• 한국자기학회지
• /
• 제24권2호
• /
• pp.51-55
• /
• 2014

$Fe_3O_4$ 나노입자는 hot-injection 제조법에 의해 제조되었으며 반응물질의 injection time에 변화를 주었다. 격자구조는 x-ray diffraction(XRD) 측정을 통해 Fd-3m 공간군을 갖는 cubic inverse spinel 구조로 분석되었으며, $Fe_3O_4$ 나노입자의 형상은 high-resolution transmission electron microscope(HR-TEM)으로 분석하였다. 반응물질을 각각 0.5분, 60분인 젝션시 각각 7.63 nm, 21.73 nm의 $Fe_3O_4$ 나노입자 사이즈를 얻을 수 있었다. $Fe_3O_4$ 나노입자의 자기적 특성은 다양한 온도에서 vibrating sample magnetometer(VSM)과 M$\ddot{o}$ssbauer spectroscopy로 측정하였으며, hyperthermia 측정을 통해 반응물질의 injection time이 60분일 때 50 kHz의 250 Oe에서 $Fe_3O_4$ 나노입자 파우더의 온도가 약 $120^{\circ}C$임을 관측할 수 있었다.

• Journal of Magnetics
• /
• 제10권3호
• /
• pp.84-88
• /
• 2005

Nanoparticles $Ni_{0.7}Zn_{0.3}Fe_2O_4$ is fabricated by a sol-gel method. The magnetic and structural properties of powders were investigated with XRD, SEM, $M\ddot{o}ssbauer$ spectroscopy, and VSM. $Ni_{0.7}Zn_{0.3}Fe_2O_4$ powders annealed at $300^{\circ}C$ have a spinel structure and behaved superparamagnetically. The estimated size of $Ni_{0.7}Zn_{0.3}Fe_2O_4$ nanoparticle is about 11 nm. $Ni_{0.7}Zn_{0.3}Fe_2O_4$ annealed at 400 and $500^{\circ}C$ has a typical spinel structure and is ferrimagnetic in nature. The isomer shifts indicate that the iron ions were ferric at the tetrahedral (A) and the octahedral (B). Blocking temperature $(T_B)\;of\;Ni_{0.7}Zn_{0.3}Fe_2O_4$ nanoparticle is about 260 K. The magnetic anisotropy constant of $Ni_{0.7}Zn_{0.3}Fe_2O_4$ annealed $300^{\circ}C$ were calculated to be $1.7X10^6\;ergs/cm^3$. Also, temperature of the sample increased up to $43^{\circ}C$ within 7 minutes under AC magnetic field of 7 MHz.

• 한국자기학회지
• /
• 제20권5호
• /
• pp.196-200
• /
• 2010

Sol-gel 법을 이용하여 초상자성 나노 입자 $\gamma-Fe_2O_3$를 제조하였다. 입자의 크기 및 자기적 성질을 x-선 회절법(XRD), Mossbauer 분광법, 진동시료 자화율 측정기(VSM)를 이용하여 연구하였다. x-선 회절 실험결과 150 이상에서 열처리한 입자는 순수한 cubic spinel 구조를 가지며, $150^{\circ}C$에서 열처리한 $\gamma-Fe_2O_3$의 평균입자 크기는 7 nm로다. Mossbauer 분광실험으로 $150^{\circ}C$에서 열처리한 입자는 상온에서 초상자성의 특성을 가지고 있음을 알 수 있었으며 초상자성의 특성을 잃어버리는 차단온도 $T_B$는 $183^{\circ}C$로 결정하였으며, 또한 자기이방성상수 K = $1.6{\times}10^6erg/cm^3$의 값을 얻었다. $150^{\circ}C$에서 열처리한 $\gamma-Fe_2O_3$의 VSM 측정 결과로부터 $150^{\circ}C$에서 열처리한 $\gamma-Fe_2O_3$의 경우 상온에서 초상자성의 특성을 확인 할 수 있었다.

• 한국자기학회지
• /
• 제16권2호
• /
• pp.144-148
• /
• 2006

초상자성 나노입자의 제작이 가능한 sol-gel법을 이용하여 초상자성 나노입자 $CoGa_{0.1}Fe_{1.9}O_4$를 제조하여 입자의 크기 및 자기적 성질을 x-선 회절법(XRD), 주사전자현미경(SEM) 측정과 $M\ddot{o}ssbauer$ 분광법, 진동시료 자화율 측정기(VSM)를 이용하여 연구하였다. SEM및 x-선 회절실험으로부터 250"C 이상에서 열처리한 입자가 순순한 cubic spinel구조를 가지며, $250^{\circ}C$에서 열처리한 $CoGa_{0.1}Fe_{1.9}O_4$의 평균입자 크기는 10 nm로 나타났으며 균일한 구형상 임을 알 수 있었다. VSM 측정 결과로부터 $250^{\circ}C$에서 열처리한 $CoGa_{0.1}Fe_{1.9}O_4$의 경우 상온에서 초상자성의 특성을 나타냈다. $M\ddot{o}ssbauer$ 분광실험으로 $250^{\circ}C$에서 열처리한 입자가 상온에서 초상자성의 특성을 가지고 있음을 확인할 수 있었으며 초상자성의 특성을 잃어버리는 차단온도 $T_B$는 250 K로 결정하였으며, 또한 자기이방성상수 $K=3.0X10^5\;ergs/cm^3$의 값을 얻었다 $250^{\circ}C$에서 열처리한$CoGa_{0.1}Fe_{1.9}O_4$의 경우 4.2K에서의 초미세 자기장은 $H_{hf}(B)=518,\;H_{hf}(A)=486\;kOe$이며, 이성질체 이동값은 $\delta_B=0.34$, $\delta_A=0.30$ 이 값은 A, B자리 모두 $Fe^{3+}$에 해당된다.

• Bulletin of the Korean Chemical Society
• /
• 제27권2호
• /
• pp.237-242
• /
• 2006

$Fe_3O_4$ and $CoFe_2O_4$ magnetic nanoparticles have been synthesized successfully in aqueous solution and coated with oleic acid. The solid and organic solution of the synthesized nanoparticles was obtained. Self-assembled monolayer films were formed using organic solution of these nanoparticles. The crystal sizes determined by Debye-Scherre equation with XRD data were found close to the particle sizes calculated from TEM images, and this indicates that the synthesized particles are nanocrystalline. Especially, EDS, ED, FT-IR, TGA/DTA and DSC were used to characterize the nanoparticles and the oleic acid adsorption, and it was found that oleic acid molecule on the $Fe_3O_4$ nanoparticle is a bilayer adsorption, while that on $CoFe_2O_4$ nanoparticle is single layer adsorption. The superparamagnetic behavior of the nanoparticles was documented by the hysteresis loop measured at 300 K.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2001년도 춘계학술발표강연 및 논문개요집
• /
• pp.29-29
• /
• 2001

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 추계총회,초청강연,특별강연,연구발표회
• /
• pp.37.1-37
• /
• 2000

• Journal of Magnetics
• /
• 제10권1호
• /
• pp.5-9
• /
• 2005

Nanoparticles $Ni_{0.9}Zn_{0.1}Fe_2O_4$ is fabricated by a sol-gel method. The magnetic and structural properties of powders were investigated with XRD, SEM, Mossbauer spectroscopy, and VSM. $Ni_{0.9}Zn_{0.1}Fe_2O_4$ powders annealed at $300{^{\circ}C}$ have a spinel structure and behaved superparamagnetically. The estimated size of $Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticle is about 10 nm. The hyperfine fields at 13 K for the A and B patterns are found to be 533 and 507 kOe, respectively. The ZFC curves are rounded at the blocking temperature ($T_B$)and show a paramagnetic-like behavior above $T_B$. $T_B$ of $Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticle is about 250 K. Nanoparticles $Ni_{0.9}Zn_{0.1}Fe_2O_4$ annealed at 400 and $500{^{\circ}C}$ have a typical spinel structure and is ferrimagnetic in nature. The isomer shifts indicate that the iron ions were ferric at the tetrahedral (A) and the octahedral (B). The saturation magnetization of nanoparticles $Ni_{0.9}Zn_{0.1}Fe_2O_4$ annealed at 400 and $500{^{\circ}C}$ are 40 and 43 emu/g, respectively. The magnetic anisotropy constant of $Ni_{0.9}Zn_{0.1}Fe_2O_4$ annealed at $300{^{\circ}C}$ were calculated to be 1.6 ${\times}$ $10^6$ ergs/$cm^3$.

• 폴리머
• /
• 제38권2호
• /
• pp.150-155
• /
• 2014

Polycaprolactone(PCL)은 생분해성 고분자로 인장강도, 신장률, 충격강도 등의 기계적 물성이 우수하다. $TiO_2$ (titanium dioxide) nanoparticle은 친수성으로 밀도가 높고 생체적합성이 우수하다. 본 연구에서는 PCL과 $TiO_2$(titanium dioxide) nanoparticle을 이용하여 salt-leaching방법으로 3차원 다공성 지지체를 제작하였다. 제작한 지지체를 FESEM, FTIR, TGA, 압축강도 측정 등을 통해 물성을 분석하였다. $TiO_2$ nanoparticle에 의해 물흡수도와 팽윤도는 감소하였으나 압축강도는 증가하였다. CCK-8 assay를 통해 세포의 증식률을 확인한 결과, $TiO_2$ nanoparticle에 의한 세포 독성은 없는 것으로 확인되었다. 이러한 연구결과는 PCL/$TiO_2$ nanoparticle 지지체의 생체재료로 사용가능성을 제시하였다.

• 한국자기학회지
• /
• 제19권2호
• /
• pp.57-61
• /
• 2009

졸-겔법을 이용하여 나노 입자 $MnFe_2O_4$를 제조하여 x-선 회절법(XRD) 및 주사전자현미경(SEM) 측정을 통하여 결정학적 특성 및 입자의 크기를 연구하였으며, 제조된 나노입자의 초상자성 성질을 $M{\ddot{o}}ssbauer$ 분광법, 진동시료 자화율 측정기(VSM)를 이용하여 연구하였다. XRD 및 SEM의 측정으로부터 열처리 온도가 $250^{\circ}C$에서 순수한 큐빅 스피넬 구조를 가지며, 이 때 열처리한 시료의 평균입자 크기는 17 nm 임을 알 수 있었다. $M{\ddot{o}}ssbauer$ 분광실험으로 $250^{\circ}C$에서 열처리한 입자가 상온에서 초상자성의 특성을 가지고 있음을 알 수 있었으며, 4.2 K에서의 초미세자기장은 $H_{hf}$(B-자리) = 508, $H_{hf}$(A-자리) = 475 kOe, 이성질체 이동값은 0.35(B-자리), 0.33 mm/s(A-자리)로 분석되었다. 상온에서 초상자성 특성을 갖는 $MnFe_2O_4$의 차단온도 $T_B$는 120 K로 결정하였으며, 자기이방성상수 $K\;=\;4.9{\times}10^5\;erg/cm^3$의 값을 얻었다. 그러나 $400^{\circ}C$ 이상에서 열처리한 경우는 준강자성의 특징을 나타냈다.