.5 M. Surface roughness of PEO film increased with increasing added Na2SiO3 concentration and appeared to be proportional to the PEO film thickness. PEO film hardness increased with increasing added Na2SiO3 concentration and reached a steady-state value of about 930 HV at more than 0.5 M of added Na2SiO3 concentration.
Epitaxial yttrium-stabilized HfO$_2$ thin films were deposited on p-type (100) Si substrates by pulsed laser deposition at a relatively lower substrate temperature of 550. Transmission electron microscopy observation revealed a fixed orientation relationship between the epitaxial film and Si; that is, (100)Si.(100)HfO$_2$ and [001]Si/[001]HfO$_2$. The film/Si interface is not atomically flat, suggesting possible interfacial reaction and diffusion, X-ray photoelectron spectrum analysis also revealed the interfacial reaction and diffusion evidenced by Hf silicate and Hf-Si bond formation at the interface. The epitaxial growth of the yttrium stabilized HfO$_2$ thin film on bare Si is via a direct growth mechanism without involoving the reaction between Hf atoms and SiO$_2$ layer. High-frequency capacitance-voltage measurement on an as-grown 40-A yttrium-stabilized HfO$_2$ epitaxial film yielded an dielectric constant of about 14 and equivalent oxide thickness to SiO$_2$ of 12 A. The leakage current density is 7.0${\times}$ 10e-2 A/$\textrm{cm}^2$ at 1V gate bias voltage.
In this study, the electrical and optical properties of $(SiO_2)_x(ZnO)_{100-x}$ (SZO) films prepared on the coming 7059 glass substrates by using rf-magnetron sputtering method are investigated. The deposition rate becomes maximum near 3 wt.% and gradually decreases when the $SiO_2$ content further increases. The growth rates of the SZO film with $SiO_2$ content of 3 wt.% is $4\;{\AA}/s$. We found that the average transmittance of all films is over 80% in the wavelength range above 500 nm. The optical band gap were decreased from 3.52 to 3.33 eV as an increase the deposition thickness. X-ray diffraction patterns showed that the film with a relatively low $SiO_2$ content (< 4 wt.%) is amorphous. SZO film with the $SiO_2$ contents of 2 wt.% showed the resistivity of about $3.8{\times}10^{-3}\;{\Omega}{\cdot}cm$. The sheet resistance decreases with increasing the heat treatment temperature.
To obtain high quality of $Ta_{2}O_{5}$ film, two dielectric layers of $Si_{3}N_{4}$ and $Ta_{2}O_{5}$ were subsequently formed on Si wafer. Silicon nitride films were thermally grown in 10 Torr ammonia ambient by R.F induced heating system. The thickness of thermally grown $Si_{3}N_{4}$ film was able to be controlled in the range of tens $\AA$ due to the self-limited growth property. $Ta_{2}O_{5}$ film of 200$\AA$ thickness was then deposited on the as-grown $Si_{3}N_{4}$ film about 25$\AA$ thickness by sputtering method and annealed at $900^{\circ}C$in $O_{2}$ ambient for 1hr. Stoichiometry film was prepared by the annealing in oxygen ambient. Despite the high temperature anneal process, silicon oxide layer was not grown at the interface of the layered films because of the oxidation barrier effect of Si$_{3}$N$_{4}$ film. The fabricated $Ta_{2}O_{5}$/$Si_{3}N_{4}$ film showed low leakage current less than several nA and high dielectric breakdown strength.
잉크젯 프린터 헤드용 기능성 막으로 많이 활용하고 있는 다층박막(SiO$_2$/poly-Si/SiN/SiO$_2$, 두께, 2.77 $\mu\textrm{m}$)과 다이아몬드 박막(두께, 1.6 $\mu\textrm{m}$)을 미소 외팔보($\mu$-CLB) 형태로 가공한 후 nanoindenter를 이용한 굽힘 시험 방법으로 탄성계수와 굽힘 강도를 측정하였으며 다층막을 이루는 박막 중 SiO$_2$ 박막(두께, 1 $\mu\textrm{m}$)과 SiN 박막(두께, 0.43 $\mu\textrm{m}$)의 탄성계수를 미소 외 팔보 굽힘 시험 방법과 nanoindentation 방법으로 측정한 후 그 결과를 비교하였다. 미소 외팔보 굽힘 시험방법으로 측정한 다층막의 탄성계수와 파괴강도는 외팔보의 폭이 18.5 $\mu\textrm{m}$에서 58.5 $\mu\textrm{m}$로 증가함에 따라 각각 68.08 ㎬과 2.495 ㎬에서 56.53 ㎬과 1.834 ㎬로 감소하였다. SiO$_2$ 박막의 탄성계수 측정값은 외팔보의 폭이 29.6$\mu\textrm{m}$ 와 59.5 $\mu\textrm{m}$ 범위에서 변하여도 영향을 받지 않고 68.16$\pm$0.942 ㎬이었으며, SiN 박막의 탄성계수는 215.45 ㎬이었다. Nanoindentation 방법으로 측정한 SiO$_2$ 박막과 SiN 박막의 탄성계수는 각각 98.78 ㎬, 219.38 ㎬이었다. 이 결과로부터 미소 외팔보 굽힘 시험방법으로 측정한 박막의 탄성계수가 nanoindentation 방법으로 측정한 탄성계수와 2% 미만의 차이를 보이며 일치함을 알 수 있었다.
This paper describes on the fabrication and characteristics of hot-film type micro-flowsensors integrated with Pt-RTD(resistance thermometer device) and micro-heater on the Si membrane in which MgO thin-film was used as medium layer in order to improve adhesion of Pt thin-film to SiO$_2$layer. The MgO layer improved adhesion of Pt thin-film to SiO$_2$layer without any chemical reactions to Pt thin-film under high annealing temperatures. Output voltages increased due to increase of heat-loss from sensor to external. The output voltage was 82 mV at $N_2$flow rate of 2000 sccm/min heating power of 1.2 W. The response time($\tau$:63%) was about 50 msec when input flow was stepinput
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.