The present investigation is concerned with the degradation characteristics of cast stainless steel(CF8M), exposed to the $\sigma$-phase degradation at $700^{\circ}C$. In the present paper, the degradation of CF8 M at $700^{\circ}C$ is evaluated by a non-destructive test, DL-EPR(double loop electrochemical potentiokinetic reactivation). The surface of specimens is observed by using scanning electron microscopy after DL-EPR test. Also. chromium contents of matrix, grain boundary and ferrite phase are analyzed by electron probe X-ray micro analyzer. Through the experiments, the following results are obtained 1) The degree of sensitization(DOS) of CF8M aged up to 15hr at $700^{\circ}C$ is increased with acing time while that is decreased with aging time from 15hr to 150hr. 2) The impact energy decreases with increase of $\sigma$-phase while DOS increases with $\sigma$-phase until aging time reaches to 15hr. After the aging time. 15hr, the $\sigma$-phase and the rate of impact energy with respect to aging time decreases. Therefore the degradation behavior of the CF8M can be evaluated by comparing SEM micrographs and the value of DOS.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.11 no.8
• /
• pp.1558-1563
• /
• 2007

In this paper, phase-locked loop (PLL) of a combinational architecture consisting of an adaptive bandwidth and fractional-N is presented to improve performances and reduce the order of ${\Delta}{\Sigma}$ modulator while maintaining equivalent or better performance with fast locking. The architecture of adaptive bandwidth PLL was simulated by HSPICE using 0.35m CMOS parameters. The behavioral simulation of the proposed adaptive bandwidth fractional-N PLL with a ${\Delta}{\Sigma}$ modulator was carried out by using MatLab to determine if the architecture could achieve the objectives. The HSPICE simulation showed that this type of PLL was able to fast locking, and reduce fractional spurs about 20dB.

• Korean Journal of Metals and Materials
• /
• v.49 no.3
• /
• pp.197-202
• /
• 2011

This study was carried out to investigate the precipitation behavior of ${\chi}$ phase and effect of ${\chi}-phase$ which precipitated at the initial stage of aging on mechanical properties of 25%Cr-7%Ni-4%Mo-0.2%N super duplex stainless steel. ${\chi}-phase$ was precipitated mainly at the interface of ferrite / austenite phases and inside of the ferrite phase at the initial stage of aging, and it was transformed into ${\sigma}-phase$ with an increase of aging time. The ferrite phase was decomposed into new $austenite({\gamma}_2)phase$ and ${\sigma}-phase$ by aging treatment. The hardness and tensile strength of the initial stage of aging when ${\chi}-phase$ was precipitated did not changed considerably, while elongation rapidly decreased. Accordingly, it is considered that ${\chi}-phase$ didn't affect the hardness and strength significantly, but it affected the elongation.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.05a
• /
• pp.13-14
• /
• 1998

• Corrosion Science and Technology
• /
• v.5 no.6
• /
• pp.189-195
• /
• 2006

Effects of tungsten (W) on the precipitation kinetics of secondary phases and the associated resistance to pitting corrosion of 25%Cr duplex stainless steels were investigated through microstructural and electrochemical noise analyses. With the partial substitution of W for Mo in duplex stainless steel, the potential and current noises of the alloy were significantly decreased in chloride solution due to retardation of the ${\sigma}$ phase precipitation. The preferential precipitation of the $\chi$ phase in the W-containing alloy during the early period of aging contributed to retarding the precipitation of the $\sigma$ phase by depleting W and Mo along grain boundaries. In addition, the retardation of the nucleation and growth of the $\sigma$ phase in the W-containing alloy appears to be attributed to the inherently low diffusivity of W compared with that of Mo.

• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.6
• /
• pp.293-299
• /
• 2013

A specimen of weld metal was prepared by GTA welding with weld wire of super duplex stainless steel. Aging treatment was conducted for the sample at the temperature range of 700 to $900^{\circ}C$ for 5 to 300 minutes. The effect of volume fraction of ${\sigma}$-phase to intergranular corrosion of weld metal has been investigated and the results were derived as follows. The volume fraction of ${\sigma}$ phase tends to increase with an increase of aging temperature and time and intergranular corrosion of weld metal was increased by an increase of ${\sigma}$ phase. Degree of sensitization representing intergranular corrosion was found to tend to increase with an increase of aging time at 700 to $800^{\circ}C$, while it decreased by an increase of aging time at $900^{\circ}C$.

• Corrosion Science and Technology
• /
• v.20 no.6
• /
• pp.426-434
• /
• 2021

The effect of two different annealing temperatures on the level of the second phase precipitated in the microstructure and the corrosion behaviors of super austenitic stainless steel were examined. The sample annealed at a higher temperature had a significantly lower fraction of the sigma phase enriched with Cr and Mo elements, showing more stable passivity behavior during the potentiodynamic polarization measurement. However, after the welding process with Inconel-type welding material, severe corrosion damage along the interface between the base metal and the weld metal was observed regardless of the annealing temperature. This was closely associated with the precipitation of the fine sigma phase with a high Mo concentration in the unmixed zone (UMZ) during the welding process, leading to the local depletion of Mo concentrations around the sigma phase. On the other hand, the fraction of the newly precipitated fine sigma phase in the UMZ was greatly reduced by post-weld heat treatment (PWHT), and the corrosion resistance was greatly improved. Based on the results, it is proposed that the alloy composition of welding materials and PWHT conditions should be further optimized to ensure the superior corrosion resistance of welded super austenitic stainless steel.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2000.10a
• /
• pp.20-25
• /
• 2000

lh deleterious Cr, Mo rich -$\sigma$phase is a hard embrittling precipitate, which forms between MU)-900 $^{\circ}C$, often associated with a reduction in both impact properties and corrosion reshame. On this study, After aging at MU) "C, fatigue crack propagation induced by a phase precipitation was evaluated and time-frequency analysis of acoustic emission was conducted It was possible to find fracture mechanism by a phase precipitation due to time-frequency anulysis of acoustic emission signals.nals.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.8 no.3
• /
• pp.179-192
• /
• 2008

A multiphase compensation method with mismatch linearization technique, is presented and demonstrated in a $\Sigma-\Delta$ fractional-N frequency synthesizer. An on-chip delay-locked loop (DLL) and a proposed delay line structure are constructed to provide multiphase compensation on $\Sigma-\Delta$ quantizetion noise. In the delay line structure, dynamic element matching (DEM) techniques are employed for mismatch linearization. The proposed $\Sigma-\Delta$ fractional-N frequency synthesizer is fabricated in a $0.18-{\mu}m$ CMOS technology with 2.14-GHz output frequency and 4-Hz resolution. The die size is 0.92 mm$\times$1.15 mm, and it consumes 27.2 mW. In-band phase noise of -82 dBc/Hz at 10 kHz offset and out-of-band phase noise of -103 dBc/Hz at 1 MHz offset are measured with a loop bandwidth of 200 kHz. The settling time is shorter than $25{\mu}s$.

• Korean Journal of Materials Research
• /
• v.4 no.8
• /
• pp.847-854
• /
• 1994

An amorphous single phase and coexistent amorphous and hcp-Mg phases in Mg-Zn-Ce system were found to form in the composition ranges of 20 to 40% Zn, 0 to 10% Ce and 5 to 20% Zn, 0 to 5% Ce, respectively. A $Mg_{85}Zn_{12}Ce_{3}$ amorphous alloy containing nanoscale hcp-Mg particles was found to form either by melt spinning or by heat treatment of melt -spun ribbon. The particle size of the hcp-Mg phase can be controlled in the range of 4 to 20 nm. The mixed phase alloy prepared thus has a good bending ductility and exhibits high ultimate tensile strength($\sigma_{B}$) ranging from 670 to 930 MPa and fracture elongation($\varepsilon_{f}$) of 5.2 to 2.0%. The highest specific strength($\sigma_{B}$/density =$\sigma_{s}$)$3.6 \times 10^5N \cdot m/kg$. It should be noted that the highest values of flB, US and ？1 are considerably higher than those (690MPa,$2.5 \times 10^5N \cdot m/kg$and 2.5%) for amorphous Mg-Zn-Ce alloys. The increase of the mechanical strengths by the formation of the mixed phase structure is presumably due to a dispersion hardening of the hcp supersaturated solution which has the hardness higher than that of the amorphous phase with the same composition.