• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.2
• /
• pp.73-77
• /
• 2021

Ga-doped ZnO thin films by RF magnetron sputtering process were synthesized according to the deposition conditions of O2 and Ar atmosphere gases, and rapid heat treatment (RTA) was performed at 600℃ in an N2 atmosphere. The thickness of the deposited ZnO : Ga thin film was measured, the crystal phase was investigated by XRD pattern analysis, and the microstructure of the thin film was observed by FE-SEM and AFM images. The intensity of the (002) plane of the X-ray diffraction pattern showed a significant difference depending on the deposition conditions of the thin films formed by O2 and Ar atmosphere gas types. In the case of a single thin f ilm doped with Ga under O2 conditions, a strong diffraction peak was observed. Under O2 and Ar conditions, in the case of a multilayer thin film with Ga doping, only a peak on the (002) plane with a somewhat weak intensity was shown. In the FE-SEM image, it was observed that the grain size of the surface of the thin film slightly increased as the thickness increased. In the case of a multilayer thin film with Ga doping under O2 and Ar atmosphere conditions, the specific resistance was 6.4 × 10-4 Ω·cm. In the case of a single thin film with Ga doping under O2 atmosphere conditions, the resistance of the thin film decreased. The resistance decreased as the thickness of the Ga-doped ZnO thin film increased to 2 ㎛, showing relatively a low specific resistance of 1.0 × 10-3 Ω·cm.

• Korean Journal of Materials Research
• /
• v.21 no.5
• /
• pp.273-276
• /
• 2011

Ultraviolet (UV) light emitting diodes (LEDs) were grown on a patterned n-type GaN substrate (PNS) with 200 nm silicon-di-oxide (SiO2) nano pattern diameter to improve the light output efficiency of the diodes. Wet etched self assembled indium tin oxide (ITO) nano clusters serve as a dry etching mask for converting the SiO2 layer grown on the n-GaN template into SiO2 nano patterns by inductively coupled plasma etching. PNS is obtained by n-GaN regrowth on the SiO2 nano patterns and UV-LEDs were fabricated using PNS as a template. Two UV-LEDs, a reference LED without PNS and a 200 nm PNS UV-LEDs were fabricated. Scanning Electron microscopy (SEM), Transmission Electron Microscopy (TEM), X-Ray Diffraction (XRD), Photoluminescence (PL) and Light output intensity- Input current- Voltage (L-I-V) characteristics were used to evaluate the ITO-$SiO_2$ nanopattern surface morphology, threading dislocation propagation, PNS crystalline property, PNS optical property and UVLED device performance respectively. The light out put intensity was enhanced by 1.6times@100mA for the LED grown on PNS compared to the reference LED with out PNS.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.6
• /
• pp.252-259
• /
• 2005

Single crystal $CuGaSe_2$ layers were grown on thoroughly etched semi-insulating CaAs(100) substrate at $450^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating $CuGaSe_2$ source at $610^{\circ}C$. The crystalline structure of the single crystal thin films was investigated by the photoluminescence (PL) and double crystal X-ray diffraction (DCXD). The carrier density and mobility of single crystal $CuGaSe_2$ thin films measured with Hall effect by Van der Pauw method are $4.87{\times}10^{17}cm^{-3}$ and $129cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CuGaSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=1.7998eV-(8.7489{\times}10^{-4}eV/K)T^2/(T+335K)$. The voltage, current density of maxiumun power, fill factor, and conversion, efficiency of $n-CdS/p-CuGaSe_2$, heterojunction solar cells under $80mW/cm^2$ illumination were found to be 0.41 V, $21.8mA/cm^2$, 0.75 and 11.17%, respectively.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.14 no.6
• /
• pp.818-823
• /
• 2014

A high-gain wideband low noise amplifier (LNA) using $0.25-{\mu}m$ Gallium-Nitride (GaN) MMIC technology is presented. The LNA shows 8 GHz to 15 GHz operation by a distributed amplifier architecture and high gain with an additional common source amplifier as a mid-stage. The measurement results show a flat gain of $25.1{\pm}0.8dB$ and input and output matching of -12 dB for all targeted frequencies. The measured minimum noise figure is 2.8 dB at 12.6 GHz and below 3.6 dB across all frequencies. It consumes 98 mA with a 10-V supply. By adjusting the gate voltage of the mid-stage common source amplifier, the overall gain is controlled stably from 13 dB to 24 dB with no significant variations of the input and output matching.

• Transactions on Electrical and Electronic Materials
• /
• v.11 no.2
• /
• pp.54-60
• /
• 2010

Polymer-assisted deposition is a chemical solution route to high quality thin films. In this process, the polymer controls the viscosity and binds metal ions, resulting in a homogeneous distribution of metal precursors in the solution and the formation of crack-free and uniform films after thermal treatment. We review our recent effort to epitaxially grow metal-nitride thin films, such as hexagonal GaN, cubic TiN, AlN, NbN, and VN, mixed-nitride $Ti_{1-x}Al_xN$, ternary nitrides tetragonal $SrTiN_2$, $BaZrN_2$, and $BaHfN_2$, hexagonal $FeMoN_2$, and nanocomposite TiN-$BaZrN_2$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.3
• /
• pp.122-126
• /
• 2003

In this study, $Zn_{0.86}Mn_{0.14}$Te epilayer of 0.7 $\mu\textrm{m}$-thickness was grown on GaAs(100) substrate by using hot wallepitaxy. GaAs(100) substrate was removed from $Zn_{0.86}Mn_{0.14}$Teepilayer by the selective etching solution. The crystal structure and the lattice constant of only Z $n_{0.86}$ M $n_{0.14}$Te epilayer were investigated to be zincblende and 6.140 $\AA$ from X-ray diffraction pattern, respectively. Mn composition x of $Zn_{1-x}Mn_x$Te epilayer was found to be 0.14 using this lattice constant and Vegard's law. The crystal quality of the epilayer was confirmed to be very good due to 256 arcsec-full-width at half-maximum of the double crystal rocking curve. The absorption spectra from the transmission ones were obtained to measure the band gap energy of $Zn_{0.86}Mn_{0.14}$Te epilayer from 300 K to 10 K. With the decreasing temperature,. strong absorption regions in the absorption spectra were shifted to higher energy side and the absorption peak meaning the free exciton formation appeared near the absorption edge. The band gap energy values of $Zn_{0.86}Mn_{0.14}$Te epilayer at 0 K and 300 K were found to be almost 2.4947 eV and 2.330 eV from the temperature dependence of the free exciton peak position energy of $Zn_{0.86}Mn_{0.14}$Te epilayer, respectively. The free exciton peak position energy of $Zn_{0.86}Mn_{0.14}$Te epilayer without GaAs substrate was larger 15.4 meV than photoluminescence peak position energy at 10 K. This energy difference between two peaks was analysed to be Stokes shift.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.99-99
• /
• 2013

In this talk, I will present two research works in progress, which are: i) mapping of piezoelectric polarization and associated charge density distribution in the heteroepitaxial InGaN/GaN multi-quantum well (MQW) structure of a light emitting diode (LED) by using inline electron holography and ii) in-situ observation of the polarization switching process of an ferroelectric Pb(Zr1-x,Tix)O3 (PZT) thin film capacitor under an applied electric field in transmission electron microscope (TEM). In the first part, I will show that strain as well as total charge density distributions can be mapped quantitatively across all the functional layers constituting a LED, including n-type GaN, InGaN/GaN MQWs, and p-type GaN with sub-nm spatial resolution (~0.8 nm) by using inline electron holography. The experimentally obtained strain maps were verified by comparison with finite element method simulations and confirmed that not only InGaN QWs (2.5 nm in thickness) but also GaN QBs (10 nm in thickness) in the MQW structure are strained complementary to accommodate the lattice misfit strain. Because of this complementary strain of GaN QBs, the strain gradient and also (piezoelectric) polarization gradient across the MQW changes more steeply than expected, resulting in more polarization charge density at the MQW interfaces than the typically expected value from the spontaneous polarization mismatch alone. By quantitative and comparative analysis of the total charge density map with the polarization charge map, we can clarify what extent of the polarization charges are compensated by the electrons supplied from the n-doped GaN QBs. Comparison with the simulated energy band diagrams with various screening parameters show that only 60% of the net polarization charges are compensated by the electrons from the GaN QBs, which results in the internal field of ~2.0 MV cm-1 across each pair of GaN/InGaN of the MQW structure. In the second part of my talk, I will present in-situ observations of the polarization switching process of a planar Ni/PZT/SrRuO3 capacitor using TEM. We observed the preferential, but asymmetric, nucleation and forward growth of switched c-domains at the PZT/electrode interfaces arising from the built-in electric field beneath each interface. The subsequent sideways growth was inhibited by the depolarization field due to the imperfect charge compensation at the counter electrode and preexisting a-domain walls, leading to asymmetric switching. It was found that the preexisting a-domains split into fine a- and c-domains constituting a $90^{\circ}$ stripe domain pattern during the $180^{\circ}$ polarization switching process, revealing that these domains also actively participated in the out-of-plane polarization switching. The real-time observations uncovered the origin of the switching asymmetry and further clarified the importance of charged domain walls and the interfaces with electrodes in the ferroelectric switching processes.

• Journal of the Korean Vacuum Society
• /
• v.22 no.6
• /
• pp.327-334
• /
• 2013

Long-wave infrared detectors using the type-II InAs/GaSb strained superlattice (T2SL) material system with the nBn structure were designed and fabricated. The band gap energy of the T2SL material was calculated as a function of the thickness of the InAs and GaSb layers by the Kronig-Penney model. Growth of the barrier material ($Al_{0.2}Ga_{0.8}Sb$) incorporated Te doping to reduce the dark current. The full width at half maximum (FWHM) of the $1^{st}$ satellite superlattice peak from the X-ray diffraction was around 45 arcsec. The cutoff wavelength of the fabricated device was ${\sim}10.2{\mu}m$ (0.12 eV) at 80 K while under an applied bias of -1.4 V. The measured activation energy of the device was ~0.128 eV. The dark current density was shown to be $1.0{\times}10^{-2}A/cm^2$ at 80 K and with a bias -1.5 V. The responsivity was 0.58 A/W at $7.5{\mu}m$ at 80 K and with a bias of -1.5 V.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.346.2-346.2
• /
• 2014

To use the GaN based light-emitting diodes (LEDs) as solid state lighting sources, the improvement of light extraction and internal quantum efficiency is essential factors for high brightness LEDs. In this study, we suggested the new materials system of a zinc tin oxide (ZTO) layer formed on blue LED epi-structures to improve the light extraction. ZTO is a representative n-type oxide material consisted of ZnO and SnO system. Moreover, ZTO is one of the promising oxide semiconductor material. Even though ZTO has higher chemical stability than IGZO owing to its SnO2 content this has high mobility and high reliability. After formation of ZTO layer on p-GaN layer by using the spin coating method, structural and optical properties are investigated. The x-ray diffraction (XRD) measurement results show the successful formation of ZTO. The photoluminescence (PL) and absorption spectrum shows that it has 3.6-4.1eV band gap. Finally, the light extraction properties of ZTO/LED chip using electroluminescence (EL) measurement were investigated. The experimental and theoretical analyses were simultaneously conducted.

• Journal of the Korean Ceramic Society
• /
• v.41 no.8
• /
• pp.573-577
• /
• 2004

We have synthesized a Eu$^{2＋}$-activated Sr$_3$MgSi$_2$ $O_{8}$ blue phosphor and investigated an attempt to develop blue LEDs by combining it with a InGaN blue LED chip (Len=405 nm). The InGaN-based Sr$_3$MgSi$_2$ $O_{8}$：Eu LED Lamp shows two bands at 405 nm and 460 nm. The 405 nm emission band is due to a radiative recombination from a InGaN active layer. This 405 nm emission was used as an optical transition of the Sr$_3$MgSi$_2$ $O_{8}$：Eu phosphor. The 460 m emission band is ascribed to a radiative recombination of Eu$^{2＋}$ impurity ions in the Sr$_3$MgSi$_2$ $O_{8}$ host matrix. As a consequence of a preparation of W blue LED Lamp using the Sr$_3$MgSi$_2$ $O_{8}$：Eu blue phosphor, the highest luminescence efficiency was obtained at the ration of epoxy/blue phosphor(1/0,202). At this time, the CIE chromaticity was x=0.1417 and y=0.0683.