The pyroelectricity of poly(vinylidenefluoride) films prepared by varying the draw ratio and the poling field was investigated. As the draw ratio and the electric field on poling of the drawn samples increased, so did the pyroelectric coefficient. But the effect of electric field on the pyroelectricity was greater than that of draw ratio. The pyroelectric and piezoelectric activities could be explained by the polarization using the thermally stimulated current. The relation between pyroelectric coefficient and piezoelectric stress constant showed a good linearity.

This paper shows the possibility of the application of the orientation density function of fibers to the mechanics of fibrous assembly. As an example, the orientation density function of a single yarn was theoretically derived in consideration of the idealized helical yarn. And the theoretical derivation of the tensile modulus of the fibrous assembly was performed in view of the fiber orientation. Application of this orientation density function to the obtained tensile modulus and to the contraction factor of the yarn was also performed so that the theoretical equations of the tensile modulus and the contraction factor of the yarn were obtained. Close agreement was shown between the theoretical and the existing equations. Consequently it was confirmed that the application of the orientation density function to the mechanics of the fibrous assembly is sufficiently possible.