• Korean Journal of Materials Research
• /
• v.12 no.11
• /
• pp.845-849
• /
• 2002

Alloys of $Fe_3$Al, $Fe_3$Al-6Cr, $Fe_3$Al-4Cr-1Mo, $Ni_3$Al, and $Ni_3$Al-2.8Cr were oxidized at $1000^{\circ}C$ in air, and the oxide scales formed were studied using XRD. SEM, EPMA, and TEM. The oxide scales that formed on $Fe_3$Al-based alloys consisted primarily of $\alpha$-$Al_2$$O_3$ containing a small amount of dissolved Fe and Cr ions, whereas those that formed on $Ni_3$Al-based alloys consisted primarily of $\alpha$-$Al_2$$O_3$, together with a small amount of $NiAl_2$$O_4$, NiO and dissolved Cr ions. For the entire alloys tested, nonadherent oxide scales formed, and voids were inevitably existed at the scale-matrix interface.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.1
• /
• pp.36-44
• /
• 1996

Fe-Cr-Al and Fe-Cr-Al-Hf alloys prepared either by arc melting or by single roll casting(melt spinning) were exposed to air isothermally at 900~$1100^{\circ}C$. Whisker-like alumina was observed on the surface of the specimens when oxidized at $900^{\circ}C$, but convoluted alumina above $1000^{\circ}C$. All the Hf-free specimens and Hf-added specimens produced by single roll casting formed only external scale mainly composed of $Al_2O_3$ after oxidation at 900~$1100^{\circ}C$ for 100 hours, but Hf-added specimen produced by arc melting formed Hf-rich internal oxides below the thin external $Al_2O_3$ scale except at $900^{\circ}C$. Most of the rapidly solidified Fe-Cr-Al alloys showed smaller weight gains than conventionally casted ones besides Hf-added one oxidized at $1100^{\circ}C$.

• Transactions of the Korean hydrogen and new energy society
• /
• v.23 no.6
• /
• pp.581-587
• /
• 2012

Thermal aging effect on NSR kinetics was studied over Pt/Co/Fe/Ba/$Al_2O_3$ catalyst. The amount of $NO_x$ uptake over Pt/Co/Fe/Ba/$Al_2O_3$ calcined at $400^{\circ}C$ increased with increasing NSR temperature from $200^{\circ}C$ to $400^{\circ}C$, where amount of $NO_x$ uptake is the highest at $400^{\circ}C$ with mol ratio of $NO_x$/Ba = 0.5. Thereafter, the amount of $NO_x$ uptake at $400^{\circ}C$ decreased with the higher calcination temperature, where Pt/Co/Fe/Ba/$Al_2O_3$ catalyst calcined at $700^{\circ}C$ showed an amount of $NO_x$ uptake with the mol ratio of $NO_x$/Ba=0.062. Result of XRD and NSR showed that Fe addition into Pt/Co/Fe/Ba/$Al_2O_3$ suppressed sintering of Pt crystallites and make $NO_x$ uptake larger, compared to no addition of Fe into Pt/Co/Fe/Ba/$Al_2O_3$ catalyst. From BET result, it was found that the change of specific surface area was relatively small by the thermal aging process. Therefore, it was found that the sintering of Pt crystallites caused the decrease of $NO_x$ uptake during NSR reaction and Fe played a role to suppress the sintering process of Pt crystallites caused by thermal aging.

• Korean Journal of Metals and Materials
• /
• v.50 no.6
• /
• pp.455-462
• /
• 2012

Al-Si coated boron steel and Zn coated DP steel plates were laser-welded to manufacture a Tailor Welded Blank (TWB) for a car body frame. Hot-stamping heat treatment ($900^{\circ}C$, 5 min) was applied to the TWB weld, and the microstructural change and transformation mechanism were investigated in the Al-rich area near the bond line of the Al-Si coated steel side. There was Al-rich area with a single phase, $Fe_3(Al,Si)$, which was transformed to ${\alpha}-Fe$ (Ferrite) after the heat treatment. It could be explained that the $Fe_3(Al,Si)$ phase was transformed to ${\alpha}-Fe$ during heat treatment at $900^{\circ}C$ for 5 min and the resultant ${\alpha}-Fe$ phase was not transformed by rapid cooling. Before the heat treatment, the microstructures around the $Fe_3(Al,Si)$ phase consisted of martensite, bainite and ${\alpha}-Fe$ while they were transformed to martensite and ${\delta}-Fe$ after the heat treatment. Due to the heat treatment, Al was diffused to the $Fe_3(Al,Si)$ and this resulted in an increase of Al content to 0.7 wt% around the Al-rich area. If the weld was held at $900^{\circ}C$ for 5 min it was transformed to a mixture of austenite (${\gamma}$) and ${\delta}-Fe$, and only ${\gamma}$ was transformed to the martensite by water cooling while the ${\delta}-Fe$ was remained unchanged.

• Korean Journal of Materials Research
• /
• v.8 no.12
• /
• pp.1127-1132
• /
• 1998

The possibilities of producing Al-10%Ti-4%Fe composites through in-situ processing and thus achieving mechanical property improvements over binary Al-10%Ti to a level or higher exhibited by PM SiC/A12124 composites were explored in this study. The microstructure of in-situ processed Al-10%Ti-4%Fe composites was similar to that of Al matrix composites reinforced with discontinuous SiC particulates(SiC/A12124) and significant enhancements in elastic modulus, tensile strength and wear resistance were observed as compared to Al-10%Ti alloy. These results can be attributed to the in-situ formed Al. Fe by third element addition, leading to additional dispersion strengthening effect over $Al_3Ti$ phase reinforcement in Al-Ti system.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.2
• /
• pp.120-131
• /
• 1996

In order to improve the mechanical properties and the high temperature oxidation resistance, aluminizing was carried out at a temperature range between $850^{\circ}C$ and $1050^{\circ}C$. The pack cementation process was used to produce uniform layer. After each treatment, the microhardness and the characteristics of high temperature oxidation were tested to evaluate the properties of the aluminide layer. The aluminide layer consisted of FeAl above $1000^{\circ}C$, and $Fe_2Al_5$ below $900^{\circ}C$, and the mixed phase of FeAl and $Fe_2Al_5$ between 90$0^{\circ}C$ and $1000^{\circ}C$ in case of the mixture powder consisted of 5%Al+5%$NH_4Cl+90%AL_2O_3$. The microhardness of $Fe_2Al_5$ was obtained much as the twice as that of FeAl. As the aluminizing temperature and time increased, the thickness of aluminide increased. After aluminizing, the high temperature oxidation resistance was remarkably improved. The high temperature oxidation resistance of FeAl was superior to the resistance of high temperature oxidation of $Fe_2Al_5$.

• Journal of the Korean Ceramic Society
• /
• v.19 no.4
• /
• pp.309-315
• /
• 1982

$FeAl_2O_4$ was formed from the starting material of $Fe_2O_3$ and $Al_2O_3$ by controlling the oxygen partial pressure using $H_2-CO_2$ gas mixture, over the temperature range of 800~120$0^{\circ}C$. The formation mechanism of $FeAl_2O_4$ was found to be a second order chemical reaction, and the activation energy of formation was observed as 39.97 kcal/mole. Vaporization behavior of $FeAl_2O_4$ under $CO_2$ atmosphere was observed over the temperature range of 800~120$0^{\circ}C$. $FeAl_2O_4$ was vaporized by a second order chemical reaction and the activation energy was found to be 21.8kcal/mole. Electrical conductivity of $FeAl_2O_4$ was also measured.

• Advanced Composite Materials
• /
• v.18 no.4
• /
• pp.351-364
• /
• 2009

The thermal stability and elevated temperature mechanical properties of $SiC_P$/Al-11.7Fe-1.3V-1.7Si (Al-11.7Fe-1.3V-1.7Si reinforced with SiC particulates) composites sheets prepared by spray deposition (SD) $\rightarrow$ hot pressing $\rightarrow$ rolling process were investigated. The experimental results showed that the composite possessed high ${\sigma}_b$ (elevated temperature tensile strength), for instance, ${\sigma}_b$ was 315.8 MPa, which was tested at $315^{\circ}C$, meanwhile the figure was 232.6 MPa tested at $400^{\circ}C$, and the elongations were 2.5% and 1.4%, respectively. Furthermore, the composite sheets exhibited excellent thermal stability: the hardness showed no significant decline after annealing at $550^{\circ}C$ for 200 h or at $600^{\circ}C$ for 10 h. The good elevated temperature mechanical properties and excellent thermal stability should mainly be attributed to the formation of spherical ${\alpha}-Al_{12}(Fe,\;V)_3Si$ dispersed phase particulates in the aluminum matrix. Furthermore, the addition of SiC particles into the alloy is another important factor, which the following properties are responsible for. The resultant Si of the reaction between Al matrix and SiC particles diffused into Al matrix can stabilize ${\alpha}-Al_{12}(Fe,\;V)_3Si$ dispersed phase; in addition, the interface (Si layer) improved the wettability of Al/$SiC_P$, hence, elevated the bonding between them. Furthermore, the fine $Al_4C_3$ phase also strengthened the matrix as a dispersion-strengthened phase. Meanwhile, load is transferred from Al matrix to SiC particles, which increased the cooling rate of the melt droplets and improved the solution strengthening and dispersion strengthening.

• Journal of Powder Materials
• /
• v.12 no.1
• /
• pp.43-50
• /
• 2005

Mechanical alloying using high-energy ball mill and subsequent spark plasma sintering (SPS) process was applied to Al-Fe-Cr and Al-Fe-Mo powder mixture to investigate effects of Cr and Mo addition on thermal stability of Al-Fe, and thereby to enhance its thermal stability up to $500^{\circC}$. Various analytical techniques including micro-Vickers hardness test, SEM, TEM, X-ray diffractometry and corrosion test were carried out. It was found that addition of Cr and Mo to Al-Fe system played a role of grain growth inhibitor of matrix Al and some precipitates such as $Al_3Fe$ during SPS and subsequent heat treatment. The inhibition of grain growth resulted in increased Vickers hardness and thermal stability up to $500^{\circC}$ comparing to those of Al-Fe alloy system.

• Journal of Magnetics
• /
• v.10 no.3
• /
• pp.99-102
• /
• 2005

Modification in exchange bias of a NiFe/FeMn/NiFe trilayer, on introduction of a nonmagnetic Al layer at the top FeMn/NiFe interface, is investigated in multilayers prepared by rf magnetron sputtering. The introduction of Al layer leads to vanishing of bias of the top NiFe layer. But the bias for the bottom NiFe layer increases steadily with increasing Al layer thickness and attains bias (230 Oe) which is greater than that of the trilayer without the Al layer (150 Oe). When the top NiFe layer thickness is varied, exchange bias has highest value at 12 nm thickness for 1 nm thicknes of Al layer. Ion beam etching of the top NiFe layer also leads to an enhancement in bias for the bottom NiFe layer.