• Korean Journal of Materials Research
• /
• v.10 no.3
• /
• pp.199-203
• /
• 2000

$Ta_2_O5$ and $Sr_0.8Bi_2.4Ta_2O_9$ films were deposited on p-type Si(100) substrates by a rf-magnetron sputtering and the metal organic decomposition (MOD), respectively.The electrical characteristics of the $Pt/SBT/Ta_2O_5/Si$ structure were obtained as the functions of $O_2$ gas flow ratio during the $Ta_2_O5$ sputtering and $Ta_2_O5$ thickness. And to certify the role of $Ta_2_O5$ as a buffer layer, the electrical characteristics of $Pt/SBT/Ta_2O_5/Si$ were compared. $Pt/SBT/Ta_2O_5/Si$ capacitor with 20% $O_2$ gas flow ratio during the $Ta_2_O5$ sputtering did now show typical C-V curve of metal/ferroelectric/insulator/semiconductor (MFIS) structure. The capacitor with 20% $O_2$ gas flow ratio during the $Ta_2_O5$ sputtering had the largest memory window. And the memory window was decreased as the $Ta_2_O5$ gas flow ratio during the $Ta_2_O5$ sputtering was increased to 40%, 60%. In the C-V characteristics of the $Pt/SBT/Ta_2O_5/Si$ capacitors with the different $Ta_2_O5$ thickness, the capacitor with 26nm thickness of $Ta_2_O5$ had the largest memory window. The C-V and leakage current characteristics of the Pt/SBT/Si structure were worse than those of $Pt/SBT/Ta_2O_5/Si$ structure. These results and Auger electron spectroscopy (AES) measurement showed that $Ta_2_O5$ films as a buffer layer tool a role to prevent from the formation of intermediate phase and interdiffusion between SBT and Si.

• Applied Chemistry for Engineering
• /
• v.9 no.6
• /
• pp.878-883
• /
• 1998

The methane combustion reaction was conducted over Pb-ZSM-5 catalysts. ZSM-5 synthesized at low temperature and atomospheric pressure was used as a support. The change of methane conversion with $SiO_2/Al_2O_3$ molar ratio was tested. The methane conversions of the synthesized Pb-ZSM-5 catalyst was compared with those of a commercial Pd-ZSM-5(PQ Co.) and $PdO/{\gamma}-Al_2O_3$. The methane conversion increased with the decrease in $SiO_2/Al_2O_3$ molar ratio. The combustion rate of methane also increased with the decrease in $SiO_2/Al_2O_3$ molar ratio. The synthesized Pb-ZSM-5 showed better methane conversion than that of the commercial one. It is found that a crucial factor in methane combustion reaction is oxygen adsorption strength on the catalysts.

• Journal of the Korean Ceramic Society
• /
• v.30 no.6
• /
• pp.433-440
• /
• 1993

The bioactivity of glasses in the CaO-SiO2 system and CaO-P2O5-SiO2 system with less than 10mol% of P2O5 was investigated by in vitro test in simulated body flood(SBF). The formation of Ca.P film and hydroxyapatite on the surface of glasses after in vitro test was analysed by X-ray photoelectron spectoscopy (XPS), fourier transform infrared reflection spectroscopy (FT-IRRS), energy dispersive X-ray spectroscopy (EDS), and scanning electron microscopy (SEM) observation. In the early stage of Ca.P film formation after in vitro test for CaO-SiO2 and CaO-P2O5-SiO2 glasses, the rate of Ca.P film formation on the surface of the glasses was dependent of structural parameter (Y) evaluated from the glass composition. First, in the case of the glasses having Y value below 2, Ca.P film and SiO2-rich layer were formed simultaneously, and there were no differences of the rate of Ca.P film formation in terms of the Y values. Second, in the case of the glasses having Y value above 2, the SiO2-rich layer was formed, and then Ca.P.Si mixed layer was formed in the silica gel structure of the SiO2-rich layer, and finally the Ca.P film on the surface of SiO2-rich layer. The rate of Ca.P film formation delayed as the Y values increased. The rate of hydroxyapatite formation of glasses (the rate of transformation from Ca.P film to hydroxyapatite) seems to be propotional to the rate of Ca.P film formation and Y value. The rate of hydroxyapatite formation of glasses belonging to the second group was delayed as structural parameter increased, and the hydroxyapatite crystal showed spherical growth in the early reaction stage, and then showed silkworm-like linear growth as the reaction time increased.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.8
• /
• pp.14-18
• /
• 2018

Generally. the Ohmic's law is an important factor to increase the conductivity in a micro device. So it is also known that the Ohmic contact in a semiconductor device is import. The PN junction as a structure of semiconductor involves the depletion layer, and this depletion layer induces the non linear electrical properties and also makes the Schottky contact as an intrinsic characteristics of semiconductor. To research the conduction effect of insulators in the semiconductor device, $SiO_2$ thin film and $V_2O_5/SiO_2$ thin film were researched by using the current-voltage system. In the nano electro-magnetic system, the $SiO_2$ thin film as a insulator had the non linear Schottky contact, and the as deposited $V_2O_5$ thin film had the linear Ohmic contact owing to the $SiO_2$ thin film with superior insulator's properties, which decreases the leakage current. In the positive voltage, the capacitance of $SiO_2$ thin film was very low, but that of $V_2O_5$ thin film increased with increasing the voltage. In the normal electric field system, it was confirmed that the conductivity of $V_2O_5$ thin film was increased by the effect of $SiO_2$ thin film. It was confirmed that the Schottky contact of semiconductors enhanced the performance of electrical properties to increased the conductivity.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.5
• /
• pp.467-471
• /
• 2016

In order to investigate the Na gettering, PSG/$SiO_2$/Al-1%Si multilevel thin films were fabricated. DC magnetron sputter techniques and APCVD (atmosphere pressure chemical vapor deposition) were utilized for the deposition of Al-1%Si thin films and PSG/$SiO_2$ passivations, respectively. Heat treatment was carried out at $300^{\circ}C$ for 5 h in air. SIMS (secondary ion mass spectrometry) depth profiling and XPS (X-ray Photoelectron Spectroscopy) analysis were used to determine the distribution and binding energies of Na, Al, Si, O, P and other elements throughout the PSG/$SiO_2$/Al-1%Si multilevel thin films. Na peaks were mainly observed at the the PSG/$SiO_2$ interface and at the $SiO_2$/Al-1%Si interfaces. Na impurity gettering in PSG/$SiO_2$/Al-1%Si multilevel thin films is considered to be caused by a segregation type of gettering. The chemical state of Si and O elements in PSG passivation appears to be $SiO_2$.

• Journal of the Korean Ceramic Society
• /
• v.31 no.11
• /
• pp.1330-1336
• /
• 1994

Ta2O5 films were deposited on the p-Si(100) substrates by ECR-PECVD and annealed in O2 atmosphere. The thicknesses of Ta2O5/SiO2 layers were measured by an ellipsometer and a cross-sectional TEM. Annealing in O2 atmosphere enhanced the stoichiometry of the Ta2O5 film and reduced the impurity carbon content. Ta2O5 films were crystallized at the annealing temperatures above 75$0^{\circ}C$. The best leakage current characteristics and the maximum dielectric constant of Ta2O5/SiO2 film capacitor were observed in the specimen annealed at $700^{\circ}C$ and 75$0^{\circ}C$, respectively. The flat band voltage of the Al/Ta2O5/SiO2/p-Si MOS capacitor was varied in the range of -0.6~-1.6 V with the annealing temperature. The conduction mechanism in the Ta2O5 film, the variation of the effective oxide charge density with the annealing temperature, and the effective electric field distribution in the Ta2O5/SiO2 double layer were also discussed.

• Applied Chemistry for Engineering
• /
• v.4 no.2
• /
• pp.291-299
• /
• 1993

Hydrothermal synthesis of 1.13nm tobermorite was performed to obtain the mixing ratio of raw materials, the optimum reaction time and the effect of aluminum in two systems, $CaO-SiO_2-H_2O$ and cement sludge-$SiO_2-H_2O$. 1.13nm tobermorite($5CaO{\cdot}6SiO_2{\cdot}5H_2O:C_5S_6H_5$) was synthesized excellently from $CaO-SiO_2-H_2O$ system on each mole ratio (0.4, 0.8) of $CaO/SiO_2$ at $180^{\circ}C$. But a tobermorite crystals had a sign of crystal conversion after 6 hours of reaction times in the case of $CaO/SiO_2=0.4$ and 4 hours of reaction time in the case of $CaO/SiO_2=0.8$. However, a tobermorite synthesized from cement sludge wastes did not show the crystal conversion on each mole ratio(0.4, 0.8) of $CaO/SiO_2$ within 10 hours of reaction times. It is considered that aluminum ions dissolved from cement sludge wastes retarded the recrystallization of tobermorite. This role of aluminum ion was confirmed in $CaO-SiO_2-H_2O+Al$ powder system. According as added amount of Al powder was increased from 0.8% to 3.0%, the crystal had a highly flatter and larger shape. Recrvstallization was not detected within the same reaction times when aluminum was added.

• Journal of the Korean Vacuum Society
• /
• v.7 no.1
• /
• pp.17-23
• /
• 1998

$Pb(Fe_{0.5}Nb_{0.5}O_3(PFN)$ thin films were prepared by rf magnetron co-sputtering method on $SiO_2/Si$, ITO/glass, and $Pt/Ti/SiO_2/Si$ substrates and post-annealed at the $N_2$ atmosphere by RTA(rapid thermal annerling). The degree of crystallinity of PFN films was identified on various substrates. Electrical properties of PFN films was characterized for $Pt/PFN/Pt/Ti/SiO_2/Si$ structure. The composition of PFN films was estimated by EPMA (electron probe micro analysis). PFN films would be crystallized better to perovskite phase on ITO/glass substrate than $SiO_2/Si$ substrate. This may be induced by the deformation of Pb deficient pyrochlore phase due to Pb diffusion into $SiO_2/Si$ substrate. PFN films on $Pt/Ti/SiO_2/Si$ substrate. PFN films with 5-10% Pb excess were crystallized to perovskite phase from $500^{\circ}C$ temperature. In summary, we show that Pb composition and annealing temperature were critically influenced on crystallinity to perovskite phase. When PFN film with 17% Pb excess was annealed at $600^{\circ}C$ at the $N_2$ atmosphere for 300kV/cm and 88. Its remnant polarization coercive field $2.0 MC/cm^2$ and 144kV/cm, respectively.

• Journal of the Korean Vacuum Society
• /
• v.20 no.5
• /
• pp.381-386
• /
• 2011

We fabricated the ZnO (zinc oxide)/$SiO_2$ (silicon dioxide) branch hierarchical nanostructures by the e-beam evaporation of $SiO_2$ onto the surface of the electrochemically grown ZnO nanorods on Si substrate, which leads to the self-assembled $SiO_2$ nanorods by oblique angle deposition between vapor flux and vertically aligned ZnO nanorods. In order to investigate the effects of $SiO_2$ deposition on the morphology and optical property of ZnO/$SiO_2$ branch hierarchical nanostructures, the evaporation time of $SiO_2$ was varied under a fixed deposition rate of 0.5 nm/s. The vertically aligned ZnO nanorods on Si substrate exhibited a low reflectance of <10% in the wavelength range of 300~535 nm. For ZnO/$SiO_2$ branch hierarchical nanostructures at 100 s of evaporation time of $SiO_2$, the more improved antireflective property was achieved. From these results, ZnO/$SiO_2$ branch hierarchical nanostructures are very promising for optoelectronic and photovoltaic device applications.

• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.2
• /
• pp.35-40
• /
• 2010

The variations of dielectric properties of $Ta_2O_5-SiO_2$ continuous composition spread thin films prepared by off-axis radio-frequency magnetron sputtering were investigated. The dielectric maps of dielectric constant and loss were plotted via 1500 micron-step measuring. The specific points showing superior dielectric properties of high dielectric constant (k~19.5) and loss (tan${\delta}$<0.05) at 1 MHz were found in area of the distance of 16 mm and 22 mm apart from $SiO_2$ side in $75{\times}25mm^2$ sized Pt/Ti/$SiO_2$/Si(100) substrates.