This study has been performed to find out the effect of austenitizing temperature, austempering temperature and its holding time, and tempering cycle on the mechanical properties such as impact resistance, hardness etc. of AISI $M_2$ Mo series high speed tool steel austempered or tempered after austempering treatment. The results obtained from the experiment are as follows ; (1) Optical micrograph has revealed that the transformation rate of bainite is delayed as the austenitizing temperature increases and that bainite is most apparently transformed at an austempering temperature of $290^{\circ}C$. (2) The amount of retained austenite during austempering has been analysed to be increased by the X-ray diffraction technique as the transformation product of bainite is increased. It has also been shown that the longer the holding time of austempering, the more the transformation quantity of bainite is formed, exhibiting, however, that the rate of bainitic transformation is considerably retarded after a certain period of holding time elapses. (3) Hardness measurement has shown that hardness values obtained after austempering increase with decreasing the amount of retained austenite. (4) The austempering and then tempering cycle has been formed to give hardness values which are more greatly improved as austenitizing temperature is increased. (5) The mechanical property of the specimen primary-tempered for 1 hour at $550^{\circ}C$ after austempering for 2 hours at $290^{\circ}C$ from the austenitizing temperature range of $1180^{\circ}C$ to $1210^{\circ}C$ have been estimated to be good values.

The formation of high $T_c$ phase is very sluggish and c parameter of unit cell of high $T_c$ phase is about $37{\AA}$. High $T_c$ oxide superconductor with a $T_c$ above 100 K has been successfully prepared by solid state reaction method in BiSrCaCuO system by Pb adding. The microstructure related to the formation of the high $T_c$ phase has been investigated. As compared with YBCO compound, the formation reaction of the high $T_c$ requires long time heat treatment. It is due to the transformation from the low $T_c$ phase to high $T_c$ phase. The sintering just below the melting point of the calcined powder mixture is effective on the formation of the high $T_c$ phase in Pb-added BiSrCaCuO system. The growth of the high $T_c$ superconducting phase has a thin plate shape, which is characterized by the c parameter of $37{\AA}$. The formation of the high $T_c$ phases is delayed by the excessive addition of Pb. The lattice parameter(c) of the unit cell (both the low and high $T_c$ phases) is increased with increase of Pb.

This study was to investigate the influence of the substrate hardness on the hardness and adhesion of TiN thin film deposited by R.F. PACVD. Although the substrate hardness changed, chemical composition, stoichiometry and structure of TiN thin film did not change. ISE index was 1.96-1.99 for the substrate and was 1.57-1.79 for TiN thin film. And ISE index of TiN thin film was inverse proportion to the substrate hardness. When the substrate hardness was low, TiN thin film had many cracks around the indentation. But as the substrate hardness increased, TiN thin film had a few cracks and the deformation was limited within indentation. In having measured the adhesion of TiN thin film by SAT, the critical load (Lc) generally increased as the substrate hardness decreased.

Effects of aging treatment on the mechanical properties of a 18 Ni maraging steel were investigated by considering the reverted austenite. Specimens were heat treated by austenitizing at $840^{\circ}C$ for 1 hr and then aged for various times at $480^{\circ}C$ and $520^{\circ}C$. The main results obtained are as follows : 1) The amounts of reverted austenite are increased up to about 4% at $480^{\circ}C$ and about 22% at $520^{\circ}C$ with 1 to 48 hrs aging time. 2) Decreasing tendencies of impact energy and fracture toughness with increasing aging time are diminished after aging for 2 hrs at two aging temperatures of $480^{\circ}C$ and $520^{\circ}C$. 3) Peak hardness and yield strength are obtained after aging for 4 hrs at $480^{\circ}C$ and 2 hrs at $520^{\circ}C$ respectively. From the above results, it was concluded that the optimum aging condition with which showed good strength and toughness combination are given to be $480^{\circ}C$ for 4 hrs and $520^{\circ}C$ for 2 hrs.

In this study, the effect of solution treatment temperature on the tensile property in intermediate thermo-mechanical treated Al-Li alloys are investigated. After the intermediate thermo-mechanical treated Al-Li, Al-Li-Mg and Al-Li-Mg-Zr alloys were solution treated at various temperatures (500, 520 and $540^{\circ}C$), these were aged at $190^{\circ}C$, $240^{\circ}C$ and tested tensile properties. The results obtained from the experiment are as follows ; 1) The optimum solution heat-treatment temperature is $540^{\circ}C$ for a Al-Li alloy, and the recrystallized grain size is about $70{\mu}m$. 2) The optimum solution heat-treatment temperature is $500^{\circ}C$ for a Al-Li-Mg alloy, and the recrystallized grain size is the most coarse in all alloys. 3) The tensile property is independent of the solution treatment temperature in a Al-Li-Mg-Zr alloy, and the recrystallized grain size is the finest owing to addition of Zr.